CN109793272B - 用于新型加热不燃烧烟草中的花香香线的制备方法和应用 - Google Patents
用于新型加热不燃烧烟草中的花香香线的制备方法和应用 Download PDFInfo
- Publication number
- CN109793272B CN109793272B CN201910092307.1A CN201910092307A CN109793272B CN 109793272 B CN109793272 B CN 109793272B CN 201910092307 A CN201910092307 A CN 201910092307A CN 109793272 B CN109793272 B CN 109793272B
- Authority
- CN
- China
- Prior art keywords
- floral
- parts
- weight
- heating non
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种用于加热不燃烧烟草中的花香香线的制备方法及应用。所述花香香线是由花香含香微胶囊、聚乳酸、共混材料、增塑剂混合均匀后置于熔融纺丝机进行纺丝，其中所述花香香型含香微胶囊是将明胶及多糖按照质量比1：1.0～1.5的比例混合，然后将混合物溶于水中制备成混合物浓度为0.5％～2.0％的壁材溶液，然后加入花香香型的香精连续搅拌乳化后调节pH至3.5～4.2，加入固化剂，并调节pH至6.0～7.0，将体系加热升温至35±5℃，固化1～4h，停止搅拌，静置，抽滤，并洗去微囊表面残留的固化剂，室温下干燥得粉末状样品。将花香香型香线添加到加热不燃烧卷烟滤棒中醋纤段，高温烟气通过时丝线可缓释香味，从而使加热不燃烧卷烟香味持久。
Description
技术领域
本发明涉及一种用于新型加热不燃烧烟草中的花香香线的制备方法和应用，属于新型烟草领域。
背景技术
加热不燃烧烟草是通过特殊的加热源对烟丝进行加热，加热时烟丝中的尼古丁及香味物质通过挥发产生烟气来满足吸烟者需求的一种新型烟草制品。与传统卷烟相比，加热不燃烧卷烟的重大变化之一在于消费过程中烟草材料所处的环境温度较低。传统卷烟的燃烧锥温度最高可达950℃，卷烟烟丝可通过蒸馏、裂解和燃烧等复杂的反应途径形成几千种产物；对于加热不燃烧卷烟，消费者使用时烟草材料所处温度一般低于500℃，且主要通过烟草材料的热解反应产生烟气。因此，消费者生理满足感不强，香气丰富性不够，是目前新型烟草制品相对于传统卷烟而言普遍存在的问题。
通过加香加料技术提升消费者抽吸加热不燃烧烟草制品时的生理满足感和香气丰富性，是行之有效的手段。传统的加香工艺是将香料按一定比例均匀喷洒到烟丝中，然而由于加热不燃烧卷烟独特的抽吸方式，在抽吸过程中，前几口风味充足，而后几口香味已非常淡薄，香料的释放不均匀、不持久。
香线材料一般采用棉纤维或香烟中允许使用的一些合成纤维，将香线浸泡在香精香料溶液中通过纤维丝束的物理吸附将其固定在香线上。当烟气通过时利用烟气的高温将香精香料释放出来。通过调节香精香料的配方和添加量来控制其在烟气中的释放量和释放速度。专利CN201710984544.X公开了一种加热不燃烧卷烟专用橙花风味香精及其制备方法，包括糖苷类香料前体，具有缓释作用，但热不燃烧烟草制品的烟草原料吸收能力较差，加入到烟草原料中的香料很容易因机械挤压而流失，导致香味物质含量低；专利CN105595415A公开了一种利用荔枝花蜜制备蜜香卷烟香线的方法，将植物短纤维浸泡在荔枝花蜜香料液中，风干得到蜜香卷烟香线。通过浸泡法制得的香线，在滤嘴的成型过程中会有部分的香精香料提早释放出来造成损失。在香烟的存储和运输过程中，由于没有有效的屏蔽，也会有香精香料部分逸出造成吸味达不到要求。更为稳定的添加和释放香精香料是香线亟待解决的问题。
发明内容
本发明根据现有技术的不足，提供一种用于新型加热不燃烧烟草中的花香香线的制备方法和应用，该方法是采用复凝聚法将沸点在200～300℃的香精包裹于微胶囊内，含香微胶囊再与成丝基材进行熔融纺丝，在纺丝过程中香料不直接受热，可抑制加工过程中香料受热分解，减少香料散失，烟气通过时微囊壁上的微隙可缓释香味，从而使加热不燃烧卷烟香味持久。
本发明提供的技术方案为：所述一种用于新型加热不燃烧烟草中的花香香线的制备方法，其特征在于具体步骤如下：
(1)花香型含香微胶囊的制备：
a.将明胶及多糖按照质量比1：1.0～1.5的比例混合配制成壁材原料，然后将壁材原料溶于水中，在温度50～65℃的搅拌条件下制备成壁材原料浓度为0.5％～2.0％的壁材溶液；
b.按照以下重量份数配制花香香精：月桂油20～30份、肉桂醇40～50份、苯乙醛5～15份、三醋酸甘油酯5～15份、乙基香兰素葡糖苷5～15份；将上述物质混合均匀配制成花香香精；
c.取步骤b中配制的花香香精按照花香精与步骤a中的壁材原料质量比1：0.4～1.5的比例加入步骤a中制备的壁材溶液中，并在500～800rpm的转速下连续搅拌乳化10～15min，乳化结束后，保持乳化溶液温度35±5℃，加入10％柠檬酸溶液缓慢调节pH至3.5～4.2，并在400～500rpm下恒温搅拌15～30min；
d.将步骤c中搅拌后的溶液降温至10±3℃，然后按照固化剂与明胶的质量比为0.01～0.2:1的比例加入固化剂，调节pH至6.0～7.0，然后将体系加热升温至35±5℃，固化1～4h，停止搅拌，静置，抽滤，并洗去微囊表面残留的固化剂，室温下干燥得粉末状样品即为花香香型含香微胶囊；
(2)取步骤(1)中制备的花香型含香微胶囊、聚乳酸、共混材料、增塑剂按照质量比0.05～0.15：1：0.1～0.15：0.02～0.08的比例混合均匀，其中所述共混材料包括聚苯乙烯、聚乙烯、聚丙烯、聚酯树脂中的任意一种或多种；所述增塑剂包括甘油、聚乙二醇、聚乙烯醇、ε-己内酯、马来酸酐中的任意一种或多种；
(3)将步骤(2)中的混合原料置于熔融纺丝机进行纺丝，其熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为170～190℃、160～180℃、150～160℃，纺丝速率为1000～2000m/min，热定温度为60～70℃，牵伸速度200～300m/min，牵伸倍数2.8～3.2，纺丝直径为0.8～1.5mm。
本发明较优的技术方案：所述一种用于加热不燃烧烟草中的花香香线的制备方法，其特征在于所述步骤(1)中的花香型含香微胶囊的制备过程如下：
a.将45重量份的明胶、25重量份的鼠李糖和30重量份的改性淀粉作为壁材原料溶解于55℃的热水中，配制成浓度为1％的壁材溶液；
b.将45重量份的月桂油、25重量份的肉桂醇、10重量份的苯乙醛、三醋酸甘油酯10份、乙基香兰素葡糖苷10份混合均匀配制成花香香精备用；
c.取130重量份步骤b中配制的花香香精，然后加入步骤a中配制的壁材溶液中，在650rpm的连续搅拌下乳化15min，保持溶液温度35℃，加入10％柠檬酸溶液缓慢调节pH至3.8，并在450rpm下恒温搅拌20min；
d.然后将步骤c中的溶液采用冰水浴降低温度至10℃，加入1.35重量份的戊二醛、0.9重量份的乙二醛用5％NaOH溶液调节pH至7，然后体系水浴加热升温至40℃，固化1h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得粉末状样品即为花香香型含香微胶囊。
本发明较优的技术方案：所述步骤(1)的a步骤中多糖包括果糖、鼠李糖、羧甲基壳聚糖、海藻酸钠、环糊精、改性淀粉中的一种或任意几种；d步骤中溶液采用冰水浴降温；采用水浴加热升温；采用浓度5％的NaOH溶液调节pH至6.0～7.0；d步骤中的固化剂包括戊二醛、乙二醛、转谷氨酰胺酶(TG酶)中的任意一种或多种，或固化剂为茶多酚、葡多酚、苹果多酚、可可多酚中的任意一种或多种
本发明较优的技术方案：所述步骤(2)中的纺丝原料是花香型含香微胶囊、聚乳酸、聚丙烯、聚乙烯醇、ε-己内酯按质量比0.1:1:0.13:0.02:0.05的比例混合均匀得到。
本发明较优的技术方案：所述步骤(3)中熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为190℃、180℃、160℃，纺丝速率为1200m/min，热定温度为70℃，牵伸速度240m/min，牵伸倍数3.0，纺丝直径为1.2mm。
本发明中的香精原料均为直接购买的产品。
本发明提供一种用于加热不燃烧烟草中的花香香线的制备方法的应用，其特征在于：将上述方法制备的用于加热不燃烧烟草中的花香香线添加到加热不燃烧卷烟滤棒中醋酸纤维段中按照常规的方法卷制成加热不燃烧卷烟。
本发明采用复凝聚法将沸点在200～300℃的香精包裹于微胶囊内，含香微胶囊再与成丝基材进行熔融纺丝，在纺丝过程中香料不直接受热，可抑制加工过程中香料受热分解，减少香料散失，烟气通过时微囊壁上的微隙可缓释香味，从而使加热不燃烧卷烟香味持久。本发明中的香线是通过纺丝技术一次成型或对所纺丝线进行后处理，制备的香线具有稳定的添加和释放香精香料的能力，并同过纺丝的过程对香精香料的释放达到可控的目的，将其添加到加热不燃烧卷烟滤棒中醋纤段，高温烟气通过时丝线可缓释香味，从而使加热不燃烧卷烟香味持久。
具体实施方式
为了更好地解释本发明，以下结合具体实施例对本发明作进一步的详细说明，但它们不对本发明构成限定。
以下实施例中的花香香精是由以下重量份数的物质制成：月桂油25份、肉桂醇45份、苯乙醛10份、三醋酸甘油酯10份、乙基香兰素葡糖苷10份配置成香精备用，将上述物质混合均匀配制成花香精。
以下实施例中的所有的物质份数均为重量份数。
实施例1提供的一种用于加热不燃烧烟草中的花香型含香微胶囊，其制备方法如下：将明胶45份、羧甲基壳聚糖25份、改性淀粉30份溶解于55℃热水中，溶液浓度为1％，加入130份上述花香香精，在650rpm的连续搅拌下乳化15min，保持溶液温度35℃，加入10％柠檬酸溶液缓慢调节pH至3.8，在450rpm下恒温搅拌20min；冰水浴降低溶液温度至10℃，加入戊二醛1.35份、乙二醛0.9份，用5％NaOH溶液调节pH至7.0；体系水浴加热升温至40℃，固化1h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得粉末状样品即为花香型含香微胶囊。
将实施例1中制备的花香型含香微胶囊、聚乳酸、聚丙烯、聚乙烯醇、ε-己内酯按质量比0.1:1:0.13:0.02:0.05混合均匀后，用熔融纺丝机进行纺丝，熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为190℃、180℃、160℃，纺丝速率为1200m/min，热定温度为70℃，牵伸速度240m/min，牵伸倍数3.0，纺丝直径为1.2mm，制备得到花香香线样品A。
上述方法制备的花香香线样品A添加到电加热卷烟滤棒中醋纤段，卷制得到加热不燃烧卷烟样品A。
实施例2提供的一种用于加热不燃烧烟草中的花香型含香微胶囊，其制备方法如下：将明胶45份、羧甲基壳聚糖25份、改性淀粉30份溶解于55℃热水中，溶液浓度为1％，加入130份上述花香香精，在650rpm的连续搅拌下乳化15min，保持溶液温度35℃，加入10％柠檬酸溶液缓慢调节pH至3.8，在450rpm下恒温搅拌20min；冰水浴降低溶液温度至10℃，加入戊二醛1.35份、乙二醛0.9份，用5％NaOH溶液调节pH至7.0；体系水浴加热升温至40℃，固化1h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得粉末状样品即为花香型含香微胶囊。
将实施例2中制备的花香型含香微胶囊、聚乳酸、聚酯树脂、甘油按质量比0.08:1:0.1:0.05混合均匀后，用熔融纺丝机进行纺丝，熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为190℃、180℃、170℃，纺丝速率为1200m/min，热定温度为65℃，牵伸速度240m/min，牵伸倍数3.0，纺丝直径为1.2mm，制备得到花香香线样品B。
上述方法制备的花香香线样品B添加到电加热卷烟滤棒中醋纤段，卷制得到加热不燃烧卷烟样品B。
对照例1：将普通棉线浸泡在上述花香香精中30min，常温风干得到花香香线样品C，然后将花香香线样品C加入滤棒中卷制得到加热不燃烧卷烟样品C。
对照例2：将上述花香香精按质量分数12％加入新型烟草卷烟薄片涂布液中，制得加热不燃烧卷烟样品D。
针对实施例1、2和对比例1中制备的香线热稳定性测试：将香线样品分别在30℃、50℃、80℃、100℃四种不同的温度下，加热8h时，测试其香精的挥发质量(单位：毫克)，详见表1：
表1为三种香线在不同温度下香精挥发量
针对四个实施例中制备的加热不燃烧卷烟逐口烟气中香精含量测试：利用加热不燃烧产品加热器具在10孔道直线型吸烟机上对添加香线的卷烟进行逐口烟气抽吸，具体抽吸参数：抽吸容量50mL，抽吸持续时间2s，抽吸间隔30s，测试主流烟气中的香精含量(单位：微克)，详见表2：
表2四个实施例中的在加热不燃烧卷烟逐口烟气中香精含量
从结果可知，采用本技术方案制备的香线A、B在热稳定性较好，香料散失较少，同时在抽吸时释放香气更均匀、持久。
Claims (2)
1.一种用于新型加热不燃烧烟草中的花香香线的制备方法，其特征在于具体步骤如下：
（1）花香型含香微胶囊的制备：
a. 将45重量份的明胶、25重量份的鼠李糖和30重量份的改性淀粉作为壁材原料溶解于55℃的热水中，配制成浓度为1%的壁材溶液；
b. 将45重量份的月桂油、25重量份的肉桂醇、10重量份的苯乙醛、三醋酸甘油酯10份、乙基香兰素葡糖苷10份混合均匀配制成花香香精备用；
c. 取130重量份步骤b中配制的花香香精，然后加入步骤a中配制的壁材溶液中，在650rpm的连续搅拌下乳化15min，保持溶液温度35℃，加入10%柠檬酸溶液缓慢调节pH至3.8，并在450rpm下恒温搅拌20min；
d. 然后将步骤c中的溶液采用冰水浴降低温度至10℃，加入1.35重量份的戊二醛、0.9重量份的乙二醛用5%NaOH溶液调节pH至7，然后体系水浴加热升温至40℃，固化1h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得粉末状样品即为花香香型含香微胶囊；
（2）取步骤（1）中制备的花香型含香微胶囊、聚乳酸、聚丙烯、聚乙烯醇、ε-己内酯按质量比0.1:1:0.13:0.02:0.05的比例混合均匀得到混合原料；
（3）将步骤（2）中的混合原料置于熔融纺丝机进行纺丝，其熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为190℃、180℃、160℃，纺丝速率为1200m/min，热定温度为70℃，牵伸速度240m/min，牵伸倍数3.0， 纺丝直径为1.2mm。
2.一种基于权利要求1中的所述制备方法制备的用于加热不燃烧烟草中的花香香线的应用，其特征在于：将用于加热不燃烧烟草中的花香香线添加到加热不燃烧卷烟滤棒中醋酸纤维段中，按照常规的方法卷制成加热不燃烧卷烟。