CN109776890A - 一种高弹耐磨的减震橡胶 - Google Patents
一种高弹耐磨的减震橡胶 Download PDFInfo
- Publication number
- CN109776890A CN109776890A CN201910140644.3A CN201910140644A CN109776890A CN 109776890 A CN109776890 A CN 109776890A CN 201910140644 A CN201910140644 A CN 201910140644A CN 109776890 A CN109776890 A CN 109776890A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- resistant
- elastic wear
- promotor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种高弹耐磨的减震橡胶,所述震橡胶的原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶40‑60份、天然橡胶20‑35份、氯丁橡胶15‑35份、改性玻璃纤维10‑15份、硬质陶土18‑23份、钛酸酯偶联剂2‑6份、环氧树脂8‑15份、3‑苯并三氮唑4‑8份、N‑环己基硫代邻苯二甲酰胺3‑7份、硫磺5‑8份、氧化锌7‑10份、促进剂3‑4份、防老剂4‑6份、炭黑25‑35份、油料2‑4份、石蜡1‑5份。本发明制备的高弹耐磨的减震橡胶,具有较高的弹性、耐磨性、耐腐蚀性、耐热性、抗拉型强、耐老化性高,本橡胶弹性高,有效的吸收汽车的震动时的力,提供车辆的舒适性。
Description
技术领域
本发明涉及一种减震橡胶,具体涉及一种高弹耐磨的减震橡胶。
背景技术
为提供车辆的舒适性,汽车大量采用高弹耐磨的减震橡胶件,当汽车受冲击产生振动时可改善汽车行驶平顺性,橡胶减震垫的特点是既有高弹性,又有高黏性。橡胶的弹性是由其卷曲分子构象的变化产生的,橡胶分子间相互作用会妨碍分子链的运动,从而表现出黏性阻尼的特点,以致应力与应变往往处于不平衡状态,在现有汽车行驶过程中,高弹耐磨的减震橡胶件的作用十分重要,高弹耐磨的减震橡胶件的弹性、耐磨性、耐腐蚀性、耐热性、抗拉型、耐老化性能显得十分必要,亟待提高。
发明内容
发明目的:本发明的目的是为了解决现有技术中的不足,提供一种高弹耐磨的减震橡胶,解决上述问题。
技术方案:本发明所述的一种高弹耐磨的减震橡胶,所述震橡胶的配方是由高顺式丁二烯橡胶、天然橡胶、氯丁橡胶、改性玻璃纤维、硬质陶土、钛酸酯偶联剂、环氧树脂、3-苯并三氮唑、N-环己基硫代邻苯二甲酰胺、硫磺、氧化锌、促进剂、防老剂、炭黑、油料、石蜡;其原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶40-60份、天然橡胶20-35份、氯丁橡胶15-35份、改性玻璃纤维10-15份、硬质陶土18-23份、钛酸酯偶联剂2-6份、环氧树脂8-15份、3-苯并三氮唑4-8份、N-环己基硫代邻苯二甲酰胺3-7份、硫磺5-8份、氧化锌7-10份、促进剂3-4份、防老剂4-6份、炭黑25-35份、油料2-4份、石蜡1-5份。
优选的,所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶40份、天然橡胶20份、氯丁橡胶15份、改性玻璃纤维10份、硬质陶土18份、钛酸酯偶联剂2份、环氧树脂8份、3-苯并三氮唑4份、N-环己基硫代邻苯二甲酰胺3份、硫磺5份、氧化锌70份、促进剂3份、防老剂4份、炭黑25-35份、油料2份、石蜡1份。
优选的,所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶50份、天然橡胶30份、氯丁橡胶24份、改性玻璃纤维12份、硬质陶土19份、钛酸酯偶联剂4份、环氧树脂10份、3-苯并三氮唑6份、N-环己基硫代邻苯二甲酰胺5份、硫磺6份、氧化锌8份、促进剂3.3份、防老剂4.8份、炭黑30份、油料2.8份、石蜡2份。
优选的,所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶60份、天然橡胶35份、氯丁橡胶35份、改性玻璃纤维15份、硬质陶土23份、钛酸酯偶联剂6份、环氧树脂15份、3-苯并三氮唑8份、N-环己基硫代邻苯二甲酰胺7份、硫磺8份、氧化锌10份、促进剂4份、防老剂6份、炭黑35份、油料4份、石蜡5份。
有益效果:本发明制备的高弹耐磨的减震橡胶,具有较高的弹性、耐磨性、耐腐蚀性、耐热性、抗拉型强、耐老化性高,本橡胶弹性高,有效的吸收汽车的震动时的力,提供车辆的舒适性。
具体实施方式
实例一
一种高弹耐磨的减震橡胶,所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶40份、天然橡胶20份、氯丁橡胶15份、改性玻璃纤维10份、硬质陶土18份、钛酸酯偶联剂2份、环氧树脂8份、3-苯并三氮唑4份、N-环己基硫代邻苯二甲酰胺3份、硫磺5份、氧化锌70份、促进剂3份、防老剂4份、炭黑25-35份、油料2份、石蜡1份。
实例二
一种高弹耐磨的减震橡胶,所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶50份、天然橡胶30份、氯丁橡胶24份、改性玻璃纤维12份、硬质陶土19份、钛酸酯偶联剂4份、环氧树脂10份、3-苯并三氮唑6份、N-环己基硫代邻苯二甲酰胺5份、硫磺6份、氧化锌8份、促进剂3.3份、防老剂4.8份、炭黑30份、油料2.8份、石蜡2份。
实例三
一种高弹耐磨的减震橡胶,所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶60份、天然橡胶35份、氯丁橡胶35份、改性玻璃纤维15份、硬质陶土23份、钛酸酯偶联剂6份、环氧树脂15份、3-苯并三氮唑8份、N-环己基硫代邻苯二甲酰胺7份、硫磺8份、氧化锌10份、促进剂4份、防老剂6份、炭黑35份、油料4份、石蜡5份。
本发明制备的高弹耐磨的减震橡胶,具有较高的弹性、耐磨性、耐腐蚀性、耐热性、抗拉型强、耐老化性高。
以上所述,仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,虽然本发明已以较佳实施例揭露如上,然而并非用以限定本发明,任何熟悉本专业的技术人员,在不脱离本发明技术方案范围内,当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例,但凡是未脱离本发明技术方案的内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (4)
1.一种高弹耐磨的减震橡胶,其特征在于:所述震橡胶的配方是由高顺式丁二烯橡胶、天然橡胶、氯丁橡胶、改性玻璃纤维、硬质陶土、钛酸酯偶联剂、环氧树脂、3-苯并三氮唑、N-环己基硫代邻苯二甲酰胺、硫磺、氧化锌、促进剂、防老剂、炭黑、油料、石蜡;其原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶40-60份、天然橡胶20-35份、氯丁橡胶15-35份、改性玻璃纤维10-15份、硬质陶土18-23份、钛酸酯偶联剂2-6份、环氧树脂8-15份、3-苯并三氮唑4-8份、N-环己基硫代邻苯二甲酰胺3-7份、硫磺5-8份、氧化锌7-10份、促进剂3-4份、防老剂4-6份、炭黑25-35份、油料2-4份、石蜡1-5份。
2.根据权利要求1所述一种高弹耐磨的减震橡胶,其特征在于:所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶40份、天然橡胶20份、氯丁橡胶15份、改性玻璃纤维10份、硬质陶土18份、钛酸酯偶联剂2份、环氧树脂8份、3-苯并三氮唑4份、N-环己基硫代邻苯二甲酰胺3份、硫磺5份、氧化锌70份、促进剂3份、防老剂4份、炭黑25-35份、油料2份、石蜡1份。
3.根据权利要求1所述一种高弹耐磨的减震橡胶,其特征在于:所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶50份、天然橡胶30份、氯丁橡胶24份、改性玻璃纤维12份、硬质陶土19份、钛酸酯偶联剂4份、环氧树脂10份、3-苯并三氮唑6份、N-环己基硫代邻苯二甲酰胺5份、硫磺6份、氧化锌8份、促进剂3.3份、防老剂4.8份、炭黑30份、油料2.8份、石蜡2份。
4.根据权利要求1所述一种高弹耐磨的减震橡胶,其特征在于:所述高弹耐磨的减震橡胶原料组合物包括如下重量份数的各组分:高顺式丁二烯橡胶60份、天然橡胶35份、氯丁橡胶35份、改性玻璃纤维15份、硬质陶土23份、钛酸酯偶联剂6份、环氧树脂15份、3-苯并三氮唑8份、N-环己基硫代邻苯二甲酰胺7份、硫磺8份、氧化锌10份、促进剂4份、防老剂6份、炭黑35份、油料4份、石蜡5份。