CN109752397B - 一种探测非晶合金的团簇类型的方法 - Google Patents

一种探测非晶合金的团簇类型的方法 Download PDF

Info

Publication number
CN109752397B
CN109752397B CN201811416082.2A CN201811416082A CN109752397B CN 109752397 B CN109752397 B CN 109752397B CN 201811416082 A CN201811416082 A CN 201811416082A CN 109752397 B CN109752397 B CN 109752397B
Authority
CN
China
Prior art keywords
amorphous alloy
crystallization
alloy strip
adopting
dsc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201811416082.2A
Other languages
English (en)
Other versions
CN109752397A (zh
Inventor
蔡安辉
安琪
冯艳娇
周果君
丁超义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Institute of Science and Technology
Original Assignee
Hunan Institute of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hunan Institute of Science and Technology filed Critical Hunan Institute of Science and Technology
Priority to CN201811416082.2A priority Critical patent/CN109752397B/zh
Publication of CN109752397A publication Critical patent/CN109752397A/zh
Application granted granted Critical
Publication of CN109752397B publication Critical patent/CN109752397B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于新材料领域，公开了一种探测非晶合金的团簇类型的方法。真空甩带法制备Zr65Al8Ni8.5Cu18.5非晶合金条带，采用DSC技术在20K/min的升温速度下研究非晶合金条带的晶化动力学行为，该非晶合金条带的起始阶段的晶化指数为1.7，表明该非晶合金的晶化过程的晶化核直接来源于非晶合金中所对应的团簇；对非晶合金条带采用DSC技术在20K/min的升温速度下升温到不同温度下进行热处理，X射线衍射技术检测热处理后的条带中只包含Zr6Al2Ni和Zr2Cu两种纳米晶化相，综合两种方法可判定出该非晶合金中只包含Zr6Al2Ni和Zr2Cu类型的团簇。

Description

一种探测非晶合金的团簇类型的方法
技术领域
本发明涉及一种探测非晶合金的团簇类型的方法。
背景技术
非晶合金具有优异的物理化学性能，这些特点来源于非晶合金的短程有序和长程无序的特殊结构，使得其在结构和功能材料领域中具有极大的应用前景。虽然通过模拟方法和高技术手段可以间接推断出或直接看到非晶合金中包含有短程有序甚至中程有序结构，另一方面，通过模拟和实验手段还可以推断出短程/中程有序的连接关系，但是，这些短程/中程有序结构的类型仍然无法清析判断，因此，如何通过实验和分析手段判定非晶合金中的短程/中程有序的种类，即团簇的类型，显得非常迫切，为建立非晶合金的微结构与性能间的定量或定性的关系具有非常重要的意义。
发明内容
本发明的目的在于提供一种探测非晶合金的团簇类型的方法。
本发明的目的是通过下述技术方案实现的：一种探测非晶合金的团簇类型的方 法，其特征在于：包括如下步骤:
Figure 139855DEST_PATH_IMAGE001
Zr65Al8Ni8.5Cu18.5非晶合金条带在20K/min的升温速度下 通过DSC测试获得其DSC曲线，采用JMAK方程得到其起始阶段的晶化指数为1.7，判定其晶化 过程的晶化核直接来源于其内部的团簇；
Figure 894184DEST_PATH_IMAGE002
所述非晶合金条带的热处理是采用DSC技术以 20K/min的升温速度分别升温到460℃、475℃、480℃、485℃和600℃，其晶化相类型采用XRD 技术鉴定，热处理后的非晶合金条带只有Zr6Al2Ni和Zr2Cu两种晶化相；③结合步骤
Figure 631196DEST_PATH_IMAGE001
和
Figure 216898DEST_PATH_IMAGE002
的结果，既然上述非晶合金条带的晶化过程的晶化核直接来源于其内部的团簇，而非晶合 金条带经过不同温度热处理后，条带中只有Zr6Al2Ni和Zr2Cu两种晶化相，表明所述非晶合 金条带在热处理过程中的晶化相不是由其他晶化相转变而成，即没有相变发生，因此，上述 非晶合金条带中只有Zr6Al2Ni和Zr2Cu两种团簇。
本发明制成的产品分别用X射线衍射仪（XRD）检测材料的非晶态结构以及晶化相的种类、用差热扫描量热计（DSC）获得非晶合金条带的DSC曲线，用JMAK方程研究非晶合金条带的晶化动力学。
具体实施方式
下面根据具体实施例对本发明作进一步说明：
实施例1
Zr65Al8Ni8.5Cu18.5非晶合金条带在20K/min的升温速度下通过DSC测试获得其DSC曲线，采用JMAK方程得到其起始阶段的晶化指数为1.7，判定其晶化过程的晶化核直接来源于其内部的团簇；将非晶合金条带通过DSC以20K/min的升温速度升温到460℃后，随炉冷却到室温，采用XRD技术检测热处理后的非晶合金条带只有Zr6Al2Ni和Zr2Cu两种晶化相。
实施例2
Zr65Al8Ni8.5Cu18.5非晶合金条带在20K/min的升温速度下通过DSC测试获得其DSC曲线，采用JMAK方程得到其起始阶段的晶化指数为1.7，判定其晶化过程的晶化核直接来源于其内部的团簇；将非晶合金条带通过DSC以20K/min的升温速度升温到480℃后，随炉冷却到室温，采用XRD技术检测热处理后的非晶合金条带只有Zr6Al2Ni和Zr2Cu两种晶化相。
实施例3
Zr65Al8Ni8.5Cu18.5非晶合金条带在20K/min的升温速度下通过DSC测试获得其DSC曲线，采用JMAK方程得到其起始阶段的晶化指数为1.7，判定其晶化过程的晶化核直接来源于其内部的团簇；将非晶合金条带通过DSC以20K/min的升温速度升温到600℃后，随炉冷却到室温，采用XRD技术检测热处理后的非晶合金条带只有Zr6Al2Ni和Zr2Cu两种晶化相。

Claims (1)

1.一种探测非晶合金的团簇类型的方法，其特征在于：所述的方法是结合Zr65Al8Ni8.5Cu18.5非晶合金条带的晶化动力学和热处理后的非晶合金条带的晶化相类型而得出的;所述的Zr65Al8Ni8.5Cu18.5非晶合金条带的晶化动力学，是将所述的非晶合金条带在20K/min的升温速度下通过DSC测试获得其DSC曲线，采用JMAK方程得到其起始阶段的晶化指数为1.7，判定其晶化过程的晶化核直接来源于其内部的团簇；所述的热处理后的Zr65Al8Ni8.5Cu18.5非晶合金条带的晶化相类型，是采用DSC技术以20K/min的升温速度分别升温到460℃、475℃、480℃、485℃和600℃对所述非晶合金条带进行热处理，其晶化相类型采用XRD技术鉴定，热处理后的非晶合金条带只有Zr6Al2Ni和Zr2Cu两种晶化相，表明所述非晶合金条带中只有上述两种团簇。
CN201811416082.2A 2018-11-26 2018-11-26 一种探测非晶合金的团簇类型的方法 Active CN109752397B (zh)