CN109747312A - The component for applying enamel of decoration - Google Patents
The component for applying enamel of decoration Download PDFInfo
- Publication number
- CN109747312A CN109747312A CN201910097005.3A CN201910097005A CN109747312A CN 109747312 A CN109747312 A CN 109747312A CN 201910097005 A CN201910097005 A CN 201910097005A CN 109747312 A CN109747312 A CN 109747312A
- Authority
- CN
- China
- Prior art keywords
- copper sheet
- enamel
- layer
- glaze layer
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the components for applying enamel of decoration, including copper sheet, ground glaze layer is provided at the top of copper sheet, cover coat is provided at the top of ground glaze layer, it is provided with glazed colour layer at the top of cover coat, the inside of glazed colour layer opens up fluted, and the groove is internally provided with top glaze layer, step 1: copper material being struck out to the copper sheet of 32mm diameter by stamping die, is then polished by sander copper sheet；Step 2: by flush coater in the upper surface even application glaze of copper sheet, forming ground glaze layer in the upper surface of copper sheet.The floral designs that the present invention is suppressed by mold, compared with silk-screen and air brushing, operation difficulty substantially reduces, operating procedure greatly reduces, and upper identical as production powdered frit in raw material materials, feeding is convenient, without worrying the ground coat enamel of glaze and bottom embryo, the matching problem of overglaze, the production that next workpiece can also be carried out using the production clout polished off, effectively reduces production cost, is conducive to people's use.
Description
Technical field
The present invention relates to decorated enamel sheet component technology fields, and that specially decorates applies the component of enamel.
Background technique
Enamel is also known as Buddhist youth, strokes youth, turns blue, and is with raw materials such as the silicon of minerals, red lead, borax, feldspar, quartz according to suitable
When ratio mix, be separately added into the metal oxide of various colour generations, be fired after grinding powdered color material being made, then according to it
The different ways of enamel technique are filled out embedding or are drawn on and are done on the body of tire with metal, fired and become enamelwork, and high temperature is saturating
Bright enamel: being the enamel fired with the marzacotto of high-temperature fusion.
With social economy, culture develop by leaps and bounds, people life just from it is simply having adequate food and clothing step into it is fairly well-off, advocate human nature and when
Still, individual character and glamour are constantly moulded, it has also become the pursuit of people, nowadays clock and watch have not been singly a kind of tool for showing the time, and
Be more it as a kind of ornament come using, currently, in existing market enamel artistic plate production be substantially divided to two classes,
It is air brushing that one kind, which is silk-screen, one kind,；However, either silk-screen or air brushing, when carrying out pattern production, operating procedure compares
Complexity, operation difficulty is also higher, requires a great deal of time and energy, generally requires the cost of manufacture of great number, is unfavorable for people
Use.
Summary of the invention
The purpose of the present invention is to provide the component for applying enamel of decoration, the component for applying enamel for having decoration is convenient for
The advantages of use, solves the problems, such as that dial plate decoration is inconvenient.
To achieve the above object, the invention provides the following technical scheme: the component for applying enamel of decoration, including copper sheet,
It is provided with ground glaze layer at the top of the copper sheet, cover coat, the top setting of the cover coat are provided at the top of the ground glaze layer
There is a glazed colour layer, the inside of the glazed colour layer opens up fluted, and the groove is internally provided with top glaze layer.
Preferably, the glazed colour layer with a thickness of 100-200um, the depth of the groove is 80-150um, the top glaze
Layer with a thickness of 80-150um.
The component production method for applying enamel of decoration, comprising the following steps:
Step 1: copper material being struck out to the copper sheet of 32mm diameter by stamping die, then copper sheet is carried out by sander
Polishing；
Step 2: by flush coater in the upper surface even application glaze of copper sheet, forming ground glaze layer in the upper surface of copper sheet；
Step 3: the copper sheet for being coated with ground glaze layer being put into dryer and is dried, is linked together to ground glaze layer and copper sheet
When, in the upper surface of ground glaze layer glaze is sprayed by flush coater again, forms cover coat in the upper surface of ground glaze layer；
Step 4: the copper sheet for being coated with cover coat being put into dryer and is dried, is linked as one to cover coat and ground glaze layer
When body, colored glaze is sprayed by flush coater in the upper surface of cover coat, forms glazed colour layer in the upper surface of cover coat；
Step 5: the copper sheet for being coated with glazed colour layer being placed again into dryer and is dried, is connected to glazed colour layer and cover coat
When being integrated, copper sheet is put into die casting, the inside of glazed colour layer is struck out to the groove of decorative pattern shape；
Step 6: will open up reeded copper sheet be put into cellar furnace in be fired, obtain enamel component crude product；
Step 7: spraying top glaze layer in the groove on enamel component crude product by flush coater, then will be coated with top glaze layer
Copper sheet be placed again into dryer and be dried, when pushing up glaze layer and groove is linked together, copper sheet taking-up is cooled down；
Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer outside groove will be overflowed
Polishing removal；
Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
Preferably, the drying temperature of the dryer in step 3 is 20-60 DEG C, and the drying time is 5-10min.
Preferably, the drying temperature of the dryer in step 4 is 30-70 DEG C, and the drying time is 8-15min.
Preferably, the drying temperature of the dryer in steps of 5 is 40-80 DEG C, and the drying time is 10-18min,
The quantity of the groove is 7, groove arranged in a manner of constituting decorative pattern.
Preferably, it is 600-900 DEG C that the copper sheet in step 6, which is put into the temperature fired in the furnace of cellar, the firing time
For 2-10min.
Preferably, the drying temperature of the dryer in step 7 is 50-90 DEG C, and the drying time is 12-20min.
Preferably, it is 750-850 DEG C that the crude product of enamel in step 8, which is put into the temperature fired again in the furnace of cellar, described
Firing time is 4-8min.
Compared with prior art, beneficial effects of the present invention are as follows: the floral designs that the present invention is suppressed by mold, with silk
Print is compared with air brushing, and operation difficulty substantially reduces, and operating procedure greatly reduces, upper identical as production powdered frit in raw material materials, is taken
Material is convenient, without worrying the ground coat enamel of glaze and bottom embryo, the matching problem of overglaze, can also using the production clout polished off come
The production for carrying out next workpiece, effectively reduces production cost, is conducive to people's use.
Detailed description of the invention
Fig. 1 is schematic structural view of the invention；
Fig. 2 is structure of the invention top view.
In figure: 1 copper sheet, 2 ground glaze layers, 3 cover coats, 4 glazed colour layers, 5 grooves, 6 top glaze layers.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
That decorates referring to FIG. 1-2, applies the component of enamel, including copper sheet 1, and the top of copper sheet 1 is provided with ground glaze layer 2,
The top of ground glaze layer 2 is provided with cover coat 3, and the top of cover coat 3 is provided with glazed colour layer 4, and the inside of glazed colour layer 4 opens up fluted
5, groove 5 is internally provided with top glaze layer 6.
The component production method for applying enamel of decoration, comprising the following steps:
Step 1: copper material is struck out to the copper sheet 1 of 32mm diameter by stamping die, then by sander to copper sheet 1 into
Row polishing；
Step 2: by flush coater in the upper surface even application glaze of copper sheet 1, forming ground glaze layer in the upper surface of copper sheet 1
2；
Step 3: the copper sheet 1 for being coated with ground glaze layer 2 being put into dryer and is dried, is linked as to ground glaze layer 2 and copper sheet 1
When integrated, glaze is sprayed by flush coater in the upper surface of ground glaze layer 2 again, forms cover coat 3 in the upper surface of ground glaze layer 2；
Step 4: the copper sheet 1 for being coated with cover coat 3 being put into dryer and is dried, is connected to cover coat 3 and ground glaze layer 2
When being integrated, colored glaze is sprayed by flush coater in the upper surface of cover coat 3, forms glazed colour layer in the upper surface of cover coat 3
4；
Step 5: the copper sheet 1 for being coated with glazed colour layer 4 being placed again into dryer and is dried, to glazed colour layer 4 and overglaze
When layer 3 is linked together, copper sheet 1 is put into die casting, the inside of glazed colour layer 4 is struck out to the groove 5 of decorative pattern shape；
Step 6: the copper sheet 1 for opening up fluted 5 being put into the furnace of cellar and is fired, enamel component crude product is obtained；
Step 7: spraying top glaze layer 6 in the groove 5 on enamel component crude product by flush coater, then will be coated with top glaze
The copper sheet 1 of layer 6, which is placed again into dryer, to be dried, and when pushing up glaze layer 6 and groove 5 is linked together, copper sheet 1 is taken out and is carried out
It is cooling；
Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer 6 outside groove 5 will be overflowed
Material polishing removal；
Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
Embodiment 1
The component production method for applying enamel of decoration, comprising the following steps: step 1: copper material is rushed by stamping die
It is pressed into the copper sheet 1 of 32mm diameter, is then polished by sander copper sheet 1；Step 2: by flush coater in the upper of copper sheet 1
Surface even application glaze forms ground glaze layer 2 in the upper surface of copper sheet 1；Step 3: the copper sheet 1 for being coated with ground glaze layer 2 is put into
It is dried in dryer, when ground glaze layer 2 and copper sheet 1 are linked together, is sprayed again in the upper surface of ground glaze layer 2 by flush coater
Glaze is applied, forms cover coat 3 in the upper surface of ground glaze layer 2；Step 4: the copper sheet 1 for being coated with cover coat 3 is put into dryer
It is dried, when cover coat 3 and ground glaze layer 2 are linked together, coloured glaze is sprayed by flush coater in the upper surface of cover coat 3
Material forms glazed colour layer 4 in the upper surface of cover coat 3；Step 5: the copper sheet 1 for being coated with glazed colour layer 4 is placed again into dryer
It is dried, when glazed colour layer 4 and cover coat 3 are linked together, copper sheet 1 is put into die casting, the inside of glazed colour layer 4 is rushed
It is pressed into the groove 5 of decorative pattern shape；Step 6: the copper sheet 1 for opening up fluted 5 being put into the furnace of cellar and is fired, enamel component is obtained
Crude product；Step 7: spraying top glaze layer 6 in the groove 5 on enamel component crude product by flush coater, then will be coated with top glaze layer 6
Copper sheet 1 be placed again into dryer and be dried, when pushing up glaze layer 6 and groove 5 is linked together, copper sheet 1 is taken out carry out it is cold
But；Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer 6 outside groove 5 will be overflowed and beaten
It grinds off and removes；Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
Embodiment 2
In embodiment 1, following steps are added:
The drying temperature of dryer is 20-60 DEG C in step 3, drying time 5-10min.
The component production method for applying enamel of decoration, comprising the following steps: step 1: copper material is rushed by stamping die
It is pressed into the copper sheet 1 of 32mm diameter, is then polished by sander copper sheet 1；Step 2: by flush coater in the upper of copper sheet 1
Surface even application glaze forms ground glaze layer 2 in the upper surface of copper sheet 1；Step 3: the copper sheet 1 for being coated with ground glaze layer 2 is put into
It is dried in dryer, when ground glaze layer 2 and copper sheet 1 are linked together, is sprayed again in the upper surface of ground glaze layer 2 by flush coater
Glaze is applied, forms cover coat 3 in the upper surface of ground glaze layer 2；Step 4: the copper sheet 1 for being coated with cover coat 3 is put into dryer
It is dried, when cover coat 3 and ground glaze layer 2 are linked together, coloured glaze is sprayed by flush coater in the upper surface of cover coat 3
Material forms glazed colour layer 4 in the upper surface of cover coat 3；Step 5: the copper sheet 1 for being coated with glazed colour layer 4 is placed again into dryer
It is dried, when glazed colour layer 4 and cover coat 3 are linked together, copper sheet 1 is put into die casting, the inside of glazed colour layer 4 is rushed
It is pressed into the groove 5 of decorative pattern shape；Step 6: the copper sheet 1 for opening up fluted 5 being put into the furnace of cellar and is fired, enamel component is obtained
Crude product；Step 7: spraying top glaze layer 6 in the groove 5 on enamel component crude product by flush coater, then will be coated with top glaze layer 6
Copper sheet 1 be placed again into dryer and be dried, when pushing up glaze layer 6 and groove 5 is linked together, copper sheet 1 is taken out carry out it is cold
But；Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer 6 outside groove 5 will be overflowed and beaten
It grinds off and removes；Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
Embodiment 3
In example 2, following steps are added:
The drying temperature of dryer is 30-70 DEG C in step 4, drying time 8-15min.
The component production method for applying enamel of decoration, comprising the following steps: step 1: copper material is rushed by stamping die
It is pressed into the copper sheet 1 of 32mm diameter, is then polished by sander copper sheet 1；Step 2: by flush coater in the upper of copper sheet 1
Surface even application glaze forms ground glaze layer 2 in the upper surface of copper sheet 1；Step 3: the copper sheet 1 for being coated with ground glaze layer 2 is put into
It is dried in dryer, when ground glaze layer 2 and copper sheet 1 are linked together, is sprayed again in the upper surface of ground glaze layer 2 by flush coater
Glaze is applied, forms cover coat 3 in the upper surface of ground glaze layer 2；Step 4: the copper sheet 1 for being coated with cover coat 3 is put into dryer
It is dried, when cover coat 3 and ground glaze layer 2 are linked together, coloured glaze is sprayed by flush coater in the upper surface of cover coat 3
Material forms glazed colour layer 4 in the upper surface of cover coat 3；Step 5: the copper sheet 1 for being coated with glazed colour layer 4 is placed again into dryer
It is dried, when glazed colour layer 4 and cover coat 3 are linked together, copper sheet 1 is put into die casting, the inside of glazed colour layer 4 is rushed
It is pressed into the groove 5 of decorative pattern shape；Step 6: the copper sheet 1 for opening up fluted 5 being put into the furnace of cellar and is fired, enamel component is obtained
Crude product；Step 7: spraying top glaze layer 6 in the groove 5 on enamel component crude product by flush coater, then will be coated with top glaze layer 6
Copper sheet 1 be placed again into dryer and be dried, when pushing up glaze layer 6 and groove 5 is linked together, copper sheet 1 is taken out carry out it is cold
But；Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer 6 outside groove 5 will be overflowed and beaten
It grinds off and removes；Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
Embodiment 4
In embodiment 3, following steps are added:
The drying temperature of dryer is 40-80 DEG C, drying time 10-18min in steps of 5, and the quantity of groove 5 is 7
It is a, the arranged in a manner of constituting decorative pattern of groove 5.
The component production method for applying enamel of decoration, comprising the following steps: step 1: copper material is rushed by stamping die
It is pressed into the copper sheet 1 of 32mm diameter, is then polished by sander copper sheet 1；Step 2: by flush coater in the upper of copper sheet 1
Surface even application glaze forms ground glaze layer 2 in the upper surface of copper sheet 1；Step 3: the copper sheet 1 for being coated with ground glaze layer 2 is put into
It is dried in dryer, when ground glaze layer 2 and copper sheet 1 are linked together, is sprayed again in the upper surface of ground glaze layer 2 by flush coater
Glaze is applied, forms cover coat 3 in the upper surface of ground glaze layer 2；Step 4: the copper sheet 1 for being coated with cover coat 3 is put into dryer
It is dried, when cover coat 3 and ground glaze layer 2 are linked together, coloured glaze is sprayed by flush coater in the upper surface of cover coat 3
Material forms glazed colour layer 4 in the upper surface of cover coat 3；Step 5: the copper sheet 1 for being coated with glazed colour layer 4 is placed again into dryer
It is dried, when glazed colour layer 4 and cover coat 3 are linked together, copper sheet 1 is put into die casting, the inside of glazed colour layer 4 is rushed
It is pressed into the groove 5 of decorative pattern shape；Step 6: the copper sheet 1 for opening up fluted 5 being put into the furnace of cellar and is fired, enamel component is obtained
Crude product；Step 7: spraying top glaze layer 6 in the groove 5 on enamel component crude product by flush coater, then will be coated with top glaze layer 6
Copper sheet 1 be placed again into dryer and be dried, when pushing up glaze layer 6 and groove 5 is linked together, copper sheet 1 is taken out carry out it is cold
But；Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer 6 outside groove 5 will be overflowed and beaten
It grinds off and removes；Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
Embodiment 5
In example 4, following steps are added:
It is 600-900 DEG C that copper sheet 1, which is put into the temperature fired in the furnace of cellar, in step 6, firing time 2-10min.
The component production method for applying enamel of decoration, comprising the following steps: step 1: copper material is rushed by stamping die
It is pressed into the copper sheet 1 of 32mm diameter, is then polished by sander copper sheet 1；Step 2: by flush coater in the upper of copper sheet 1
Surface even application glaze forms ground glaze layer 2 in the upper surface of copper sheet 1；Step 3: the copper sheet 1 for being coated with ground glaze layer 2 is put into
It is dried in dryer, when ground glaze layer 2 and copper sheet 1 are linked together, is sprayed again in the upper surface of ground glaze layer 2 by flush coater
Glaze is applied, forms cover coat 3 in the upper surface of ground glaze layer 2；Step 4: the copper sheet 1 for being coated with cover coat 3 is put into dryer
It is dried, when cover coat 3 and ground glaze layer 2 are linked together, coloured glaze is sprayed by flush coater in the upper surface of cover coat 3
Material forms glazed colour layer 4 in the upper surface of cover coat 3；Step 5: the copper sheet 1 for being coated with glazed colour layer 4 is placed again into dryer
It is dried, when glazed colour layer 4 and cover coat 3 are linked together, copper sheet 1 is put into die casting, the inside of glazed colour layer 4 is rushed
It is pressed into the groove 5 of decorative pattern shape；Step 6: the copper sheet 1 for opening up fluted 5 being put into the furnace of cellar and is fired, enamel component is obtained
Crude product；Step 7: spraying top glaze layer 6 in the groove 5 on enamel component crude product by flush coater, then will be coated with top glaze layer 6
Copper sheet 1 be placed again into dryer and be dried, when pushing up glaze layer 6 and groove 5 is linked together, copper sheet 1 is taken out carry out it is cold
But；Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer 6 outside groove 5 will be overflowed and beaten
It grinds off and removes；Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
Embodiment 6
In embodiment 5, following steps are added:
The drying temperature of dryer is 50-90 DEG C in step 7, drying time 12-20min.
The component production method for applying enamel of decoration, comprising the following steps: step 1: copper material is rushed by stamping die
It is pressed into the copper sheet 1 of 32mm diameter, is then polished by sander copper sheet 1；Step 2: by flush coater in the upper of copper sheet 1
Surface even application glaze forms ground glaze layer 2 in the upper surface of copper sheet 1；Step 3: the copper sheet 1 for being coated with ground glaze layer 2 is put into
It is dried in dryer, when ground glaze layer 2 and copper sheet 1 are linked together, is sprayed again in the upper surface of ground glaze layer 2 by flush coater
Glaze is applied, forms cover coat 3 in the upper surface of ground glaze layer 2；Step 4: the copper sheet 1 for being coated with cover coat 3 is put into dryer
It is dried, when cover coat 3 and ground glaze layer 2 are linked together, coloured glaze is sprayed by flush coater in the upper surface of cover coat 3
Material forms glazed colour layer 4 in the upper surface of cover coat 3；Step 5: the copper sheet 1 for being coated with glazed colour layer 4 is placed again into dryer
It is dried, when glazed colour layer 4 and cover coat 3 are linked together, copper sheet 1 is put into die casting, the inside of glazed colour layer 4 is rushed
It is pressed into the groove 5 of decorative pattern shape；Step 6: the copper sheet 1 for opening up fluted 5 being put into the furnace of cellar and is fired, enamel component is obtained
Crude product；Step 7: spraying top glaze layer 6 in the groove 5 on enamel component crude product by flush coater, then will be coated with top glaze layer 6
Copper sheet 1 be placed again into dryer and be dried, when pushing up glaze layer 6 and groove 5 is linked together, copper sheet 1 is taken out carry out it is cold
But；Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer 6 outside groove 5 will be overflowed and beaten
It grinds off and removes；Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
Embodiment 7
In embodiment 6, following steps are added:
It is 750-850 DEG C that enamel crude product, which is put into the temperature fired again in the furnace of cellar, in step 8, firing time 4-
8min。
The component production method for applying enamel of decoration, comprising the following steps: step 1: copper material is rushed by stamping die
It is pressed into the copper sheet 1 of 32mm diameter, is then polished by sander copper sheet 1；Step 2: by flush coater in the upper of copper sheet 1
Surface even application glaze forms ground glaze layer 2 in the upper surface of copper sheet 1；Step 3: the copper sheet 1 for being coated with ground glaze layer 2 is put into
It is dried in dryer, when ground glaze layer 2 and copper sheet 1 are linked together, is sprayed again in the upper surface of ground glaze layer 2 by flush coater
Glaze is applied, forms cover coat 3 in the upper surface of ground glaze layer 2；Step 4: the copper sheet 1 for being coated with cover coat 3 is put into dryer
It is dried, when cover coat 3 and ground glaze layer 2 are linked together, coloured glaze is sprayed by flush coater in the upper surface of cover coat 3
Material forms glazed colour layer 4 in the upper surface of cover coat 3；Step 5: the copper sheet 1 for being coated with glazed colour layer 4 is placed again into dryer
It is dried, when glazed colour layer 4 and cover coat 3 are linked together, copper sheet 1 is put into die casting, the inside of glazed colour layer 4 is rushed
It is pressed into the groove 5 of decorative pattern shape；Step 6: the copper sheet 1 for opening up fluted 5 being put into the furnace of cellar and is fired, enamel component is obtained
Crude product；Step 7: spraying top glaze layer 6 in the groove 5 on enamel component crude product by flush coater, then will be coated with top glaze layer 6
Copper sheet 1 be placed again into dryer and be dried, when pushing up glaze layer 6 and groove 5 is linked together, copper sheet 1 is taken out carry out it is cold
But；Step 8: being polished by sander enamel component crude product after cooling, the glaze for pushing up glaze layer 6 outside groove 5 will be overflowed and beaten
It grinds off and removes；Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the portion of enamel
Part.
In summary: the component for applying enamel of the decoration solves the problems, such as that dial plate decoration is inconvenient.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. the component for applying enamel of decoration, including copper sheet (1), it is characterised in that: be provided with ground coat enamel at the top of the copper sheet (1)
Layer (2) is provided with cover coat (3) at the top of the ground glaze layer (2), is provided with glazed colour layer (4) at the top of the cover coat (3),
The inside of the glazed colour layer (4) opens up fluted (5), and the groove (5) is internally provided with top glaze layer (6).
2. the component for applying enamel of decoration according to claim 1, it is characterised in that: the thickness of the glazed colour layer (4)
For 100-200um, the depth of the groove (5) is 80-150um, top glaze layer (6) with a thickness of 80-150um.
3. the component production method for applying enamel of decoration, it is characterised in that: the following steps are included:
Step 1: copper material is struck out to the copper sheet (1) of 32mm diameter by stamping die, then by sander to copper sheet (1) into
Row polishing；
Step 2: by flush coater in the upper surface even application glaze of copper sheet (1), forming ground glaze layer in the upper surface of copper sheet (1)
(2)；
Step 3: the copper sheet (1) for being coated with ground glaze layer (2) being put into dryer and is dried, to ground glaze layer (2) and copper sheet (1)
When being linked together, in the upper surface of ground glaze layer (2) glaze is sprayed by flush coater again, formed in the upper surface of ground glaze layer (2)
Cover coat (3)；
Step 4: the copper sheet (1) for being coated with cover coat (3) being put into dryer and is dried, to cover coat (3) and ground glaze layer
(2) when being linked together, colored glaze is sprayed by flush coater in the upper surface of cover coat (3), in the upper surface shape of cover coat (3)
At glazed colour layer (4)；
Step 5: the copper sheet (1) for being coated with glazed colour layer (4) being placed again into dryer and is dried, to glazed colour layer (4) and face
When glaze layer (3) is linked together, copper sheet (1) is put into die casting, the inside of glazed colour layer (4) is struck out into the recessed of decorative pattern shape
Slot (5)；
Step 6: the copper sheet (1) for opening up fluted (5) being put into the furnace of cellar and is fired, enamel component crude product is obtained；
Step 7: by interior spraying top glaze layer (6) of groove (5) of the flush coater on enamel component crude product, then will be coated with top glaze
The copper sheet (1) of layer (6), which is placed again into dryer, to be dried, when being linked together wait push up glaze layer (6) and groove (5), by copper sheet
(1) it takes out and is cooled down；
Step 8: being polished by sander enamel component crude product after cooling, spilling groove (5) is pushed up to the glaze of glaze layer (6) outside
Material polishing removal；
Step 9: the enamel crude product after polishing being put into the furnace of cellar and is fired again, that is decorated applies the component of enamel.
4. the component production method for applying enamel of decoration according to claim 3, it is characterised in that: described in step 3
The drying temperature of middle dryer is 20-60 DEG C, and the drying time is 5-10min.
5. the component production method for applying enamel of decoration according to claim 3, it is characterised in that: described in step 4
The drying temperature of middle dryer is 30-70 DEG C, and the drying time is 8-15min.
6. the component production method for applying enamel of decoration according to claim 3, it is characterised in that: described in step 5
The drying temperature of middle dryer is 40-80 DEG C, and the drying time is 10-18min, and the quantity of the groove (5) is 7, institute
State groove (5) arranged in a manner of constituting decorative pattern.
7. the component production method for applying enamel of decoration according to claim 3, it is characterised in that: described in step 6
It is 600-900 DEG C that middle copper sheet (1), which is put into the temperature fired in the furnace of cellar, and the firing time is 2-10min.
8. the component production method for applying enamel of decoration according to claim 3, it is characterised in that: described in step 7
The drying temperature of middle dryer is 50-90 DEG C, and the drying time is 12-20min.
9. the component production method for applying enamel of decoration according to claim 3, it is characterised in that: described in step 8
It is 750-850 DEG C that middle enamel crude product, which is put into the temperature fired again in the furnace of cellar, and the firing time is 4-8min.