CN101891478A - Dazzling china used for decorating bone china - Google Patents
Dazzling china used for decorating bone china Download PDFInfo
- Publication number
- CN101891478A CN101891478A CN 201010226426 CN201010226426A CN101891478A CN 101891478 A CN101891478 A CN 101891478A CN 201010226426 CN201010226426 CN 201010226426 CN 201010226426 A CN201010226426 A CN 201010226426A CN 101891478 A CN101891478 A CN 101891478A
- Authority
- CN
- China
- Prior art keywords
- parts
- firing
- china
- dazzling
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to technology for firing dazzling china for decorating bone china and formula composition of the dazzling china. According to the technology, a product of the dazzling china of the invention meets the requirements by changing the conventional process, making use of colors prepared by modern high technology, applying a particular process means and adopting a multi-firing method. The process flow of the technology comprises the following steps of: stock preparing, slurry casting or mechanically pressing and forming (preparing by using a die), drying, fettling, water replenishing, finished green body inspecting, low-temperature biscuit firing, biscuit inspecting, dusting agent painting, color spraying, inspecting, loading, high-temperature biscuit firing, unloading, inspecting, polishing, cleaning, drying, glaze spraying, glazing and firing, glaze firing, deglazing and firing, inspecting and selecting, semi-finished product warehousing, decaling, enamel firing, foot rim milling, enamel selecting, packaging and finished product warehousing. The dazzling china for decorating the bone china has the advantages that: the dazzling china provided by the invention is obtained by decorating the bone china by using traditional bright red and golden yellow, and the product has pure and brilliant colors and bright glaze and is rich and elegant.
Description
Technical field:
The present invention relates to a kind of preparation and dazzle the burning techniques and the formula combination thereof of porcelain, particularly a kind of relating to, be used for the sclerotin porcelain decoration burning techniques and the formula combination thereof of dazzling porcelain, and it belongs to chemical field and can directly apply to the ornamental technology of china.
Background technology:
China town of porcelain Jing Dezhen foremost " all red ", " holding a memorial ceremony for red " and transmutation yellow porcelain device are subjected to treasuring of Chinese people deeply.Firing " all red ", " holding a memorial ceremony for red " and transmutation Huang is to make its color produce transmutation by process for calcining to reach its purpose.There are the color aberration in existing but " all red ", " holding a memorial ceremony for red " and transmutation yellow porcelain device, and complex manufacturing technology is produced the requirement that color can't reach basically identical in batches.
This shows in preparation process because temperature or other corresponding condition are all more restive, so not only cause the waste of material easily, but also influence working efficiency, and then influence quality problems such as product is attractive in appearance, and, cause to consume more cost because explained hereafter is complicated.
Summary of the invention:
The technical problem to be solved in the present invention provides a kind of relating to and is used for sclerotin and decorates with the burning techniques and the formula combination thereof of dazzling porcelain.It is by changing traditional technology, utilize the color of modern high technology making, use special process means, adopting the method for repeatedly burning till to make product reach requirement that china among the present invention has another name called " porcelain dazzled in state's rhythm ".There are the color aberration in existing " all red ", " holding a memorial ceremony for red " and transmutation yellow porcelain device, and complex manufacturing technology is produced the requirement that color can't reach basically identical in batches.
By improving technology, the problem that produces in the making processes is done the following improvement of system:
A, be from process for calcining; We are by burning till for twice into being to burn till for three times;
B, be from enameling method: we change color spray into by color spray glaze and separate with glaze spraying and carry out, thereby solve aberration;
C, be that we select regular trading company as supplier from the selecting materials of color.Technical scheme of the present invention is as follows:
Be used for the porcelain of dazzling that sclerotin decorates, comprise and dazzle porcelain pug and glaze frit, wherein: dazzle porcelain mud prescription and comprise by weight bone carbon 38-43 part, quartzy 5-8 part, feldspar 16-20 part, greensand 10-13 part, kaolin 7-9 part, porcelain powder 6-8 part, bentonite 7-9 part;
Be used for the porcelain of dazzling of sclerotin decoration, wherein: glaze frit prescription comprises feldspar 14-18 part by weight, quartzy 28-36 part, sandstone 2-4 part, borax 12-15 part, light calcium carbonate 12-15 part, talcum 2-3 part, 2 parts of zircons, barium carbonate 4-6 part, zinc oxide 3-6 part, 2 parts of soda ash, Quilonum Retard 0-3 part is wrapped up bright red 63 parts, 1.5 parts of methylcellulose gum.
The porcelain of dazzling that is used for the sclerotin decoration, its technical process comprises system pug, slip casting or mechanical pressing (Mold Making), drying, repaired biscuit, moisturizing, the check of smart base, low temperature biscuiting, biscuit check, brushes separant, color spray, check, loading of kiln, high temperature biscuiting, opens kiln, check, polishing, cleaning, oven dry, glaze spraying, dress glost kiln, glaze firing, opens glost kiln, pick, goes into the work in-process warehouse, applique, color roasting, mill foot, color selection, pack, go into, wherein: low temperature biscuiting temperature be 1030 spend, firing time is 5 hours; High temperature biscuiting temperature is that 1230 degree, firing time are 8-9 hour; Temperature of glaze firing is that 1130 degree, firing time are 8 hours; Color roasting temperature gold class marble paper 800 degree, the in-glaze decoration marble paper is 1050 degree.
Advantage of the present invention: the porcelain of dazzling provided by the invention is that the sclerotin porcelain is bright red and golden yellow with tradition, is decorated, and product color is pure gorgeous, and the glaze light is rich and honour graceful.
Specific embodiment
Embodiment 1, be used for the porcelain of dazzling that sclerotin decorates, comprise pug and glaze frit wherein: pug formula comprises bone carbon 38-43 part by weight, quartzy 5-8 part, feldspar 16-20 part, greensand 10-13 part, kaolin 7-9 part, porcelain powder 6-8 part, bentonite 7-9 part;
Glaze frit prescription comprises feldspar 14-18 part by weight, quartzy 28-36 part, sandstone 2-4 part, borax 12-15 part, light calcium carbonate 12-15 part, talcum 2-3 part, 2 parts of zircons, barium carbonate 4-6 part, zinc oxide 3-6 part, 2 parts of soda ash, Quilonum Retard 0-3 part, wrap up bright red 63 parts, 1.5 parts of methylcellulose gum.
Embodiment 2, be used for the porcelain of dazzling that sclerotin decorates, wherein: its technical process comprises slip casting or mechanical pressing, drying, repaired biscuit, moisturizing, the check of smart base, low temperature biscuiting, biscuit check that system pug, Mold Making become, brushes separant, color spray, check, loading of kiln, high temperature biscuiting, opens kiln, check, polishing, cleaning, oven dry, glaze spraying, dress glost kiln, glaze firing, opens glost kiln, pick, goes into the work in-process warehouse, applique, color roasting, mill foot, color selection, pack, go into stockyard;
Wherein: low temperature biscuiting temperature is that 1030 degree, firing time are 5 hours in the technical process; High temperature biscuiting temperature is that 1230 degree, firing time are 8-9 hour; Temperature of glaze firing is that 1130 degree, firing time are 8 hours; Color roasting temperature gold class marble paper 800 degree, the in-glaze decoration marble paper is 1050 degree;
The processing of raw material in the technical process comprises by weight bone carbon 38-43 part, quartzy 5-8 part, feldspar 16-20 part, greensand 10-13 part, kaolin 7-9 part, porcelain powder 6-8 part, bentonite 7-9 part with pug formula;
The glaze frit prescription of glaze spraying process comprises feldspar 14-18 part by weight, quartzy 28-36 part, sandstone 2-4 part, borax 12-15 part, light calcium carbonate 12-15 part, talcum 2-3 part, 2 parts of zircons, barium carbonate 4-6 part, zinc oxide 3-6 part, 2 parts of soda ash, Quilonum Retard 0-3 part, 1.5 parts of methylcellulose gum.
Embodiment 3, be used for the porcelain of dazzling that sclerotin decorates, wherein: pug formula 1 comprises 43 parts in bone carbon by weight, quartzy 5 parts, 17 parts of feldspars, 10 parts of greensands, 8 parts of kaolin, 8 parts in porcelain powder, 9 parts of bentonites.
Glaze frit prescription 1 comprises 16 parts of feldspars, quartzy 32 parts, and 3 parts of sandstones, 14 parts of boraxs, 14 parts of light calcium carbonates, 2 parts in talcum, 2 parts of zircons, 6 parts of barium carbonates, 5 parts in zinc oxide, 2 parts of soda ash, 2 parts of Quilonum Retards wrap up bright red 63 parts, 1.5 parts of methylcellulose gum.All the other are with embodiment 2.
Embodiment 4, be used for the porcelain of dazzling that sclerotin decorates, wherein: pug formula 2 comprises 42 parts in bone carbon by weight, quartzy 6 parts, 18 parts of feldspars, 11 parts of greensands, 9 parts of kaolin, 6 parts in porcelain powder, 8 parts of bentonites.
Glaze frit prescription 2 comprises 17 parts of feldspars, quartzy 34 parts, and 3 parts of sandstones, 13 parts of boraxs, 13 parts of light calcium carbonates, 2 parts in talcum, 2 parts of zircons, 5 parts of barium carbonates, 4 parts in zinc oxide, 2 parts of soda ash, 3 parts of Quilonum Retards wrap up bright red 63 parts, 1.5 parts of methylcellulose gum.All the other are with embodiment 2.
Embodiment 5, be used for the porcelain of dazzling that sclerotin decorates, wherein: pug formula 3 comprises 41 parts in bone carbon by weight, quartzy 7 parts, 16 parts of feldspars, 12 parts of greensands, 8 parts of kaolin, 7 parts in porcelain powder, 9 parts of bentonites.
Glaze frit prescription 3 comprises 18 parts of feldspars by weight, quartzy 36 parts, and 2 parts of sandstones, 12 parts of boraxs, 12 parts of light calcium carbonates, talcum-+3 part, 2 parts of zircons, 5 parts of barium carbonates, 5 parts in zinc oxide, 2 parts of soda ash, 2 parts of Quilonum Retards wrap up bright red 63 parts, 1.5 parts of methylcellulose gum.All the other are with embodiment 2.
Embodiment 6, be used for the porcelain of dazzling that sclerotin decorates, wherein: pug formula 4 comprises 40 parts in bone carbon by weight, quartzy 7 parts, 19 parts of feldspars, 13 parts of greensands, 7 parts of kaolin, 7 parts in porcelain powder, 7 parts of bentonites.
Glaze frit prescription 4 comprises 15 parts of feldspars by weight, quartzy 30 parts, and 3 parts of sandstones, 15 parts of boraxs, 15 parts of light calcium carbonates, 2 parts in talcum, 2 parts of zircons, 5 parts of barium carbonates, 6 parts in zinc oxide, 2 parts of soda ash wrap up bright red 63 parts, 1.5 parts of methylcellulose gum.All the other are with embodiment 2.
Embodiment 7, be used for the porcelain of dazzling that sclerotin decorates, wherein: pug formula 5 comprises 38 parts in bone carbon by weight, quartzy 8 parts, 20 parts of feldspars, 12 parts of greensands, 7 parts of kaolin, 7 parts in porcelain powder, 8 parts of bentonites.
Glaze frit prescription 5 comprises 14 parts of feldspars by weight, quartzy 28 parts, and 4 parts of sandstones, 14 parts of boraxs, 14 parts of light calcium carbonates, 3 parts in talcum, 2 parts of zircons, 4 parts of barium carbonates, 3 parts in zinc oxide, 2 parts of soda ash, 2 parts of Quilonum Retards wrap up bright red 63 parts, 1.5 parts of methylcellulose gum.All the other are with embodiment 2.
Embodiment 8, be used for the porcelain of dazzling that sclerotin decorates, wherein: pug formula 6 comprises 38 parts in bone carbon by weight, quartzy 5 parts, 16 parts of feldspars, 10 parts of greensands, 7 parts of kaolin, 6 parts in porcelain powder, 7 parts of bentonites;
Glaze frit prescription comprises 14 parts of feldspars by weight, quartzy 28 parts, and 2 parts of sandstones, 12 parts of boraxs, 12 parts of light calcium carbonates, 2 parts in talcum, 2 parts of zircons, 4 parts of barium carbonates, 3 parts in zinc oxide, 2 parts of soda ash, 0 part of Quilonum Retard.All the other are with embodiment 2.
Embodiment 9, be used for the porcelain of dazzling that sclerotin decorates, wherein: pug formula 7 comprises 43 parts in bone carbon by weight, quartzy 8 parts, 20 parts of feldspars, 13 parts of greensands, 9 parts of kaolin, 8 parts in porcelain powder, 9 parts of bentonites;
Glaze frit prescription comprises 18 parts of feldspars by weight, quartzy 36 parts, and 4 parts of sandstones, 15 parts of boraxs, 15 parts of light calcium carbonates, 3 parts in talcum, 2 parts of zircons, 6 parts of barium carbonates, 6 parts in zinc oxide, 2 parts of soda ash, 3 parts of Quilonum Retards.All the other are with embodiment 2.
The technique effect contrast is as follows:
20 of each random chooses of the product that embodiment 3,4,5,6,7,8,9 burns till are observed:
Technology is relatively: the quality product that makes of the technical formula combination adopted of embodiment 3 is respond well more as can be seen by above technique effect.
Claims (2)
1. be used for the porcelain of dazzling that sclerotin decorates, it is characterized in that: dazzle the porcelain pug prescription and comprise by weight bone carbon 38-43 part, quartzy 5-8 part, feldspar 16-20 part, greensand 10-13 part, kaolin 7-9 part, porcelain powder 6-8 part, bentonite 7-9 part; Glaze frit prescription comprises feldspar 14-18 part by weight, quartzy 28-36 part, sandstone 2-4 part, borax 12-15 part, light calcium carbonate 12-15 part, talcum 2-3 part, 2 parts of zircons, barium carbonate 4-6 part, zinc oxide 3-6 part, 2 parts of soda ash, Quilonum Retard 0-3 part, wrap up bright red 63 parts, 1.5 parts of methylcellulose gum.
2. be used for the porcelain of dazzling that sclerotin decorates, technical process comprises slip casting or mechanical pressing, drying, repaired biscuit, moisturizing, the check of smart base, low temperature biscuiting, biscuit check that system pug, Mold Making are made, brushes separant, color spray, check, loading of kiln, high temperature biscuiting, opens kiln, check, polishing, cleaning, oven dry, glaze spraying, dress glost kiln, glaze firing, opens glost kiln, pick, goes into the work in-process warehouse, applique, color roasting, mill foot, color selection, pack, go into stockyard;
It is characterized in that: low temperature biscuiting temperature is that 1030 degree, firing time are 5 hours in the technical process; High temperature biscuiting temperature is that 1230 degree, firing time are 8-9 hour; Temperature of glaze firing is that 1130 degree, firing time are 8 hours; Color roasting temperature gold class marble paper 800 degree, the in-glaze decoration marble paper is 1050 degree;
The processing of raw material in the technical process comprises by weight bone carbon 38-43 part, quartzy 5-8 part, feldspar 16-20 part, greensand 10-13 part, kaolin 7-9 part, porcelain powder 6-8 part, bentonite 7-9 part with pug formula;
The glaze frit prescription of glaze spraying process comprises feldspar 14-18 part by weight, quartzy 28-36 part, sandstone 2-4 part, borax 12-15 part, light calcium carbonate 12-15 part, talcum 2-3 part, 2 parts of zircons, barium carbonate 4-6 part, zinc oxide 3-6 part, 2 parts of soda ash, Quilonum Retard 0-3 part, wrap up bright red 63 parts, 1.5 parts of methylcellulose gum.