CN109734951A - 一种环保发泡剂及其制备方法 - Google Patents
一种环保发泡剂及其制备方法 Download PDFInfo
- Publication number
- CN109734951A CN109734951A CN201811463636.4A CN201811463636A CN109734951A CN 109734951 A CN109734951 A CN 109734951A CN 201811463636 A CN201811463636 A CN 201811463636A CN 109734951 A CN109734951 A CN 109734951A
- Authority
- CN
- China
- Prior art keywords
- parts
- foaming agent
- environment
- sodium bicarbonate
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种环保发泡剂及其制备方法,发泡剂主要包括以下成分:碳酸镁、聚丙烯酸钠、碳酸氢钠、硅藻土、方解石、超细铝粉、碳化硅、碳酸盐、二氯二氟甲烷、碳酸氢钠、稳定剂、水。该环保发泡剂的制备方法包括以下步骤:1、将碳酸镁、聚丙烯酸钠、碳酸氢钠、硅藻土、方解石混合,用粉碎机粉碎成粉末,混合物在溶剂中混合均匀,得到溶液A;2、将超细铝粉、碳化硅、碳酸盐、二氯二氟甲烷、碳酸氢钠、稳定剂用粉碎机粉碎成粉末,并倒入水中搅拌,在30‑50℃条件下反应40‑60min,得到溶液B;3、将溶液A和溶液B注入密闭搅拌容器中搅拌,搅拌完毕后保温,然后倒出烘干即可。
Description
技术领域
本发明涉及材料工程领域,尤其涉及一种环保发泡剂及其制备方法。
背景技术
发泡剂是指所有其水溶液能在引入空气的情况下大量产生泡沫的表面活性剂或表面活性物质。发泡剂具有较高的表面活性,能有效降低液体的表面张力,并在液膜表面双电子层排列而包围空气,形成气泡,再由气泡组成泡沫。目前,发泡剂被越来越广泛地使用。但是现有发泡物质也存在降解时间长、回收难的缺陷,会对环境造成较大污染。
本发明主要提出一种制备过程简单,可大大降低对环境污染的环保发泡剂。
发明内容
本发明的目的是为了解决现有技术中存在的缺点,而提出的一种环保发泡剂及其制备方法。
为了实现上述目的,本发明采用了如下技术方案:
一种环保发泡剂,由以下组分原材料组成:
碳酸镁20-36份、聚丙烯酸钠10-15份、碳酸氢钠15-23份、硅藻土20-45份、方解石4-8份、超细铝粉1-3份、碳化硅3-5份、碳酸盐1-3份、二氯二氟甲烷2-6份、碳酸氢钠0.5-1份、稳定剂5-10份、水50-80份。
优选地,所述稳定剂包括有机锡、亚硫酸盐、钙皂、稀土均量混合而成。
优选地,所述的碳酸盐为碳酸镁。
一种环保发泡剂的制备方法,包括以下步骤:
S1、按标准将各组分称量,分开放置;
S2、将碳酸镁、聚丙烯酸钠、碳酸氢钠、硅藻土、方解石混合,用粉碎机粉碎成300-400目数的粉末,混合物在溶剂中混合均匀,并进行抽真空排氧,在30-45℃条件下反应50-80min,得到溶液A;
S3、将步骤S2中得到的溶液A采用紫外线灯灭菌30-60min;
S4、将超细铝粉、碳化硅、碳酸盐、二氯二氟甲烷、碳酸氢钠、稳定剂用粉碎机粉碎成350-400目数的粉末,并倒入水中搅拌,在30-50℃条件下反应40-60min,得到溶液B;
S5、将步骤S2得到的溶液A和步骤S4得到的溶液B注入密闭搅拌容器中搅拌,搅拌完毕后保温10-20min;然后倒出烘干,即可得到环保发泡剂。
与现有技术相比,本发明的有益效果是:本发明提出的环保发泡剂制备过程简单,工序易操作,生产成本可以控制在一个较低水准;制得的环保发泡剂腐蚀性极低,降解时间短,容易回收,对环境不会造成恶劣影响。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。
一种环保发泡剂,由以下组分原材料组成:
碳酸镁20-36份、聚丙烯酸钠10-15份、碳酸氢钠15-23份、硅藻土20-45份、方解石4-8份、超细铝粉1-3份、碳化硅3-5份、碳酸盐1-3份、二氯二氟甲烷2-6份、碳酸氢钠0.5-1份、稳定剂5-10份、水50-80份。
优选地,所述稳定剂包括有机锡、亚硫酸盐、钙皂、稀土均量混合而成。
优选地,所述的碳酸盐为碳酸镁。
一种环保发泡剂的制备方法,包括以下步骤:
S1、按标准将各组分称量,分开放置;
S2、将碳酸镁、聚丙烯酸钠、碳酸氢钠、硅藻土、方解石混合,用粉碎机粉碎成300-400目数的粉末,混合物在溶剂中混合均匀,并进行抽真空排氧,在30-45℃条件下反应50-80min,得到溶液A;
S3、将步骤S2中得到的溶液A采用紫外线灯灭菌30-60min;
S4、将超细铝粉、碳化硅、碳酸盐、二氯二氟甲烷、碳酸氢钠、稳定剂用粉碎机粉碎成350-400目数的粉末,并倒入水中搅拌,在30-50℃条件下反应40-60min,得到溶液B;
S5、将步骤S2得到的溶液A和步骤S4得到的溶液B注入密闭搅拌容器中搅拌,搅拌完毕后保温10-20min;然后倒出烘干,即可得到环保发泡剂。
实施例一
一种环保发泡剂,由以下组分原材料组成:
碳酸镁20份、聚丙烯酸钠10份、碳酸氢钠15份、硅藻土20份、方解石4份、超细铝粉1份、碳化硅3份、碳酸盐1份、二氯二氟甲烷2份、碳酸氢钠0.5份、稳定剂5份、水50份。
实施例二
一种环保发泡剂,由以下组分原材料组成:
碳酸镁36份、聚丙烯酸钠15份、碳酸氢钠23份、硅藻土45份、方解石8份、超细铝粉3份、碳化硅5份、碳酸盐3份、二氯二氟甲烷6份、碳酸氢钠1份、稳定剂10份、水80份。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。
Claims (4)
1.一种环保发泡剂,其特征在于,由以下组分原材料组成:
碳酸镁20-36份、聚丙烯酸钠10-15份、碳酸氢钠15-23份、硅藻土20-45份、方解石4-8份、超细铝粉1-3份、碳化硅3-5份、碳酸盐1-3份、二氯二氟甲烷2-6份、碳酸氢钠0.5-1份、稳定剂5-10份、水50-80份。
2.根据权利要求1所述的一种环保发泡剂,其特征在于,所述稳定剂包括有机锡、亚硫酸盐、钙皂、稀土均量混合而成。
3.根据权利要求1所述的一种环保发泡剂,其特征在于,所述的碳酸盐为碳酸镁。
4.一种环保发泡剂的制备方法,其特征在于,包括以下步骤:
S1、按标准将各组分称量,分开放置;
S2、将碳酸镁、聚丙烯酸钠、碳酸氢钠、硅藻土、方解石混合,用粉碎机粉碎成300-400目数的粉末,混合物在溶剂中混合均匀,并进行抽真空排氧,在30-45℃条件下反应50-80min,得到溶液A;
S3、将步骤S2中得到的溶液A采用紫外线灯灭菌30-60min;
S4、将超细铝粉、碳化硅、碳酸盐、二氯二氟甲烷、碳酸氢钠、稳定剂用粉碎机粉碎成350-400目数的粉末,并倒入水中搅拌,在30-50℃条件下反应40-60min,得到溶液B;
S5、将步骤S2得到的溶液A和步骤S4得到的溶液B注入密闭搅拌容器中搅拌,搅拌完毕后保温10-20min;然后倒出烘干,即可得到环保发泡剂。