CN109734351A - 一种新型丙烯酸盐灌浆料及其制备方法 - Google Patents
一种新型丙烯酸盐灌浆料及其制备方法 Download PDFInfo
- Publication number
- CN109734351A CN109734351A CN201910157848.8A CN201910157848A CN109734351A CN 109734351 A CN109734351 A CN 109734351A CN 201910157848 A CN201910157848 A CN 201910157848A CN 109734351 A CN109734351 A CN 109734351A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- grouting material
- novel propylene
- propylene hydrochlorate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于丙烯酸盐灌浆料制备技术领域,尤其为一种新型丙烯酸盐灌浆料,包含A组分和B组分,其中,A组分包括丙烯酸盐水溶液70份~95份,交联剂5份~20份,促进剂1份~20份,无机助剂5份~20份,B组分包括引发剂0.1份~10份,水5份~50份,橡胶助剂5份~20份,缓凝剂0.1份~0.5份,其中,所述A组分和所述B组分的比例为100:80~90;该配方生产出来的丙烯酸盐灌浆料收缩率大幅度降低,在90天内收缩率仅为10%~20%,大大降低了因收缩应力带来的注浆材料破坏,从而降低了复漏的风险。
Description
技术领域
本发明属于丙烯酸盐灌浆料制备技术领域,具体涉及一种新型丙烯酸盐灌浆料及其制备方法。
背景技术
混凝土中存在贯穿性裂缝或地下工程变形缝出现渗漏时,往往需要注浆堵漏来进行维修。目前,市面上使用的注浆材料包括环氧树脂类、聚氨酯类和丙烯酸盐类。其中,由于丙烯酸盐灌浆料采用了无毒的交联剂之后,因其粘度低、无毒环保、凝胶时间可调和弹性高等特点,市场前景备受关注。但丙烯酸盐灌浆料在使用过程中,由于采用的丙烯酸盐水溶液,其固含量较低。固化之后的灌浆材料在干燥环境下出现不同程度的收缩,在90天内其收缩率可达80%。特别是在变形缝部位,当灌浆材料出现大尺寸收缩时,其收缩应力会使得灌浆材料与混凝土粘接破坏或者从材料内部产生破坏,从而出现复漏的风险。
发明内容
为实现上述目的,本发明提供如下技术方案:一种新型丙烯酸盐灌浆料,包含A组分和B组分,其中,A组分包括丙烯酸盐水溶液70份~95份,交联剂5份~20份,促进剂1份~20份,无机助剂5份~20份;
B组分包括引发剂0.1份~10份,水5份~50份,橡胶助剂5份~20份,缓凝剂0.1份~0.5份;
其中,所述A组分和所述B组分的比例为100:80~90。
作为本发明的一种新型丙烯酸盐灌浆料优选技术方案,所述丙烯酸盐水溶液为丙烯酸镁、丙烯酸钙、丙烯酸锌、甲基丙烯酸镁、甲基丙烯酸钙和甲基丙烯酸锌中的一种或几种复合物。
作为本发明的一种新型丙烯酸盐灌浆料优选技术方案,所述交联剂为丙烯酸甲酯、丙烯酸丁酯、聚甲基丙烯酸甲酯、聚甲基丙烯酸丁酯、丙三醇、乙二醇二丙烯酸酯或季戊四醇二丙烯酸酯中的一种或几种复合物。
作为本发明的一种新型丙烯酸盐灌浆料优选技术方案,所述促进剂为三乙醇胺、二乙醇胺、四甲基乙二胺、三乙烯二胺、氯化亚锡和乙二醇单甲醚中的一种或几种的复合物。
作为本发明的一种新型丙烯酸盐灌浆料优选技术方案,所述无机助剂为氯化镁、氯化钙和氯化钠水溶液中的一种或几种复合物。
作为本发明的一种新型丙烯酸盐灌浆料优选技术方案,所述引发剂为过硫酸铵、过硫酸钾和过硫酸钠中的至少一种。
作为本发明的一种新型丙烯酸盐灌浆料优选技术方案,所述缓凝剂为铁氰化钾。
作为本发明的一种新型丙烯酸盐灌浆料优选技术方案,所述橡胶助剂为溶聚丁苯橡胶、水性氯化橡胶乳液、丁晴乳液、丙烯酸乳液中的至少一种。
作为本发明的一种新型丙烯酸盐灌浆料优选技术方案,所述包含A组分和B组分,其中,A组分包括丙烯酸盐水溶液80份,交联剂15份,促进剂15份,无机助剂15份;
B组分包括引发剂5份,水25份,橡胶助剂15份,缓凝剂0.3份;
其中,所述A组分和所述B组分的比例为100:85。
作为本发明的一种制备方法优选技术方案,包括如下步骤:
S1、选择丙烯酸盐水溶液80份、交联剂15份、促进剂15份和无机助剂15份放置到反应釜中搅拌30分钟~50分钟,得到A组分,取出备用;
S2、把水25份、引发剂5份、橡胶助剂15份和缓凝剂0.3份放置到反应釜中搅拌30分钟~50分钟,得到B组分,取出备用;
S3、按照A组分和B组分为100:85质量比进行配制,用注浆机将灌浆材料注入到裂缝或者变形缝中,得到柔性的丙烯酸盐灌浆料。
与现有技术相比,本发明的有益效果是:该配方生产出来的丙烯酸盐灌浆料收缩率大幅度降低,在90天内收缩率仅为10%~20%,大大降低了因收缩应力带来的注浆材料破坏,从而降低了复漏的风险。
附图说明
附图用来提供对本发明的进一步理解,并且构成说明书的一部分,与本发明的实施例一起用于解释本发明,并不构成对本发明的限制。在附图中:
图1为本发明的流程示意图。
具体实施方式
下面将结合本发明实施例中的附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
一种新型丙烯酸盐灌浆料,包含A组分和B组分,其中,A组分包括丙烯酸盐水溶液70份,交联剂5份,促进剂1份,无机助剂5份;
B组分包括引发剂0.1份,水5份,橡胶助剂5份,缓凝剂0.1份;
其中,所述A组分和所述B组分的比例为100:80。
一种制备方法,包括如下步骤:
S1、选择丙烯酸盐水溶液70份、交联剂5份、促进剂1份和无机助剂5份放置到反应釜中搅拌30分钟,得到A组分,取出备用;
S2、把水5份、引发剂0.1份、橡胶助剂5份和缓凝剂0.1份放置到反应釜中搅拌30分钟,得到B组分,取出备用;
S3、按照A组分和B组分为100:80质量比进行配制,用注浆机将灌浆材料注入到裂缝或者变形缝中,得到柔性的丙烯酸盐灌浆料。
实施例2
一种新型丙烯酸盐灌浆料,包含A组分和B组分,其中,A组分包括丙烯酸盐水溶液80份,交联剂15份,促进剂15份,无机助剂15份;
B组分包括引发剂5份,水25份,橡胶助剂15份,缓凝剂0.3份;
其中,所述A组分和所述B组分的比例为100:85。
一种制备方法,包括如下步骤:
S1、选择丙烯酸盐水溶液80份、交联剂15份、促进剂15份和无机助剂15份放置到反应釜中搅拌40分钟,得到A组分,取出备用;
S2、把水25份、引发剂5份、橡胶助剂15份和缓凝剂0.3份放置到反应釜中搅拌40分钟,得到B组分,取出备用;
S3、按照A组分和B组分为100:85质量比进行配制,用注浆机将灌浆材料注入到裂缝或者变形缝中,得到柔性的丙烯酸盐灌浆料。
实施例3
一种新型丙烯酸盐灌浆料,包含A组分和B组分,其中,A组分包括丙烯酸盐水溶液95份,交联剂20份,促进剂20份,无机助剂20份;
B组分包括引发剂10份,水50份,橡胶助剂20份,缓凝剂0.5份;
其中,所述A组分和所述B组分的比例为100:90。
一种制备方法,包括如下步骤:
S1、选择丙烯酸盐水溶液95份、交联剂20份、促进剂20份和无机助剂20份放置到反应釜中搅拌50分钟,得到A组分,取出备用;
S2、把水50份、引发剂10份、橡胶助剂20份和缓凝剂0.5份放置到反应釜中搅拌50分钟,得到B组分,取出备用;
S3、按照A组分和B组分为100:90质量比进行配制,用注浆机将灌浆材料注入到裂缝或者变形缝中,得到柔性的丙烯酸盐灌浆料。
本发明的有益效果是:该配方生产出来的丙烯酸盐灌浆料收缩率大幅度降低,在90天内收缩率仅为10%~20%,大大降低了因收缩应力带来的注浆材料破坏,从而降低了复漏的风险。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (10)
1.一种新型丙烯酸盐灌浆料,其特征在于:包含A组分和B组分,其中,A组分包括丙烯酸盐水溶液70份~95份,交联剂5份~20份,促进剂1份~20份,无机助剂5份~20份;
B组分包括引发剂0.1份~10份,水5份~50份,橡胶助剂5份~20份,缓凝剂0.1份~0.5份;
其中,所述A组分和所述B组分的比例为100:80~90。
2.根据权利要求1所述的一种新型丙烯酸盐灌浆料,其特征在于:所述丙烯酸盐水溶液为丙烯酸镁、丙烯酸钙、丙烯酸锌、甲基丙烯酸镁、甲基丙烯酸钙和甲基丙烯酸锌中的一种或几种复合物。
3.根据权利要求1所述的一种新型丙烯酸盐灌浆料,其特征在于:所述交联剂为丙烯酸甲酯、丙烯酸丁酯、聚甲基丙烯酸甲酯、聚甲基丙烯酸丁酯、丙三醇、乙二醇二丙烯酸酯或季戊四醇二丙烯酸酯中的一种或几种复合物。
4.根据权利要求1所述的一种新型丙烯酸盐灌浆料,其特征在于:所述促进剂为三乙醇胺、二乙醇胺、四甲基乙二胺、三乙烯二胺、氯化亚锡和乙二醇单甲醚中的一种或几种的复合物。
5.根据权利要求1所述的一种新型丙烯酸盐灌浆料,其特征在于:所述无机助剂为氯化镁、氯化钙和氯化钠水溶液中的一种或几种复合物。
6.根据权利要求1所述的一种新型丙烯酸盐灌浆料,其特征在于:所述引发剂为过硫酸铵、过硫酸钾和过硫酸钠中的至少一种。
7.根据权利要求1所述的一种新型丙烯酸盐灌浆料,其特征在于:所述缓凝剂为铁氰化钾。
8.根据权利要求1所述的一种新型丙烯酸盐灌浆料,其特征在于:所述橡胶助剂为溶聚丁苯橡胶、水性氯化橡胶乳液、丁晴乳液、丙烯酸乳液中的至少一种。
9.根据权利要求1所述的一种新型丙烯酸盐灌浆料,其特征在于:所述包含A组分和B组分,其中,A组分包括丙烯酸盐水溶液80份,交联剂15份,促进剂15份,无机助剂15份;
B组分包括引发剂5份,水25份,橡胶助剂15份,缓凝剂0.3份;
其中,所述A组分和所述B组分的比例为100:85。
10.根据权利要求1所述的一种制备方法,其特征在于,包括如下步骤:
S1、选择丙烯酸盐水溶液80份、交联剂15份、促进剂15份和无机助剂15份放置到反应釜中搅拌30分钟~50分钟,得到A组分,取出备用;
S2、把水25份、引发剂5份、橡胶助剂15份和缓凝剂0.3份放置到反应釜中搅拌30分钟~50分钟,得到B组分,取出备用;
S3、按照A组分和B组分为100:85质量比进行配制,用注浆机将灌浆材料注入到裂缝或者变形缝中,得到柔性的丙烯酸盐灌浆料。