CN109706587A - A kind of polyamide fibre cloth processing technology that tensile strength is high - Google Patents
A kind of polyamide fibre cloth processing technology that tensile strength is high Download PDFInfo
- Publication number
- CN109706587A CN109706587A CN201811540145.5A CN201811540145A CN109706587A CN 109706587 A CN109706587 A CN 109706587A CN 201811540145 A CN201811540145 A CN 201811540145A CN 109706587 A CN109706587 A CN 109706587A
- Authority
- CN
- China
- Prior art keywords
- cloth
- polyamide fibre
- tensile strength
- degrees celsius
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polyamide fibre cloth processing technologys that tensile strength is high, including the high polyamide cloth material manufacturing technique of the high polyamide fibre cloth factory formula of tensile strength and tensile strength, the high polyamide fibre cloth factory formula of the tensile strength is as follows: polyamide fibre 45%-65%;Acid fiber by polylactic 5%-10%;Spandex 15%-20%;Bamboo charcoal fiber 5%-18%;Viscose rayon 5%-19%;Polyketone fiber 10%-18%, it is preferred that the high polyamide cloth material manufacturing technique of the tensile strength is as follows: step 1: twisting thread, and polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber are passed through in twisting machine respectively and combineeed.The polyamide fibre cloth tensile strength that the present invention solves the problems, such as that existing polyamide fibre cloth processing technology is produced is low, it is high that the high polyamide fibre cloth processing technology of the tensile strength produces polyamide fibre cloth tensile strength, the person of being convenient to use uses, and improves the application prospect of polyamide fibre cloth.
Description
Technical field
The present invention relates to polyamide fibre technical field, specially a kind of polyamide fibre cloth processing technology that tensile strength is high.
Background technique
Polyamide fibre is the first synthetic fibers occurred in the world, and polyamide fibre is a kind of saying of Fypro (nylon), brocade
The appearance of synthetic fibre makes assuming an entirely new aspect for textile, its synthesis is the important breakthrough of synthetic fiber industry, while being also high score
One extremely important milestone of sub- chemistry, polyamide are commonly called as nylon, and density 1.15g/cm3 is on molecular backbone containing repetition
The thermoplastic resin general name nylon of amide group is a kind of saying of Fypro (polyamide fibre), can be made into long fine or short fibre, brocade
Synthetic fibre is the product name of Fypro, also known as nylon, and basic component is the aliphatic connected by amido bond
Polyamide, polyamide are mainly used for synthetic fibers, and most prominent advantage is that wearability is higher than other all fibres, more resistance to than cotton
Mill property is 10 times high, 20 times higher than wool, and some Fypros are slightly entered in blended fabric, are greatly improved its wearability;
Foldings up to ten thousand time are amenable to scratch and not broken.
Polyamide fibre is one of cloth common in life, and polyamide fibre cloth is employed in every field, however existing polyamide fibre
The polyamide fibre cloth tensile strength that cloth processing technology is produced is low, it has not been convenient to which user uses, and limits polyamide fibre cloth
Application prospect.
Summary of the invention
The purpose of the present invention is to provide a kind of polyamide fibre cloth processing technologys that tensile strength is high, have tensile strength
High advantage, the polyamide fibre cloth tensile strength for solving the problems, such as that existing polyamide fibre cloth processing technology is produced are low.
To achieve the above object, the invention provides the following technical scheme: a kind of polyamide fibre cloth that tensile strength is high is processed
Technique, it is described including the high polyamide cloth material manufacturing technique of the high polyamide fibre cloth factory formula of tensile strength and tensile strength
The high polyamide fibre cloth factory formula of tensile strength is as follows:
Polyamide fibre 45%-65%;
Acid fiber by polylactic 5%-10%;
Spandex 15%-20%;
Bamboo charcoal fiber 5%-18%;
Viscose rayon 5%-19%;
Polyketone fiber 10%-18%.
Preferably, the high polyamide cloth material manufacturing technique of the tensile strength is as follows:
Step 1: twisting thread, and polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber are passed through respectively and twisted thread
Combineeed in machine, yarn is made, the ingot speed of twisting machine is controlled in 3500 rev/min to 8100 rev/min.
Step 2: warping, by polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber by twisting thread
Yarn is attached by way of knotting, is adjusted using draft regulator on warping machine by the setting of yarn made of machine
The tension of each yarn.
Step 3: woven fabric, using loom by the yarn weaving after warping at embryo cloth.
Step 4: 2 to 3 vacuum suction apparatus, adjacent vacuum is arranged in the top and bottom of the live-roller of embryo cloth in cleaning
Distance is between 50 centimetres to 100 centimetres between suction unit.
Step 5: washing, and after soda ash is added in the water in cleaning device, opens agitating device, stirring rate 100
Rev/min adjusts pH value between 8.0-9.0, is put into embryo cloth, adjustment stirring dress after cleaning agent is added to 150 rev/min
It sets, stirring rate is adjusted to 30 rev/min to 45 rev/min, to after ten minutes, is heated in cleaning device within 5 minutes
Liquid, make liquid with 2 degrees Celsius/per minute to 4 degrees Celsius/per minute speed heating, when to be promoted to 65 Celsius for fluid temperature
It when degree is to 75 degrees Celsius, is kept the temperature, continues to add cleaning agent, clean 20 minutes to 25 minutes, stop heating liquid, allow cleaning
Stop stirring when liquid in device restores to room temperature, after the liquid discharge in cleaning device, clear water is added, opens stirring dress
It sets, to closing after five minutes, rejoins clear water within 3 minutes, repeat previous step two to three times.
Step 6: the embryo cloth through over cleaning is put into dehydration device and is dehydrated by pre-setting, then dewatered embryo cloth is passed through
Live-roller, which is sent in tenter, carries out expanding, and after expanding, embryo cloth is placed in the immersion liquid that the agent of high temperature xanthochromia is added, immersion liquid
Temperature is controlled at 170 degrees Celsius to 180 degrees Celsius, is impregnated 30 minutes to after forty minutes, is immersed in clear water and clean.
Step 7: dyeing, the embryo cloth after cleaning are placed into dye vat into dyeing, and the temperature control of dye vat is Celsius 25 at this time
To 30 degrees Celsius, embryo cloth is stirred after being put into dye vat using agitating device degree, is stirred while being gradually heated up the dye in dye vat
Material, improves 4 degrees Celsius to 5 degrees Celsius per minute, when temperature rises to 140 degrees Celsius to 145 degrees Celsius, stops heating dye
Material, and 45 minutes to 50 minutes are kept the temperature, after soaking time, stops heating dye vat, the dyestuff in dye vat is allowed to be gradually brought to room
Stop stirring after temperature, the painting cloth after dyeing is taken out.
Step 8: dehydration is placed into centrifugal dehydrator after taking out the painting cloth after dyeing and is dehydrated, and removes in painting cloth
Moisture.
Step 9: drying, placing flat is dried in dryer after dewatered painting cloth is taken out, drying time 15
Minute was to 20 minutes.
Step 10: trimming tentering, the painting cloth after drying open retracting device retracting after trimming tentering.
Preferably, vacuum suction apparatus is made of blower and airscoop shroud, filtering emission pipe in the step 4 cleaning.
Preferably, in the step 5 washing, cleaning device is in closed space, and the stirring rate of agitating device is
30 rev/min to 60 rev/min.
Preferably, the dosage of the step 6 high temperature xanthochromia agent be 4 grams/often rise to 7 grams/every liter.
Preferably, the temperature of dryer is controlled at 65 degrees Celsius to 70 degrees Celsius in the step 9 drying.
Compared with prior art, beneficial effects of the present invention are as follows:
The present invention is used cooperatively by polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon and polyketone fiber, is solved
The low problem of the polyamide fibre cloth tensile strength that existing polyamide fibre cloth processing technology is produced, the tensile strength are high
Polyamide fibre cloth processing technology produces polyamide fibre cloth tensile strength height, and the person of being convenient to use uses, and improves polyamide fibre cloth
Application prospect.
Specific embodiment
The embodiments described below is only a part of the embodiment of the present invention, instead of all the embodiments.Based on this hair
Embodiment in bright, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
Embodiment 1:
A kind of polyamide fibre cloth processing technology that tensile strength is high including the high polyamide fibre cloth factory formula of tensile strength and resists
The high polyamide cloth material manufacturing technique of tensile strength, the high polyamide fibre cloth factory formula of tensile strength are as follows:
Polyamide fibre 45%;
Acid fiber by polylactic 5%;
Spandex 15%;
Bamboo charcoal fiber 5%;
Viscose rayon 15%;
Polyketone fiber 15%.
In the present invention: the high polyamide cloth material manufacturing technique of tensile strength is as follows:
Step 1: twisting thread, and polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber are passed through respectively and twisted thread
Combineeed in machine, yarn is made, the ingot speed of twisting machine is controlled in 5400 rev/min.
Step 2: warping, by polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber by twisting thread
Yarn is attached by way of knotting, is adjusted using draft regulator on warping machine by the setting of yarn made of machine
The tension of each yarn.
Step 3: woven fabric, using loom by the yarn weaving after warping at embryo cloth.
Step 4: 2 vacuum suction apparatus are arranged in the top and bottom of the live-roller of embryo cloth in cleaning, and adjacent vacuum is taken out
Inhaling distance between device is 50 centimetres, and vacuum suction apparatus is by blower and airscoop shroud, filtering emission pipe composition in step 4 cleaning.
Step 5: washing, and after soda ash is added in the water in cleaning device, opens agitating device, stirring rate 100
Rev/min, adjusting pH value is 8.0, is put into embryo cloth, adjusts agitating device after cleaning agent is added, stirring rate is adjusted to 30
Rev/min heats the liquid in cleaning device after five minutes, so that liquid is heated up with 4 degrees Celsius/speed per minute, works as liquid
It when temperature is promoted to 75 degrees Celsius, is kept the temperature, continues to add cleaning agent, clean 25 minutes, stopped heating liquid, allow cleaning
Stop stirring when liquid in device restores to room temperature, after the liquid discharge in cleaning device, clear water is added, opens stirring dress
It sets, is closed after 4 minutes, rejoin clear water, repeat previous step twice, in step 5 washing, cleaning device is closed
In space, the stirring rate of agitating device is 30 rev/min.
Step 6: the embryo cloth through over cleaning is put into dehydration device and is dehydrated by pre-setting, then dewatered embryo cloth is passed through
Live-roller, which is sent in tenter, carries out expanding, and after expanding, embryo cloth is placed in the immersion liquid that the agent of high temperature xanthochromia is added, immersion liquid
Temperature is controlled at 170 degrees Celsius to 180 degrees Celsius, is impregnated 30 minutes to after forty minutes, is immersed in clear water and clean, step 6 high temperature
The dosage of xanthochromia agent is 4 grams/every liter.
Step 7: dyeing, the embryo cloth after cleaning are placed into dye vat into dyeing, and the temperature control of dye vat is Celsius 25 at this time
Degree, embryo cloth are stirred after being put into dye vat using agitating device, are stirred while being gradually heated up the dyestuff in dye vat, mention per minute
It is 4 degrees Celsius high, when temperature rises to 140 degrees Celsius, stop heating dyestuff, and keep the temperature 45 minutes, after soaking time, stops
Dye vat is heated, allows the dyestuff in dye vat to be gradually brought to stopping stirring after room temperature, the painting cloth after dyeing is taken out.
Step 8: dehydration is placed into centrifugal dehydrator after taking out the painting cloth after dyeing and is dehydrated, and removes in painting cloth
Moisture.
Step 9: drying, placing flat is dried in dryer after dewatered painting cloth is taken out, drying time 15
Minute, the temperature of dryer is controlled at 65 degrees Celsius to 70 degrees Celsius in step 9 drying.
Step 10: trimming tentering, the painting cloth after drying open retracting device retracting after trimming tentering.
Embodiment 2:
A kind of polyamide fibre cloth processing technology that tensile strength is high including the high polyamide fibre cloth factory formula of tensile strength and resists
The high polyamide cloth material manufacturing technique of tensile strength, the high polyamide fibre cloth factory formula of tensile strength are as follows:
Polyamide fibre 55%;
Acid fiber by polylactic 8%;
Spandex 15%;
Bamboo charcoal fiber 12%;
Viscose rayon 10%;
Polyketone fiber 10%.
In the present invention: the high polyamide cloth material manufacturing technique of tensile strength is as follows:
Step 1: twisting thread, and polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber are passed through respectively and twisted thread
Combineeed in machine, yarn is made, the ingot speed of twisting machine is controlled in 8100 rev/min.
Step 2: warping, by polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber by twisting thread
Yarn is attached by way of knotting, is adjusted using draft regulator on warping machine by the setting of yarn made of machine
The tension of each yarn.
Step 3: woven fabric, using loom by the yarn weaving after warping at embryo cloth.
Step 4: 3 vacuum suction apparatus are arranged in the top and bottom of the live-roller of embryo cloth in cleaning, and adjacent vacuum is taken out
Inhaling distance between device is 100 centimetres, and vacuum suction apparatus is by blower and airscoop shroud, filtering emission pipe group in step 4 cleaning
At.
Step 5: washing, and after soda ash is added in the water in cleaning device, opens agitating device, stirring rate 120
Rev/min, adjusting pH value is 9.0, is put into embryo cloth, adjusts agitating device after cleaning agent is added, stirring rate is adjusted to 45
Rev/min heats the liquid in cleaning device after ten minutes, so that liquid is heated up with 2 degrees Celsius/speed per minute, works as liquid
It when temperature is promoted to 65 degrees Celsius, is kept the temperature, continues to add cleaning agent, clean 25 minutes, stopped heating liquid, allow cleaning
Stop stirring when liquid in device restores to room temperature, after the liquid discharge in cleaning device, clear water is added, opens stirring dress
It sets, closes after five minutes, rejoin clear water, repeat previous step three times, in step 5 washing, cleaning device is closed
In space, the stirring rate of agitating device is 55 rev/min.
Step 6: the embryo cloth through over cleaning is put into dehydration device and is dehydrated by pre-setting, then dewatered embryo cloth is passed through
Live-roller, which is sent in tenter, carries out expanding, and after expanding, embryo cloth is placed in the immersion liquid that the agent of high temperature xanthochromia is added, immersion liquid
Temperature is controlled at 180 degrees Celsius, is impregnated after forty minutes, is immersed in clear water and clean, and the dosage of step 6 high temperature xanthochromia agent is 7 grams/
Every liter.
Step 7: dyeing, the embryo cloth after cleaning are placed into dye vat into dyeing, and the temperature control of dye vat is Celsius 28 at this time
Degree, embryo cloth are stirred after being put into dye vat using agitating device, are stirred while being gradually heated up the dyestuff in dye vat, mention per minute
It is 5 degrees Celsius high, when temperature rises to 145 degrees Celsius, stop heating dyestuff, and keep the temperature 45 minutes, after soaking time, stops
Dye vat is heated, allows the dyestuff in dye vat to be gradually brought to stopping stirring after room temperature, the painting cloth after dyeing is taken out.
Step 8: dehydration is placed into centrifugal dehydrator after taking out the painting cloth after dyeing and is dehydrated, and removes in painting cloth
Moisture.
Step 9: drying, placing flat is dried in dryer after dewatered painting cloth is taken out, drying time 20
Minute, the temperature of dryer is controlled at 70 degrees Celsius in step 9 drying.
Step 10: trimming tentering, the painting cloth after drying open retracting device retracting after trimming tentering.
In summary: the high polyamide fibre cloth processing technology of the tensile strength passes through polyamide fibre, acid fiber by polylactic, spandex, bamboo
Carbon fibe, viscose rayon and polyketone fiber are used cooperatively, and solve the brocade that existing polyamide fibre cloth processing technology is produced
The low problem of synthetic fibre cloth tensile strength.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
The electric elements occurred in this article are electrically connected with extraneous main controller and 220V alternating current, and main controller can be meter
Calculation machine etc. plays the conventionally known equipment of control.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of polyamide fibre cloth processing technology that tensile strength is high, including the high polyamide fibre cloth factory formula of tensile strength and
The high polyamide cloth material manufacturing technique of tensile strength, it is characterised in that: the high polyamide fibre cloth factory formula of the tensile strength
It is as follows:
Polyamide fibre 45%-65%;
Acid fiber by polylactic 5%-10%;
Spandex 15%-20%;
Bamboo charcoal fiber 5%-18%;
Viscose rayon 5%-19%;
Polyketone fiber 10%-18%.
2. a kind of high polyamide fibre cloth processing technology of tensile strength according to claim 1, it is characterised in that: described anti-
The high polyamide cloth material manufacturing technique of tensile strength is as follows:
Step 1: twisting thread, and polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber are passed through respectively and twisted thread
Combineeed in machine, yarn is made, the ingot speed of twisting machine is controlled in 3500 rev/min to 8100 rev/min;
Step 2: polyamide fibre, acid fiber by polylactic, spandex, bamboo charcoal fiber, viscose rayon, polyketone fiber are passed through the mechanism of twisting thread by warping
At yarn setting with warping machine on, yarn is attached by way of knotting, is adjusted using draft regulator each
The tension of yarn;
Step 3: woven fabric, using loom by the yarn weaving after warping at embryo cloth;
Step 4: 2 to 3 vacuum suction apparatus, adjacent vacuum suction is arranged in the top and bottom of the live-roller of embryo cloth in cleaning
Distance is between 50 centimetres to 100 centimetres between device;
Step 5: washing after soda ash is added in the water in cleaning device, opens agitating device, and stirring rate is 100 turns/it is every
Minute to 150 rev/min, adjusting pH value is put into embryo cloth between 8.0-9.0, adjusts agitating device after cleaning agent is added, will
Stirring rate is adjusted to 30 rev/min to 45 rev/min, to after ten minutes, heats the liquid in cleaning device within 5 minutes,
Make liquid with 2 degrees Celsius/per minute to 4 degrees Celsius/per minute speed heating, when fluid temperature is promoted to 65 degrees Celsius to 75
Degree Celsius when, kept the temperature, continue to add cleaning agent, clean 20 minutes to 25 minutes, stopped heating liquid, allow in cleaning device
Liquid stop stirring when restoring to room temperature, after the liquid discharge in cleaning device, clear water is added, opens agitating device, 3 points
Clock rejoins clear water to closing after five minutes, repeats previous step two to three times;
Step 6: the embryo cloth through over cleaning is put into dehydration device and is dehydrated by pre-setting, then dewatered embryo cloth is passed through transmission
Roller, which is sent in tenter, carries out expanding, after expanding, embryo cloth is placed in the immersion liquid that the agent of high temperature xanthochromia is added, the temperature of immersion liquid
Control impregnates 30 minutes to after forty minutes, immerses in clear water and clean at 170 degrees Celsius to 180 degrees Celsius;
Step 7: dyeing, the embryo cloth after cleaning are placed into dye vat into dyeing, and the temperature of dye vat is controlled at 25 degrees Celsius extremely at this time
30 degrees Celsius, embryo cloth is stirred after being put into dye vat using agitating device, is stirred while being gradually heated up the dyestuff in dye vat, often
Minute improves 4 degrees Celsius to 5 degrees Celsius, when temperature rises to 140 degrees Celsius to 145 degrees Celsius, stops heating dyestuff, and protect
Temperature 45 minutes to 50 minutes after soaking time, stops heating dye vat, stops after allowing the dyestuff in dye vat to be gradually brought to room temperature
The painting cloth after dyeing is taken out in stirring;
Step 8: dehydration is placed into centrifugal dehydrator after taking out the painting cloth after dyeing and is dehydrated, and removes the water in painting cloth
Point;
Step 9: drying, placing flat is dried in dryer after dewatered painting cloth is taken out, and drying time is 15 minutes
To 20 minutes;
Step 10: trimming tentering, the painting cloth after drying open retracting device retracting after trimming tentering.
3. a kind of high polyamide fibre cloth processing technology of tensile strength according to claim 2, it is characterised in that: the step
Vacuum suction apparatus is by blower and airscoop shroud, filtering emission pipe composition in rapid four cleaning.
4. a kind of high polyamide fibre cloth processing technology of tensile strength according to claim 2, it is characterised in that: the step
In rapid five washing, cleaning device be in closed space, the stirring rate of agitating device be 30 rev/min to 60 turns/often
Minute.
5. a kind of high polyamide fibre cloth processing technology of tensile strength according to claim 2, it is characterised in that: the step
The dosage of rapid six high temperature xanthochromia agent be 4 grams/often rise to 7 grams/every liter.
6. a kind of high polyamide fibre cloth processing technology of tensile strength according to claim 2, it is characterised in that: the step
The temperature of dryer is controlled at 65 degrees Celsius to 70 degrees Celsius in rapid nine drying.