CN106987948A - A kind of production method of the blended yarn weaved fabric of cotton fiber and sisal fiber - Google Patents
A kind of production method of the blended yarn weaved fabric of cotton fiber and sisal fiber Download PDFInfo
- Publication number
- CN106987948A CN106987948A CN201710180144.3A CN201710180144A CN106987948A CN 106987948 A CN106987948 A CN 106987948A CN 201710180144 A CN201710180144 A CN 201710180144A CN 106987948 A CN106987948 A CN 106987948A
- Authority
- CN
- China
- Prior art keywords
- fiber
- sisal fiber
- sisal
- blended yarn
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses the production method of a kind of cotton fiber and the blended yarn weaved fabric of sisal fiber, the production method includes the preparation of sisal fiber, the preparation of sliver, the preparation of sisal fiber bar, the drafting of blended yarn weaved fabric, coarse sand, spun yarn operation.The blended yarn weaved fabric of the present invention, fabric is produced using the composite fibre of sisal fiber and cotton fiber, and compact spinning has been used in spun yarn operation so that composite fibre arrangement is close, improves the fracture strength and tearing resistance of blending, and fabric flat smooth, feel is preferable.
Description
Technical field
The present invention relates to textile technology field, and in particular to a kind of producer of the blended yarn weaved fabric of cotton fiber and sisal fiber
Method.
Background technology
Blending chemical ＆ blended fabric is that chemical fibre waits until that natural fiber mixes the weaving that spinning is made into other cotton wools, silk, fiber crops
Product.For example：Polyester-mixed cotton cloth, wash mao gabardine etc..Polyester cotton blending thing be using terylene as Main Ingredients and Appearance, using 65%-67% terylene and
The textile that 33%-35% cotton mixed yarn is made into, polyester-mixed cotton cloth is commonly called as that cotton is really cool, has not only highlighted the style of terylene but also has had cotton to knit
The strong point of thing, elasticity and wearability are all preferable in the case of dry, wet, and dimensionally stable, washing shrinkage is small, with it is tall and straight, be difficult fold,
The characteristics of washable, quick-drying, it is impossible to soaked with hot iron and boiling water.
Sisal fiber gel content is high, and fibrous fracture intensity is high, and rigidity is big, and elasticity and retractility are smaller, thus spinnability is poor,
Resultant yarn is uneven.How sisal fiber is extracted, it is increased in terms of fineness and pliability, be also that sisal fiber extracts work
The larger technical barrier of industry.
Authorization Notice No. CN104846507B patent of invention discloses a kind of short fine blending work fine with cotton of polyesteramide
Fill fabric, this kind of tooling fabric, through drafting, rove, spinning process after the fine each blowing of the short fine and cotton of polyesteramide and cotton carding
Scribbled is made, then is made by the scribbled by weaving process.The invention is entered using composite fibre with high quality cotton fibre
Row blending so that yarn and fabric strength are more preferably, feel is more preferable, regain is higher, anti-fuzz balls advantage, but stretch-proof is strong
Degree is also because the addition of polyesteramide has obvious reduction.
The content of the invention
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, there is provided the mixed of a kind of cotton fiber and sisal fiber
The production method of textile fabric, the method increase the fineness and pliability of sisal fiber, and the sisal fiber blending fine with cotton causes
Fabric elastic force is good, and intensity is high, and feel is more preferable.
The present invention solves technical problem and adopted the following technical scheme that：
The invention provides the production method of a kind of cotton fiber and the blended yarn weaved fabric of sisal fiber, comprise the following steps：
（1）The preparation of sisal fiber：The surface colloid of sisal leaves is struck off using blade, the sodium chloride water that concentration is 3-8% is put into
Immersion cures fiber in 3-6 minutes in solution, reuses sodium hydroxide solution heating stirring 3-5 hours, filters while hot, uses water
Rinse, the pH value of fiber is reached after 6.5-7.2, be put into convection oven and be dried to obtain sisal fiber；
（2）The preparation of sliver：The cotton of selection function admirable carries out blowing, combing successively, in combing process, the lower 35-38% of comb
Short flannel and impurity, be made sliver；
（3）The preparation of sisal fiber bar：After oil supply is carried out to sisal fiber, being dehydrated, shake up again, it is ensured that the water content of sisal fiber
After 30%, then blowing, cotton carding operation are carried out, obtain sisal fiber bar；
（4）The drafting of blended yarn weaved fabric, coarse sand, spun yarn operation：The sliver and sisal fiber bar are carried out after 6-8 drafting, then
By drawing-off so that composite fibre bar stretches parallel, it is subject to 5-8 turn and obtains ripe bar, then carries out rove, spun yarn operation, its
In, spun yarn operation is carried out using compact spinning, the blended yarn weaved fabric is made.
Preferably, the step（1）The middle sodium-chloride water solution temperature used is 40-45 DEG C.
Preferably, the step（1）The concentration of the middle sodium hydroxide solution used is 3-5%.
Preferably, the step（1）The condition for being put into convection oven drying is dry 2-3 hours for 50-60 DEG C.
Preferably, the step（2）Cotton variety be selected from 127,128,129 or 130.
Preferably, the step（3）Oil supply operation be by sisal fiber oil emulsion in impregnate 40-50 minutes.
Preferably, the oily emulsion in parts by weight, including 60-80 parts vegetable oil, 5-10 parts of sodium carbonate, ten
3-5 parts of sodium dialkyl sulfate, 0.5-2 parts of calgon, 30-50 parts of water.
Preferably, the step（4）Weaving process parameter is specially：800~1000 revs/min of speed, injecting time is
85 °, heald level time is 360 °, and clamper traverse is 0.6mm, and clamper closing time is 360 °, and the flying angle open hour are
120 °, left strand side closing time is 30 °, and right strand side closing time is 300 °, and warp tension is 30~35cN/cm.
Compared with prior art, the present invention has following beneficial effect：
（1）The blended yarn weaved fabric of the present invention, fabric is produced using the composite fibre of sisal fiber and cotton fiber, is made in spun yarn operation
With compact spinning so that composite fibre arrangement is close, and mutual cohesive force is big, improves the intensity of blending, and fabric is smooth
It is smooth.
（2）The preparation of the sisal fiber of the present invention, scrapes a large amount of colloids except sisal leaves surface, sodium chloride is molten using blade
Liquid causes sisal fiber to cure, and the heating stirring of sodium hydroxide solution also been removed pectin, hemicellulose, lignin and other glue
Matter, obtained sisal fiber is enhanced in terms of fineness and pliability.
Embodiment
Invention is described in further detail below in conjunction with specific embodiment.
Embodiment 1.
A kind of production method of the blended yarn weaved fabric of cotton fiber and sisal fiber, comprises the following steps：
（1）The preparation of sisal fiber：The surface colloid of sisal leaves is struck off using blade, be put into temperature be 40-45 DEG C, concentration be
Immersion cures fiber in 3-6 minutes in 3% sodium-chloride water solution, reuses the sodium hydroxide solution heating stirring that concentration is 3%
3-5 hours, filter, rinsed using water while hot, the pH value of fiber is reached after 6.5-7.2, be put into convection oven, 50-60 DEG C is done
Dry 2-3 hours obtains sisal fiber；
（2）The preparation of sliver：127 cottons of selection function admirable carry out blowing, combing successively, in combing process, the lower 35- of comb
38% short flannel and impurity, is made sliver；
（3）The preparation of sisal fiber bar：After oil supply is carried out to sisal fiber, being dehydrated, shake up again, it is ensured that the water content of sisal fiber
After 30%, then blowing, cotton carding operation are carried out, obtain sisal fiber bar；
（4）The drafting of blended yarn weaved fabric, coarse sand, spun yarn operation：The sliver and sisal fiber bar are carried out after 6-8 drafting, then
By drawing-off so that composite fibre bar stretches parallel, it is subject to 5-8 turn and obtains ripe bar, then carries out rove, spun yarn operation, its
In, spun yarn operation is carried out using compact spinning, the blended yarn weaved fabric is made.
Wherein, oil supply operation is to impregnate sisal fiber 40-50 minutes in the emulsion of oil.The emulsion of oil is with weight
Part meter, including 60-80 parts vegetable oil, 5-10 parts of sodium carbonate, 3-5 parts of lauryl sodium sulfate, calgon 0.5-2
Part, 30-50 parts of water.Step（4）Weaving process parameter is specially：800~1000 revs/min of speed, injecting time is 85 °, comprehensive
It is 360 ° between usually, clamper traverse is 0.6mm, clamper closing time is 360 °, and the flying angle open hour are 120 °, left to twist
Side closing time is 30 °, and right strand side closing time is 300 °, and warp tension is 30~35cN/cm.
Embodiment 2.
A kind of production method of the blended yarn weaved fabric of cotton fiber and sisal fiber, comprises the following steps：
（1）The preparation of sisal fiber：The surface colloid of sisal leaves is struck off using blade, be put into temperature be 40-45 DEG C, concentration be
Immersion cures fiber in 3-6 minutes in 5% sodium-chloride water solution, reuses the sodium hydroxide solution heating stirring that concentration is 4%
3-5 hours, filter, rinsed using water while hot, the pH value of fiber is reached after 6.5-7.2, be put into convection oven, 50-60 DEG C is done
Dry 2-3 hours obtains sisal fiber；
（2）The preparation of sliver：128 cottons of selection function admirable carry out blowing, combing successively, in combing process, the lower 35- of comb
38% short flannel and impurity, is made sliver；
（3）The preparation of sisal fiber bar：After oil supply is carried out to sisal fiber, being dehydrated, shake up again, it is ensured that the water content of sisal fiber
After 30%, then blowing, cotton carding operation are carried out, obtain sisal fiber bar；
（4）The drafting of blended yarn weaved fabric, coarse sand, spun yarn operation：The sliver and sisal fiber bar are carried out after 6-8 drafting, then
By drawing-off so that composite fibre bar stretches parallel, it is subject to 5-8 turn and obtains ripe bar, then carries out rove, spun yarn operation, its
In, spun yarn operation is carried out using compact spinning, the blended yarn weaved fabric is made.
Wherein, oil supply operation is to impregnate sisal fiber 40-50 minutes in the emulsion of oil.The emulsion of oil is with weight
Part meter, including 60-80 parts vegetable oil, 5-10 parts of sodium carbonate, 3-5 parts of lauryl sodium sulfate, calgon 0.5-2
Part, 30-50 parts of water.Step（4）Weaving process parameter is specially：800~1000 revs/min of speed, injecting time is 85 °, comprehensive
It is 360 ° between usually, clamper traverse is 0.6mm, clamper closing time is 360 °, and the flying angle open hour are 120 °, left to twist
Side closing time is 30 °, and right strand side closing time is 300 °, and warp tension is 30~35cN/cm.
Embodiment 3.
A kind of production method of the blended yarn weaved fabric of cotton fiber and sisal fiber, comprises the following steps：
（1）The preparation of sisal fiber：The surface colloid of sisal leaves is struck off using blade, be put into temperature be 40-45 DEG C, concentration be
Immersion cures fiber in 3-6 minutes in 6% sodium-chloride water solution, reuses the sodium hydroxide solution heating stirring that concentration is 5%
3-5 hours, filter, rinsed using water while hot, the pH value of fiber is reached after 6.5-7.2, be put into convection oven, 50-60 DEG C is done
Dry 2-3 hours obtains sisal fiber；
（2）The preparation of sliver：129 cottons of selection function admirable carry out blowing, combing successively, in combing process, the lower 35- of comb
38% short flannel and impurity, is made sliver；
（3）The preparation of sisal fiber bar：After oil supply is carried out to sisal fiber, being dehydrated, shake up again, it is ensured that the water content of sisal fiber
After 30%, then blowing, cotton carding operation are carried out, obtain sisal fiber bar；
（4）The drafting of blended yarn weaved fabric, coarse sand, spun yarn operation：The sliver and sisal fiber bar are carried out after 6-8 drafting, then
By drawing-off so that composite fibre bar stretches parallel, it is subject to 5-8 turn and obtains ripe bar, then carries out rove, spun yarn operation, its
In, spun yarn operation is carried out using compact spinning, the blended yarn weaved fabric is made.
Wherein, oil supply operation is to impregnate sisal fiber 40-50 minutes in the emulsion of oil.The emulsion of oil is with weight
Part meter, including 60-80 parts vegetable oil, 5-10 parts of sodium carbonate, 3-5 parts of lauryl sodium sulfate, calgon 0.5-2
Part, 30-50 parts of water.Step（4）Weaving process parameter is specially：800~1000 revs/min of speed, injecting time is 85 °, comprehensive
It is 360 ° between usually, clamper traverse is 0.6mm, clamper closing time is 360 °, and the flying angle open hour are 120 °, left to twist
Side closing time is 30 °, and right strand side closing time is 300 °, and warp tension is 30~35cN/cm.
Embodiment 4.
A kind of production method of the blended yarn weaved fabric of cotton fiber and sisal fiber, comprises the following steps：
（1）The preparation of sisal fiber：The surface colloid of sisal leaves is struck off using blade, be put into temperature be 40-45 DEG C, concentration be
Immersion cures fiber in 3-6 minutes in 8% sodium-chloride water solution, reuses the sodium hydroxide solution heating stirring that concentration is 5%
3-5 hours, filter, rinsed using water while hot, the pH value of fiber is reached after 6.5-7.2, be put into convection oven, 50-60 DEG C is done
Dry 2-3 hours obtains sisal fiber；
（2）The preparation of sliver：130 cottons of selection function admirable carry out blowing, combing successively, in combing process, the lower 35- of comb
38% short flannel and impurity, is made sliver；
（3）The preparation of sisal fiber bar：After oil supply is carried out to sisal fiber, being dehydrated, shake up again, it is ensured that the water content of sisal fiber
After 30%, then blowing, cotton carding operation are carried out, obtain sisal fiber bar；
（4）The drafting of blended yarn weaved fabric, coarse sand, spun yarn operation：The sliver and sisal fiber bar are carried out after 6-8 drafting, then
By drawing-off so that composite fibre bar stretches parallel, it is subject to 5-8 turn and obtains ripe bar, then carries out rove, spun yarn operation, its
In, spun yarn operation is carried out using compact spinning, the blended yarn weaved fabric is made.
Wherein, oil supply operation is to impregnate sisal fiber 40-50 minutes in the emulsion of oil.The emulsion of oil is with weight
Part meter, including 60-80 parts vegetable oil, 5-10 parts of sodium carbonate, 3-5 parts of lauryl sodium sulfate, calgon 0.5-2
Part, 30-50 parts of water.Step（4）Weaving process parameter is specially：800~1000 revs/min of speed, injecting time is 85 °, comprehensive
It is 360 ° between usually, clamper traverse is 0.6mm, clamper closing time is 360 °, and the flying angle open hour are 120 °, left to twist
Side closing time is 30 °, and right strand side closing time is 300 °, and warp tension is 30~35cN/cm.
The ultimate strength and tearing brute force of blended yarn weaved fabric made from above-described embodiment 1-4 are detected, data such as following table
It is shown, wherein, the examination criteria of fabric ultimate strength is GB 12014-2009 4.1.3, the examination criteria of fabric tearing brute force
For GB/T 3917.3-2009.
| Embodiment | Warp-wise ultimate strength/N | Broadwise ultimate strength/N | Warp-wise tearing brute force/N | Broadwise tearing brute force/N |
| 1 | 920 | 412 | 30 | 18 |
| 2 | 926 | 425 | 32 | 20 |
| 3 | 932 | 428 | 36 | 22 |
| 4 | 935 | 431 | 39 | 26 |
As can be seen from the above table, blended yarn weaved fabric ultimate strength of the invention and tearing brute force are higher, are especially suitable for extensive
Production.
Described above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (8)
1. the production method of the blended yarn weaved fabric of a kind of cotton fiber and sisal fiber, it is characterised in that comprise the following steps：
（1）The preparation of sisal fiber：The surface colloid of sisal leaves is struck off using blade, the sodium chloride water that concentration is 3-8% is put into
Immersion cures fiber in 3-6 minutes in solution, reuses sodium hydroxide solution heating stirring 3-5 hours, filters while hot, uses water
Rinse, the pH value of fiber is reached after 6.5-7.2, be put into convection oven and be dried to obtain sisal fiber；
（2）The preparation of sliver：The cotton of selection function admirable carries out blowing, combing successively, in combing process, the lower 35-38% of comb
Short flannel and impurity, be made sliver；
（3）The preparation of sisal fiber bar：After oil supply is carried out to sisal fiber, being dehydrated, shake up again, it is ensured that the water content of sisal fiber
After 30%, then blowing, cotton carding operation are carried out, obtain sisal fiber bar；
（4）The drafting of blended yarn weaved fabric, coarse sand, spun yarn operation：The sliver and sisal fiber bar are carried out after 6-8 drafting, then
By drawing-off so that composite fibre bar stretches parallel, it is subject to 5-8 turn and obtains ripe bar, then carries out rove, spun yarn operation, its
In, spun yarn operation is carried out using compact spinning, the blended yarn weaved fabric is made.
2. the production method of the blended yarn weaved fabric of cotton fiber according to claim 1 and sisal fiber, it is characterised in that described
Step（1）The middle sodium-chloride water solution temperature used is 40-45 DEG C.
3. the production method of the blended yarn weaved fabric of cotton fiber according to claim 1 and sisal fiber, it is characterised in that described
Step（1）The concentration of the middle sodium hydroxide solution used is 3-5%.
4. the production method of the blended yarn weaved fabric of cotton fiber according to claim 1 and sisal fiber, it is characterised in that described
Step（1）The condition for being put into convection oven drying is dry 2-3 hours for 50-60 DEG C.
5. the production method of the blended yarn weaved fabric of cotton fiber according to claim 1 and sisal fiber, it is characterised in that described
Step（2）Cotton variety be selected from 127,128,129 or 130.
6. the production method of the blended yarn weaved fabric of cotton fiber according to claim 1 and sisal fiber, it is characterised in that described
Step（3）Oil supply operation be by sisal fiber oil emulsion in impregnate 40-50 minutes.
7. the production method of the blended yarn weaved fabric of cotton fiber according to claim 6 and sisal fiber, it is characterised in that described
Oil emulsion in parts by weight, including 60-80 parts vegetable oil, 5-10 parts of sodium carbonate, 3-5 parts of lauryl sodium sulfate,
0.5-2 parts of calgon, 30-50 parts of water.
8. the production method of the blended yarn weaved fabric of cotton fiber according to claim 1 and sisal fiber, it is characterised in that described
Step（4）Weaving process parameter is specially：800~1000 revs/min of speed, injecting time is 85 °, and heald level time is 360 °,
Clamper traverse is 0.6mm, and clamper closing time is 360 °, and the flying angle open hour are 120 °, and left strand side closing time is
30 °, right strand side closing time is 300 °, and warp tension is 30~35cN/cm.