CN104818570A - Knitted full nylon Roma fabric and production technology thereof - Google Patents
Knitted full nylon Roma fabric and production technology thereof Download PDFInfo
- Publication number
- CN104818570A CN104818570A CN201510194196.7A CN201510194196A CN104818570A CN 104818570 A CN104818570 A CN 104818570A CN 201510194196 A CN201510194196 A CN 201510194196A CN 104818570 A CN104818570 A CN 104818570A
- Authority
- CN
- China
- Prior art keywords
- polyamide fibre
- production technology
- nylon
- yarns
- addition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a knitted full nylon Roma fabric and production technology thereof, and belongs to the technical field of textile fabrics. 70D nylon and 40D polyurethane are twisted to form yarns, the yarns are woven to form the knitted full nylon Roma fabric, or 50D nylon and 40D polyurethane are twisted to form yarns, and the yarns are woven to form the knitted full nylon Roma fabric. The production technology particularly includes the steps: twisting the 70D nylon and the 40D polyurethane to form the yarns, weaving the yarns to form gray fabrics, or twisting the 50D nylon and the 40D polyurethane to form the yarns, and weaving the yarns to form the gray fabrics; unrolling; cold stacking; flattening; presetting; pre-treating; dyeing; scotching, drying; sizing finished products; rolling and packaging. The knitted full nylon Roma fabric is fine in abrasion resistance, comfort, elastic recovery and breathability, free of constraint and suitable for producing various garments including jackets, underwear and the like.
Description
Technical field
The present invention relates to a kind of knitting full polyamide fibre Roman cloth and production technology thereof, belong to the technical field of weaving face fabric.
Background technology
Nylon fabric is owing to having excellent ABRASION RESISTANCE, and the application therefore in clothes is comparatively extensive.But simultaneously because its comfortableness is general, be therefore mainly used in making overcoat.In order to expand the range of application of nylon fabric, this case produces thus.
Summary of the invention
The object of this invention is to provide a kind of ABRASION RESISTANCE is good, comfortableness is good, elastic recovery is good knitting full polyamide fibre Roman cloth and production technology thereof.
For achieving the above object, the technical solution adopted in the present invention is:
A kind of knitting full polyamide fibre Roman cloth, adopts the yarn weaving after the twisting of the spandex of the polyamide fibre of 70D and 40D to form, or adopts the yarn weaving after the twisting of the spandex of the polyamide fibre of 50D and 40D to form.
A production technology for knitting full polyamide fibre Roman cloth, comprises the following steps:
Yarn weaving after being twisted with the spandex of 40D by the polyamide fibre of 70D becomes grey cloth, or the yarn weaving after being twisted with the spandex of 40D by the polyamide fibre of 50D becomes grey cloth → debatching → cold dome → smooth → predetermined → pre-treatment → dyeing → open-width → oven dry → finished product sizing → clot, packaging.
As the further setting of such scheme, in the operation of described pre-treatment, the water temperature in machine cylinder, when 30-40 DEG C, adds refining agent, degreaser, bleeding agent stirring, after being then warming up to 90-100 DEG C with the speed of 1 DEG C/min, and insulation 30-50min.Because the greasy dirt on chemical fiber plus material, slurry are more, so just higher to the requirement of emulsifying effectiveness when doing pre-treatment, also meticulous selection will be carried out to auxiliary agent, the temperature of pre-treatment can not be too high, because grey cloth ratio is easier to occur that shank prints, so in pre-treatment of the present invention, select the temperature at 90-100 DEG C to be incubated, the speeds control of intensification is at 1 DEG C/min.
In the operation of described dyeing, water temperature in machine cylinder, when 30-40 DEG C, adds ACID DYES, acid levelling agent, glacial acetic acid stirring, after being then warming up to 95-100 DEG C with the speed of 1 DEG C/min, insulation 30-50min, is finally down to normal temperature with the speed of 1 DEG C/min.For avoiding producing look flower, the present invention, in dyeing process, will be elevated the speeds control of temperature at 1 DEG C/min.
In the operation of described finished product sizing, the speed of a motor vehicle is 22-25m/min, and temperature is 160-180 DEG C.For effectively avoiding the knitting full polyamide fibre Roman cloth of the present invention to produce the phenomenon of hardening, the speed of a motor vehicle controls at 22-25m/min by the present invention, and temperature controls at 160-180 DEG C.
The addition of described refining agent is 1-3g/L, and the addition of degreaser is 2-5g/L, and the addition of bleeding agent is 2-5g/L.
The addition of described acid levelling agent is 1-4g/L, and the addition of glacial acetic acid is 2-4g/L.Glacial acetic acid is used for control ph at 4.2-4.8.
In the knitting full polyamide fibre Roman cloth of the present invention, the blending ratio between polyamide fibre and spandex during dry weight is 90-93%:7-10%.
The knitting full polyamide fibre Roman cloth of the present invention, ABRASION RESISTANCE is good, comfortableness is good, good, the chainless sense of elastic recovery, good permeability, be suitable for making all kinds of clothes, comprise overcoat, underclothes etc.Adopt the clothes made by the knitting full polyamide fibre Roman cloth of the present invention, the good woman body of stature especially can be made more to highlight.
The knitting full polyamide fibre Roman cloth of the present invention can reach following technical indicator:
Water-fastness COLOR FASTNESS >=4 grade;
Colour fastness to perspiration >=3 grade;
Colour fastness to rubbing (unlubricated friction) >=4 grade;
Colour fastness to rubbing (wet and rub) >=3 grades;
Washing size changing rate (radial direction) is within-4%;
Washing size changing rate (broadwise) is within-2%;
Ultimate strength (radial direction): 1100N-1200N;
Ultimate strength (broadwise): 600N-700N;
Anti-pilling >=3 grade;
Ecological index: free formaldehyde content≤20mg/kg.
Detailed description of the invention
Below by specific embodiment, the invention will be further described, but the present invention not limited by following examples.
Embodiment 1
The knitting full polyamide fibre Roman cloth of the present invention, adopts the yarn weaving after the twisting of the spandex of the polyamide fibre of 70D and 40D to form.
The production technology of the knitting full polyamide fibre Roman cloth of the present invention, comprises the following steps:
Yarn weaving after being twisted with the spandex of 40D by the polyamide fibre of 70D becomes grey cloth → debatching → cold dome → smooth → predetermined → pre-treatment → dyeing → open-width → oven dry → finished product sizing → clot, packaging.
Wherein, in the operation of pre-treatment, the water temperature in machine cylinder, 30 DEG C time, adds refining agent, degreaser, bleeding agent stirring, after being then warming up to 90 DEG C with the speed of 1 DEG C/min, and insulation 50min.The addition of refining agent is 1g/L, and the addition of degreaser is 2g/L, and the addition of bleeding agent is 2g/L.
In the operation of dyeing, water temperature in machine cylinder, 30 DEG C time, adds ACID DYES (ACID DYES that market is sold), acid levelling agent, glacial acetic acid stir, after being then warming up to 95 DEG C with the speed of 1 DEG C/min, insulation 50min, is finally down to normal temperature with the speed of 1 DEG C/min.The addition of acid levelling agent is 1g/L, and the addition of glacial acetic acid is 2g/L.
In the operation of finished product sizing, the speed of a motor vehicle is 22m/min, and temperature is 160 DEG C.
Embodiment 2
The knitting full polyamide fibre Roman cloth of the present invention, adopts the yarn weaving after the twisting of the spandex of the polyamide fibre of 70D and 40D to form.
The production technology of the knitting full polyamide fibre Roman cloth of the present invention, comprises the following steps:
Yarn weaving after being twisted with the spandex of 40D by the polyamide fibre of 70D becomes grey cloth → debatching → cold dome → smooth → predetermined → pre-treatment → dyeing → open-width → oven dry → finished product sizing → clot, packaging.
Wherein, in the operation of pre-treatment, the water temperature in machine cylinder, 40 DEG C time, adds refining agent, degreaser, bleeding agent stirring, after being then warming up to 100 DEG C with the speed of 1 DEG C/min, and insulation 30min.The addition of refining agent is 3g/L, and the addition of degreaser is 5g/L, and the addition of bleeding agent is 5g/L.
In the operation of dyeing, water temperature in machine cylinder, 40 DEG C time, adds ACID DYES (ACID DYES that market is sold), acid levelling agent, glacial acetic acid stir, after being then warming up to 100 DEG C with the speed of 1 DEG C/min, insulation 30min, is finally down to normal temperature with the speed of 1 DEG C/min.The addition of acid levelling agent is 4g/L, and the addition of glacial acetic acid is 4g/L.
In the operation of finished product sizing, the speed of a motor vehicle is 25m/min, and temperature is 180 DEG C.
Embodiment 3
The knitting full polyamide fibre Roman cloth of the present invention, adopts the yarn weaving after the twisting of the spandex of the polyamide fibre of 50D and 40D to form.
The production technology of the knitting full polyamide fibre Roman cloth of the present invention, comprises the following steps:
Yarn weaving after being twisted with the spandex of 40D by the polyamide fibre of 50D becomes grey cloth → debatching → cold dome → smooth → predetermined → pre-treatment → dyeing → open-width → oven dry → finished product sizing → clot, packaging.
Wherein, in the operation of pre-treatment, the water temperature in machine cylinder, 35 DEG C time, adds refining agent, degreaser, bleeding agent stirring, after being then warming up to 95 DEG C with the speed of 1 DEG C/min, and insulation 40min.The addition of refining agent is 2g/L, and the addition of degreaser is 3g/L, and the addition of bleeding agent is 3g/L.
In the operation of dyeing, water temperature in machine cylinder, 35 DEG C time, adds ACID DYES (ACID DYES that market is sold), acid levelling agent, glacial acetic acid stir, after being then warming up to 98 DEG C with the speed of 1 DEG C/min, insulation 40min, is finally down to normal temperature with the speed of 1 DEG C/min.The addition of acid levelling agent is 2g/L, and the addition of glacial acetic acid is 3g/L.
In the operation of finished product sizing, the speed of a motor vehicle is 23m/min, and temperature is 170 DEG C.
Above in all embodiments, refining agent all selects the YJ-9611A of Shaoxing Zhendong Chemicals Co., Ltd. to permeate refining agent; Degreaser all selects the TF-109A degreaser of Zhejiang Province Chuanhua Co., Ltd; The nonionic penetrant of Hangzhou Meigao Huayi Chemical Industry Co., Ltd all selected by bleeding agent; The acid levelling agent of the HD-362L of Han Ke Fine Chemical Co., Ltd of Zhongshan city all selected by acid levelling agent.
Above-described embodiment only illustrates inventive concept of the present invention for explaining, but not the restriction to rights protection of the present invention, all changes utilizing this design the present invention to be carried out to unsubstantiality, all should fall into protection scope of the present invention.
Claims (7)
1. a knitting full polyamide fibre Roman cloth, is characterized in that: adopt the yarn weaving after the twisting of the spandex of the polyamide fibre of 70D and 40D to form, or adopts the yarn weaving after the twisting of the spandex of the polyamide fibre of 50D and 40D to form.
2. the production technology of knitting full polyamide fibre Roman cloth as claimed in claim 1, is characterized in that comprising the following steps:
Yarn weaving after being twisted with the spandex of 40D by the polyamide fibre of 70D becomes grey cloth, or the yarn weaving after being twisted with the spandex of 40D by the polyamide fibre of 50D becomes grey cloth → debatching → cold dome → smooth → predetermined → pre-treatment → dyeing → open-width → oven dry → finished product sizing → clot, packaging.
3. the production technology of knitting full polyamide fibre Roman cloth as claimed in claim 2, it is characterized in that: in the operation of described pre-treatment, water temperature in machine cylinder is when 30-40 DEG C, add refining agent, degreaser, bleeding agent stirring, then after being warming up to 90-100 DEG C with the speed of 1 DEG C/min, insulation 30-50min.
4. the production technology of knitting full polyamide fibre Roman cloth as claimed in claim 2, it is characterized in that: in the operation of described dyeing, water temperature in machine cylinder is when 30-40 DEG C, add ACID DYES, acid levelling agent, glacial acetic acid stirring, then after being warming up to 95-100 DEG C with the speed of 1 DEG C/min, insulation 30-50min, is finally down to normal temperature with the speed of 1 DEG C/min.
5. the production technology of knitting full polyamide fibre Roman cloth as claimed in claim 2, is characterized in that: in the operation of described finished product sizing, the speed of a motor vehicle is 22-25m/min, and temperature is 160-180 DEG C.
6. the production technology of knitting full polyamide fibre Roman cloth as claimed in claim 3, it is characterized in that: the addition of described refining agent is 1-3g/L, the addition of degreaser is 2-5g/L, and the addition of bleeding agent is 2-5g/L.
7. the production technology of knitting full polyamide fibre Roman cloth as claimed in claim 4, it is characterized in that: the addition of described acid levelling agent is 1-4g/L, the addition of glacial acetic acid is 2-4g/L.