CN109629268A - A kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric - Google Patents
A kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric Download PDFInfo
- Publication number
- CN109629268A CN109629268A CN201811469962.6A CN201811469962A CN109629268A CN 109629268 A CN109629268 A CN 109629268A CN 201811469962 A CN201811469962 A CN 201811469962A CN 109629268 A CN109629268 A CN 109629268A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- fabric
- fiber
- printing process
- diacetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses the dyeing and printing process of a kind of diacetate fiber and zein fiber High-elasticity fabric, are related to printing technology field, solve that dye uniformity is poor and the poor technical problem of fabric hand feel.Mainly include the following steps: desizing treatment, dyes, soaps, drying, being formed, decatizing and clot packaging, wherein fabric by warp is acetate fiber, weft is that zein fiber misplaces be interwoven up and down, using fabric produced by the present invention, have the advantages that high color fastness, even dyeing and fabric performance are excellent.
Description
Technical field
The present invention relates to printing technology fields, more specifically, it relates to which a kind of diacetate fiber and zein fiber are high-elastic
The dyeing and printing process of property fabric.
Background technique
Zein fiber is that the fermented lactic acid that is converted to is aggregated again, spinning and manufactured synthetic fibers.Diacetate fiber is
Using the partly-hydrolysed resulting cellulose diacetate of Triafol T as raw material, processes and be made through spinning.It is made by the two is blended
Fabric, there is good hygroscopicity and perspiration wicking, and utilize the low strong of the high-strength force compensating diacetate fiber of zein fiber
Power, this fabric have excellent feel degree, resilience performance and wrinkle resistance.
But this High-elasticity fabric is interwoven by zein fiber and diacetate fiber, when dyeing, to dyestuff and
Dyeing condition is more demanding, and general dyeing and finishing technology is difficult that this High-elasticity fabric is made to obtain color uniform.
It is, therefore, desirable to provide a kind of dyeing and finishing technology solves the above problems.
Summary of the invention
It is high in view of the deficiencies of the prior art, the present invention intends to provide a kind of diacetate fiber and zein fiber
The dyeing and printing process of elastic fabric enables disperse dyes to exist by adding superfine fibre high speed levelling agent YC-201 in dye liquor
110 DEG C or so carry out upper dye, and the fabric after upper dye to fabric, and color has preferable color fastness and saturation degree, feel
With soft and smooth as silk and high resiliency.
To achieve the above object, the present invention provides the following technical scheme that
A kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, includes the following steps:
Step a, desizing treatment: fabric being added in desizing aqueous solution and carries out desizing treatment, and treatment temperature is 95~100 DEG C, place
The reason time is 0.5h, and washing is then carried out at 55~75 DEG C and removes fabric surface residue;
Step b, it dyes: taking step a treated cloth, put into overflow dyeing machine, clear water is added, gradually rises to bath temperature
108~112 DEG C, disperse dyes and color additive are added when bath temperature is 70~75 DEG C, keeps the temperature 0.5 at 108~112 DEG C
~1h;
Step c, it soaps: taking out cloth and be added in liquid of soaping, be warming up to 95 DEG C with (5~8 DEG C)/min, soap 10~20min, then
It is washed;
Step d, it dries: cloth obtained in step c being put into dryer and carries out drying and processing;
Step e, it is formed: the cloth after drying being soaked into softening agent, then dewatered drying, carries out shaping processing later;
Step f, decatizing: decatizing processing is carried out to the cloth after sizing using decator, decator pressure is 4kg, and the time is
10min;
Step g, clot and packaging.
The fabric is misplaced up and down using diacetate fiber and zein fiber and is interwoven, and the warp is that two acetic acid are fine
Dimension, the weft are zein fiber.
By using above-mentioned technical proposal, zein fiber is softly smooth, and intensity is big, and moisture absorption is ventilative, there is the gloss as silk
And comfortable skin sense of touch and feel, drapability is good, and good heat resistance and anti-ultraviolet function, diacetate fiber both have one
Fixed water imbibition, and there is the performance quickly sloughed after water suction, the fabric that the two is woven into, with the feel as silk;It is excellent
Different resilience performance and good wrinkle resistance, by optimizing dyeing and finishing technology, making fabric, full color, gloss are bright after dyeing
It is beautiful.
Further preferably, the desizing liquid group in the pre-treatment becomes 2~3g/L of sodium carbonate, 4~6g/L of hydrogen peroxide, moves back
Starch 1~3g/L of agent.
The slurry of web surface, the feel of Lai Tigao fabric are removed by alkali process by using above-mentioned technical proposal
Degree accelerates the hydrolysis of slurry under alkaline conditions by addition desizing agent, makes its quickly sufficiently removal, improves desizing rate and feel
Degree.
Further preferably, the desizing agent uses neopelex or sodium secondary alkyl sulfonate.
By using above-mentioned technical proposal, neopelex and sodium secondary alkyl sulfonate are surfactant, as
Desizing agent and subtract concentration no-float, greatly speeds up slurry and removed from fabric surface, improve hydrolysis rate, fiber can be effectively removed
The finish and wax on surface, improve the wettability of fabric, are conducive to subsequent dyestuff and are combined with limit.
Further preferably, the dyestuff uses disperse dyes, and the color additive is using 2~5g/L superfine fibre high speed
Levelling agent YC-201.
By using above-mentioned technical proposal, superfine fibre high speed levelling agent YC-201 have excellent high temperature dispersibility, just
Phase delays metachromia and later period migration property, can help dyestuff is uniformly upper to contaminate fiber in temperature-rise period, and it also has low blistering
Property, dye defect and dyeing flower etc. caused by capable of preventing cloth from floating being caused to knot because steeping in the process of running more.
Further preferably, added with 1~3g/L multifunctional assistant HSE-302 in the liquid of soaping.
By using above-mentioned technical proposal, after multifunctional assistant HSE-302 is to the ahthraquinone disperse dye dyeing of hardly possible removal
Loose colour taking-up ability with super strength, can replace reduction cleaning, save water and the energy.
Further preferably, the softening agent uses concentration for the hydrophilic silicone oil TF-4918 of 5~8g/L.
By using above-mentioned technical proposal, hydrophilic silicone oil be a kind of ultrafine particle it is non-/ weak cation type amino silicone softener,
With preferable hydrophily and additive compatibility, it can assign fiber sliding soft fluffy feel, there is preferable washability, energy
Cloth antistatic property and pollution resistance are significantly improved, cloth moisture absorption that treated and to perspire effect more preferable.
Further preferably, in the step e, at 170~175 DEG C, revolving speed is controlled in 35~40m/ for setting temperature control
min。
The washing shrinkage of cloth is reduced by setting treatment by using above-mentioned technical proposal, fine wrinkle is eliminated, improves cloth
Wrinkle resistance, and can also improve the wearability of cloth: elasticity, feel and fuzz balls phenomenon are improved.
In conclusion compared with prior art, the invention has the following advantages:
(1) by by zein fiber and diacetate fiber interlacement weave at fabric, the zein fiber of high-tenacity can compensate for two
The low strength of acetate fiber, diacetate fiber can be further compensate for the perspiration discharging performance of zein fiber, diacetate fiber and corn
The fabric of fiber weaving has soft and smooth, resilience performance and good wrinkle resistance that high stretch yarn is excellent as silk.
(2) disperse dyes can be to contaminating and reach preferable color fastness and full in the environment of 135 DEG C or so on fabric
And degree, diacetate fiber non-refractory enable disperse dyes at 110 DEG C by adding color additive in dispersion dye liquor
Left and right can carry out upper dye to fabric, and color can reach preferable color fastness and saturation degree;
(3) with super strength to the loose colour after disperse dyeing by adding multifunctional assistant HSE-302 in liquid of soaping
Removal ability, and without carrying out reduction cleaning, it is saved greatly water and the energy.
Detailed description of the invention
Fig. 1 is process flow chart of the invention.
Specific embodiment
With reference to the accompanying drawings and examples, the present invention will be described in detail.
Embodiment 1: a kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, as shown in Figure 1, include with
Lower step:
Step a, fabric addition group desizing treatment: is become into moving back for 2g/L, 4g/L hydrogen peroxide and 2g/L neopelex
Desizing treatment is carried out in pulp-water solution, treatment temperature is 98 DEG C, and the processing time is 0.5h, and washing removing is then carried out at 55 DEG C
Fabric surface residue;
Step b, it dyes: taking step a treated cloth, put into overflow dyeing machine, clear water is added, gradually rises to bath temperature
110 DEG C, disperse dyes and 3g/L superfine fibre high speed levelling agent YC-201 are added when bath temperature is 70 DEG C, at 110 DEG C
0.45h is kept the temperature, disperse dyes use disperse blue EX-SF 300%3-3.5% (owf), superfine fibre high speed levelling agent YC-201
Surpass Chemical Co., Ltd. from Hangzhou-;
Step c, it soaps: taking out cloth and be added in the liquid of soaping that component is 2g/L multifunctional assistant HSE-302, with 6 DEG C/min liter
To 95 DEG C, soap temperature 10min, then is washed;
Step d, it dries: cloth obtained in step c being put into dryer and carries out drying and processing;
Step e, it is formed: being the hydrophilic silicone oil TF-4918 of 6g/L by the cloth leaching concentration after drying, then dewatered drying, later
Processing is carried out shaping, setting temperature is 170 DEG C, and speed control comes from Zhejiang development of evil in febrile disease stock in 35m/min, hydrophilic silicone oil TF-4918
Part Co., Ltd;
Step f, decatizing: decatizing processing is carried out to the cloth after sizing using decator, decator pressure is 4kg, and the time is
10min;
Step g, clot and packaging.
Embodiment 2: a kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, the difference with embodiment 1
Place is, in step a, fabric addition group desizing treatment: is become 2g/L, 4g/L hydrogen peroxide and 2g/L sodium secondary alkyl sulfonate
Desizing treatment is carried out in desizing aqueous solution, treatment temperature is 98 DEG C, and the processing time is 0.5h, and washing is then carried out at 55 DEG C and is removed
Remove fabric surface residue.
Embodiment 3: a kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, the difference with embodiment 1
Place is, in step b, dyeing: takes step a treated cloth, put into overflow dyeing machine, clear water is added, gradually by water-bath
Temperature rises to 110 DEG C, and disperse dyes and 5g/L superfine fibre high speed levelling agent YC-201 are added when bath temperature is 70 DEG C,
0.45h is kept the temperature at 110 DEG C, disperse dyes use disperse blue EX-SF 300%3-3.5% (owf), superfine fibre high speed levelling agent
YC-201 surpasses Chemical Co., Ltd. from Hangzhou-.
Embodiment 4: a kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, the difference with embodiment 1
Place is, in step c, soaps: taking out cloth and is added in the liquid of soaping that component is 2g/L multifunctional assistant HSE-302, with 6
DEG C/min is warming up to 95 DEG C, soap 15min, then is washed.
Comparative example 1: a kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, the difference with embodiment 1
Place is, in step a, desizing treatment: fabric addition group is become in the desizing aqueous solution of 2g/L and 4g/L hydrogen peroxide and is carried out
Processing, treatment temperature are 98 DEG C, and the processing time is 0.5h, and washing is then carried out at 55 DEG C and removes fabric surface residue.
Comparative example 2: a kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, the difference with embodiment 1
Place is, in step b, dyeing: takes step a treated cloth, put into overflow dyeing machine, clear water is added, gradually by water-bath
Temperature rises to 135 DEG C, and disperse dyes and 3g/L superfine fibre high speed levelling agent YC-201 are added when bath temperature is 70 DEG C,
0.45h is kept the temperature at 135 DEG C, disperse dyes use disperse blue EX-SF 300%3-3.5% (owf), superfine fibre high speed levelling agent
YC-201 surpasses Chemical Co., Ltd. from Hangzhou-.
Comparative example 3: a kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, the difference with embodiment 1
Place is, dyes in step b: taking step a treated cloth, put into overflow dyeing machine, clear water is added, gradually by water-bath temperature
Degree rises to 110 DEG C, and disperse dyes are added when bath temperature is 70 DEG C, and 0.45h is kept the temperature at 110 DEG C, and disperse dyes, which use, to be divided
Dissipate indigo plant EX-SF 300%3-3.5% (owf).
Comparative example 4: a kind of dyeing and printing process of diacetate fiber and zein fiber High-elasticity fabric, the difference with embodiment 1
Place is, in step e, sizing: the cloth after drying is carried out shaping processing, setting temperature is 170 DEG C, and speed control exists
35m/min。
Test dyeability test
Test specimen: using the fabric obtained in embodiment 1-4 as test specimen 1-4, using the face obtained in comparative example 1-4
Material is used as control sample 1-4, and each sample makees 10 samples at random, amounts to 8 groups.
Test method: by 8 groups of samples respectively according to the colouring method of embodiment 1-4 and comparative example 1-4 carry out dyeing and according to
Detect the dye uniformity and color fastness of sample respectively according to GB/T 6508-2001 and GB/T 6151-2016.
Test result: as shown in table 1, the washing color fastness and PERSPIRATION COLOR FASTNESS of test specimen 1-4 is 4=5 grades, and right
Washing color fastness and PERSPIRATION COLOR FASTNESS than sample 1-4 are 3-4 grades, by dyestuff in test specimen 1-4 known to test result with
The conjugation of fabric is higher than the conjugation of dyestuff and fabric in control sample 1-4;The dye uniformity of test specimen 1-4 is >=4
Grade, dye uniformity≤4 grade of control sample 1-4, i.e., again with the diacetate fiber and jade after dyeing and finishing technology dyeing of the invention
Rice fiber High-elasticity fabric, with good color uniformity.
The test result of table 1 test specimen 1-4 and control sample 1-4
Sample | Wash color fastness | PERSPIRATION COLOR FASTNESS | Dye uniformity |
Test specimen 1 | 4 grades | 4-5 grades | 4.5 grade |
Test specimen 2 | 4 grades | 4-5 grades | 4 grades |
Test specimen 3 | 5 grades | 4-5 grades | 4.5 grade |
Test specimen 4 | 5 grades | 4-5 grades | 4 grades |
Control sample 1 | 3 grades | 3-4 grades | 3 grades |
Control sample 2 | 3 grades | 3-4 grades | 3 grades |
Control sample 3 | 4 grades | 3-4 grades | 3.5 grade |
Control sample 4 | 4 grades | 3-4 grades | 3.5 grade |
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-described embodiment,
All technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
For those of ordinary skill, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (7)
1. the dyeing and printing process of a kind of diacetate fiber and zein fiber High-elasticity fabric, which comprises the steps of:
Step a, desizing treatment: fabric being added in desizing aqueous solution and carries out desizing treatment, and treatment temperature is 95~100 DEG C, place
The reason time is 0.5h, and washing is then carried out at 55~75 DEG C and removes fabric surface residue;
Step b, it dyes: taking step a treated cloth, put into overflow dyeing machine, clear water is added, gradually rises to bath temperature
108~112 DEG C, dyestuff and color additive are added when bath temperature is 70~75 DEG C, keep the temperature 0.5 at 108~112 DEG C~
1h;
Step c, it soaps: taking out cloth and be added in liquid of soaping, be warming up to 95 DEG C with (5~8 DEG C)/min, soap 10~20min, then
It is washed;
Step d, it dries: cloth obtained in step c being put into dryer and carries out drying and processing;
Step e, it is formed: the cloth after drying being soaked into softening agent, then dewatered drying, carries out shaping processing later;
Step f, decatizing: decatizing processing is carried out to the cloth after sizing using decator, decator pressure is 4kg, and the time is
10min;
Step g, clot and packaging;
The fabric is misplaced up and down using diacetate fiber and zein fiber and is interwoven, and the warp is diacetate fiber, institute
Stating weft is zein fiber.
2. the dyeing and printing process of diacetate fiber according to claim 1 and zein fiber High-elasticity fabric, which is characterized in that
Desizing liquid group in the pre-treatment becomes 2~3g/L of sodium carbonate, 4~6g/L of hydrogen peroxide, 1~3g/L of desizing agent.
3. the dyeing and printing process of diacetate fiber according to claim 2 and zein fiber High-elasticity fabric, which is characterized in that
The desizing agent uses neopelex or sodium secondary alkyl sulfonate.
4. the dyeing and printing process of diacetate fiber according to claim 1 and zein fiber High-elasticity fabric, which is characterized in that
The dyestuff uses disperse dyes, and the color additive uses 2~5g/L superfine fibre high speed levelling agent YC-201.
5. the dyeing and printing process of diacetate fiber according to claim 1 and zein fiber High-elasticity fabric, which is characterized in that
Added with 1~3g/L multifunctional assistant HSE-302 in the liquid of soaping.
6. the dyeing and printing process of diacetate fiber according to claim 1 and zein fiber High-elasticity fabric, which is characterized in that
The softening agent uses concentration for the hydrophilic silicone oil TF-4918 of 5~8g/L.
7. the dyeing and printing process of diacetate fiber according to claim 1 and zein fiber High-elasticity fabric, which is characterized in that
In the step e, at 170~175 DEG C, revolving speed is controlled in 35~40m/min for setting temperature control.