CN105714584B - A kind of dyeing for washing viscous Modal textile fabric - Google Patents

A kind of dyeing for washing viscous Modal textile fabric Download PDF

Info

Publication number
CN105714584B
CN105714584B CN201610273660.6A CN201610273660A CN105714584B CN 105714584 B CN105714584 B CN 105714584B CN 201610273660 A CN201610273660 A CN 201610273660A CN 105714584 B CN105714584 B CN 105714584B
Authority
CN
China
Prior art keywords
dyeing
textile fabric
parts
sizing
time
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610273660.6A
Other languages
Chinese (zh)
Other versions
CN105714584A (en
Inventor
叶民
应浩
戴国荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Zhuoda Printing & Dyeing Co Ltd
Original Assignee
Hangzhou Zhuoda Printing & Dyeing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hangzhou Zhuoda Printing & Dyeing Co Ltd filed Critical Hangzhou Zhuoda Printing & Dyeing Co Ltd
Priority to CN201610273660.6A priority Critical patent/CN105714584B/en
Publication of CN105714584A publication Critical patent/CN105714584A/en
Application granted granted Critical
Publication of CN105714584B publication Critical patent/CN105714584B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of dyeing for washing viscous Modal textile fabric of disclosure of the invention, includes the following steps:S1, viscous Modal textile fabric pretreatment is washed;S2, sizing treatment will be carried out through above-mentioned textile fabric;S3, the textile fabric for obtaining S2 carry out first time pad dyeing dyeing, bake, clean for the first time;S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing, second of cleaning;S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing;S6, the textile fabric obtained in S5 is tested and packed;Stoving temperature is 190 215 DEG C in the S3;First time pad dyeing dyeing is using pad dyeing agent in the S3;Second of pad dyeing dyeing is using vital staining agent in the S4;Vapour steaming colour fixing uses fixation liquid in the S4.By fixation and cleaning after the dyeing of pad dyeing twice, continuous knot dyeing dyeing makes combination between the fiber in textile fabric and dyestuff strong, is less prone to discolouration phenomena, textile fabric is made to reach more excellent coloring.

Description

A kind of dyeing for washing viscous Modal textile fabric
Technical field
The present invention relates to textile printing and dyeing process technical field, more specifically, it relates to which one kind washs viscous Modal textile fabric Dyeing.
Background technology
The dyeing of fabric is more crucial, is directly related to the texture and aesthetic measure of finished product fabric.Weave forming face In the yarn of material, Modal fibre and viscose fiber are respectively provided with the advantages of gloss is soft and drapability is excellent, and Modal also has There are good elasticity and moisture pick-up properties;Terylene has excellent intensity and wrinkle resistance, and heat-resistant antifriction, but dyeability is poor, It is not easy to be caught color.It is more soft, ventilative comfortable that terylene, viscose and Modal weave the textile to be formed, also with excellent Elasticity, wrinkle resistance and vertical sense.
The Chinese patent that application publication number is CN103225212A, data of publication of application is on 07 31st, 2013 discloses one The heat-sensitive variable colour pigment dyeing technique of kind textile fabric, technological process are:The selection of thermochromic dye and composition;Temperature-sensitive becomes The preparation of color dye microcapsule;The preparation and dyeing of heat-sensitive variable colour pigment printing paste, dehydration, bake, finally obtain heat-sensitive variable colour and knit Object.The warps such as the textile fabric is cotton, tencel, Modal, the blended cotton of chemical fibre (viscous cotton, polyester-cotton blend, bright and beautiful cotton), silk, wool cotton Fabric after pre-treatment.The heat-sensitive variable colour textile applied through the present invention, through temperature in ambient temperature, clothes and body temperature three The comprehensive function of person, when fabric surface temperature meets or exceeds discoloring temperature, color changes, and when temperature drops to discoloration When below temperature, and it is restored to original color.
The dyeing used in documents after being padded using thermochromic dye to textile fabric, will be knitted Object is carried out after washing twice, drying and processing is carried out under conditions of 80-90 DEG C, then it is carried out at the secured enhancer of wet friction Reason, then carries out drying and processing under conditions of 80-90 DEG C successively, and baking processing is carried out under conditions of 140-150 DEG C, make, Textile fabric catches heat-sensitive variable colour coating.However, due to the fabric of terylene class, without specific dyeing base on terylene strand Group, and polarity is smaller, dye molecule is not easily accessible fiber, needs to carry out dyeing sizing at a high temperature of 130 DEG C or more, makes dyestuff It signs an undertaking conjunction with the fiber in fabric.And in documents, after being padded by dyestuff, only dried under conditions of 80-90 DEG C Dry-cure causes dyestuff that cannot reach good combination with the terylene fiber in fabric, it is made to be carried in progress fastness to wet rubbing During high agent processing, unstable dyestuff is fixed with terylene fiber, also will continue to come off on the basis of original, eventually cause The problem of textile dyeing effect is poor.
Invention content
In view of the deficiencies of the prior art, the present invention intends to provide a kind of dyeing for washing viscous Modal textile fabric Technique, which solve terylene kind fabric coloring it is poor the problem of so that between dyestuff and terylene fiber it is strong bonded so as to Reach excellent coloring.
To achieve the above object, the present invention provides following technical solutions:
A kind of dyeing for washing viscous Modal textile fabric, which is characterized in that include the following steps:
S1, viscous Modal textile fabric pretreatment is washed;
S2, viscous Modal textile fabric progress sizing treatment is washed by after pretreatment;
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, baked, cleaned for the first time;
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing, second of cleaning;
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing;
S6, the textile fabric obtained in S5 is tested and packed;
The temperature baked in the step S3 is 190-215 DEG C;
Using pad dyeing agent, the pad dyeing agent includes the group of following parts by weight for first time pad dyeing dyeing in the step S3 Point:
37-45 parts of disperse dyes;
0.1-1.5 parts of glacial acetic acid;
MIP7-15 parts of migration inhibitor;
Second of pad dyeing dyeing includes following parts by weight using vital staining agent, the vital staining agent in the step S4 Several components:
41-54 parts of reactive dye;
2-9 parts of reservehao S;
5-15 parts of urea;
MIP5-13 parts of migration inhibitor;
5-15 parts of sodium bicarbonate;
Vapour steaming colour fixing uses fixation liquid in the step S4, and the fixation liquid includes the component of following parts by weight:
20-40 parts of sodium carbonate sodium carbonate;
192-213 parts of sodium chloride.
In the application, first time pad dyeing dyeing is carried out to the textile fabric after pretreatment and sizing treatment, in the mistake Cheng Zhong, migration inhibitor MIP coordinate with acetic acid, can be with the carboxylic in acetic acid due to having a large amount of hydrophilic radical in migration inhibitor MIP Base matches, and disperse dyes is made to uniformly disperse in water, and migration inhibitor MIP be high molecular polymer, the adsorbable dyestuff in surface Molecule, so that dye molecule is not susceptible to migration.Acetic acid causes dye liquor to keep acid, and dyestuff is made to be more easy in acid condition Polyester fiber is dyed.Using 190-215 DEG C of high temperature to the spinning after pad dyeing is dyed after first time pad dyeing dyeing Fabric is baked, and high temperature so that dye molecule is strong bonded with polyester fiber, and polyster fibre dyeing is made to shape.
Fabric surface will be floated on and do not cleaned with the dyestuff of fiber firm connection in fabric and removed, to passing through first time pad dyeing Fabric after dyeing and being baked carries out second of pad dyeing dyeing, in this process, using the adsorbable activity of migration inhibitor MIP Dyestuff and reservehao S make the dye molecule that reservehao S pair combined with fiber provide protection, prevent it by external influence and It is detached from fiber.Urea and sodium bicarbonate make entire dye liquor system be carried out in alkalinity convenient for other fibers in dye molecule and fabric With reference to so as to make other stock-dyes.
After second of pad dyeing dyeing, polyester fiber and Modal fiber in the textile fabric shape between dye molecule Into good combination, so that whole have good coloring.In dye liquor, all kinds of fiber surfaces carry negative electrical charge, And dye molecule surface carries negative electrical charge, the addition of sodium chloride and caustic soda so that the elecrtonegativity in dye liquor is neutralized, and reduces dyestuff The coulomb repulsion of molecule and fiber surface, vapour steaming colour fixing has higher temperature, so that fiber expanded by heating, can promote to contaminate Material is quickly and uniformly spread to amorphous region, makes the binding force between dyestuff and fiber stronger, more secured so as to reach dyeing. The process can not only increase the binding force of dye molecule and fiber, so as to enhance the coloring of textile fabric, and reduce dye Expect the possibility fallen from fiber.
Segmented cleaning, the dye for textile surfaces being floated on after each pad dyeing respectively are carried out to dyed treated textile fabric Material removal, since most dyestuff has been combined with textile fabric, thus, when cleaning, can reduce water consumption, energy conservation and environmental protection.
Further preferably:The disperse dyes, which are selected, disperses black EV-ST, big Ai Nikesi carbunclies SE-B and big Ai Nike It takes charge of at least one of golden yellow;The reactive dye include at least one in active black SBE, reactive brilliant blue and reactive brilliant red CES Part.
Due to the more difficult dyeing of polyester fiber, the deeper color of use, and disperse dyes are penetrated into reactive dye In the fiber of textile fabric, make to wash viscous Modal textile fabric and be more easy to fully be dyed, reach required coloring.
Further preferably:Cleaning for the first time is using caustic soda and sodium dithionite in the step S3;The step S4 In second cleaning using soaping agent, the soaping agent is preferably 209 soaping agents.
First time pad dyeing dyeing mainly dyes textile fabric using acidic materials, and basic species are used in cleaning for the first time Remaining acidic materials are neutralized in confrontation textile fabric, prevent acid therein from contaminating second of the pad dyeing subsequently carried out Color has an impact, and prevents from reducing by second of pad dyeing coloring.Second of pad dyeing dyeing is mainly using reactive dye cooperation alkalinity Substance is dyed, and alkaline matter is employed in laking process so that textile fabric is in alkalinity, the main component of 209 soaping agents For N- oleoyls-N methyl taurine sodium, with a large amount of hydrophilic radicals, so as to which it be made to be dissolved in water, and it is more easy under alkaline environment Water is dissolved in, the alkaline matter in textile fabric is adsorbed and it is soluble in water together, so that the alkaline matter in textile fabric It is cleaned, textile fabric can be made preferably to carry out next step reaction.
Further preferably:The temperature that soaping agent is added in second of cleaning is 90-105 DEG C.
Under 90-105 DEG C of temperature condition, the soaping agent of addition, as 209 soaping agents can preferably be dissolved in the water, Alkaline matter is disengaged to the effect in water by raising from textile surfaces.
Further preferably:Speed in the step S3 and step S4 is 20-40m/min.
It is relatively stable and at the uniform velocity using the speed of 20-40m/min, it can make textile fabric that there is the sufficient time to carry out pad dyeing Dyeing, baking, fixation and cleaning so that the textile fabric after dyed can reach required coloring, and is less prone to and fades The phenomenon that, there is excellent colour fixation.
Further preferably:The pretreatment includes turning over cloth margin to seam, the arrangement of open width contracting and big volume through cylinder pre-treatment;Institute State sizing treatment include first time squezzing sizing, singe and second of squezzing sizing.
In the application, processing early period is carried out to textile fabric using pretreatment and sizing treatment, makes textile surfaces
Further preferably:For the big volume through cylinder pre-treatment using inorganic agent, the inorganic agent includes following parts by weight Component:13-20 parts of hydrogen peroxide;
5-15 parts of caustic soda;
HDS3-10 parts of hydrogen peroxide stabilizer;
The clever TF-410 that deoils is 2-9 parts.
In the application, using deoiling, clever TF-410 carries out oil processing to textile fabric, makes its institute in weaving production The oily substance of carrying, and hydrogen peroxide and caustic soda carry out bleaching to original cloth, both with stronger permeance property, Help to deoil clever TF-410 to the fiber generation adequately effect of deoiling in textile fabric, dye the fiber in textile fabric It is more easy to be combined with dye molecule in journey.
Further preferably:The temperature of the first time squezzing sizing and second of squezzing sizing is 150-175 DEG C, described First time squezzing is shaped and the speed of second of squezzing sizing is 25-40m/min.
Using higher temperature in squezzing type-approval process, make it is smaller by front and rear temperature difference of singing, and using 25-40m/ The speed of min shapes to textile fabric into squezzing, and the fiber expanded by heating in textile fabric, the specific surface area of increased fiber and makes fibre Water between dimension and in the unformed area of fiber can be squeezed and discharge, and make the contact between fiber and fiber in textile fabric It is more close, so as to increase the bonded area between dye molecule and fiber.
Further preferably:It is described roll it is soft sizing handled using setting agent, the setting agent include following parts by weight Several components:
5-15 parts of HS softening agents;
30-45 parts of CY color fixing agent;
0.5-1.3 parts of citric acid.
In acid condition, with reference to CY color fixing agent and HS softening agents, last consolidate is carried out to each fiber in textile fabric Color makes its binding force between dyestuff stronger, it is prevented to be detached between fiber and decoloration phenomenon occurs, and reinforcing fiber Soft effect so that textile fabric after processing has more good softness.
In conclusion the invention has the advantages that:
It is cleaned, then second pad dyeing dyeing, decatize are carried out to it using baking and for the first time after first time pad dyeing dyeing Fixation and second of cleaning, continuous knot dyeing dyeing make each fiber in textile fabric be more easy to by dyeing, and fiber and dyestuff Between combination it is strong, be less prone to discolouration phenomena, textile fabric made to reach more excellent coloring.
Specific embodiment
Embodiment 1:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 155 DEG C when first time squezzing is shaped, speed 30m/min;Speed is 105m/min when two burners are singed;The Temperature is 165 DEG C during secondary squezzing sizing, speed 30m/min.
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, bakes and cleaned for the first time;First time pad dyeing is pressed when dyeing Disperse black EV-ST, big Ai Nikesi carbunclies SE-B, big Ai Nikesi golden yellow, glacial acetic acid according to the addition of corresponding parts by weight and prevent Migration agent, speed 20m/min;Temperature is 200 DEG C during baking, speed 22m/min;According to corresponding weight when cleaning for the first time Measure number addition caustic soda and sodium dithionite, speed 20m/min.
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing and second clean;It rolls for the second time Contaminate dyeing course according to corresponding parts by weight addition active black SBE, reactive brilliant blue, reactive brilliant red CES, reservehao S, urea, Migration inhibitor MIP and sodium bicarbonate;During vapour steaming colour fixing soda ash and sodium chloride are added according to corresponding parts by weight;During second of cleaning 209 soaping agents are added according to corresponding parts by weight, temperature is 100 DEG C;Speed is 20m/min.
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 160 DEG C, speed 37m/min.
S6, the textile fabric obtained in S5 is tested and packed.
Embodiment 2:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 160 DEG C when first time squezzing is shaped, speed 25m/min;Speed is 125m/min when two burners are singed;The Temperature is 163 DEG C during secondary squezzing sizing, speed 25m/min.
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, bakes and cleaned for the first time;First time pad dyeing is pressed when dyeing Disperse black EV-ST, big Ai Nikesi carbunclies SE-B, big Ai Nikesi golden yellow, glacial acetic acid according to the addition of corresponding parts by weight and prevent Migration agent, speed 28m/min;Temperature is 195 DEG C during baking, speed 25m/min;According to corresponding weight when cleaning for the first time Measure number addition caustic soda and sodium dithionite, speed 28m/min.
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing and second clean;It rolls for the second time Contaminate dyeing course according to corresponding parts by weight addition active black SBE, reactive brilliant blue, reactive brilliant red CES, reservehao S, urea, Migration inhibitor MIP and sodium bicarbonate;During vapour steaming colour fixing soda ash and sodium chloride are added according to corresponding parts by weight;During second of cleaning 209 soaping agents are added according to corresponding parts by weight, temperature is 105 DEG C;Speed is 28m/min.
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 155 DEG C, speed 35m/min.
S6, the textile fabric obtained in S5 is tested and packed.
Embodiment 3:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 170 DEG C when first time squezzing is shaped, speed 35m/min;Speed is 110m/min when two burners are singed;The Temperature is 155 DEG C during secondary squezzing sizing, speed 35m/min.
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, bakes and cleaned for the first time;First time pad dyeing is pressed when dyeing Disperse black EV-ST, big Ai Nikesi carbunclies SE-B, big Ai Nikesi golden yellow, glacial acetic acid according to the addition of corresponding parts by weight and prevent Migration agent, speed 36m/min;Temperature is 190 DEG C during baking, speed 20m/min;According to corresponding weight when cleaning for the first time Measure number addition caustic soda and sodium dithionite, speed 36m/min.
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing and second clean;It rolls for the second time Contaminate dyeing course according to corresponding parts by weight addition active black SBE, reactive brilliant blue, reactive brilliant red CES, reservehao S, urea, Migration inhibitor MIP and sodium bicarbonate;During vapour steaming colour fixing soda ash and sodium chloride are added according to corresponding parts by weight;During second of cleaning 209 soaping agents are added according to corresponding parts by weight, temperature is 95 DEG C;Speed is 36m/min.
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 150 DEG C, speed 35m/min.
S6, the textile fabric obtained in S5 is tested and packed.
Embodiment 4:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 165 DEG C when first time squezzing is shaped, speed 40m/min;Speed is 100m/min when two burners are singed;The Temperature is 170 DEG C during secondary squezzing sizing, speed 40m/min.
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, bakes and cleaned for the first time;First time pad dyeing is pressed when dyeing Disperse black EV-ST, big Ai Nikesi carbunclies SE-B, big Ai Nikesi golden yellow, glacial acetic acid according to the addition of corresponding parts by weight and prevent Migration agent, speed 35m/min;Temperature is 210 DEG C during baking, speed 21m/min;According to corresponding weight when cleaning for the first time Measure number addition caustic soda and sodium dithionite, speed 35m/min.
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing and second clean;It rolls for the second time Contaminate dyeing course according to corresponding parts by weight addition active black SBE, reactive brilliant blue, reactive brilliant red CES, reservehao S, urea, Migration inhibitor MIP and sodium bicarbonate;During vapour steaming colour fixing soda ash and sodium chloride are added according to corresponding parts by weight;During second of cleaning 209 soaping agents are added according to corresponding parts by weight, temperature is 90 DEG C;Speed is 35m/min.
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 165 DEG C, speed 45m/min.
S6, the textile fabric obtained in S5 is tested and packed.
Embodiment 5:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 171 DEG C when first time squezzing is shaped, speed 28m/min;Speed is 115m/min when two burners are singed;The Temperature is 160 DEG C during secondary squezzing sizing, speed 28m/min.
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, bakes and cleaned for the first time;First time pad dyeing is pressed when dyeing Disperse black EV-ST, big Ai Nikesi carbunclies SE-B, big Ai Nikesi golden yellow, glacial acetic acid according to the addition of corresponding parts by weight and prevent Migration agent, speed 25m/min;Temperature is 205 DEG C during baking, speed 23m/min;According to corresponding weight when cleaning for the first time Measure number addition caustic soda and sodium dithionite, speed 25m/min.
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing and second clean;It rolls for the second time Contaminate dyeing course according to corresponding parts by weight addition active black SBE, reactive brilliant blue, reactive brilliant red CES, reservehao S, urea, Migration inhibitor MIP and sodium bicarbonate;During vapour steaming colour fixing soda ash and sodium chloride are added according to corresponding parts by weight;During second of cleaning 209 soaping agents are added according to corresponding parts by weight, temperature is 103 DEG C;Speed is 25m/min.
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 153 DEG C, speed 40m/min.
S6, the textile fabric obtained in S5 is tested and packed.
Embodiment 6:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 175 DEG C when first time squezzing is shaped, speed 33m/min;Speed is 120m/min when two burners are singed;The Temperature is 150 DEG C during secondary squezzing sizing, speed 33m/min.
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, bakes and cleaned for the first time;First time pad dyeing is pressed when dyeing Disperse black EV-ST, big Ai Nikesi carbunclies SE-B, big Ai Nikesi golden yellow, glacial acetic acid according to the addition of corresponding parts by weight and prevent Migration agent, speed 40m/min;Temperature is 215 DEG C during baking, speed 24m/min;According to corresponding weight when cleaning for the first time Measure number addition caustic soda and sodium dithionite, speed 40m/min.
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing and second clean;It rolls for the second time Contaminate dyeing course according to corresponding parts by weight addition active black SBE, reactive brilliant blue, reactive brilliant red CES, reservehao S, urea, Migration inhibitor MIP and sodium bicarbonate;During vapour steaming colour fixing soda ash and sodium chloride are added according to corresponding parts by weight;During second of cleaning 209 soaping agents are added according to corresponding parts by weight, temperature is 97 DEG C;Speed is 40m/min.
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 158 DEG C, speed 38m/min.
S6, the textile fabric obtained in S5 is tested and packed.
Embodiment 7:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 150 DEG C when first time squezzing is shaped, speed 38m/min;Speed is 116m/min when two burners are singed;The Temperature is 175 DEG C during secondary squezzing sizing, speed 38m/min.
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, bakes and cleaned for the first time;First time pad dyeing is pressed when dyeing Disperse black EV-ST, big Ai Nikesi carbunclies SE-B, big Ai Nikesi golden yellow, glacial acetic acid according to the addition of corresponding parts by weight and prevent Migration agent, speed 33m/min;Temperature is 199 DEG C during baking, speed 24m/min;According to corresponding weight when cleaning for the first time Measure number addition caustic soda and sodium dithionite, speed 33m/min.
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing and second clean;It rolls for the second time Contaminate dyeing course according to corresponding parts by weight addition active black SBE, reactive brilliant blue, reactive brilliant red CES, reservehao S, urea, Migration inhibitor MIP and sodium bicarbonate;During vapour steaming colour fixing soda ash and sodium chloride are added according to corresponding parts by weight;During second of cleaning 209 soaping agents are added according to corresponding parts by weight, temperature is 92 DEG C;Speed is 33m/min.
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 163 DEG C, speed 41m/min.
S6, the textile fabric obtained in S5 is tested and packed.
There is excellent coloring by the textile fabric that embodiment 1-7 is prepared.The component added in embodiment 1-7 And its parts by weight are as shown in table 1.
The component and its parts by weight of addition in 1 embodiment 1-7 of table
Comparative example
Test sample:The sample prepared with embodiment 2,3 and 5 is respectively test sample 1,2 and 3;In control sample 1-5 Component is as shown in table 2 with parts by weight.
The preparation method of control sample 1-5 is according to following steps:
Control sample 1:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 170 DEG C when first time squezzing is shaped, speed 38m/min;Speed is 116m/min when two burners are singed;The Temperature is 165 DEG C during secondary squezzing sizing, speed 38m/min.
S3, above-mentioned textile fabric is subjected to pad dyeing dyeing, bakes and clean;Pad dyeing adds when dyeing according to corresponding parts by weight Bonus point dissipates black EV-ST, big Ai Nikesi carbunclies SE-B, big Ai Nikesi golden yellow, glacial acetic acid and migration inhibitor, speed 33m/ min;Temperature is 209 DEG C during baking, speed 22m/min;During cleaning caustic soda and Lian Erya are added according to corresponding parts by weight Sodium sulphate, speed 33m/min.
S4, the textile fabric obtained in S3 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 165 DEG C, speed 37m/min.
S5, the textile fabric obtained in S4 is tested and packed.
Control sample 2:
S1, it the pretreatment of viscous Modal textile fabric will be washed turns over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;Open width Cropping 7 is into doing after contracting arranges, and big volume according to corresponding parts by weight during cylinder pre-treatment through adding hydrogen peroxide, caustic soda, hydrogen peroxide The stabilizer HDS and clever TF-410 that deoils, specification are 1500-3000m/ cylinders.
S2, viscous Modal textile fabric progress first time squezzing sizing is washed by after pretreatment, singed and second of squezzing Sizing;Temperature is 150 DEG C when first time squezzing is shaped, speed 38m/min;Speed is 116m/min when two burners are singed;The Temperature is 175 DEG C during secondary squezzing sizing, speed 38m/min.
S3, the textile fabric obtained in S2 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing and second clean;It rolls for the second time Contaminate dyeing course according to corresponding parts by weight addition active black SBE, reactive brilliant blue, reactive brilliant red CES, reservehao S, urea, Migration inhibitor MIP and sodium bicarbonate;During vapour steaming colour fixing soda ash and sodium chloride are added according to corresponding parts by weight;During second of cleaning 209 soaping agents are added according to corresponding parts by weight, temperature is 92 DEG C;Speed is 33m/min.
S4, the textile fabric obtained in S3 is carried out to roll soft sizing and preshrunk processing, rolls soft type-approval process process according to corresponding Parts by weight addition HS softening agents, CY color fixing agent and citric acid, temperature is 163 DEG C, speed 41m/min.
S5, the textile fabric obtained in S4 is tested and packed.
The preparation method of control sample 3-5 is with reference to the preparation method of embodiment 3-5.
Test method:
It 1st, will be by the step of test sample 1-3 and control sample 1-5 and prepared by the component of the corresponding parts by weight of addition The sample gone out removes textile fabric 10cm × 10cm from each sample respectively, marked as A, B, C, D, E, F, G and H, using CR-10 The textile fabric of different labels and standard sample numerical value are carried out value of chromatism comparison by Konica Minolta colour difference meter respectively, record data And it is analyzed.
It 2nd, will be by the step of test sample 1-3 and control sample 1-5 and prepared by the component of the corresponding parts by weight of addition The sample gone out removes textile fabric 1m from each sample respectively2, marked as A, B, C, D, E, F, G and H, wherein A, B and C is respectively Test sample 1-3.Prepare 8 identical basins, place 2L clear water in each basin, be respectively put into 1ml with money colorless detergent, then will spin Fabric is put into basin successively, every piece of fabric is rubbed wash 15 times after, each fabric is rinsed, every time rinse 2L water is added in basin, after which time rinsing, fabric will no longer fade.
Laboratory apparatus:CR-10 Konicas Minolta colour difference meter.
Experimental result:
1st, the value of chromatism of test sample 1-3 and control sample 1-5 are as shown in table 3.
2nd, test sample 1-3 with detergent after being rubbed and washing, and color change hardly occurs for the water in tri- basins of A, B, C, almost Do not occur discolouration phenomena, when rinsing first time without any colour fading;Control sample 1,2,3,4 and 5 goes out after being rubbed and washing with detergent No longer there is discolouration phenomena after 5 rinsings in now more apparent discolouration phenomena, control sample 1;Control sample 2 through 6 times rinsing after not Occurs discolouration phenomena again;Control sample 3 is no longer faded after 3 rinsings;Control sample 4 is no longer faded after 3 rinsings;Control sample 5 It no longer fades after 2 rinsings.
The component and its parts by weight added in table 2 test sample 1-3 and control sample 1-5
The value of chromatism of table 3 test sample 1-3 and control sample 1-5
As shown in Table 3,3 values of chromatism between test sample and standard sample are small, i.e., the color phase between standard color Seemingly, coloring is excellent;And 5 values of chromatism between control sample and standard sample are larger, i.e., the color between standard color Gap is larger, and coloring is undesirable.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications It should be regarded as protection scope of the present invention.

Claims (8)

1. a kind of dyeing for washing viscous Modal textile fabric, which is characterized in that include the following steps:
S1, viscous Modal textile fabric pretreatment is washed;
S2, viscous Modal textile fabric progress sizing treatment is washed by after pretreatment;
S3, above-mentioned textile fabric is subjected to first time pad dyeing dyeing, baked, cleaned for the first time;
S4, the textile fabric obtained in S3 is carried out to second of pad dyeing dyeing, vapour steaming colour fixing, second of cleaning;
S5, the textile fabric obtained in S4 is carried out to roll soft sizing and preshrunk processing;
S6, the textile fabric obtained in S5 is tested and packed;
The temperature baked in the step S3 is 190-215 DEG C;
Using pad dyeing agent, the pad dyeing agent includes the component of following parts by weight for first time pad dyeing dyeing in the step S3:
37-45 parts of disperse dyes;
0.1-1.5 parts of glacial acetic acid;
MIP7-15 parts of migration inhibitor;
Second of pad dyeing dyeing includes following parts by weight using vital staining agent, the vital staining agent in the step S4 Component:
41-54 parts of reactive dye;
2-9 parts of reservehao S;
5-15 parts of urea;
MIP5-13 parts of migration inhibitor;
5-15 parts of sodium bicarbonate;
Vapour steaming colour fixing uses fixation liquid in the step S4, and the fixation liquid includes the component of following parts by weight:
20-40 parts of sodium carbonate;
192-213 parts of sodium chloride;
It is described roll it is soft sizing handled using setting agent, the setting agent includes the component of following parts by weight:
5-15 parts of HS softening agents;
30-45 parts of CY color fixing agent;
0.5-1.3 parts of citric acid.
A kind of 2. dyeing for washing viscous Modal textile fabric according to claim 1, which is characterized in that the dispersion dye At least one of the black EV-ST of material selection dispersion, big Ai Nikesi carbunclies SE-B and big Ai Nikesi are golden yellow;The reactive dye Including at least a in active black SBE, reactive brilliant blue and reactive brilliant red CES.
A kind of 3. dyeing for washing viscous Modal textile fabric according to claim 1, which is characterized in that the step S3 Middle first time cleaning is using caustic soda and sodium dithionite;Second of cleaning is described to soap using soaping agent in the step S4 Agent is 209 soaping agents.
4. a kind of dyeing for washing viscous Modal textile fabric according to claim 3, which is characterized in that described second The temperature that soaping agent is added in cleaning is 90-105 DEG C.
A kind of 5. dyeing for washing viscous Modal textile fabric according to claim 1, which is characterized in that the step S3 It is 20-40m/min with the speed in step S4.
A kind of 6. dyeing for washing viscous Modal textile fabric according to claim 1, which is characterized in that the pretreatment Including turning over cloth margin to seam, open width contracting arranges and big volume is through cylinder pre-treatment;The sizing treatment includes first time squezzing sizing, burns Hair and second of squezzing sizing.
A kind of 7. dyeing for washing viscous Modal textile fabric according to claim 6, which is characterized in that the big volume warp Cylinder pre-treatment uses inorganic agent, and the inorganic agent includes the component of following parts by weight:
13-20 parts of hydrogen peroxide;
5-15 parts of caustic soda;
HDS3-10 parts of hydrogen peroxide stabilizer;
The clever TF-410 that deoils is 2-9 parts.
A kind of 8. dyeing for washing viscous Modal textile fabric according to claim 7, which is characterized in that the first time Squezzing is shaped and the temperature of second of squezzing sizing is 150-175 DEG C, the first time squezzing sizing and second of squezzing sizing Speed be 25-40m/min.
CN201610273660.6A 2016-04-27 2016-04-27 A kind of dyeing for washing viscous Modal textile fabric Active CN105714584B (en)