CN107142758B - The production method of Modal and the double-colored woven fabric of polyester filament intertexture wide cut jacquard weave - Google Patents

The production method of Modal and the double-colored woven fabric of polyester filament intertexture wide cut jacquard weave Download PDF

Info

Publication number
CN107142758B
CN107142758B CN201710502096.5A CN201710502096A CN107142758B CN 107142758 B CN107142758 B CN 107142758B CN 201710502096 A CN201710502096 A CN 201710502096A CN 107142758 B CN107142758 B CN 107142758B
Authority
CN
China
Prior art keywords
owf
follows
plus
speed
dye
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710502096.5A
Other languages
Chinese (zh)
Other versions
CN107142758A (en
Inventor
欧卫国
徐建华
葛忠平
王月华
薛鹏飞
钱银平
丁正品
杨莹莹
杨晓玲
杨静新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Jinshida Gaojing Industrial Co ltd
Original Assignee
NANTONG ISO SPECIAL FABRIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG ISO SPECIAL FABRIC CO Ltd filed Critical NANTONG ISO SPECIAL FABRIC CO Ltd
Priority to CN201710502096.5A priority Critical patent/CN107142758B/en
Publication of CN107142758A publication Critical patent/CN107142758A/en
Priority to PCT/CN2017/102916 priority patent/WO2019000663A1/en
Application granted granted Critical
Publication of CN107142758B publication Critical patent/CN107142758B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses the production method of a kind of Modal and the double-colored woven fabric of polyester filament intertexture wide cut jacquard weave, main production process includes turning over seam → light-burned hair → to roll amylase cold dome desizing → dye jigger pre-treatment → dyeing by jigger → formaldehydeless shiinkproof finish → anti-pilling finishing → machine shrunk → test package.Product is -3.0%~+1.0% through broadwise washing size changing rate, has resisted Mao Qiqiu≤4 grade, and fastness to light is 4 grades, is broken strong power≤260N, choicest quality figureofmerit is fully achieved.The present invention contaminates polyester filament on normal pressure dye jigger, with low temperature disperse dyes, and simple production process is easy to operate.

Description

The production method of Modal and the double-colored woven fabric of polyester filament intertexture wide cut jacquard weave
Technical field
The present invention relates to the dyeing and finishing production technology of a kind of Modal and the double-colored woven fabric of polyester filament intertexture wide cut jacquard weave, Especially improve woven fabric anti-fluffing and anti-pilling performance and fastness to light, the printing and dyeing final finishing production skill for reducing woven fabric washing shrinkage Art.
Technical background
Pure Modal fibre fabric has good water absorption, and dyeability is good, and soft, drapability is good, but pure Modal is fine It is lower to tie up fabric strength, especially broadwise strength is relatively low, in printing and dyeing wet-milling product and washing process, is easy to produce pilling defect Point.In addition, fabric shrinkage is bigger since Modal fibre water absorption of fabrics is very good, feel is too soft, stiffness and conformal Property is not good enough, and wrinkle resistance in fabrics is poor.Pure polyester fabric has very high-tenacity, and good luster is cheap, but terylene water imbibition is extremely low, It is such as used as B class textile, wearability is very poor.Designing Modal fibre yarn is through to polyester filament is that broadwise intertexture mentions Loom figured, then well-designed dyeing and finishing producing process, not only wearability of fabric is fine, and unique double-colored color is presented, Favor by consumer.With weaving on Modal and the bed of the double-colored woven fabric production of polyester filament intertexture wide cut jacquard weave Product are popular on the market.
Summary of the invention
It is -3.0%~+1.0% that the purpose of the present invention is to provide a kind of through broadwise washing size changing rate, anti-to fluff Qiu≤4 grade, fastness to light are 4 grades, are broken the Modal and the double-colored wide cut woven fabric of polyester filament intertexture jacquard weave of Qiang Li≤260N And its production method.
The technical solution of the invention is as follows:
A kind of production method of Modal and the double-colored wide cut woven fabric of polyester filament intertexture jacquard weave, main production process Amylase cold dome desizing → dye jigger pre-treatment → dyeing by jigger → formaldehydeless shiinkproof finish is rolled including turning over seam → light-burned hair → → anti-pilling finishing → machine shrunk → test package；It is characterized in that: when light-burned hair, using a positive and a negative technique, speed 120m/min, quality of singing reach 4 grades；
When rolling amylase cold dome desizing, desizing liquid composition: liquefaction type alpha-amylase 2g/L, penetrating agent JFC-S 3g/L, pH Value 6~6.5；50~55 DEG C of padding liquid temperature, padding machine 0.15~0.20Mpa of pressure, liquid carrying rate 120% is wrapped up with plastic film, Bank up 2h；
When only contaminating light grey with low temperature disperse dyes, dyeing recipe are as follows: disperse red FB 0.027%owf, disperse yellow E- 4G0.016%owf, Disperse Blue 2BLN 0.0099%owf, highly effective oil remover Goon105 1g/L, acetic acid tune pH 5.5, bath raio 2: 1；Dye gigging technique are as follows: 100 DEG C of dyes 4, speed are 120~130m/min；
When with low temperature disperse dyes and Nowe clone's reactive dye two-bath process dye ochre red, disperse dyeing formula Are as follows: disperse red FB 0.0088%owf, disperse yellow E-4G 0.0135%owf, 0.022% owf of Disperse Blue 2BLN, highly effective oil remover Goon105 1g/L, acetic acid tune pH 5.5, bath raio 2:1；Dye gigging technique are as follows: 100 DEG C of dyes 4, speed are 120~130m/ min；Reactive dyeing formula are as follows: Nowe clones red 0.098% owf of FN-2BL, Nowe clones Huang FN-2R 0.14% Owf, Nowe clone indigo plant FN-R 0.079% owf, anhydrous sodium sulphate 30g/L, soda ash 10g/L, bath raio 2:1；Dye gigging technique are as follows: fabric Into cylinder → cold water together → plus dyestuff be warming up to 40 DEG C of Shang Ran, tetra- → 40 DEG C of anhydrous sodium sulphate Cu Ran bis-, wherein start for first plus 2/3 anhydrous sodium sulphate, second starts plus 1/3 anhydrous sodium sulphate → 40 DEG C soda ash fixation two, wherein start for first to add 2/3 soda ash, the Two start plus 1/3 soda ash → 70 DEG C two → cold water of fixation wash two → 80 DEG C washing two → 40 DEG C washing two → Add acetic acid to neutralize together → cold water and goes out cylinder；Speed is 90~100m/min；
When only with Nowe clone's reactive dye dye rose golden, dyeing recipe are as follows: Nowe clones red FN-2BL 0.0555% Owf, Nowe clone 0.088% owf of Huang FN-2R, Nowe clone 0.010% owf of indigo plant FN-R, anhydrous sodium sulphate 30g/L, soda ash 10g/L, bath raio 2:1；Dye gigging technique are as follows: fabric into cylinder → cold water together → plus dyestuff be warming up to tetra- → 40 DEG C of 40 DEG C of Shang Ran Anhydrous sodium sulphate Cu Ran bis-, wherein starting for first to add 2/3 anhydrous sodium sulphate, second starts plus 1/3 anhydrous sodium sulphate → 40 DEG C soda ash fixation Two, wherein starting for first plus 2/3 soda ash, second starts plus 1/3 soda ash → 70 DEG C two → cold water of fixation wash two → 80 DEG C of washings, two → 40 DEG C of washings two → plus acetic acid neutralize together → cold water and go out cylinder；Speed is 90~100m/min；
When formaldehydeless shiinkproof finish, the composition of shiinkproof finish liquid are as follows:
50~70 g/L of Arkofix NZF
MgCl2·6H25~7g/L of O
Remaining is water, and with citric acid tune pH to 5.0~5.5；
By open width cloth feeding when shiinkproof finish, second dipping and rolling shiinkproof finish liquid, liquid carrying rate 65%, 110~120 DEG C of loose formulas are pre- It dries, needle plate on overfeeding 2%~4%, eight lattice hot winds bake, wherein 150 DEG C of the first~bis- lattice temperature, third~tetra- lattice temperature 160 DEG C, the five~eight 165 DEG C of lattice temperature, the cooling cropping step of two cylinders, speed is 40~45m/min；
When anti-pilling finishing, anti-pilling finishing liquid composition are as follows: anti-pilling finishing agent FK-839 10~ 14g/L；Anti-pilling finishing technique is open width cloth feeding, an immersing and rolling anti-pilling finishing liquid, liquid carrying rate 75%, overfeeding Needle plate on 1.5%~3%, 140~150 DEG C of drying, cooling cropping step, speed are 40~50m/min；Cropping door width reaches 100 Inch；
When machine shrunk, the uniform dewing of fabric, moisture percentage 8%~10%, rubber blanket bearing roller steam pressure 0.1~ 0.15Mpa, blanket cylinder 0.1~0.15Mpa of steam pressure control preshrinking rate 2%~4%, 40~50m/min of cloth speed.
Modal and polyester filament intertexture fabric specification: 106 inches of door, figured texture weave, the first yarn count is M40sXT75D, density 173X115；Second of yarn count is M60sXT50D, density 173X160.Design finished product door 98.5 Inch.
The present invention contaminates polyester filament, simple production process, operation side on normal pressure dye jigger, with low temperature disperse dyes Just.It is no matter single using Modal and polyester filament to reactive dye and disperse dyes reactivity worth difference and figured texture weave structure Private low temperature disperse dyes or reactive dyeing, or contaminated simultaneously with low temperature disperse dyes and reactive dye two-bath process Color, fabric can all generate two-color effect.Product washes size changing rate between -3.0% and+1.0% through broadwise, anti-fluffing Qiu≤4 grade Qi, are broken Qiang Li≤260N, excellent product performance by 4 grades of fastness to light.
Below with reference to embodiment, the invention will be further described.
Specific embodiment
Embodiment 1:
Modal with 106 inches of door of polyester filament intertexture figured texture weave fabric, yarn count M40sXT75D, density is 173X115。
A kind of production method of Modal and the double-colored wide cut woven fabric of polyester filament intertexture jacquard weave, main production process Amylase cold dome desizing → dye jigger pre-treatment → dyeing by jigger → formaldehydeless shiinkproof finish is rolled including turning over seam → light-burned hair → → anti-pilling finishing → machine shrunk → test package；It is characterized in that: when light-burned hair, using a positive and a negative technique, speed 120m/min, quality of singing reach 4 grades；
When rolling amylase cold dome desizing, desizing liquid composition: liquefaction type alpha-amylase 2g/L, penetrating agent JFC-S3g/L, pH Value 6~6.5.50~55 DEG C of padding liquid temperature, padding machine 0.15~0.20Mpa of pressure, liquid carrying rate 120% is wrapped up with plastic film, Bank up 2h.
When only contaminating light grey with low temperature disperse dyes, dyeing recipe are as follows: disperse red FB 0.027%(owf), disperse yellow E- 4G0.016%(owf), Disperse Blue 2BLN 0.0099%(owf), highly effective oil remover Goon105 1g/L, acetic acid tune pH 5.5, bath Compare 2:1.Dye gigging technique are as follows: 100 DEG C of dyes 4, speed are 120~130m/min.
When formaldehydeless shiinkproof finish, the composition of shiinkproof finish liquid are as follows:
50~70 g/L of Arkofix NZF
5~7g/L of MgCl26H2O
Remaining is water, and with citric acid tune pH to 5.0~5.5；
By open width cloth feeding when shiinkproof finish, second dipping and rolling shiinkproof finish liquid, liquid carrying rate 65%, 110~120 DEG C of loose formulas are pre- It dries, needle plate on overfeeding 2%~4%, eight lattice hot winds bake, wherein 150 DEG C of the first~bis- lattice temperature, third~tetra- lattice temperature 160 DEG C, the five~eight 165 DEG C of lattice temperature, the cooling cropping step of two cylinders, speed is 40~45m/min.
When anti-pilling finishing, anti-pilling finishing liquid composition are as follows: anti-pilling finishing agent FK-83910~ 14g/L.Anti-pilling finishing technique is open width cloth feeding, an immersing and rolling anti-pilling finishing liquid, liquid carrying rate 75%, overfeeding Needle plate on 1.5%~3%, 140~150 DEG C of drying, cooling cropping step, speed are 40~50m/min.Cropping door width reaches 100 Inch.
When machine shrunk, the uniform dewing of fabric, moisture percentage 8%~10%, rubber blanket bearing roller steam pressure 0.1~ 0.15Mpa, blanket cylinder 0.1~0.15Mpa of steam pressure control preshrinking rate 2%~4%, 40~50m/min of cloth speed.
The warp of product, broadwise washing size changing rate are respectively -2.5.0%, -1.2%, and 4 grades of anti-fluffing and anti-pilling, fast light jail 4 grades of degree, through to ultimate strength 280N.
Embodiment 2:
Modal with 106 inches of door of polyester filament intertexture figured texture weave fabric, yarn count is M60s × T50D, and density is 173×160。
A kind of production method of Modal and the double-colored wide cut woven fabric of polyester filament intertexture jacquard weave, main production process Amylase cold dome desizing → dye jigger pre-treatment → dyeing by jigger → formaldehydeless shiinkproof finish is rolled including turning over seam → light-burned hair → → anti-pilling finishing → machine shrunk → test package；It is characterized in that: when light-burned hair, using a positive and a negative technique, speed 120m/min, quality of singing reach 4 grades；
When rolling amylase cold dome desizing, desizing liquid composition: liquefaction type alpha-amylase 2g/L, penetrating agent JFC-S3g/L, pH Value 6~6.5.50~55 DEG C of padding liquid temperature, padding machine 0.15~0.20Mpa of pressure, liquid carrying rate 120% is wrapped up with plastic film, Bank up 2h.
When with low temperature disperse dyes and Nowe clone's reactive dye two-bath process dye ochre red, disperse dyeing formula Are as follows: disperse red FB 0.0088%(owf), disperse yellow E-4G 0.0135%(owf), Disperse Blue 2BLN 0.022% (owf), efficiently Degreaser Goon105 1g/L, acetic acid tune pH 5.5, bath raio 2:1.Dye gigging technique are as follows: 100 DEG C dye 4, speed be 120~ 130m/min.Reactive dyeing formula are as follows: Nowe clones red FN-2BL 0.098%(owf), Nowe clone Huang FN-2R 0.14%(owf), Nowe clones indigo plant FN-R 0.079%(owf), anhydrous sodium sulphate 30g/L, soda ash 10g/L, bath raio 2:1.Dye gigging technique Are as follows: fabric into cylinder → cold water together → plus dyestuff be warming up to 40 DEG C of Shang Ran, tetra- → 40 DEG C of anhydrous sodium sulphate Cu Ran bis- and (open for first Begin plus 2/3 anhydrous sodium sulphate, second starts plus 1/3 anhydrous sodium sulphate) → 40 DEG C of soda ash fixation two (start for first plus 2/3 soda ash, Second start plus 1/3 soda ash) → 70 DEG C of two → cold water of fixation wash two → 80 DEG C washing two → 40 DEG C washing two → add acetic acid one → cold water of neutralization to go out cylinder.Speed is 90~100m/min.
When formaldehydeless shiinkproof finish, the composition of shiinkproof finish liquid are as follows:
50~70 g/L of Arkofix NZF
5~7g/L of MgCl26H2O
Remaining is water, and with citric acid tune pH to 5.0~5.5；
By open width cloth feeding when shiinkproof finish, second dipping and rolling shiinkproof finish liquid, liquid carrying rate 65%, 110~120 DEG C of loose formulas are pre- It dries, needle plate on overfeeding 2%~4%, eight lattice hot winds bake, wherein 150 DEG C of the first~bis- lattice temperature, third~tetra- lattice temperature 160 DEG C, the five~eight 165 DEG C of lattice temperature, the cooling cropping step of two cylinders, speed is 40~45m/min.
When anti-pilling finishing, anti-pilling finishing liquid composition are as follows: anti-pilling finishing agent FK-83910~ 14g/L.Anti-pilling finishing technique is open width cloth feeding, an immersing and rolling anti-pilling finishing liquid, liquid carrying rate 75%, overfeeding Needle plate on 1.5%~3%, 140~150 DEG C of drying, cooling cropping step, speed are 40~50m/min.Cropping door width reaches 100 Inch.
When machine shrunk, the uniform dewing of fabric, moisture percentage 8%~10%, rubber blanket bearing roller steam pressure 0.1~ 0.15Mpa, blanket cylinder 0.1~0.15Mpa of steam pressure control preshrinking rate 2%~4%, 40~50m/min of cloth speed.
The warp of product, broadwise washing size changing rate are respectively -2.8.0%, -1.5%, and 4 grades of anti-fluffing and anti-pilling, fast light jail 4 grades of degree, through to ultimate strength 270N.

Claims (1)

1. the production method of a kind of Modal and the double-colored wide cut woven fabric of polyester filament intertexture jacquard weave, it is characterized in that: using not generation You successively pass through with polyester filament intertexture fabric: turn over seam → light-burned hair → roll amylase cold dome desizing → dye jigger pre-treatment → Dyeing by jigger → formaldehydeless shiinkproof finish → anti-pilling finishing → machine shrunk → test package；When light-burned hair, use A positive and a negative technique, speed 120m/min, quality of singing reach 4 grades；
When rolling amylase cold dome desizing, desizing liquid composition: liquefaction type alpha-amylase 2g/L, penetrating agent JFC-S 3g/L, pH value 6 ~6.5；50~55 DEG C of padding liquid temperature, padding machine pressure 0.15~0.20MP a, liquid carrying rate 120% is wrapped up, heap with plastic film Set 2h；
When only contaminating light grey with low temperature disperse dyes, dyeing recipe are as follows: disperse red FB 0.027%owf, disperse yellow E- 4G0.016%owf, Disperse Blue 2BLN 0.0099%owf, highly effective oil remover Goon105 1g/L, acetic acid tune pH 5.5, bath raio 2: 1；Dye gigging technique are as follows: 100 DEG C of dyes 4, speed are 120~130m/min；
When with low temperature disperse dyes and Nowe clone's reactive dye two-bath process dye ochre red, disperse dyeing formula are as follows: point Dissipate red FB 0.0088%owf, disperse yellow E-4G 0.0135%owf, 0.022% owf of Disperse Blue 2BLN, highly effective oil remover Goon105 1g/L, acetic acid tune pH 5.5, bath raio 2:1；Dye gigging technique are as follows: 100 DEG C of dyes 4, speed are 120~130m/min； Reactive dyeing formula are as follows: Nowe clones red 0.098% owf of FN-2BL, Nowe clones 0.14% owf of Huang FN-2R, promise Brunswick grand indigo plant FN-R 0.079% owf, anhydrous sodium sulphate 30g/L, soda ash 10g/L, bath raio 2:1；Dye gigging technique are as follows: fabric into cylinder → Cold water together → plus dyestuff be warming up to 40 DEG C of Shang Ran, tetra- → 40 DEG C of anhydrous sodium sulphate Cu Ran bis-, wherein starting for first plus 2/3 yuan Bright powder, second starts plus 1/3 anhydrous sodium sulphate → 40 DEG C soda ash fixation two, wherein starting for first to add 2/3 soda ash, second Start plus 1/3 soda ash → 70 DEG C two → cold water of fixation washes two → 80 DEG C of washings, two → 40 DEG C of washings two → plus vinegar Acid neutralizes together → cold water and goes out cylinder；Speed is 90~100m/min；
When only with Nowe clone's reactive dye dye rose golden, dyeing recipe are as follows: Nowe clones red FN-2BL 0.0555% Owf, Nowe clone 0.088% owf of Huang FN-2R, Nowe clone 0.010% owf of indigo plant FN-R, anhydrous sodium sulphate 30g/L, soda ash 10g/L, bath raio 2:1；Dye gigging technique are as follows: fabric into cylinder → cold water together → plus dyestuff be warming up to 40 DEG C of Shang Ran, tetra- → 40 DEG C of members Bright powder Cu Ran bis-, wherein starting for first to add 2/3 anhydrous sodium sulphate, second starts plus 1/3 anhydrous sodium sulphate → 40 DEG C soda ash fixation two Road, wherein starting for first plus 2/3 soda ash, second starts plus 1/3 soda ash → 70 DEG C two → cold water of fixation wash two → 80 DEG C of washings, two → 40 DEG C of washings two → plus acetic acid neutralize together → cold water and go out cylinder；Speed is 90~100m/min；
When formaldehydeless shiinkproof finish, the composition of shiinkproof finish liquid are as follows:
50~70 g/L of Arkofix NZF
MgCl2·6H25~7g/L of O
Remaining is water, and with citric acid tune pH to 5.0~5.5；
By open width cloth feeding when shiinkproof finish, second dipping and rolling shiinkproof finish liquid, liquid carrying rate 65%, 110~120 DEG C of loose formula preliminary dryings surpass Needle plate on 2%~4% is fed, eight lattice hot winds bake, wherein 150 DEG C of the first~bis- lattice temperature, third~160 DEG C of tetra- lattice temperature, the Five~eight 165 DEG C of lattice temperature, the cooling cropping step of two cylinders, speed is 40~45m/min；
When anti-pilling finishing, anti-pilling finishing liquid composition are as follows: 10~14g/ of anti-pilling finishing agent FK-839 L；Anti-pilling finishing technique is open width cloth feeding, an immersing and rolling anti-pilling finishing liquid, liquid carrying rate 75%, overfeeding 1.5%~ Needle plate on 3%, 140~150 DEG C of drying, cooling cropping step, speed are 40~50m/min；Cropping door width reaches 100 inches；
When machine shrunk, the uniform dewing of fabric, moisture percentage 8%~10%, rubber blanket bearing roller steam pressure 0.1~0.15MP a, Blanket cylinder steam pressure 0.1~0.15MP a controls preshrinking rate 2%~4%, 40~50m/min of cloth speed.
CN201710502096.5A 2017-06-27 2017-06-27 The production method of Modal and the double-colored woven fabric of polyester filament intertexture wide cut jacquard weave Active CN107142758B (en)