CN106283727A - Anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric and production method thereof - Google Patents
Anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric and production method thereof Download PDFInfo
- Publication number
- CN106283727A CN106283727A CN201610647567.7A CN201610647567A CN106283727A CN 106283727 A CN106283727 A CN 106283727A CN 201610647567 A CN201610647567 A CN 201610647567A CN 106283727 A CN106283727 A CN 106283727A
- Authority
- CN
- China
- Prior art keywords
- pilling
- fluffing
- woven fabric
- dye
- wide cut
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti pilling Lyocell fibers wide cut woven fabric and production method thereof, production method includes singing, desizing, bleach, dye, cellulose treatment, chemistry shiinkproof finish, anti-pilling finishing, machine shrunk, test package；Described desizing, bleach, dye, cellulose treatment technique produces on Large Copacity dye jigger.Production technology of the present invention is simple, easy to operate, excellent product performance；Anti-fluffing and anti-pilling >=4 grade, product washes change in size 2.5%～1.0%, fastness to soaping >=4 grade, broadwise ultimate strength 250N through broadwise.
Description
Technical field
The present invention relates to a kind of anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric and production method thereof.
Background technology
Lyocell fibers came out in the mid-90 in 20th century, had been described as since nearly half a century in staple fibre history most
The product being worth, its raw material is cellulose inexhaustible in nature, and in production process, solvent for use is nontoxic also
Can reclaim and use, garbage is biodegradable.Lyocell is a kind of green fiber, has the multiple of natural fiber and synthetic fibers
Premium properties, by consumers.But Lyocell fibers easily fibrillable, easy pilling after friction.Therefore, FZ/T
14014 2009 Lyocell fibers dyeing cloth standards, pilling property is not as performance assessment criteria.Easily pilling performance have impact on
Fabric serviceability, along with growth in the living standard, the requirement to the width Lyocell fibers woven fabric for bedding has
Good anti-fluffing and anti-pilling performance.
Summary of the invention
It is an object of the invention to provide the anti-fluffing and anti-pilling Lyocell fibers wide cut that a kind of anti-fluffing and anti-pilling performance is excellent
Woven fabric and production method thereof.
The technical solution of the present invention is:
A kind of anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric, is characterized in that: anti-fluffing and anti-pilling >=4 grade, product is through broadwise water
Wash change in size-2.5%～1.0%, fastness to soaping >=4 grade, broadwise ultimate strength 250N.
Woven fabric grey cloth specification is the one in following two kinds: the first width is 110 inches, yarn count is 60s × 60s,
Density is the figured texture weave of 173 × 130 pieces/inch；The second door width is 120 inches, yarn count is 40s × 40s, density is
The satin weave of 173 × 90 pieces/inch.
A kind of anti pilling Lyocell fibers wide cut woven fabric and production method thereof, include successively singing → desizing → bleaching →
Dyeing → cellulose treatment → chemistry shiinkproof finish → anti-pilling finishing → machine shrunk → test package；Its feature
It is: during dyeing to use reactive dye jig dyeing method, the dye dosage (owf) of the light grey product of dye: Nowe clones red FN 2BL
0.1098%, the yellow FN 2R 0.0879% of Nowe clone, the blue FN R 0.2633% of Nowe clone；The dye of dye cameo brown product
Material consumption (owf): Nowe clones red FN 2BL 0.193%, the yellow FN 2R 0.114% of Nowe clone, Nowe clone's indigo plant
FN—R 0.097% ；Dye gigging technique is: fabric enter cylinder → cold water together → add dyestuff be warming up to 35 DEG C → above dye two～four roads →
Add Matrii Sulfas Exsiccatus Cu Ran bis-road → add fixation two roads, 35 DEG C of fixation two road → 65 DEG C of soda → cold water and wash two road → 75 DEG C washings two
Washing two roads, road → 45 DEG C.
During cellulose treatment, consisting of of cellulase: cellulase 0.5%～2%(owf), pH 4.5 ~ 6.0, bath
Ratio 8 ~ 12:1；Process technique is: processes 40～60 minutes in 45 ~ 60 DEG C of water-baths, after having processed, is warming up to 80 DEG C, then locates
Manage 10～20 minutes, make enzyme lose activity.
During chemistry shiinkproof finish, consisting of of dressing liquid:
Formaldehydeless permanent press finishing agent Arkofix NZF(i.e. formaldehyde-free resins Arkofix NZF) 60～100g/L
MgCl2 6H2O 6～10g/L
NON IONIC SOFTNER V-12 6.0 g/L
Remaining is water, and adjusts pH to 4.0～5.5 with citric acid；
Technological process is for enter cloth by open width, and two leachings two are rolled shiinkproof finish liquid, liquid carrying rate 75%～80%, 110～130 DEG C of loose formula and dried
Dry, needle plate on overfeeding 2%～5%, eight lattice hot blasts bake, wherein the first lattice temperature 160 DEG C, the second lattice temperature 165 DEG C, the 3rd～
Eight lattice temperature 170 DEG C, two cylinder cooling cropping steps, speed is 30～40m/min.
During anti-pilling finishing, consisting of of anti-pilling finishing liquid: anti-fluffing and anti-pilling auxiliary agent FK-833 10～
20g/L；During anti-pilling finishing, entering cloth by open width, anti-pilling finishing liquid is rolled in two leachings two, liquid carrying rate 70%～75%,
Needle plate on overfeeding 1.5%～3.0%, 130～140 DEG C of drying, cool down cropping step, speed is 30～40m/min.
During machine shrunk, the uniform dewing of fabric, moisture percentage 10% ~ 15%, rubber blanket bearing roller steam pressure 0.1～
0.2Mpa, blanket cylinder steam pressure 0.1～0.2Mpa, control preshrinking rate 2%～4%, cloth speed 40～50m/min.
By series dyeing and finishing Final finishing technology, produce anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric.First, by dye
Cellulose treatment after color, removes the micro-fibril of fabric face that is exposed at after fibrillation, makes fabric face bright and clean.Secondly,
Carrying out formaldehydeless chemistry shiinkproof finish, covalent cross-linking occurs between fiber, fabric is difficult to fibril during post-treatment and use
Change, also reduce fabric shrinkage simultaneously.3rd, carry out anti-fluffing and anti-pilling special finishing, it is ensured that anti-fluffing and anti-pilling >=4 grade.With
In time, reach between-2.5%～1.0% through broadwise washing change in size, fastness to soaping >=4 grade, broadwise ultimate strength 250N.
Production technology of the present invention is simple, easy to operate, excellent product performance；Anti-fluffing and anti-pilling >=4 grade, product longitude and latitude
To washing change in size-2.5%～1.0%, fastness to soaping >=4 grade, broadwise ultimate strength 250N.
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
Figured texture weave woven fabric grey cloth door width is 110 inches, yarn count is 60s × 60s, density is 173 × 130/English
Very little.
A kind of anti pilling Lyocell fibers wide cut woven fabric and production method thereof, include successively singing → desizing → bleaching →
Dyeing → cellulose treatment → chemistry shiinkproof finish → anti-pilling finishing → machine shrunk → test package；Its feature
It is: during dyeing to use reactive dye jig dyeing method, the dye dosage (owf) of the light grey product of dye: Nowe clones red FN 2BL
0.1098%, the yellow FN 2R 0.0879% of Nowe clone, the blue FN R 0.2633% of Nowe clone；Dye gigging technique is: fabric
Enter cylinder → cold water together → add dyestuff and be warming up to 35 DEG C → upper Matrii Sulfas Exsiccatus Cu Ran bis-road, dye two～four roads → add → add soda 35
DEG C fixation two roads, fixation two road → 65 DEG C → cold water washes two washing two roads, washing two road → 45 DEG C, road → 75 DEG C.
During cellulose treatment, consisting of of cellulase: cellulase 1.0%～1.5%(owf), pH 4.5～5.5,
Bath raio 8～12:1；Process technique is: processes 40～60 minutes in 45～60 DEG C of water-baths, after having processed, is warming up to 80 DEG C,
Reprocess 10～20 minutes, make enzyme lose activity.
During chemistry shiinkproof finish, consisting of of dressing liquid:
Formaldehydeless permanent press finishing agent Arkofix NZF 60～80g/L(example 60 g/L, 70 g/L, 80 g/L)
MgCl26H2O 6～8g/L
NON IONIC SOFTNER V-12 6.0 g/L
Remaining is water, and adjusts pH to 4.5～5.0 with citric acid；
Technological process is for enter cloth by open width, and two leachings two are rolled shiinkproof finish liquid, liquid carrying rate 75%～80%, 110～130 DEG C of loose formula and dried
Dry, needle plate on overfeeding 2%～5%, eight lattice hot blasts bake, wherein the first lattice temperature 160 DEG C, the second lattice temperature 165 DEG C, the 3rd～
Eight lattice temperature 170 DEG C, two cylinder cooling cropping steps, speed is 35～40m/min.
During anti-pilling finishing, consisting of of anti-pilling finishing liquid: anti-fluffing and anti-pilling auxiliary agent FK-833 10～
15g/L；During anti-pilling finishing, entering cloth by open width, anti-pilling finishing liquid is rolled in two leachings two, liquid carrying rate 70%～75%,
Needle plate on overfeeding 1.5%～3.0%, 130～140 DEG C of drying, cool down cropping step, speed is 45～50m/min.
During machine shrunk, the uniform dewing of fabric, moisture percentage 10% ~ 12%, rubber blanket bearing roller steam pressure 0.1～
0.2Mpa, blanket cylinder steam pressure 0.1～0.2Mpa, control preshrinking rate 2%～3%, cloth speed 45～50m/min.
Embodiment 2:
Satin weave woven fabric grey cloth door width is 120 inches, yarn count is 40s × 40s, density is 173 × 90 pieces/inch.
A kind of anti pilling Lyocell fibers wide cut woven fabric and production method thereof, include successively singing → desizing → bleaching →
Dyeing → cellulose treatment → chemistry shiinkproof finish → anti-pilling finishing → machine shrunk → test package；Its feature
It is: during dyeing to use reactive dye jig dyeing method, the dye dosage (owf) of dye cameo brown product: Nowe clones red FN 2BL
0.193%, the yellow FN 2R 0.114% of Nowe clone, the blue FN R 0.097% of Nowe clone；Dye gigging technique is: fabric enters cylinder
→ cold water together → add dyestuff be warming up to 35 DEG C → above Matrii Sulfas Exsiccatus Cu Ran bis-road, dye two～four roads → add → add soda 35 DEG C solid
Fixation two roads, color two road → 65 DEG C → cold water washes two washing two roads, washing two road → 45 DEG C, road → 75 DEG C.
During cellulose treatment, consisting of of cellulase: cellulase 0.5%～1.2%(owf), pH 4.5～5.0,
Bath raio 8 ~ 12:1；Process technique is: processes 40～60 minutes in 45 ~ 60 DEG C of water-baths, after having processed, is warming up to 80 DEG C, then
Process 10～20 minutes, make enzyme lose activity.
During chemistry shiinkproof finish, consisting of of dressing liquid:
Formaldehydeless permanent press finishing agent Arkofix NZF 80～100g/L(example 80 g/L, 90 g/L, 100 g/L)
MgCl26H2O 8～10g/L
NON IONIC SOFTNER V-12 6.0 g/L
Remaining is water, and adjusts pH to 4.0～4.5 with citric acid；
Technological process is for enter cloth by open width, and two leachings two are rolled shiinkproof finish liquid, liquid carrying rate 75%～80%, 110～130 DEG C of loose formula and dried
Dry, needle plate on overfeeding 2%～5%, eight lattice hot blasts bake, wherein the first lattice temperature 160 DEG C, the second lattice temperature 165 DEG C, the 3rd～
Eight lattice temperature 170 DEG C, two cylinder cooling cropping steps, speed is 30～35m/min.
During anti-pilling finishing, consisting of of anti-pilling finishing liquid: anti-fluffing and anti-pilling auxiliary agent FK-833 15～
20g/L；During anti-pilling finishing, entering cloth by open width, anti-pilling finishing liquid is rolled in two leachings two, liquid carrying rate 70%～75%,
Needle plate on overfeeding 1.5%～3.0%, 130～140 DEG C of drying, cool down cropping step, speed is 40～45m/min.
During machine shrunk, the uniform dewing of fabric, moisture percentage 12% ~ 15%, rubber blanket bearing roller steam pressure 0.1～
0.2Mpa, blanket cylinder steam pressure 0.1～0.2Mpa, control preshrinking rate 3%～4%, cloth speed 40～45m/min.
Claims (7)
1. an anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric, is characterized in that: anti-fluffing and anti-pilling >=4 grade, product is through broadwise
Washing change in size-2.5%～1.0%, fastness to soaping >=4 grade, broadwise ultimate strength 250N.
2., according to the anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric described in claim 1, it is characterized in that: woven fabric base
Cloth specification is the one in following two kinds: the first width is 110 inches, yarn count is 60s × 60s, density be 173 ×
The figured texture weave of 130 pieces/inch；The second door width is 120 inches, yarn count is 40s × 40s, density is 173 × 90/English
Very little satin weave.
3. a production method for the anti pilling Lyocell fibers wide cut woven fabric described in claim 1, include successively singing →
Desizing → bleaching → dyeing → cellulose treatment → chemistry shiinkproof finish → anti-pilling finishing → machine shrunk → inspection
Packaging；It is characterized in that: during dyeing, use reactive dye jig dyeing method, the dye dosage of the light grey product of dye: clone is red for Nowe
The yellow FN 2R 0.0879 owf % of FN 2BL 0.1098 owf %, Nowe clone, the blue FN R 0.2633 of Nowe clone
owf % ；The dye dosage of dye cameo brown product: Nowe clones red FN 2BL 0.193 owf %, the yellow FN of Nowe clone
The blue FN R 0.097 owf % of 2R 0.114 owf %, Nowe clone；Dye gigging technique is: fabric enter cylinder → cold water together →
Add dyestuff and be warming up to 35 DEG C → upper Matrii Sulfas Exsiccatus Cu Ran bis-road, dye two～four roads → add → add 35 DEG C of fixation two road → 65 DEG C of soda
Fixation two roads → cold water washes two washing two roads, washing two road → 45 DEG C, road → 75 DEG C.
The production method of anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric the most according to claim 3, is characterized in that: fine
Dimension element ferment treatment time, consisting of of cellulase: cellulase consumption is 0.5%～2%owf, pH 4.5～6.0, bath raio 8～
12:1；Process technique is: processes 40～60 minutes in 45～60 DEG C of water-baths, after having processed, is warming up to 80 DEG C, reprocesses 10
～20 minutes, make enzyme lose activity.
The production method of anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric the most according to claim 3, is characterized in that: change
When learning shiinkproof finish, consisting of of dressing liquid:
Formaldehydeless permanent press finishing agent Arkofix NZF 60～100g/L
MgCl2 6H2O 6～10g/L
NON IONIC SOFTNER V-12 6.0 g/L
Remaining is water, and adjusts pH to 4.0～5.5 with citric acid；
Technological process is for enter cloth by open width, and two leachings two are rolled shiinkproof finish liquid, liquid carrying rate 75%～80%, 110～130 DEG C of loose formula and dried
Dry, needle plate on overfeeding 2%～5%, eight lattice hot blasts bake, wherein the first lattice temperature 160 DEG C, the second lattice temperature 165 DEG C, the 3rd～
Eight lattice temperature 170 DEG C, two cylinder cooling cropping steps, speed is 30～40m/min.
6., according to the production method of the anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric described in claim 3, it is characterized in that:
During anti-pilling finishing, consisting of of anti-pilling finishing liquid: anti-fluffing and anti-pilling auxiliary agent FK-833 10～20g/L, remaining
Amount is water；During anti-pilling finishing, entering cloth by open width, anti-pilling finishing liquid is rolled in two leachings two, liquid carrying rate 70%～75%,
Needle plate on overfeeding 1.5%～3.0%, 130～140 DEG C of drying, cool down cropping step, speed is 40～50m/min.
The production method of anti-fluffing and anti-pilling Lyocell fibers wide cut woven fabric the most according to claim 3, is characterized in that: machine
During tool preshrunk, the uniform dewing of fabric, moisture percentage 10% ~ 15%, rubber blanket bearing roller steam pressure 0.1～0.2Mpa, blanket cylinder
Steam pressure 0.1～0.2Mpa, controls preshrinking rate 2%～4%, cloth speed 40～50m/min.