CN109750530A - The production method of the high day wire type wide cut woven fabric of anti-pilling property - Google Patents

The production method of the high day wire type wide cut woven fabric of anti-pilling property Download PDF

Info

Publication number
CN109750530A
CN109750530A CN201910027518.7A CN201910027518A CN109750530A CN 109750530 A CN109750530 A CN 109750530A CN 201910027518 A CN201910027518 A CN 201910027518A CN 109750530 A CN109750530 A CN 109750530A
Authority
CN
China
Prior art keywords
cold
pilling
lattice
pad
washing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910027518.7A
Other languages
Chinese (zh)
Inventor
欧卫国
王春梅
王月华
葛忠平
薛鹏飞
徐建华
陈刚
杨莹莹
陆健
杨小玲
蔡云芸
叶国庆
曹锦妹
杨静新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG ISO SPECIAL FABRIC CO Ltd
Nantong University
Original Assignee
NANTONG ISO SPECIAL FABRIC CO Ltd
Nantong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG ISO SPECIAL FABRIC CO Ltd, Nantong University filed Critical NANTONG ISO SPECIAL FABRIC CO Ltd
Priority to CN201910027518.7A priority Critical patent/CN109750530A/en
Publication of CN109750530A publication Critical patent/CN109750530A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of production method of day wire type wide cut woven fabric that anti-pilling property is high, production procedure includes turning over to stitch → singing → and pad oxalic acid → banking up → to wash → dry → alkaline oxygen bath cold-pad-batch preparation → washing → drying → cold-rolling heap staining → washing → drying → shrinkproof and anti pilling one-bath finishing → calendering → machine shrunk → test package.The invention discloses day wire type fabric segments energy emission reduction cold-pad-batch preparation, dyeing and shrinkproof and anti pilling one-bath finishing dyeing and finishing production new technologies.Pilling performance≤4 grade of product, broadwise are broken strong power≤280N, wash size changing rate -2.5%~+0.5%, resistance to fastness to wet rubbing≤3-4 grades, product comprehensive performance reaches high-class product bedding quality index.

Description

The production method of the high day wire type wide cut woven fabric of anti-pilling property
Technical field
The present invention relates to a kind of dyeing and finishing production technologies of day wire type wide cut woven fabric that anti-pilling property is high.
Background technique
Tencel comes out in mid-term the 1990s, most valuable in staple fibre history since being known as nearly half a century Product.Have both a variety of excellent performances of natural fiber and synthetic fibers.Tencel is green fiber, and raw material is to take it in nature Cellulose nexhaustible not to the utmost, for production process without chemical reaction, solvent for use is nontoxic.Tencel can divide completely in soil Solution, no pollution to the environment.But tencel easily fibrillable, easy pilling after friction, influences Tencel fabric wearability.Tencel and cotton Blended or tencel makes the pilling property containing Tencel fabric by the dyeing and finishing production technology of present specification with cotton ramie blended spinning fabric >=4 grades, broadwise is broken strong power≤280N, washes size changing rate -2.5%~+0.5%, resistance to fastness to wet rubbing≤3-4 grades, becomes The wide cut woven fabric of textile processing on high-grade bed.
Summary of the invention
The purpose of the present invention is to provide a kind of fabric pilling performance >=4 grade, broadwise is broken Qiang Li≤280N, washes size Change rate -2.5%~+0.5%, the production of the high day wire type wide cut woven fabric of resistance to fastness to wet rubbing≤3-4 grades of anti-pilling property Method.
The technical solution of the invention is as follows:
A kind of production method for the day wire type wide cut woven fabric that anti-pilling property is high, production procedure include turning over to stitch → singing → and pad Oxalic acid → banking up → washes → dries → and alkaline oxygen bath cold-pad-batch preparation → washing → drying → cold-rolling heap staining → washing → Drying → shrinkproof and anti pilling one-bath finishing → calendering → machine shrunk → test package;It is characterized in that: pilling performance≤4 grade, Strong power≤the 280N of broadwise fracture, washing size changing rate -2.5%~+0.5%, resistance to fastness to wet rubbing≤3-4 grades.
When padding oxalic acid, 7~8g/L of concentration of oxalic acid, liquid carrying rate 70%~80%.After banking up 2~4h, five cell compartment temperature open washings.
When alkaline oxygen bath cold-pad-batch preparation, alkaline oxygen bath liquid composition are as follows:
(100%) 30~35g/L of NaOH
H2O2(100%) 16~18g/L
It is cold to help clever 25g/L
5~6g/L of waterglass
When cold-pad-batch preparation, pass through open width cloth feeding, second dipping and rolling cold-pad-batch preparation liquid, liquid carrying rate 70%~80%.Bank up 20 ~for 24 hours after, high temperature open washing.
When cold-rolling heap staining, when contaminating the shallow colour of camel's hair, dye liquor composition: Nowe clones red FN -2BL 0.347g/L, Nowe clone Yellow FN -2R 0.202g/L, Nowe clone indigo plant FN-R 0.258g/L;Lye composition: caustic soda 24g/L, low temperature cold dome are solid Color alkali EW-956 26/L;When contaminating grey, dye liquor composition: it is yellow that Nowe clones red FN -2BL 1.560g/L, Nowe clone FN -2R 0.605g/L, Nowe clone indigo plant FN-R 2.480g/L;Lye composition: caustic soda 26g/L, low temperature cold dome fixation alkali EW-956 28/L ;Dyeing are as follows: dye liquor and 4: 1 ratio of lye mix, pick-up rate 65%, 60~65m/ of speed Min, stacking at room temperature 16~for 24 hours;Dye aftertreatment technology are as follows: cloth feeding → room temperature passes through reductive steam box → first, second and third lattice Flowing cool water washes 80~90 DEG C of → fourth, fifth lattice, add the lattice of high concentrated low temperature releasing soaping agent 2~3g/L of ANT soap boiling → the 6th 70~ 80 DEG C of washing the → the seven lattice flowing cool water washing → croppings.
When shrinkproof and anti pilling one-bath finishing, working solution composition are as follows:
Non-aldehyde low-temperature crease and shrink resistant finishing agent KNITTEX FFRC 60g/L
Fluffy 25 g/L of silicone oil Goon1202
Hydrophilic silicone oil 5g/L
Fibre trimmer FFS 3g/L
When shrinkproof and anti pilling one-bath finishing, by open width cloth feeding, second dipping and rolling shiinkproof finish liquid, liquid carrying rate 70%~75% surpasses Needle plate on 4%~6% is fed, ten lattice hot winds bake, wherein 140 DEG C of the first~bis- lattice temperature, third~165 DEG C of tetra- lattice temperature, the Five~ten 170~175 DEG C of lattice temperature, the cooling cropping step of two cylinders, speed 30m/min.
The present invention pads oxalic acid after fabric is singed, and to remove the metal ions such as iron on fabric, avoids in pretreatment process Cause fabric damage, it is ensured that grain cross is broken Qiang Li≤280N.Present specification, which makes public for the first time a day wire type fabric segments, to be subtracted Arrange cold-pad-batch preparation, dyeing and shrinkproof and anti pilling one-bath finishing dyeing and finishing production new technology.Pilling performance≤4 of product Grade washes size changing rate -2.5%~+0.5%, and resistance to fastness to wet rubbing≤3-4 grades, product comprehensive performance reaches on high-class product bed Articles quality index.
Specific embodiment
Embodiment 1:
A kind of production method for the day wire type wide cut woven fabric that anti-pilling property is high, the blended fabric rule in 45/ cotton of tencel, 45/ fiber crops/10 Lattice: 106 inches of door, yarn count 28s×28s, density is 90 × 65.Production procedure is stitched including turning over, and → singing → pads oxalic acid → alkaline oxygen bath cold-pad-batch preparation → washing → drying → cold-rolling heap staining → washing → drying is washed → dried to → banking up → → shrinkproof and anti pilling one-bath finishing → calendering → machine shrunk → test package;Pilling performance≤4 grade, the strong power of broadwise fracture≤ 280N, washing size changing rate -2.5%~+0.5%, resistance to fastness to wet rubbing≤3-4 grades.
When padding oxalic acid, 7~8g/L of concentration of oxalic acid, liquid carrying rate 70%~80%.After banking up 2~4h, five cell compartment temperature open washings.
When alkaline oxygen bath cold-pad-batch preparation, alkaline oxygen bath liquid composition are as follows:
(100%) 30~35g/L of NaOH
H2O2(100%) 16~18g/L
It is cold to help clever 25g/L
5~6g/L of waterglass
When cold-pad-batch preparation, pass through open width cloth feeding, second dipping and rolling cold-pad-batch preparation liquid, liquid carrying rate 70%~80%.Bank up 20 ~for 24 hours after, high temperature open washing.
When cold-rolling heap staining, when contaminating the shallow colour of camel's hair, dye liquor composition: Nowe clones red FN -2BL 0.347g/L, Nowe clone Yellow FN -2R 0.202g/L, Nowe clone indigo plant FN-R 0.258g/L;Lye composition: caustic soda 24g/L, low temperature cold dome are solid Color alkali EW-956 26/L;Dyeing are as follows: dye liquor and 4: 1 ratio of lye mix, pick-up rate 65%, speed 60~ 65m/min, stacking at room temperature 16~for 24 hours;Dye aftertreatment technology are as follows: cloth feeding → room temperature pass through reductive steam box → the first and second, Three lattice flowing cool waters wash 80~90 DEG C of → fourth, fifth lattice, add high concentrated low temperature releasing soaping agent 2~3g/L of ANT soap boiling → the 6th lattice 70~80 DEG C of washing the → the seven lattice flowing cool water washing → croppings.
When shrinkproof and anti pilling one-bath finishing, working solution composition are as follows:
Non-aldehyde low-temperature crease and shrink resistant finishing agent KNITTEX FFRC 60g/L
Softener B 60g/L
Fluffy 25 g/L of silicone oil Goon1202
Fibre trimmer FFS 3g/L
When shrinkproof and anti pilling one-bath finishing, by open width cloth feeding, second dipping and rolling shiinkproof finish liquid, liquid carrying rate 70%~75% surpasses Needle plate on 4%~6% is fed, ten lattice hot winds bake, wherein 140 DEG C of the first~bis- lattice temperature, third~165 DEG C of tetra- lattice temperature, the Five~ten 170~175 DEG C of lattice temperature, the cooling cropping step of two cylinders, speed 30m/min.
4 grades of product pilling property, broadwise is broken Qiang Li≤290N, washes size changing rate -2.2%, wet rubbing fastness 4 Grade.
Embodiment 2
A kind of production method for the day wire type wide cut woven fabric that anti-pilling property is high, the blended fabric specification of 55/ cotton of tencel 45/: door 106 inches, yarn count 28s×28s, density is 95 × 70.
Production procedure include turn over stitch → singing → pad oxalic acid → banking up → wash → dry → alkaline oxygen bath cold pad--batch before Processing → washing → drying → cold-rolling heap staining → washing → drying → shrinkproof pre- with anti pilling one-bath finishing → calendering → machinery Contracting → test package;It is characterized in that: pilling performance≤4 grade, the strong power≤280N of broadwise fracture, washing size changing rate -2.5%~+ 0.5%, resistance to fastness to wet rubbing≤3-4 grades.
When padding oxalic acid, 7~8g/L of concentration of oxalic acid, liquid carrying rate 70%~80%.After banking up 2~4h, five cell compartment temperature open washings.
When alkaline oxygen bath cold-pad-batch preparation, alkaline oxygen bath liquid composition are as follows:
(100%) 30~35g/L of NaOH
H2O2(100%) 16~18g/L
It is cold to help clever 25g/L
5~6g/L of waterglass
When cold-pad-batch preparation, pass through open width cloth feeding, second dipping and rolling cold-pad-batch preparation liquid, liquid carrying rate 70%~80%.Bank up 20 ~for 24 hours after, high temperature open washing.
When cold-rolling heap staining, when contaminating grey, dye liquor composition: it is yellow that Nowe clones red FN -2BL 1.560g/L, Nowe clone FN -2R0.605g/L, Nowe clone indigo plant FN-R 2.480g/L;Lye composition: caustic soda 26g/L, low temperature cold dome fixation alkali EW-956 28/L ;Dyeing are as follows: dye liquor and 4: 1 ratio of lye mix, pick-up rate 65%, 60~65m/ of speed Min, stacking at room temperature 16~for 24 hours;Dye aftertreatment technology are as follows: cloth feeding → room temperature passes through reductive steam box → first, second and third lattice Flowing cool water washes 80~90 DEG C of → fourth, fifth lattice, add the lattice of high concentrated low temperature releasing soaping agent 2~3g/L of ANT soap boiling → the 6th 70~ 80 DEG C of washing the → the seven lattice flowing cool water washing → croppings.
When shrinkproof and anti pilling one-bath finishing, working solution composition are as follows:
Non-aldehyde low-temperature crease and shrink resistant finishing agent KNITTEX FFRC 60g/L
Fluffy 25 g/L of silicone oil Goon1202
Hydrophilic silicone oil 5g/L
Fibre trimmer FFS 3g/L
When shrinkproof and anti pilling one-bath finishing, by open width cloth feeding, second dipping and rolling shiinkproof finish liquid, liquid carrying rate 70%~75% surpasses Needle plate on 4%~6% is fed, ten lattice hot winds bake, wherein 140 DEG C of the first~bis- lattice temperature, third~165 DEG C of tetra- lattice temperature, the Five~ten 170~175 DEG C of lattice temperature, the cooling cropping step of two cylinders, speed 30m/min.
4 grades of product pilling property, broadwise is broken Qiang Li≤320N, washes size changing rate -2.0%, wet rubbing fastness 3- 4 grades.

Claims (3)

1. a kind of production method for the day wire type wide cut woven fabric that anti-pilling property is high, it is characterized in that: production procedure includes turning over seam → singing → pads oxalic acid → banking up → and washes → dry → alkaline oxygen bath cold-pad-batch preparation → washing → drying → cold pad--batch Dyeing → washing → drying → shrinkproof and anti pilling one-bath finishing → calendering → machine shrunk → test package;Product pilling property ≤ 4 grades, the strong power≤280N of broadwise fracture, washing size changing rate -2.5%~+0.5%, resistance to fastness to wet rubbing≤3-4 grades;
When padding oxalic acid, 7~8g/L of concentration of oxalic acid, liquid carrying rate 70%~80%;After banking up 2~4h, five cell compartment temperature open washings;
When alkaline oxygen bath cold-pad-batch preparation, alkaline oxygen bath liquid composition are as follows:
30~35g/L of 100%NaOH
100%H2O216~18g/L
It is cold to help clever 25g/L
5~6g/L of waterglass
When cold-pad-batch preparation, pass through open width cloth feeding, second dipping and rolling cold-pad-batch preparation liquid, liquid carrying rate 70%~80%;Bank up 20 ~for 24 hours after, high temperature open washing.
2. a kind of production method of the high day wire type wide cut woven fabric of anti-pilling property according to claim 1, feature Be: when cold-rolling heap staining, when contaminating the shallow colour of camel's hair, dye liquor composition: it is yellow that Nowe clones red FN -2BL 0.347g/L, Nowe clone FN -2R 0.202g/L, Nowe clone indigo plant FN-R 0.258g/L;Lye composition: caustic soda 24g/L, low temperature cold dome fixation alkali EW-956 26/L ;When contaminating grey, dye liquor composition: Nowe clones red FN -2BL 1.560g/L, Nowe clones Huang FN -2R 0.605g/L, Nowe clone indigo plant FN-R 2.480g/L;Lye composition: caustic soda 26g/L, low temperature cold dome fixation alkali EW-956 28/L ;Dyeing are as follows: dye liquor and 4: 1 ratio of lye mix, pick-up rate 65%, 60~65m/min of speed, room temperature Bank up 16~for 24 hours;Dye aftertreatment technology are as follows: cloth feeding → room temperature passes through reductive steam box → first, second and third lattice flowing cool water 80~90 DEG C of → fourth, fifth lattice are washed, high concentrated low temperature releasing soaping agent 2~3g/L of ANT soap boiling → 70~80 DEG C of the 6th lattice washing is added → the seven lattice flowing cool water washing → cropping.
3. a kind of production method of the high day wire type wide cut woven fabric of anti-pilling property according to claim 1, feature It is: when shrinkproof and anti pilling one-bath finishing, working solution composition are as follows:
Non-aldehyde low-temperature crease and shrink resistant finishing agent KNITTEX FFRC 60g/L
Fluffy 25 g/L of silicone oil Goon1202
Hydrophilic silicone oil 5g/L
Fibre trimmer FFS 3g/L
When shrinkproof and anti pilling one-bath finishing, by open width cloth feeding, second dipping and rolling shiinkproof finish liquid, liquid carrying rate 70%~75% surpasses Needle plate on 4%~6% is fed, ten lattice hot winds bake, wherein 140 DEG C of the first~bis- lattice temperature, third~165 DEG C of tetra- lattice temperature, the Five~ten 170~175 DEG C of lattice temperature, the cooling cropping step of two cylinders, speed 30m/min.
CN201910027518.7A 2019-01-11 2019-01-11 The production method of the high day wire type wide cut woven fabric of anti-pilling property Pending CN109750530A (en)