CN109594336A - A kind of preparation method of extinction heat generating and retention functional fabric - Google Patents

A kind of preparation method of extinction heat generating and retention functional fabric Download PDF

Info

Publication number
CN109594336A
CN109594336A CN201811489029.5A CN201811489029A CN109594336A CN 109594336 A CN109594336 A CN 109594336A CN 201811489029 A CN201811489029 A CN 201811489029A CN 109594336 A CN109594336 A CN 109594336A
Authority
CN
China
Prior art keywords
fabric
heat generating
preparation
warp thread
weft yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811489029.5A
Other languages
Chinese (zh)
Inventor
蔡俊杰
詹华
钟增元
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Quanzhou Lianxing Hair Knitting And Weaving Co Ltd
Original Assignee
Quanzhou Lianxing Hair Knitting And Weaving Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Quanzhou Lianxing Hair Knitting And Weaving Co Ltd filed Critical Quanzhou Lianxing Hair Knitting And Weaving Co Ltd
Priority to CN201811489029.5A priority Critical patent/CN109594336A/en
Publication of CN109594336A publication Critical patent/CN109594336A/en
Pending legal-status Critical Current

Abstract

The present invention relates to garment material preparation fields, relate to a kind of preparation method of extinction heat generating and retention functional fabric, the following steps are included: preparing warp thread and weft yarn → dyeing → sizing → weaving → reprocessing, according to heat-preserving function fabric obtained by above-mentioned steps under sunlight irradiation, temperature is 3-5 DEG C high compared with similar fabric, and it can keep the temperature, and other than having the function of extinction heat generating and retention, be also equipped with certain wash resistant, moisture absorption and wrinkle resistance.

Description

A kind of preparation method of extinction heat generating and retention functional fabric
Technical field
The present invention relates to garment material preparation field, specially a kind of preparation method of extinction heat generating and retention functional fabric.
Background technique
Warming is the important indicator of water clothes comfort, traditional heating method be usually the conduction for controlling heat, Heat leakage caused by convection current, radiation, such as use thick fabric, using metal coating fabric or use cotton-wool as filling Material is to play heat insulation effect.However modern people are higher and higher to the comfort, functionality and cosmetic requirements of clothes, tradition Insulation garment, the clothes of especially filling cotton-wool are excessively fluffy, too fat to move, are not only not easy to activity, but also lack aesthetic feeling, and keep the temperature effect Fruit is bad.With the fast development and continuous improvement of people's living standards of science and technology, people are to fabric and the practical function of clothes The requirement of energy tends to diversification, therefore actively extinction heat generating and retention developing material is of great significance.
Summary of the invention
It is of the invention to synthesize, production process simplicity, can be used for greatly for fiber in order to solve the above technical problems, providing one kind A kind of preparation method of extinction heat generating and retention functional fabric of batch production, comprising the following steps:
1) it prepares warp thread and weft yarn, selects the blended yarns of 56%-70% polyester fiber and 30%-44% far IR fibre cellulose fiber to be Warp thread, selecting the blended yarns of 60%-70% polypropylene fibre and 30%-40% polyester doughnut is weft yarn, the branch of the warp thread Number is 65-37s, and twist multiplier 460-500, the weft yarn specification is 50D~300D, and twist multiplier is 350~470；
2) it dyes, the warp thread and weft yarn that prepare is dyed, water is added in dye vat, bath raio 1:15~20 slowly increase Temperature is warming up to 115 DEG C~135 DEG C, keeps the temperature 10~15 minutes, then soaps firm to color, dries on radio frequency dryer；
3) sizing is first original with converted starch, phosphate ester starch, solid acrylic, wax disk(-sc), slurry, foaming agent and detergent Material, is put into water in mixing cirtern, slowly puts into carboxymethyl cellulose, sodium alginate, softening agent, activating agent, shallow lake in defined order Powder distintegrant and preservative, in the environment of temperature is 26-35 °, stirring 25-35min is added with being steam heated to 40-50 DEG C Water adjusts concentration, and adjusts its viscosity and pH value, and the stock tank for transporting to sizing machine through pipeline is spare, and warp thread and weft yarn are added to slurry In yarn machine, sizing is completed；
4) weaving is made into fabric cloth at fabric cloth, warp thread and weft yarn on air-jet loom；
5) it reprocesses, fabric cloth is reprocessed using dyeing and finishing technology, form heat-preserving function fabric.
Preferably, in step 3, the softening agent is one of tallow, suet and cottonseed oil or a variety of, the table Face activating agent is a kind of anionic or nonionic surface active agent, and the starch distintegrant is sodium metasilicate, toluene-sodium-sulfonchloramide and secondary One of sodium chlorate is a variety of, and the preservative is a kind of alpha-Naphthol.
Preferably, in steps of 5, the dyeing and finishing technology refers to the pigment that removal heat-preserving function fabric is floated using chlorine.
Preferably, in steps of 5, the dyeing and finishing technology refers to is had by surface of revolution for cutting using raising treatment process The villus of the idler wheel removal heat-preserving function web surface of the needle knife of disconnected surface fiber of the fabric, makes the bright and clean softness of heat-preserving function fabric.
Preferably, in steps of 5, the dyeing and finishing technology refers to the moisture pick-up properties for increasing heat-preserving function fabric terylene using alkali.
Preferably, in steps of 5, the dyeing and finishing technology, which refers to, increases heat-preserving function fabric gloss and softness by liquid ammonia finishing Property；Keep heat-preserving function web surface gloss beautiful using noniron finish.
By using above-mentioned technical solution, the beneficial effects of the present invention are: fabric prepares yarn used by far infrared Fiber and polyester filament are entwined, and have the good far infrared function of far infrared fiber and anti-static function, can be effective Storage temperature it is warming, promote blood circulation, the strengths and weaknesses of two kinds of fibers obtains complementation, while ensuring quality, and substantially reduces Production cost, obtained extinction heat generating and retention functional fabric generate heat under light illumination, and existing especially under sunlight irradiation The fabric of technology is 3-5 DEG C high compared to temperature, and can keep the temperature, and be also equipped with certain wash resistant, moisture absorption and wrinkle resistance.
Specific embodiment
The present invention will be further described in detail with reference to the specific embodiments:
A kind of preparation method of extinction heat generating and retention functional fabric, comprising the following steps:
1) warp thread and weft yarn are prepared, selecting the blended yarns of 60% polyester fiber and 40% far IR fibre cellulose fiber is warp thread, choosing Blended yarns with 65% polypropylene fibre and 35% polyester doughnut are weft yarn, and the number of the warp thread is 60s, twist multiplier It is 500, the weft yarn specification is 200D, twist multiplier 400；
2) it dyeing, the warp thread and weft yarn that prepare is dyed, water is added in dye vat, bath raio 1:18 slowly increases temperature, 120 DEG C are warming up to, keeps the temperature 15 minutes, then soaps firm to color, is dried on radio frequency dryer；
3) sizing is first original with converted starch, phosphate ester starch, solid acrylic, wax disk(-sc), slurry, foaming agent and detergent Material, is put into water in mixing cirtern, slowly puts into carboxymethyl cellulose, sodium alginate, softening agent, activating agent, shallow lake in defined order Powder distintegrant and preservative stir 30min in the environment of temperature is 30 °, with being steam heated to 45 DEG C, add water adjustment dense Degree, and its viscosity and pH value are adjusted, the stock tank for transporting to sizing machine through pipeline is spare, warp thread and weft yarn is added into sizing machine, Complete sizing；
4) weaving is made into fabric cloth at fabric cloth, warp thread and weft yarn on air-jet loom；
5) it reprocesses, fabric cloth is reprocessed using dyeing and finishing technology, form heat-preserving function fabric.
Preferably, in step 3, the softening agent is one of tallow, suet and cottonseed oil or a variety of, the table Face activating agent is a kind of anionic or nonionic surface active agent, and the starch distintegrant is sodium metasilicate, toluene-sodium-sulfonchloramide and secondary One of sodium chlorate is a variety of, and the preservative is a kind of alpha-Naphthol.
Preferably, in steps of 5, the dyeing and finishing technology refers to the pigment that removal heat-preserving function fabric is floated using chlorine.
Preferably, in steps of 5, the dyeing and finishing technology refers to is had by surface of revolution for cutting using raising treatment process The villus of the idler wheel removal heat-preserving function web surface of the needle knife of disconnected surface fiber of the fabric, makes the bright and clean softness of heat-preserving function fabric.
Preferably, in steps of 5, the dyeing and finishing technology refers to the moisture pick-up properties for increasing heat-preserving function fabric terylene using alkali.
Preferably, in steps of 5, the dyeing and finishing technology, which refers to, increases heat-preserving function fabric gloss and softness by liquid ammonia finishing Property；Keep heat-preserving function web surface gloss beautiful using noniron finish.
The present invention has been described in detail through specific embodiments, but these are not constituted to limit of the invention System.Without departing from the principles of the present invention, those skilled in the art can also make many modification and improvement, these are also answered It is considered as protection scope of the present invention.

Claims (6)

1. a kind of preparation method of extinction heat generating and retention functional fabric, it is characterised in that: it successively includes the following steps；
1) it prepares warp thread and weft yarn, selects the blended yarns of 56%-70% polyester fiber and 30%-44% far IR fibre cellulose fiber to be Warp thread, selecting the blended yarns of 60%-70% polypropylene fibre and 30%-40% polyester doughnut is weft yarn, the branch of the warp thread Number is 65-37s, and twist multiplier 460-500, the weft yarn specification is 50D~300D, and twist multiplier is 350~470；
2) it dyes, the warp thread and weft yarn that prepare is dyed, water is added in dye vat, bath raio 1:15~20 slowly increase Temperature is warming up to 115 DEG C~135 DEG C, keeps the temperature 10~15 minutes, then soaps firm to color, dries on radio frequency dryer；
3) sizing is first original with converted starch, phosphate ester starch, solid acrylic, wax disk(-sc), slurry, foaming agent and detergent Material, is put into water in mixing cirtern, slowly puts into carboxymethyl cellulose, sodium alginate, softening agent, activating agent, shallow lake in defined order Powder distintegrant and preservative, in the environment of temperature is 26-35 °, stirring 25-35min is added with being steam heated to 40-50 DEG C Water adjusts concentration, and adjusts its viscosity and pH value, and the stock tank for transporting to sizing machine through pipeline is spare, and warp thread and weft yarn are added to slurry In yarn machine, sizing is completed；
4) weaving is made into fabric cloth at fabric cloth, warp thread and weft yarn on air-jet loom；
5) it reprocesses, fabric cloth is reprocessed using dyeing and finishing technology, form heat-preserving function fabric.
2. a kind of preparation method of extinction heat generating and retention functional fabric as described in claim 1, it is characterised in that: in step In 3, the softening agent is one of tallow, suet and cottonseed oil or a variety of, and the surfactant is a kind of anion Type or nonionic surface active agent, the starch distintegrant are one of sodium metasilicate, toluene-sodium-sulfonchloramide and sodium hypochlorite or more Kind, the preservative is a kind of alpha-Naphthol.
3. a kind of preparation method of extinction heat generating and retention functional fabric as described in claim 1, it is characterised in that: in step In 5, the dyeing and finishing technology refers to the pigment that removal heat-preserving function fabric is floated using chlorine.
4. a kind of preparation method of extinction heat generating and retention functional fabric as described in claim 1, it is characterised in that: in step In 5, the dyeing and finishing technology refers to using raising treatment process through surface of revolution with the needle knife for cutting off surface fiber of the fabric Idler wheel removal heat-preserving function web surface villus, make the bright and clean softness of heat-preserving function fabric.
5. a kind of preparation method of extinction heat generating and retention functional fabric as described in claim 1, it is characterised in that: in step In 5, the dyeing and finishing technology refers to the moisture pick-up properties for increasing heat-preserving function fabric terylene using alkali.
6. a kind of preparation method of extinction heat generating and retention functional fabric as described in claim 1, it is characterised in that: in step In 5, the dyeing and finishing technology, which refers to, increases heat-preserving function fabric gloss and flexibility by liquid ammonia finishing；Make to keep warm using noniron finish Functional fabric lustrous surface is beautiful.
CN201811489029.5A 2018-12-06 2018-12-06 A kind of preparation method of extinction heat generating and retention functional fabric Pending CN109594336A (en)