CN108660793A - A kind of processing method of the high-elastic flannelette of cloud - Google Patents
A kind of processing method of the high-elastic flannelette of cloud Download PDFInfo
- Publication number
- CN108660793A CN108660793A CN201810492632.2A CN201810492632A CN108660793A CN 108660793 A CN108660793 A CN 108660793A CN 201810492632 A CN201810492632 A CN 201810492632A CN 108660793 A CN108660793 A CN 108660793A
- Authority
- CN
- China
- Prior art keywords
- flannelette
- elastic
- processing method
- drying
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing method of the high-elastic flannelette of cloud, including following processing method, S1, raw material preparations, and carry out pre-treatment to processing flannelette；S2 adequately dyes flannelette；S3 carries out drying and processing to the flannelette after dyeing；S4 makes and reinforces elastic sols, and by solution spraying to flannelette appearance, reinforces elasticity；Flannelette after immersion is carried out raising, and is fully combed by S5；Flannelette after raising is sent into forming machine and carried out shaping, carries out carry out product inspection, clot, packaging after the completion by S6.The flannelette that the present invention produces is not only soft and thick and solid, it is ventilative and warming, and effect of creasing is good, with the splendid conformal effect of rivel, there is good fabric form, structural stability, be easy to smooth, while soft, bright in color, it is by force and ideal elastic with three-dimensional sense, and overall processing is of low cost, and production process is simple, suitable for batch machining.
Description
Technical field
The present invention relates to technical field of textile processing, the processing method of especially a kind of high-elastic flannelette of cloud.
Background technology
Flannelette refers to is presented plump villous cotton fabric by napping rear surface, is pricked by the pin hole done on the surface of cloth
Suede technique generates more villus, and three-dimensional sense is strong, and glossiness is high, touches up soft thick and solid.Velveteen is the high relatively low suede of hair
Cloth also has for flannelette and does Clean- cleaning suede, and hair height is higher, and woven, knitting has, and is also divided into high and low shift.Flannelette
It is divided to two kinds of single-side pile and double-sided plush.Single-side pile tissue is based on twill, also referred to as serge；Double-sided plush is based on plain weave.Flannelette cloth
Body is soft, and dress is fit comfortable, and warmth retention property is good, preferably makees winter underwear, nightwear.Tulle baran, color knit grid flannelette and are fit to do woman
Female, children's spring and autumn coat.Be printed on animal, flowers, children's stories image style flannelette be also known as bud bud suede, be suitble to children use.This
Color suede, bleaching suede, assorted color suede, jasper flannelette are typically used as winter clothes, gloves, shoes and hats underedge etc..The raising of flannelette is to lean on napping
The multiple repeated action of machine steel wire needle point, pull-up is a part of fibroplastic on fabric cloth cover, and villus requires short, close, even.Print
Flower flannelette napping before stamp, bleaching is with variegated flannelette then in last napping.Warp thread is preferably thin used in the fabric of flannelette；Weft yarn
Suitable thick and twist will be lacked.The cotton fiber for spinning weft yarn is preferably thick, and has preferable regularity.For fabric through close smaller, filling density is larger,
So that weft yarn emerges in surface, is conducive to weft yarn cotton fiber and forms plentiful and uniform villus.Flannelette is after napping, broadwise
Strength loss is larger, therefore grasp cotton yarn quality and napping process operation are particularly significant.
However after traditional flannelette is processed, elasticity is poor, and the fabrics product produced is easy out due to elastic problem
Phenomenon is now torn, problems above just needs to be improved traditional technique, herein it is proposed that a kind of cloud is high-elastic
The processing method of flannelette.
Invention content
The present invention is to solve above-mentioned phenomenon, using the technical solution of following modification, a kind of processing side of the high-elastic flannelette of cloud
Method, including following processing method, S1, raw material preparation, and pre-treatment is carried out to processing flannelette；
S2 adequately dyes flannelette；
S3 carries out drying and processing to the flannelette after dyeing；
S4 makes and reinforces elastic sols, and by solution spraying to flannelette appearance, reinforces elasticity；
Flannelette after immersion is carried out raising, and is fully combed by S5；
Flannelette after raising is sent into forming machine and carried out shaping, carries out carry out product inspection, clot, packet after the completion by S6
Dress.
As present invention further optimization mode, in step S1, including raw material is bleached, compound concentration 45-
67% sodium hypochlorite is adequately impregnated raw material, and the temperature of immersion is controlled at 55-75 DEG C, and time control is in 5-
15min。
As present invention further optimization mode, in step S2, dyeing is as follows, it is necessary first to go oil processing, add
After degreaser is warmed to 75 DEG C, start to heat into clear water again after bleeding off sewage, opening steam valve is warmed to 95 DEG C and starts into dye
Material selects disperse red and disperse blue this amount kind environmental protection type dye, and levelling agent, weak carbonic acid is added, and is warmed to 110 DEG C of heat preservations 45
Minute, it is then shut off evaporator valve and starts to cool down into cold water, 0.5-1.5% sodium hydroxides are added after cooling to 25 DEG C of room temperature or less
It it is warmed to 75 DEG C again adds and handled into 0.3-0.8% glacial acetic acid tune, after carrying out reduction treatment, fabric goes out after putting clean and dirt water
Cylinder enters postchannel process.
As present invention further optimization mode, in step S3, drying carries out cold wind drying first, utilizes air-cooler
Then drying, drying time control bit 20-45min carry out hot-air seasoning again, drying time control is 0.8-1.2h, whole mistake
Cheng Qian's phase soon dry after dry slowly, last natural cooling, ensure shape raw material it is soft, can be carried out after drying it is whole scald, flatiron is set
Standby gait of march adjustment control is 10-30m/min, is pressed comprehensively back and forth back and forth, ironing equipment Weight control is in 0.2-
1.8kg, ironing temperature control are 85-105 DEG C.
As present invention further optimization mode, in step S4, by polyurethane resin, villus elasticity powder, antistatic agent
It is added to mould inhibitor in common blender, mixing time 10-20min, speed of agitator 180-260r/min, by wash resistant
Agent, crosslinking agent and toluene are added in common blender, mixing time 30min, 100~120r/min of speed of agitator, are made
Mixed solution；Masking liquid is sprayed on flannelette napped fabric layer by flush coater, quantity for spray is in 50-80g/m2。
As present invention further optimization mode, in step S6, need to carry out the end of a thread processing, extra the end of a thread to flannelette
It is cut, then carries out sterilizing using ultraviolet disinfection lamp, control sterilisation temp continues 5-12min at 60-85 DEG C.
The flannelette that patent of the present invention is produced is not only soft and thick and solid, ventilative and warming, and effect of creasing is good, has pole
The conformal effect of good rivel has good fabric form, structural stability, is easy to smooth, while soft, color and luster light
It is bright, have three-dimensional sense by force and ideal elasticity, and overall processing is of low cost, production process is simple, and product is not allowed to be also easy to produce
Crackle maintains the original fine air permeability of flannelette, suitable for batch machining.
Specific implementation mode
Below in conjunction in the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
The present invention provides a kind of technical solution：A kind of processing method of the high-elastic flannelette of cloud, including following processing method,
S1, raw material preparation, and pre-treatment is carried out to processing flannelette；
S2 adequately dyes flannelette；
S3 carries out drying and processing to the flannelette after dyeing；
S4 makes and reinforces elastic sols, and by solution spraying to flannelette appearance, reinforces elasticity；
Flannelette after immersion is carried out raising, and is fully combed by S5；
Flannelette after raising is sent into forming machine and carried out shaping, carries out carry out product inspection, clot, packet after the completion by S6
Dress.
In step S1, including raw material is bleached, compound concentration is the sodium hypochlorite of 45-67%, and raw material is filled
The temperature of the immersion divided, immersion is controlled at 55-75 DEG C, and time control is in 5-15min.
In step S2, dyeing is as follows, it is necessary first to go oil processing, after adding degreaser to be warmed to 75 DEG C, bleed off sewage
Start to heat into clear water again afterwards, open steam valve and be warmed to 95 DEG C and start into dyestuff, selects disperse red and disperse blue this amount kind ring
Type dye is protected, and levelling agent, weak carbonic acid is added, 110 DEG C is warmed to and keeps the temperature 45 minutes, be then shut off evaporator valve and start into cold water
Cooling, cools to addition 0.5-1.5% sodium hydroxides after 25 DEG C of room temperature or less and is warmed to 75 DEG C again and add into 0.3-0.8%
Glacial acetic acid tune is handled, and after carrying out reduction treatment, is put fabric after clean and dirt water and is gone out cylinder and enter postchannel process.
In step S3, drying carries out cold wind drying first, is dried using air-cooler, drying time control bit 20-45min,
Then hot-air seasoning is carried out again, and drying time control is 0.8-1.2h, and overall process dries slowly after drying soon early period, last naturally cold
But, ensure the soft of shape raw material, can be carried out after drying it is whole scald, be 10- by the adjustment control of the gait of march of ironing equipment
30m/min is pressed comprehensively back and forth back and forth, and ironing equipment Weight control is 85- in 0.2-1.8kg, ironing temperature control
105℃。
In step S4, polyurethane resin, villus elasticity powder, antistatic agent and mould inhibitor are added to common blender
In, wash resistant agent, crosslinking agent and toluene are added to common by mixing time 10-20min, speed of agitator 180-260r/min
In blender, mixed solution is made in mixing time 30min, 100~120r/min of speed of agitator；Masking liquid is sprayed by flush coater
It is coated on flannelette napped fabric layer, quantity for spray is in 50-80g/m2。
It in step S6, needs to carry out the end of a thread processing to flannelette, extra the end of a thread is cut, and disinfection by ultraviolet light is then utilized
Lamp carries out sterilizing, and control sterilisation temp continues 5-12min at 60-85 DEG C.
To sum up, the flannelette that patent of the present invention is produced is not only soft and thick and solid, ventilative and warming, and effect of creasing is good, tool
There is the conformal effect of splendid rivel, there is good fabric form, structural stability, be easy to smooth, while soft, color
It is damp bright, have three-dimensional sense by force and ideal elasticity, and overall processing is of low cost, production process is simple, and product is not easy
It cracks, maintains the original fine air permeability of flannelette, suitable for batch machining.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field
For technical staff, it is clear that invention is not limited to the details of the above exemplary embodiments, and in the spirit without departing substantially from the present invention
Or in the case of essential characteristic, the present invention can be realized in other specific forms.It therefore, in all respects, should all
Regard embodiment as exemplary, and be non-limiting, the scope of the present invention is above-mentioned by appended claims
Illustrate to limit, it is intended that including all changes that come within the meaning and range of equivalency of the claims in this hair
In bright.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only
It contains an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art answer
When considering the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms people in the art
The other embodiment that member is appreciated that.
Claims (6)
1. a kind of processing method of the high-elastic flannelette of cloud, it is characterised in that：Including following processing method, S1, raw material preparation, and it is right
It processes flannelette and carries out pre-treatment；
S2 adequately dyes flannelette；
S3 carries out drying and processing to the flannelette after dyeing；
S4 makes and reinforces elastic sols, and by solution spraying to flannelette appearance, reinforces elasticity；
Flannelette after immersion is carried out raising, and is fully combed by S5；
Flannelette after raising is sent into forming machine and carried out shaping, carries out carry out product inspection, clot, packaging after the completion by S6.
2. a kind of processing method of the high-elastic flannelette of cloud according to claim 1, which is characterized in that in step S1, including
Raw material is bleached, compound concentration is the sodium hypochlorite of 45-67%, raw material is adequately impregnated, the temperature control of immersion
System is at 55-75 DEG C, and time control is in 5-15min.
3. a kind of processing method of the high-elastic flannelette of cloud according to claim 1, which is characterized in that in step S2, dyeing
Technique is as follows, it is necessary first to go oil processing, after adding degreaser to be warmed to 75 DEG C, start to heat into clear water again after bleeding off sewage, beat
Open steam valve and be warmed to 95 DEG C and start into dyestuff, select disperse red and disperse blue this amount kind environmental protection type dye, and be added levelling agent,
Weak carbonic acid is warmed to 110 DEG C and keeps the temperature 45 minutes, is then shut off evaporator valve and starts to cool down into cold water, cool to 25 DEG C of room temperature or less
It 0.5-1.5% sodium hydroxides are added afterwards are warmed to 75 DEG C again and add and handled into 0.3-0.8% glacial acetic acid tune, carry out also original place
After reason, puts fabric after clean and dirt water and go out cylinder and enter postchannel process.
4. a kind of processing method of the high-elastic flannelette of cloud according to claim 1, which is characterized in that in step S3, drying
Cold wind drying is carried out first, is dried using air-cooler, and then drying time control bit 20-45min carries out hot-air seasoning again, dry
Dry time control is 0.8-1.2h, and overall process dries slowly after drying soon early period, and last natural cooling ensures the soft of shape raw material,
Can be carried out after drying it is whole scald, be 10-30m/min by the adjustment control of the gait of march of ironing equipment, back and forth it is round-trip carry out it is comprehensive
Flatiron, ironing equipment Weight control are 85-105 DEG C in 0.2-1.8kg, ironing temperature control.
5. a kind of processing method of the high-elastic flannelette of cloud according to claim 1, which is characterized in that in step S4, will gather
Urethane resin, villus elasticity powder, antistatic agent and mould inhibitor are added in common blender, and mixing time 10-20min is stirred
Wash resistant agent, crosslinking agent and toluene are added in common blender by mix rotating speed 180-260r/min, mixing time 30min,
Mixed solution is made in 100~120r/min of speed of agitator；Masking liquid is sprayed on flannelette napped fabric layer by flush coater, quantity for spray is in 50-
80g/m2。
6. a kind of processing method of the high-elastic flannelette of cloud according to claim 1, which is characterized in that in step S6, need
The end of a thread processing is carried out to flannelette, extra the end of a thread is cut, and then carries out sterilizing, control disinfection using ultraviolet disinfection lamp
Temperature continues 5-12min at 60-85 DEG C.