CN105595703A - Production technology of coral fleece blanket - Google Patents

Abstract

The invention discloses a production technology of a coral fleece blanket. The production technology comprises the steps of weaving, slitting, high temperature setting, alkali deweighting treatment, boiling-off and bleaching, dyeing, aging, washing and drying and after finishing. The coral fleece blanket is low in mass, soft in sense of touch and convenient to carry and use next to the skin.

Description

A kind of production technology of coral blanket

Technical field

The present invention relates to a kind of production technology of coral blanket.

Background technology

Along with the raising that people require sleep comfort level, also more and more higher to the requirement of bed necessaries, traditional cotton productsThrough meeting people's requirement, its texture is hard, surface roughness is high, and the application of coral chenille article in bed necessaries more and moreExtensively, its quality softness, skin-friendly is good, and has good warmth retention property. But the woven coral chenille article of high density is still inclined to one sideHeavy, and can affect surface touch after dyed. How to develop feel better, the lighter more warming bed necessaries of quality become nowResearch direction.

Summary of the invention

The object of the present invention is to provide a kind of production technology of coral blanket, adopt the coral suede system of this explained hereafterProduct quality is light, feel is more soft, and thermal property is good, and pattern is bright-coloured, and color fastness is high.

To achieve these goals, technical scheme of the present invention is:

A production technology for coral blanket, comprises the steps:

1) weave: adopt 100D/48F half delustring dacron thread as end silk, weave with double-needle bed raschel tricot machine;

2) cut open width: employing is cutd open width machine and cutd open width;

3) high-temperature shaping: before sizing, grey cloth is tested, remove faulty materials; 1-shapes at the temperature of 180-220 DEG C2min, in sizing, overfeeding is made as 4%;

4) alkali decrement treatment: adopt the NaOH of 3-5% to carry out alkali decrement treatment at 80-100 DEG C, the processing time is 1.5-2h, and add auxiliary agent, this auxiliary agent is dodecyl benzyl dimethyl ammonium chloride, concentration is 0.8-1.1g/L;

5) kiering bleaching: adopt hydrogen peroxide to carry out kiering bleaching to the coral suede grey cloth through alkali decrement treatment;

6) dyeing: the coral suede grey cloth after adopting the active method of printing and dyeing to bleaching carries out pattern-printing and dyeing;

7) evaporate: at 110-130 DEG C, carry out high temperature and evaporate, the time is 15-20min;

8) washing is dried: carry out soaping for 2 times and 2 washings, then at 120 DEG C, dry 10min, then at 60-80 DEG CFinish-drying;

9) after, arrange: comprise that softening agent and antistatic additive carry out rear arrangement to coral blanket; This softening agent main component is carboxylicBase modified silicon oil.

Advantage of the present invention and beneficial effect are:

1) end silk adopts the dacron thread of 100D/48F can improve the density of coral pile fabric, strengthens its warmth retention property;

2) adopt after alkali decrement treatment, fiber is subject to damage to a certain extent, can make polyster fibre minimizing, makes coral suede systemProduct weight saving, between fiber molecule, hole increases, and has improved gas permeability and the pliability of woollen blanket;

3) adopt the active method of printing and dyeing to carry out pattern-printing and dyeing, and carry out high temperature and evaporate, can make dye molecule and fiber molecule betterIn conjunction with, improve color fastness;

4) soap and softening agent after arrange and can further improve the pliability of coral blanket, realize the super soft of coral blanketSoft, pro-skin more, sense of touch is better.

Detailed description of the invention

Below in conjunction with embodiment, the specific embodiment of the present invention is further described. Following examples are only for moreAdd technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.

The concrete technical scheme of implementing of the present invention is:

A production technology for coral blanket, comprises the steps:

1) weave: adopt 100D/48F half delustring dacron thread as end silk, weave with double-needle bed raschel tricot machine;

2) cut open width: employing is cutd open width machine and cutd open width;

3) high-temperature shaping: before sizing, grey cloth is tested, remove faulty materials; At the temperature of 180-220 DEG C, shape1.5min, in sizing, overfeeding is made as 4%;

4) alkali decrement treatment: adopt 5% NaOH to carry out alkali decrement treatment at 80-100 DEG C, the processing time is 2h, and addsEnter auxiliary agent, this auxiliary agent is dodecyl benzyl dimethyl ammonium chloride, and concentration is 1.0g/L;

5) kiering bleaching: adopt hydrogen peroxide to carry out kiering bleaching to the coral suede grey cloth through alkali decrement treatment;

6) dyeing: the coral suede grey cloth after adopting the active method of printing and dyeing to bleaching carries out pattern-printing and dyeing;

7) evaporate: at 110-130 DEG C, carry out high temperature and evaporate, the time is 18min;

8) washing is dried: carry out soaping for 2 times and 2 washings, then at 120 DEG C, dry 10min, then at 60-80 DEG CFinish-drying;

9) after, arrange: comprise that softening agent and antistatic additive carry out rear arrangement to coral blanket; This softening agent main component is carboxylicBase modified silicon oil.

The above is only the preferred embodiment of the present invention, it should be pointed out that the ordinary skill people for the artMember, not departing under the prerequisite of the technology of the present invention principle, can also make some improvements and modifications, these improvements and modificationsAlso should be considered as protection scope of the present invention.

Claims (1)

1. a production technology for coral blanket, is characterized in that, comprises the steps:

1) weave: adopt 100D/48F half delustring dacron thread as end silk, weave with double-needle bed raschel tricot machine;

2) cut open width: employing is cutd open width machine and cutd open width;

3) high-temperature shaping: before sizing, described grey cloth is tested, remove faulty materials; Fixed at the temperature of 180-220 DEG CType 1-2min, in sizing, overfeeding is made as 4%;

4) alkali decrement treatment: adopt the NaOH of 3-5% to carry out alkali decrement treatment at 80-100 DEG C, the processing time is 1.5-2h, and add auxiliary agent, described auxiliary agent is dodecyl benzyl dimethyl ammonium chloride, concentration is 0.8-1.1g/L;

5) kiering bleaching: adopt hydrogen peroxide to carry out kiering bleaching to the described coral suede grey cloth through alkali decrement treatmentProcess;

6) dyeing: adopt the active method of printing and dyeing to carry out pattern-printing and dyeing to described coral suede grey cloth;

7) evaporate: at 110-130 DEG C, carry out high temperature and evaporate, the time is 15-20min;

8) washing is dried: carry out soaping for 2 times and 2 washings, then at 120 DEG C, dry 10min, then at 60-80 DEG CFinish-drying;

9) after, arrange: comprise that softening agent and antistatic additive carry out rear arrangement to described coral blanket; Described softening agent masterWanting composition is Carboxyl Modified Polydimethylsiloxane.