CN109487587A - A kind of preparation method of the ventilative uvioresistant fabrics of light weight - Google Patents
A kind of preparation method of the ventilative uvioresistant fabrics of light weight Download PDFInfo
- Publication number
- CN109487587A CN109487587A CN201811263177.5A CN201811263177A CN109487587A CN 109487587 A CN109487587 A CN 109487587A CN 201811263177 A CN201811263177 A CN 201811263177A CN 109487587 A CN109487587 A CN 109487587A
- Authority
- CN
- China
- Prior art keywords
- uvioresistant
- fabric
- light weight
- yarn
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of the ventilative uvioresistant fabrics of light weight, comprising the following steps: (1) base fabric makes: being weaved using 20D polyamide fibre fine dinier yarn;(2) warping, sizing and axis are carried out to yarn to handle, then it is weaved;(3) uvioresistant auxiliary agent is configured to the uvioresistant solution that concentration is 3-5 grams per liter, dyeing, again fixation, reduction cleaning in uvioresistant solution will be dipped in after the embryo cloth desizing being made into through step (2), then by fabric drying and shaping, uvioresistant fabrics are made.The present invention is by being added ultraviolet-resistant aid in dyeing course, and the fine-denier fabric grammes per square metre is still in 35-40 g/m2, the good permeability of fabric, uvioresistant protecting factor>=40, ultraviolet ray transmissivity<5%, with preferable anti-ultraviolet function.
Description
Technical field
The present invention relates to a kind of preparation method of fabric more particularly to a kind of preparation sides of the ventilative uvioresistant fabrics of light weight
Method.
Background technique
With the development of industry, the ozone layer in atmosphere is destroyed, and ultraviolet irradiation amount increases, and ultraviolet light is long to human body
Phase irradiation can bring various different degrees of injuries, accelerate the obscure aging of skin and carcinogenic etc., more and more consumers requirement
Fabric has good function of shielding ultraviolet radiation.
A pulvis is added in precursor usually to stop ultraviolet light to enter in existing uvioresistant fabrics, but this kind of
The general denser of fabric and thick and heavy that goes out of yarn production;Another kind is to coat a coating after dyeing in fabric, to reach
To anti-ultraviolet purpose, but the general poor air permeability of such fabric.
Uvioresistant fabrics are daily more at present, and production technology is relatively complete.But it mainly there is problems:
(1) UPF value how is improved, UVA how is reduced, improves fabric UVResistant effect, and guarantee fabric feasibility;
(2) how to guarantee product UVResistant effect permanence (water-fastness, photostability, ironing etc.);
(3) uvioresistant fabric mainly uses high and fine filament nylon fabric, how when not damaging fabric itself to make it again
Reach UVResistant effect, while making fabric hand feel comfortable and easy to wear.
Summary of the invention
In order to solve the above technical problems, the present invention provides a kind of preparation method of ventilative uvioresistant fabrics of light weight, resist
Ultraviolet effect is good, fabric is comfortable.
The technical solution adopted by the present invention:
A kind of preparation method of the ventilative uvioresistant fabrics of light weight, comprising the following steps:
(1) base fabric makes: being weaved using 20D polyamide fibre fine dinier yarn;
(2) warping, sizing and axis are carried out to yarn to handle, then it is weaved;
(3) uvioresistant auxiliary agent is configured to the uvioresistant solution that concentration is 3-5 grams per liter, will be made into through step (2)
It is dipped in dyeing, again fixation, reduction cleaning in uvioresistant solution after embryo cloth desizing, then by fabric drying and shaping, uvioresistant is made
Line fabric.
In the titanium dioxide of 20D polyamide fibre fine dinier yarn spinning phase addition mass fraction 1.5-1.8%, Density is
The plain cloth of 400-420T, fabric is in 35-40 g/m2。
Dyeing: dye bath bath raio 1:9-11 controls dye bath pH value 4.8-5.2, and at 40 DEG C, acid level dyeing is added
Agent 1.1-1.3 g/l, glacial acetic acid 1.3-1.8 g/l of mass fraction 50%, acid dyes 20-30g/l, anti-uv finishing
Agent 4-6 g/l.
In dyeing course, according to 1.2 DEG C/min of heating rate, 70 DEG C are warming up to, 20 minutes is kept the temperature, heats up again, is heated up
0.8 DEG C/min of speed is warming up to 98 DEG C, keeps the temperature 50 minutes, cools down by 0.8 DEG C/min of cooling rate, is cooled to 70 DEG C, drops again
Temperature, 1.2 DEG C/min of cooling rate.
Color fixing process: fixation formula, fixation formula: acidic color fixing agent DM-2539G 3-5 % are added at 40 DEG C
(o.w.f.), glacial acetic acid 0.4-0.6g/l, control PH are 4-5.In laking process, by 1.2 DEG C/min of heating rate, 40 DEG C
80 DEG C are warming up to, keeps the temperature 30 minutes, then is cooled down by 1.5 DEG C/min of cooling rate.
Reduction cleaning technique: at 40 DEG C, reduction cleaning auxiliary agent is added, reduction cleaning auxiliary agent formula is as follows:
NaOH:1-3g/l;
Reducing agent: 1-3 g/l;
Scouring agent: 0.3-0.8 g/l;
Softening agent: 1-1.5 g/l;
Defoaming agent: 0.8-1.2 g/l;
In reduction clearing step, by 0.8 DEG C/min of heating rate, 40 DEG C are warming up to 70 DEG C, and heat preservation is cleaned 20 minutes, then by drop
Warm 2 DEG C/min of speed cooling.
At 160-180 DEG C of setting temperature, speed is to carry out stentering forming between 35-45m/min.
Compared with prior art, beneficial effects of the present invention: the present invention, should by the way that ultraviolet-resistant aid is added in dyeing course
Fine-denier fabric grammes per square metre is still in 35-40 g/m2, the good permeability of fabric, uvioresistant protecting factor >=40, ultraviolet ray transmissivity
< 5%, there is preferable anti-ultraviolet function.
Specific embodiment
In order to deepen the understanding of the present invention, it is described in detail, is retouched in this specification With reference to embodiment
It states that the examples are only for explaining the invention, is not used to limit the present invention.
Embodiment 1
A kind of preparation method of the ventilative uvioresistant fabrics of light weight of the invention, comprising the following steps:
(1) base fabric makes: being weaved using 20D polyamide fibre fine dinier yarn;
(2) warping, sizing and axis are carried out to yarn to handle, then it is weaved;
(3) uvioresistant auxiliary agent is configured to the uvioresistant solution that concentration is 3 grams per liters, the embryo that will be made into through step (2)
It is dipped in dyeing, again fixation, reduction cleaning in uvioresistant solution after cloth desizing, then by fabric drying and shaping, uvioresistant is made
Fabric.
In order to reach fabric light weight and have certain UVResistant effect, quality is added in 20D polyamide fibre fine dinier yarn spinning phase
The titanium dioxide of score 1.5%, Density are the plain cloth of 400T, and fabric is in 35g/m2, there is certain uvioresistant function
Energy;
Dyeing:
At dye bath bath raio 1:9, dye bath pH value 4.8 is controlled, 1.1 g/l of acid levelling agent, quality point are added at 40 DEG C
Glacial acetic acid 1.3g/l, acid dyes 20g/l, the anti-ultraviolet finishing agent 4g/l of number 50%, according to 1.2 DEG C/min of heating rate,
70 DEG C are warming up to, 20 minutes is kept the temperature, heats up again, 0.8 DEG C/min of heating rate is warming up to 98 DEG C, 50 minutes is kept the temperature, by cooling
0.8 DEG C/min of speed cooling, is cooled to 70 DEG C, cools down again, 1.2 DEG C/min of cooling rate.
Color fixing process:
Fixation formula, fixation formula: 3 % of acidic color fixing agent DM-2539G (o.w.f.), glacial acetic acid are added at 40 DEG C
0.4g/l, control PH is 4,1.2 DEG C/min of heating rate, is warming up to 80 DEG C, keeps the temperature 30 minutes, then by 1.5 DEG C of cooling rate/
Min cooling.
Reduction cleaning technique:
At 40 DEG C, reduction cleaning auxiliary agent is added, reduction cleaning auxiliary agent formula is as follows:
NaOH:1g/l;
Reducing agent: 1g/l;
Scouring agent: 0.3g/l;
Softening agent: 1g/l;
Defoaming agent: 0.8g/l;
By 0.8 DEG C/min of heating rate, 70 DEG C are warming up to, heat preservation is cleaned 20 minutes, then is cooled down by 2 DEG C/min of cooling rate.
Setting process:
At 160 DEG C of setting temperature, speed is stentering forming to be carried out, using 4 positive overfeedings between 35m/min.
Embodiment 2
A kind of preparation method of the ventilative uvioresistant fabrics of light weight of the invention, comprising the following steps:
(1) base fabric makes: being weaved using 20D polyamide fibre fine dinier yarn;
(2) warping, sizing and axis are carried out to yarn to handle, then it is weaved;
(3) uvioresistant auxiliary agent is configured to the uvioresistant solution that concentration is 4 grams per liters, the embryo that will be made into through step (2)
It is dipped in dyeing, again fixation, reduction cleaning in uvioresistant solution after cloth desizing, then by fabric drying and shaping, uvioresistant is made
Fabric.
In order to reach fabric light weight and have certain UVResistant effect, quality is added in 20D polyamide fibre fine dinier yarn spinning phase
The titanium dioxide of score 1.6%, Density are the plain cloth of 410T, and fabric is in 38 g/m2, there is certain uvioresistant
Function;
Dyeing:
At dye bath bath raio 1:10, dye bath pH value 5 is controlled, acid levelling agent 1.2g/l, mass fraction are added at 40 DEG C
50% glacial acetic acid 1.6g/l, acid dyes 25g/l, anti-ultraviolet finishing agent 5g/l rise according to 1.2 DEG C/min of heating rate
Temperature keeps the temperature 20 minutes, heats up again to 70 DEG C, and 0.8 DEG C/min of heating rate is warming up to 98 DEG C, keeps the temperature 50 minutes, by cooling speed
0.8 DEG C/min cooling is spent, 70 DEG C is cooled to, cools down again, 1.2 DEG C/min of cooling rate.
Color fixing process:
Fixation formula, fixation formula: acidic color fixing agent DM-2539G 4% (o.w.f.), glacial acetic acid are added at 40 DEG C
0.5g/l, control PH is 4.5,1.2 DEG C/min of heating rate, is warming up to 80 DEG C, keeps the temperature 30 minutes, then by 1.5 DEG C of cooling rate/
Min cooling.
Reduction cleaning technique:
At 40 DEG C, reduction cleaning auxiliary agent is added, reduction cleaning auxiliary agent formula is as follows:
NaOH:2g/l;
Reducing agent: 2g/l;
Scouring agent: 0.5g/l;
Softening agent: 1.3g/l;
Defoaming agent: 1g/l;
By 0.8 DEG C/min of heating rate, 70 DEG C are warming up to, heat preservation is cleaned 20 minutes, then is cooled down by 2 DEG C/min of cooling rate.
Setting process:
At 170 DEG C of setting temperature, speed is stentering forming to be carried out, using 4 positive overfeedings between 40m/min.
Embodiment 3
A kind of preparation method of the ventilative uvioresistant fabrics of light weight of the invention, comprising the following steps:
(1) base fabric makes: being weaved using 20D polyamide fibre fine dinier yarn;
(2) warping, sizing and axis are carried out to yarn to handle, then it is weaved;
(3) uvioresistant auxiliary agent is configured to the uvioresistant solution that concentration is 5 grams per liters, the embryo cloth that will be made into through step (2)
It is dipped in dyeing, again fixation, reduction cleaning in uvioresistant solution after desizing, then by fabric drying and shaping, uvioresistant face is made
Material.
In order to reach fabric light weight and have certain UVResistant effect, quality is added in 20D polyamide fibre fine dinier yarn spinning phase
The titanium dioxide of score 1.8%, Density are the plain cloth of 420T, and fabric is in 40 g/m2, there is certain uvioresistant
Function;
Dyeing:
At dye bath bath raio 1:11, dye bath pH value 5.2 is controlled, 1.3 g/l of acid levelling agent, quality point are added at 40 DEG C
1.8 g/l of glacial acetic acid, acid dyes 30g/l, 6 g/l of anti-ultraviolet finishing agent of number 50%, according to 1.2 DEG C of heating rate/
Min is warming up to 70 DEG C, keeps the temperature 20 minutes, heats up again, and 0.8 DEG C/min of heating rate is warming up to 98 DEG C, keeps the temperature 50 minutes, presses
0.8 DEG C/min of cooling rate cooling, is cooled to 70 DEG C, cools down again, 1.2 DEG C/min of cooling rate.
Color fixing process:
Fixation formula, fixation formula: 5 % of acidic color fixing agent DM-2539G (o.w.f.), glacial acetic acid are added at 40 DEG C
0.6g/l, control PH is 5,1.2 DEG C/min of heating rate, is warming up to 80 DEG C, keeps the temperature 30 minutes, then by 1.5 DEG C of cooling rate/
Min cooling.
Reduction cleaning technique:
At 40 DEG C, reduction cleaning auxiliary agent is added, reduction cleaning auxiliary agent formula is as follows:
NaOH:3g/l;
Reducing agent: 3 g/l;
Scouring agent: 0.8 g/l;
Softening agent: 1.5 g/l;
Defoaming agent: 1.2 g/l;
By 0.8 DEG C/min of heating rate, 70 DEG C are warming up to, heat preservation is cleaned 20 minutes, then is cooled down by 2 DEG C/min of cooling rate.
Setting process:
At 180 DEG C of setting temperature, speed is stentering forming to be carried out, using 4 positive overfeedings between 45m/min.
In order to further enhance its uvioresistant function, is not increasing fabric grammes per square metre, do not changing the case where fabric hand feel style
Under, uvioresistant auxiliary agent is added by rational proportion in dyeing, makes fabric that there is better anti-ultraviolet function.
The present invention is by being added ultraviolet-resistant aid in dyeing course, and the fine-denier fabric grammes per square metre is still in 35-40 g/m2, face
The good permeability of material, uvioresistant protecting factor>=40, ultraviolet ray transmissivity<5% have preferable anti-ultraviolet function.
Claims (4)
- The preparation method of uvioresistant fabrics 1. a kind of light weight is breathed freely, it is characterised in that: the following steps are included:(1) base fabric makes: being weaved using 20D polyamide fibre fine dinier yarn;(2) warping, sizing and axis are carried out to yarn to handle, then it is weaved;(3) uvioresistant auxiliary agent is configured to the uvioresistant solution that concentration is 3-5 grams per liter, will be made into through step (2) It is dipped in dyeing, again fixation, reduction cleaning in uvioresistant solution after embryo cloth desizing, then by fabric drying and shaping, uvioresistant is made Line fabric.
- The preparation method of uvioresistant fabrics 2. a kind of light weight according to claim 1 is breathed freely, it is characterised in that: in 20D Polyamide fibre fine dinier yarn spinning phase adds the titanium dioxide of mass fraction 1.5-1.8%, and Density is that the plain weave of 400-420T is knitted Object, fabric is in 35-40 g/m2。
- The preparation method of uvioresistant fabrics 3. a kind of light weight according to claim 1 is breathed freely, it is characterised in that: dyer Skill: dye bath bath raio 1:9-11 controls dye bath pH value 4.8-5.2, and at 40 DEG C, acidity levelling agent 1.1-1.3 g/ is added L, glacial acetic acid 1.3-1.8 g/l of mass fraction 50%, acid dyes 20-30g/l, anti-ultraviolet finishing agent 4-6 g/l.
- The preparation method of uvioresistant fabrics 4. a kind of light weight according to claim 3 is breathed freely, it is characterised in that: dyed Cheng Zhong is warming up to 70 DEG C according to 1.2 DEG C/min of heating rate, keeps the temperature 20 minutes, heats up again, 0.8 DEG C/min of heating rate, 98 DEG C are warming up to, keeps the temperature 50 minutes, is cooled down by 0.8 DEG C/min of cooling rate, is cooled to 70 DEG C, cools down again, cooling rate 1.2 ℃/min。