CN109437685A - House decoration material and its preparation method and application - Google Patents
House decoration material and its preparation method and application Download PDFInfo
- Publication number
- CN109437685A CN109437685A CN201811427098.3A CN201811427098A CN109437685A CN 109437685 A CN109437685 A CN 109437685A CN 201811427098 A CN201811427098 A CN 201811427098A CN 109437685 A CN109437685 A CN 109437685A
- Authority
- CN
- China
- Prior art keywords
- parts
- sawdust
- house decoration
- decoration material
- husk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of house decoration material and its preparation method and application, the house decoration material includes the following raw material: cement, perlite, rubber powder, sawdust, sawdust, husk, glass fibre, wall grid cloth, Peitou mountain flour, sierozem power, pine needle meal, nano zircite, hydroxy resin, nanometer Tao Jing, alum powder, zinc stearate and hydroxypropylcellulose.House decoration material of the invention, with insulation, fire-proof and damp-proof and heat resistanceheat resistant performance, also there is certain toughness, traditional brick technique can be replaced, save labour cost and material cost, shorten the construction period, it is ensured that assure the fastness of decoration and the safety of construction, have material light, it is readily transported carrying, mold speed of production is fast, out high yield rate, and product rib is wide clearly demarcated, it can bear to will not change after Wall brick, the wall brick of surface patch will not fall off, quick for installation, there is energy-saving and environment-friendly effect.
Description
Technical field
The invention belongs to building fields, and in particular to a kind of house decoration material and its preparation method and application.
Background technique
As the improvement of people's living standards, people decorate living environment while being increasingly particular about to quality of the life
The requirement of quality is higher and higher, and the environmental protection of ornament materials whether affects the health of user, at the same with rhythm of life plus
Fastly, compare care as consumer in use, pernicious gas, harmful ion or harmful radiation whether can be generated in ornament materials
Problem, in addition, existing interior conduit is decorated by brick, sand, cement, artificial masonry, due to present artificial, sand cost mistake
The defects of height, finishing is long in time limit, and the technical level of worker is inconsistent, can generate a series of problems.Therefore, environmental protection and public nuisance free, be easy
It is mounted to the research direction for Novel environment-friendlymaterial material.
Summary of the invention
An object of the present invention is to provide a kind of house decoration materials.
A kind of house decoration material of the invention, the raw material including following parts by weight: 50 parts of cement~80 parts, perlite
20 parts~40 parts, 1 part~10 parts of rubber powder, 1 part~8 parts of sawdust, 10 parts~20 parts of sawdust, 10 parts of husk~20 parts, glass fibers
Tie up 1 part~15 parts, 10 parts~25 parts of wall grid cloth, 1 part~10 parts of Peitou mountain flour, 1 part~15 parts, 5 parts of pine needle meal of sierozem power
~15 parts, 1 part~20 parts of nano zircite, 2 parts~8 parts of 1 part~10 part, nanometer Tao Jing of hydroxy resin, alum powder 3 parts~10
Part, 1 part~10 parts of zinc stearate and 1 part~10 parts of hydroxypropylcellulose.
House decoration material of the invention has insulation, fire-proof and damp-proof and heat resistanceheat resistant performance, also has centainly tough
Property, traditional brick technique can be replaced, save labour cost and material cost, shorten the construction period, it is ensured that assure decoration
The safety of fastness and construction has material light, is readily transported carrying, mold speed of production is fast, out high yield rate, product
Rib is wide clearly demarcated, can bear to will not change after Wall brick, and the wall brick of surface patch will not fall off, quick for installation, has energy-saving and environment-friendly
Effect.
In addition, the house decoration material that the present invention is above-mentioned, can also have the following additional technical features:
As a preferred embodiment of the present invention, the house decoration material, the raw material including following parts by weight: water
50 parts of mud, 40 parts of perlite, 1 part of rubber powder, 8 parts of sawdust, 10 parts of sawdust, 20 parts of husk, 1 part of glass fibre, wall grid cloth
25 parts, 1 part of Peitou mountain flour, 15 parts of sierozem power, 5 parts of pine needle meal, 20 parts of nano zircite, 8 parts of 1 part, nanometer Tao Jing of hydroxy resin,
3 parts of alum powder, 10 parts of zinc stearate and 1 part of hydroxypropylcellulose.
As a preferred embodiment of the present invention, the house decoration material, the raw material including following parts by weight: water
80 parts of mud, 20 parts of perlite, 10 parts of rubber powder, 1 part of sawdust, 20 parts of sawdust, 10 parts of husk, 15 parts of glass fibre, wall grid
10 parts of cloth, 10 parts of Peitou mountain flour, 1 part of sierozem power, 15 parts of pine needle meal, 1 part of nano zircite, 10 part, nanometer Tao Jing 2 of hydroxy resin
Part, 10 parts of alum powder, 1 part of zinc stearate and 10 parts of hydroxypropylcellulose.
As a preferred embodiment of the present invention, the house decoration material, the raw material including following parts by weight: water
65 parts of mud, 30 parts of perlite, 5 parts of rubber powder, 4 parts of sawdust, 15 parts of sawdust, 15 parts of husk, 7 parts of glass fibre, wall grid cloth
17 parts, 5 parts of Peitou mountain flour, 7 parts of sierozem power, 10 parts of pine needle meal, 10 parts of nano zircite, 5 parts of 5 part, nanometer Tao Jing of hydroxy resin,
7 parts of alum powder, 5 parts of zinc stearate and 5 parts of hydroxypropylcellulose.
As a preferred embodiment of the present invention, the house decoration material, the raw material including following parts by weight: water
57 parts of mud, 35 parts of perlite, 2 parts of rubber powder, 6 parts of sawdust, 13 parts of sawdust, 18 parts of husk, 4 parts of glass fibre, wall grid cloth
17 parts, 8 parts of Peitou mountain flour, 4 parts of sierozem power, 12 parts of pine needle meal, 5 parts of nano zircite, 3 parts of 8 part, nanometer Tao Jing of hydroxy resin,
7 parts of alum powder, 2 parts of zinc stearate and 7 parts of hydroxypropylcellulose.
As a preferred embodiment of the present invention, the house decoration material, the raw material including following parts by weight: water
72 parts of mud, 25 parts of perlite, 8 parts of rubber powder, 3 parts of sawdust, 18 parts of sawdust, 12 parts of husk, 12 parts of glass fibre, wall grid cloth
13 parts, 8 parts of Peitou mountain flour, 4 parts of sierozem power, 12 parts of pine needle meal, 5 parts of nano zircite, 4 parts of 8 part, nanometer Tao Jing of hydroxy resin,
8 parts of alum powder, 3 parts of zinc stearate and 7 parts of hydroxypropylcellulose.
It is another object of the present invention to the processing methods for proposing the house decoration material.
The processing method of the house decoration material, includes the following steps: S101: first by the raw material 60 DEG C~
20min~30min is mixed at a temperature of 85 DEG C, obtains mixed material；S102: and then the mixture is placed in hot press,
At a temperature of 120 DEG C~150 DEG C, hot pressing 20min~30min under 15MPa~25MPa pressure, sizing is then cold-pressed in cold press,
Obtain house decoration material.
Another object of the present invention is to propose the house decoration material in fields such as house decoration, indoor designs
In application.
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description
Obviously, or practice through the invention is recognized.
Specific embodiment
The embodiment of the present invention is described below in detail, the embodiment is exemplary, it is intended to it is used to explain the present invention, and
It is not considered as limiting the invention.
Embodiment 1
Embodiment 1 proposes a kind of house decoration material, the house decoration material, the original including following parts by weight
Material: 50 parts of cement, 40 parts of perlite, 1 part of rubber powder, 8 parts of sawdust, 10 parts of sawdust, 20 parts of husk, 1 part of glass fibre, wall net
25 parts of lattice cloth, 1 part of Peitou mountain flour, 15 parts of sierozem power, 5 parts of pine needle meal, 20 parts of nano zircite, 1 part, nanometer Tao Jing of hydroxy resin
8 parts, 3 parts of alum powder, 10 parts of zinc stearate and 1 part of hydroxypropylcellulose.
The processing method of the house decoration material of embodiment 1, includes the following steps:
(1) raw material is mixed into 30min at a temperature of 60 DEG C first, obtains mixed material.
(2) then the mixture is placed in hot press, at a temperature of 120 DEG C, hot pressing 20min under 25MPa pressure, so
Sizing is cold-pressed in cold press afterwards, obtains house decoration material.
Embodiment 2
Embodiment 2 proposes a kind of house decoration material, the house decoration material, the original including following parts by weight
Material: 80 parts of cement, 20 parts of perlite, 10 parts of rubber powder, 1 part of sawdust, 20 parts of sawdust, 10 parts of husk, 15 parts of glass fibre, wall
10 parts of grid cloth, 10 parts of Peitou mountain flour, 1 part of sierozem power, 15 parts of pine needle meal, 1 part of nano zircite, hydroxy resin 10 part, nanometer
2 parts of Tao Jing, 10 parts of alum powder, 1 part of zinc stearate and 10 parts of hydroxypropylcellulose.
The processing method of the house decoration material of embodiment 2, includes the following steps:
(1) raw material is mixed into 20min at a temperature of 85 DEG C first, obtains mixed material.
(2) then the mixture is placed in hot press, at a temperature of 150 DEG C, hot pressing 30min under 15MPa pressure, so
Sizing is cold-pressed in cold press afterwards, obtains house decoration material.
Embodiment 3
Embodiment 3 proposes a kind of house decoration material, the house decoration material, the original including following parts by weight
Material: 65 parts of cement, 30 parts of perlite, 5 parts of rubber powder, 4 parts of sawdust, 15 parts of sawdust, 15 parts of husk, 7 parts of glass fibre, wall net
17 parts of lattice cloth, 5 parts of Peitou mountain flour, 7 parts of sierozem power, 10 parts of pine needle meal, 10 parts of nano zircite, 5 part, nanometer Tao Jing of hydroxy resin
5 parts, 7 parts of alum powder, 5 parts of zinc stearate and 5 parts of hydroxypropylcellulose.
The processing method of the house decoration material of embodiment 3, includes the following steps:
(1) raw material is mixed into 25min at a temperature of 67 DEG C first, obtains mixed material.
(2) then the mixture is placed in hot press, at a temperature of 135 DEG C, hot pressing 25min under 20MPa pressure, so
Sizing is cold-pressed in cold press afterwards, obtains house decoration material.
Embodiment 4
Embodiment 4 proposes a kind of house decoration material, the house decoration material, the original including following parts by weight
Material: 57 parts of cement, 35 parts of perlite, 2 parts of rubber powder, 6 parts of sawdust, 13 parts of sawdust, 18 parts of husk, 4 parts of glass fibre, wall net
17 parts of lattice cloth, 8 parts of Peitou mountain flour, 4 parts of sierozem power, 12 parts of pine needle meal, 5 parts of nano zircite, 8 part, nanometer Tao Jing 3 of hydroxy resin
Part, 7 parts of alum powder, 2 parts of zinc stearate and 7 parts of hydroxypropylcellulose.
The processing method of the house decoration material of embodiment 4, includes the following steps:
(1) raw material is mixed into 20min at a temperature of 60 DEG C first, obtains mixed material.
(2) then the mixture is placed in hot press, at a temperature of 120 DEG C, hot pressing 20min under 15MPa pressure, so
Sizing is cold-pressed in cold press afterwards, obtains house decoration material.
Embodiment 5
Embodiment 5 proposes a kind of house decoration material, the house decoration material, the original including following parts by weight
Material: 72 parts of cement, 25 parts of perlite, 8 parts of rubber powder, 3 parts of sawdust, 18 parts of sawdust, 12 parts of husk, 12 parts of glass fibre, wall
13 parts of grid cloth, 8 parts of Peitou mountain flour, 4 parts of sierozem power, 12 parts of pine needle meal, 5 parts of nano zircite, hydroxy resin 8 part, nanometer pottery
4 parts brilliant, 8 parts of alum powder, 3 parts of zinc stearate and 7 parts of hydroxypropylcellulose.
The processing method of the house decoration material of embodiment 5, includes the following steps:
(1) raw material is mixed into 30min at a temperature of 85 DEG C first, obtains mixed material.
(2) then the mixture is placed in hot press, at a temperature of 150 DEG C, hot pressing 30min under 25MPa pressure, so
Sizing is cold-pressed in cold press afterwards, obtains house decoration material.
To sum up, house decoration material of the invention has insulation, fire-proof and damp-proof and heat resistanceheat resistant performance, also has certain
Toughness, can replace traditional brick technique, save labour cost and material cost, shorten the construction period, it is ensured that assure dress
The fastness of decorations and the safety of construction have material light, are readily transported carrying, and mold speed of production is fast, out high yield rate,
Product rib is wide clearly demarcated, can bear to will not change after Wall brick, and the wall brick of surface patch will not fall off, quick for installation, there is energy-saving ring
The effect of guarantor.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means specific features, structure, material or spy described in conjunction with this embodiment or example
Point is included at least one embodiment or example of the invention.In the present specification, schematic expression of the above terms are not
It must be directed to identical embodiment or example.Moreover, particular features, structures, materials, or characteristics described can be in office
It can be combined in any suitable manner in one or more embodiment or examples.In addition, without conflicting with each other, the skill of this field
Art personnel can tie the feature of different embodiments or examples described in this specification and different embodiments or examples
It closes and combines.
Although the embodiments of the present invention has been shown and described above, it is to be understood that above-described embodiment is example
Property, it is not considered as limiting the invention, those skilled in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, modifies, replacement and variant.
Claims (8)
1. a kind of house decoration material, which is characterized in that the raw material including following parts by weight: 50 parts of cement~80 parts, pearl
20 parts~40 parts of rock, 1 part~10 parts of rubber powder, 1 part~8 parts of sawdust, 10 parts~20 parts of sawdust, 10 parts of husk~20 parts, glass
1 part~15 parts of fiber, 10 parts~25 parts of wall grid cloth, 1 part~10 parts of Peitou mountain flour, 1 part~15 parts of sierozem power, pine needle meal 5
Part~15 parts, 1 part~20 parts of nano zircite, 2 parts~8 parts of 1 part~10 part, nanometer Tao Jing of hydroxy resin, alum powder 3 parts~10
Part, 1 part~10 parts of zinc stearate and 1 part~10 parts of hydroxypropylcellulose.
2. house decoration material according to claim 1, which is characterized in that the raw material including following parts by weight: cement
50 parts, 40 parts of perlite, 1 part of rubber powder, 8 parts of sawdust, 10 parts of sawdust, 20 parts of husk, 1 part of glass fibre, wall grid cloth 25
It is part, 1 part of Peitou mountain flour, 15 parts of sierozem power, 5 parts of pine needle meal, 20 parts of nano zircite, 8 parts of 1 part, nanometer Tao Jing of hydroxy resin, white
3 parts of alum flour, 10 parts of zinc stearate and 1 part of hydroxypropylcellulose.
3. house decoration material according to claim 1, which is characterized in that the raw material including following parts by weight: cement
80 parts, 20 parts of perlite, 10 parts of rubber powder, 1 part of sawdust, 20 parts of sawdust, 10 parts of husk, 15 parts of glass fibre, wall grid cloth
10 parts, 10 parts of Peitou mountain flour, 1 part of sierozem power, 15 parts of pine needle meal, 1 part of nano zircite, 10 part, nanometer Tao Jing 2 of hydroxy resin
Part, 10 parts of alum powder, 1 part of zinc stearate and 10 parts of hydroxypropylcellulose.
4. house decoration material according to claim 1, which is characterized in that the raw material including following parts by weight: cement
65 parts, 30 parts of perlite, 5 parts of rubber powder, 4 parts of sawdust, 15 parts of sawdust, 15 parts of husk, 7 parts of glass fibre, wall grid cloth 17
It is part, 5 parts of Peitou mountain flour, 7 parts of sierozem power, 10 parts of pine needle meal, 10 parts of nano zircite, 5 parts of 5 part, nanometer Tao Jing of hydroxy resin, white
7 parts of alum flour, 5 parts of zinc stearate and 5 parts of hydroxypropylcellulose.
5. house decoration material according to claim 1, which is characterized in that the raw material including following parts by weight: cement
57 parts, 35 parts of perlite, 2 parts of rubber powder, 6 parts of sawdust, 13 parts of sawdust, 18 parts of husk, 4 parts of glass fibre, wall grid cloth 17
It is part, 8 parts of Peitou mountain flour, 4 parts of sierozem power, 12 parts of pine needle meal, 5 parts of nano zircite, 3 parts of 8 part, nanometer Tao Jing of hydroxy resin, white
7 parts of alum flour, 2 parts of zinc stearate and 7 parts of hydroxypropylcellulose.
6. house decoration material according to claim 1, which is characterized in that the raw material including following parts by weight: cement
72 parts, 25 parts of perlite, 8 parts of rubber powder, 3 parts of sawdust, 18 parts of sawdust, 12 parts of husk, 12 parts of glass fibre, wall grid cloth 13
It is part, 8 parts of Peitou mountain flour, 4 parts of sierozem power, 12 parts of pine needle meal, 5 parts of nano zircite, 4 parts of 8 part, nanometer Tao Jing of hydroxy resin, white
8 parts of alum flour, 3 parts of zinc stearate and 7 parts of hydroxypropylcellulose.
7. the processing method of house decoration material described in any one of claims 1-6, which comprises the steps of:
S101: the raw material is mixed to 20min~30min at a temperature of 60 DEG C~85 DEG C first, obtains mixed material；
S102: and then the mixture is placed in hot press, at a temperature of 120 DEG C~150 DEG C, under 15MPa~25MPa pressure
Then hot pressing 20min~30min is cold-pressed sizing in cold press, obtains house decoration material.
8. application of the described in any item house decoration materials of claim 1-7 in the fields such as house decoration, indoor design.