CN103936354A - Production process for external tiles with decorative surfaces during construction waste production - Google Patents

Production process for external tiles with decorative surfaces during construction waste production Download PDF

Info

Publication number
CN103936354A
CN103936354A CN201410150055.0A CN201410150055A CN103936354A CN 103936354 A CN103936354 A CN 103936354A CN 201410150055 A CN201410150055 A CN 201410150055A CN 103936354 A CN103936354 A CN 103936354A
Authority
CN
China
Prior art keywords
weight
decorative
exterior
tile
tiles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410150055.0A
Other languages
Chinese (zh)
Other versions
CN103936354B (en
Inventor
郭建淼
李福安
朱献峰
贺翔
詹海玲
张同均
尤少阳
高琦
贺方方
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuchang Jinke Architecture Cleaning And Transport Co Ltd
Original Assignee
Xuchang Jinke Architecture Cleaning And Transport Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xuchang Jinke Architecture Cleaning And Transport Co Ltd filed Critical Xuchang Jinke Architecture Cleaning And Transport Co Ltd
Priority to CN201410150055.0A priority Critical patent/CN103936354B/en
Publication of CN103936354A publication Critical patent/CN103936354A/en
Application granted granted Critical
Publication of CN103936354B publication Critical patent/CN103936354B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a production process for external tiles with decorative surfaces during construction waste production. The external tiles comprise base layers and decorative surface layers. The production process comprises the following steps: crushing, removing impurities and screening the collected construction wastes, and preparing coarse aggregate and fine aggregate; preparing base layer raw materials from the coarse aggregate, the fine aggregate, cement and water for performing first-time pressing; preparing raw materials of the decorative surface layers; performing second-time pressing, and molding the external tiles with decorative surfaces. The pressed and molded external tiles with decorative surfaces are fed into a kiln for maintenance. According to the production process for external tiles with decorative surfaces during construction waste production, the external tiles with decorative surfaces can be produced through a two-step pressing method, the decorative surface layers of the tiles and the tile base are connected through pressing and are firm in bonding and durable. Moreover, after the tiles are used for building an outer wall, the outer wall is not needed to be subjected to secondary painting, tiles are not needed to be attached to the wall, and products of different colors can be selected to be combined into different textures and patterns according to the needs.

Description

Building waste is produced the production technique of the exterior wall tile with decorative cover
Technical field
The present invention relates to the technical field of building waste second stage employ, particularly a kind of building waste is produced the production technique of the exterior wall tile with decorative cover.
Background technology
In prior art, the exterior wall of buildings all will carry out plastering of exterior wall after having built by laying bricks or stones, whitewash, or exterior wall pastes the ornament such as ceramics, and follow-up duration holding time and the money of exterior wall, have much room for improvement.
Summary of the invention
To the object of the invention is in order addressing the above problem, to provide a kind of building waste to produce the production technique of the exterior wall tile with decorative cover.
Technical scheme of the present invention is: a kind of building waste is produced the production technique of the exterior wall tile with decorative cover, and this exterior wall tile comprises that base layer and architectural surface comprise the steps;
A. the building waste of collection is carried out to fragmentation, removal of impurities, screening, be made into coarse aggregate and fine aggregate, coarse aggregate size is 5mm-10mm, and the particle diameter of fine aggregate is at 0mm-5mm;
B. prepare the raw material of base layer;
Selecting above-mentioned coarse aggregate 100-140 weight part, fine aggregate 90-98 weight part, cement 250-330 weight part, moisture content is 53-63 weight part, be uniformly mixed, this proportioning can ensure combination between material closely, become brick after integraty good, solid,
C. the raw material for preparing base layer in step b is sent in exterior wall tile mould and suppressed for the first time; After compacting, base layer is kept in mould for the first time, and it is stand-by that mould top reserves compacting architectural surface space;
D. prepare the raw material of architectural surface;
Prepare color sand 180-220 weight part, white cement 90-110 weight part, pigment 1.4-1.6 weight part for bright decorative cover, water 15-18 weight part, is uniformly mixed, and its sand of prizing is 8-12 object, and strength of cement grade is 32.5;
Or quartz sand 180-220 weight part, white cement 90-110 weight part, pigment 1.4-1.6 weight part for the uneven surface of preparation granular sensation, water 15-18 weight part, is uniformly mixed; Wherein quartz sand particle size 2mm-4mm, strength of cement grade is 32.5;
E. the raw material of the architectural surface of preparing in steps d is put into the reserved architectural surface space of step c, carried out the exterior wall tile of compression moulding band decorative cover for the second time.
F. the exterior wall tile with decorative cover of the compression moulding in step e is delivered to kiln the inside maintenance.
Beneficial effect of the present invention
This building waste is produced the production technique of the exterior wall tile with decorative cover, and the method that can suppress by secondary is produced the exterior wall tile with decorative cover, between the architectural surface of this brick and brick matrix, connects by compacting, and the two is in conjunction with firm and durable; After this brick one-tenth exterior wall, exterior wall whitewashes without secondary, need not paste ceramics, and can be according to different lines and the patterns of product mix of the demand apolegamy different colours of oneself.
Embodiment
Embodiment mono-: a kind of building waste is produced the production technique of the exterior wall tile with decorative cover, and this exterior wall tile comprises that base layer and architectural surface comprise the steps;
A. the building waste of collection is carried out to fragmentation, removal of impurities, screening, be made into coarse aggregate and fine aggregate, coarse aggregate size is 5mm-10mm, and the particle diameter of fine aggregate is at 0mm-5mm; Very general in recycling prior art about building waste in this step, specifically do not set forth.
B. prepare the raw material of base layer;
Selecting above-mentioned coarse aggregate 100-140 weight part, fine aggregate 90-98 weight part, cement 250-330 weight part, moisture content is 53-63 weight part, be uniformly mixed,
C. the raw material for preparing base layer in step b is sent in exterior wall tile mould and suppressed for the first time; After compacting, base layer is kept in mould for the first time, and it is stand-by that mould top reserves compacting architectural surface space;
D. prepare the raw material of architectural surface;
Prepare color sand 180-220 weight part, white cement 90-110 weight part, pigment 1.4-1.6 weight part for bright decorative cover, water 15-18 weight part, is uniformly mixed, and its sand of prizing is 8-12 object, and strength of cement grade is 32.5;
E. the raw material of the architectural surface of preparing in steps d is put into the reserved architectural surface space of step c, carried out the exterior wall tile of compression moulding band decorative cover for the second time.
F. the exterior wall tile with decorative cover of the compression moulding in step e is delivered to kiln the inside maintenance.
In embodiment mono-, the raw material of base layer; Optimum ratio is that coarse aggregate 120 weight parts, fine aggregate 94 weight parts, cement 29 weight parts, moisture content are 33 weight parts, and the brick that such proportioning suppresses is out more solid.
 
Embodiment bis-: a kind of building waste is produced the production technique of the exterior wall tile with decorative cover, and this exterior wall tile comprises that base layer and architectural surface comprise the steps;
A. the building waste of collection is carried out to fragmentation, removal of impurities, screening, be made into coarse aggregate and fine aggregate, coarse aggregate size is 5mm-10mm, and the particle diameter of fine aggregate is at 0mm-5mm; Very general in recycling prior art about building waste in this step, specifically do not set forth.
B. prepare the raw material of base layer;
Selecting above-mentioned coarse aggregate 100-140 weight part, fine aggregate 90-98 weight part, cement 250-330 weight part, moisture content is 53-63 weight part, be uniformly mixed,
C. the raw material for preparing base layer in step b is sent in exterior wall tile mould and suppressed for the first time; After compacting, base layer is kept in mould for the first time, and it is stand-by that mould top reserves compacting architectural surface space;
D. prepare the raw material of architectural surface;
Quartz sand 180-220 weight part, white cement 90-110 weight part, pigment 1.4-1.6 weight part for the uneven surface of preparation granular sensation, water 15-18 weight part, is uniformly mixed; Wherein quartz sand particle size 2mm-4mm, strength of cement grade is 32.5;
E. the raw material of the architectural surface of preparing in steps d is put into the reserved architectural surface space of step c, carried out the exterior wall tile of compression moulding band decorative cover for the second time.
F. the exterior wall tile with decorative cover of the compression moulding in step e is delivered to kiln the inside maintenance.
In embodiment bis-, the raw material of base layer; Optimum ratio is that coarse aggregate 120 weight parts, fine aggregate 94 weight parts, cement 29 weight parts, moisture content are 33 weight parts, and the brick that such proportioning suppresses is out more solid.

Claims (1)

1. building waste is produced a production technique for the exterior wall tile with decorative cover, and this exterior wall tile comprises that base layer and architectural surface comprise the steps;
A. the building waste of collection is carried out to fragmentation, removal of impurities, screening, be made into coarse aggregate and fine aggregate, coarse aggregate size is 5mm-10mm, and the particle diameter of fine aggregate is at 0mm-5mm;
B. prepare the raw material of base layer;
Selecting above-mentioned coarse aggregate 100-140 weight part, fine aggregate 90-98 weight part, cement 250-330 weight part, moisture content is 53-63 weight part, be uniformly mixed,
C. the raw material for preparing base layer in step b is sent in exterior wall tile mould and suppressed for the first time; After compacting, base layer is kept in mould for the first time, and it is stand-by that mould top reserves compacting architectural surface space;
D. prepare the raw material of architectural surface;
Prepare color sand 180-220 weight part, white cement 90-110 weight part, pigment 1.4-1.6 weight part for bright decorative cover, water 15-18 weight part, is uniformly mixed, and its sand of prizing is 8-12 object, and strength of cement grade is 32.5;
Or quartz sand 180-220 weight part, white cement 90-110 weight part, pigment 1.4-1.6 weight part for the uneven surface of preparation granular sensation, water 15-18 weight part, is uniformly mixed; Wherein quartz sand particle size 2mm-4mm, strength of cement grade is 32.5;
E. the raw material of the architectural surface of preparing in steps d is put into the reserved architectural surface space of step c, carried out the exterior wall tile of compression moulding band decorative cover for the second time;
F. the exterior wall tile with decorative cover of the compression moulding in step e is delivered to kiln the inside maintenance.
CN201410150055.0A 2014-04-16 2014-04-16 Production process for external tiles with decorative surfaces during construction waste production Active CN103936354B (en)