CN103771819A - Stone dust waste residue aerated brick and preparation method thereof - Google Patents

Stone dust waste residue aerated brick and preparation method thereof Download PDF

Info

Publication number
CN103771819A
CN103771819A CN201410015655.6A CN201410015655A CN103771819A CN 103771819 A CN103771819 A CN 103771819A CN 201410015655 A CN201410015655 A CN 201410015655A CN 103771819 A CN103771819 A CN 103771819A
Authority
CN
China
Prior art keywords
parts
dust waste
waste residue
stone
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410015655.6A
Other languages
Chinese (zh)
Inventor
任劲松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SHENGREN NEW BUILDING MATERIAL Co Ltd
Original Assignee
ANHUI SHENGREN NEW BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHENGREN NEW BUILDING MATERIAL Co Ltd filed Critical ANHUI SHENGREN NEW BUILDING MATERIAL Co Ltd
Priority to CN201410015655.6A priority Critical patent/CN103771819A/en
Publication of CN103771819A publication Critical patent/CN103771819A/en
Pending legal-status Critical Current

Abstract

The invention discloses a stone dust waste residue aerated brick which is characterized by being prepared from the following raw materials in parts by weight: 25-28 parts of stone dust waste residues, 13-15 parts of fluorgypsum, 20-25 parts of macadam, 0.05-0.1 part of powdered aluminum, 5-10 parts of cement, 0.4-0.9 part of calcium formate, 0.2-0.4 part of sodium thiocyanate, 0.1-0.4 part of phenanthrene, 2-5 parts of polypropylene fibers, 3-7 parts of starch, 3-5 parts of lauryl sodium sulfate, 0.5-1 part of aluminum oxide, 0.2-0.5 part of soda ash, 2-3 parts of an white emulsion, 0.1-0.3 part of roses, 0.04-0.06 part of elecampane, 3-6 parts of an assistant and a proper amount of water. By adopting stone dust waste residues as the raw materials, the cost of the raw materials can be greatly lowered, waste is turned into wealth, the resources are fully utilized and the environment is protected. The aerated brick prepared by the process disclosed by the invention is high in strength and not easy to break.

Description

A kind of stone material dust waste residue aerated bricks and preparation method thereof
Technical field
The present invention relates to aerated bricks technical field, be specifically related to a kind of stone material dust waste residue aerated bricks and preparation method thereof.
Background technology
In recent years, along with the quickening of process of industrialization and the raising of the level of urbanization, also various environmental stresss and problem have been brought, the various solid wastes that Industrial processes produce and urban construction are removed and are remake the solid waste brought etc. and perplexing always resident's living environment, the present invention adds in aerated bricks solid waste as starting material, realize the cyclic utilization of waste, reduced the pollution to environment, met strategy of sustainable development requirement.
Aerated bricks is the air-entrained concrete building block of producing by autoclave at high temperature apparatus and process.Air-entrained concrete building block is take cement, slag, sand, lime etc. as main raw material, add foaming agent, the solid block forming through stirring moulding, steam press maintenance, gas concrete is by purposes, can be divided into five kinds, non-bearing building block, bearing building block, insulation block, wallboard and roof boarding.
Tradition solid clay brick weight is large, not only wastes outside national clay resource, price height, and cannot meet the requirement of some special buildings brick, and therefore common brick use has been completely forbidden in present many advanced areas, replaces and advocates energetically aerated bricks.Compare with normal concrete brick with traditional clay brick, aerated bricks is not only lightweight, also has heat insulating, an advantage such as sound-proofing properties is excellent, shock resistance is strong, good processability, resistance to elevated temperatures are good, strong adaptability.But China, about the production technology of aerated bricks is ripe not enough, makes aerated bricks Development Technology slow at present, also cannot meet the demand of multiple market.
Summary of the invention
Object of the present invention is just to provide a kind of stone material dust waste residue aerated bricks and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of stone material dust waste residue aerated bricks, it is characterized in that, made by the raw material of following weight part: stone material dust waste residue 25-28, fluorgypsum 13-15, rubble 20-25, aluminium powder 0.05-0.1, cement 5-10, calcium formiate 0.4-0.9, Sodium Thiocyanate 99 0.2-0.4, luxuriant and rich with fragrance 0.1-0.4, polypropylene fibre 2-5, starch 3-7, sodium lauryl sulphate 3-5, aluminum oxide 0.5-1, soda ash 0.2-0.5, white glue with vinyl 2-3, Rose 0.1-0.3, banksia rose 0.04-0.06, auxiliary agent 3-6, suitable quantity of water; Described auxiliary agent is made up of following raw materials in part by weight: poly(vinylidene fluoride) 1.2-3.1, silicon carbide powder 2-4, titanium dioxide 3-5, silicon sol 0.3-0.6, redispersible latex powder 0.6-1.2, pamorusa oil 3-6, borneol 1-3, ultra micro wax powder 0.7-0.9, grape vine 4-7, its preparation method is that each crushing material is mixed, be heated to 70-80 ℃, stirring reaction 30-40 minute, to obtain final product.
The preparation method of described a kind of stone material dust waste residue aerated bricks, is characterized in that comprising the following steps:
(1) Rose, the banksia rose are decocted together in water to filtration in 2-3 hour, gained filtrate vacuum concentration extracts, and obtains Chinese medical extract;
(2) after the filter residue of step (1) and stone material dust waste residue, fluorgypsum, rubble, polypropylene fibre are mixed, at 770-900 ℃, calcine 3-4 hour, cooling, grind, add white glue with vinyl to stir;
(3) by step (1), (2) reaction mass and other remaining component, drop in stirrer and be uniformly mixed 8-10 minute, obtain mixed slurry;
(4) gained mixed slurry is poured into the mold moulding, precuring 1-3 hour at 35-43 ℃, the demoulding, cutting, obtains building block base; Again building block base is put into reactor steam press maintenance 13-15 hour, put in storage and get final product.
The present invention has following beneficial effect: in the present invention, adopting stone material dust waste residue is raw material, can greatly reduce raw materials cost, turns waste into wealth, and makes full use of resource, protection of the environment, and the aerated bricks intensity that adopts technique of the present invention to make is high, not easy fracture.
Embodiment
Described a kind of stone material dust waste residue aerated bricks, it is characterized in that, made by the raw material of following weight part: stone material dust waste residue 27, fluorgypsum 13, rubble 20, aluminium powder 0.05, cement 5, calcium formiate 0.4, Sodium Thiocyanate 99 0.24, phenanthrene 0.14, polypropylene fibre 2, starch 3, sodium lauryl sulphate 5, aluminum oxide 0.5, soda ash 0.25, white glue with vinyl 2, Rose 0.1, the banksia rose 0.04, auxiliary agent 3, suitable quantity of water; Described auxiliary agent is made up of following raw materials in part by weight: poly(vinylidene fluoride) 1.2, silicon carbide powder 4, titanium dioxide 3, silicon sol 0.3, redispersible latex powder 0.6, pamorusa oil 6, borneol 1, ultra micro wax powder 0.7, grape vine 4, its preparation method is that each crushing material is mixed, be heated to 70-80 ℃, stirring reaction 30-40 minute, to obtain final product.
Making method comprises the following steps:
(1) Rose, the banksia rose are decocted together in water to filtration in 2-3 hour, gained filtrate vacuum concentration extracts, and obtains Chinese medical extract;
(2) after the filter residue of step (1) and stone material dust waste residue, fluorgypsum, rubble, polypropylene fibre are mixed, at 770-900 ℃, calcine 3-4 hour, cooling, grind, add white glue with vinyl to stir;
(3) by step (1), (2) reaction mass and other remaining component, drop in stirrer and be uniformly mixed 8-10 minute, obtain mixed slurry;
(4) gained mixed slurry is poured into the mold moulding, precuring 1-3 hour at 35-43 ℃, the demoulding, cutting, obtains building block base; Again building block base is put into reactor steam press maintenance 13-15 hour, put in storage and get final product.
The performance data of processing the aerated bricks obtaining by above-described embodiment is as follows: the average unit weight of this building block is 535-678kg/m 3, water suction leads that wet slowly it is 5.5 times of clay brick that same volume absorbs water to saturated required time, good heat insulating, and mean value ultimate compression strength is 7.4-8.7MPa.

Claims (2)

1. a stone material dust waste residue aerated bricks, it is characterized in that, made by the raw material of following weight part: stone material dust waste residue 25-28, fluorgypsum 13-15, rubble 20-25, aluminium powder 0.05-0.1, cement 5-10, calcium formiate 0.4-0.9, Sodium Thiocyanate 99 0.2-0.4, luxuriant and rich with fragrance 0.1-0.4, polypropylene fibre 2-5, starch 3-7, sodium lauryl sulphate 3-5, aluminum oxide 0.5-1, soda ash 0.2-0.5, white glue with vinyl 2-3, Rose 0.1-0.3, banksia rose 0.04-0.06, auxiliary agent 3-6, suitable quantity of water; Described auxiliary agent is made up of following raw materials in part by weight: poly(vinylidene fluoride) 1.2-3.1, silicon carbide powder 2-4, titanium dioxide 3-5, silicon sol 0.3-0.6, redispersible latex powder 0.6-1.2, pamorusa oil 3-6, borneol 1-3, ultra micro wax powder 0.7-0.9, grape vine 4-7, its preparation method is that each crushing material is mixed, be heated to 70-80 ℃, stirring reaction 30-40 minute, to obtain final product.
2. the making method of a kind of stone material dust waste residue aerated bricks according to claim 1, is characterized in that comprising the following steps:
(1) Rose, the banksia rose are decocted together in water to filtration in 2-3 hour, gained filtrate vacuum concentration extracts, and obtains Chinese medical extract;
(2) after the filter residue of step (1) and stone material dust waste residue, fluorgypsum, rubble, polypropylene fibre are mixed, at 770-900 ℃, calcine 3-4 hour, cooling, grind, add white glue with vinyl to stir;
(3) by step (1), (2) reaction mass and other remaining component, drop in stirrer and be uniformly mixed 8-10 minute, obtain mixed slurry;
(4) gained mixed slurry is poured into the mold moulding, precuring 1-3 hour at 35-43 ℃, the demoulding, cutting, obtains building block base; Again building block base is put into reactor steam press maintenance 13-15 hour, put in storage and get final product.
CN201410015655.6A 2014-01-14 2014-01-14 Stone dust waste residue aerated brick and preparation method thereof Pending CN103771819A (en)