CN109423739A - A kind of double-sided cloth and its processing method - Google Patents

A kind of double-sided cloth and its processing method Download PDF

Info

Publication number
CN109423739A
CN109423739A CN201710783524.6A CN201710783524A CN109423739A CN 109423739 A CN109423739 A CN 109423739A CN 201710783524 A CN201710783524 A CN 201710783524A CN 109423739 A CN109423739 A CN 109423739A
Authority
CN
China
Prior art keywords
cloth
cotton
double
sided
sliver
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710783524.6A
Other languages
Chinese (zh)
Inventor
章恩绮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Keqiao Shaoxing Union Textile Technology Co Ltd
Original Assignee
Keqiao Shaoxing Union Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Keqiao Shaoxing Union Textile Technology Co Ltd filed Critical Keqiao Shaoxing Union Textile Technology Co Ltd
Priority to CN201710783524.6A priority Critical patent/CN109423739A/en
Publication of CN109423739A publication Critical patent/CN109423739A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of double-sided cloth and its processing method comprising steps of raw cotton sorting, mixing, blowing-carding machinery separation, press to form cotton layer, combing machine point comb, it is spun into ripe bar, it is spun into rove, it is spun into cheese, cause embryo cloth, again by the embryo cloth by flame or in red-hot metal surface burning-off surface fine hair, finally handled with caustic lye of soda, fabric is uniformly put into dye vat, glacial acetic acid and neutralizing acid is added, dyestuff is put into again, high temperature cylinder dyes to obtain sample cloth, sample cloth is cleaned, it is well-pressed that sizing and preshrunk obtain the finished fabric two-sided cloth fabric, wrinkle resistance is more preferable, it is not easy pilling corrugation；Size is more stable, overhangs and feels, feel is finer and smoother；Washed long with the general gloss of silk fabrics it is non-discolouring, meanwhile, remain the sweat-absorbing breathable performance of raw cotton fabric, which effectively increases the production efficiency of double-sided cloth, saved production cost.

Description

A kind of double-sided cloth and its processing method
Technical field
The present invention relates to clothes to produce and process manufacturing technology field, and in particular to a kind of double-sided cloth and its processing method.
Background technique
Double-sided cloth is the cloth that often use in people's daily life, has been played in people's daily life huge Effect, be applied to many aspects of daily life, stamp can be made than such fabric, can also make solid color fabric use, with Economic level is continuously improved, and product quality requirement is also continuously improved in people, for example, finer and smoother feel, more preferably glossiness, Better sweat-absorbing breathable etc., therefore, we are also required to make product further improve to meet the needs of people.
Summary of the invention
The technical problem to be solved by the present invention is to provide that a kind of feel is fine and smooth, light in view of the above shortcomings of the prior art The double-sided cloth and its processing method of Ze Dujia.
The present invention in order to solve the above problem used by technical solution are as follows:
A kind of double-sided cloth, the cloth composition of the double-sided cloth are cotton cloth.
A kind of processing method of double-sided cloth, comprising the following steps:
(1) sorting is carried out to raw cotton, and the raw cotton handle except matter；
(2) different grades are chosen in proportion and the raw cotton of length is mixed；
(3) raw cotton mixed in step (2) is separated, secondary removal of impurities processing using blowing-carding machinery, makes gained Raw cotton fiber formation sliver arranged in parallel；
(4) combing is carried out to gained sliver in step (3) and separates it into single fiber state, and removed remaining in cotton roll Impurity, fault and staple fiber；
(5) gained sliver in step (4) press and to form uniform broadband shape cotton layer, the cotton layer using and roll up Associative mechanism is at cloth cotton roll；
(6) gained cloth cotton roll in step (5) is carried out point being combed into sliver using combing machine, the sliver is combed and opens, stretch, And remove undesirable set of staple fiber, impurity and staple fiber knot grain；
(7) gained sliver in step (6) merged using drawing frame, mixed and drawing-off, be spun into ripe bar；
(8) ripe bar described in step (7) passes through 4~12 times of drawing-offs, so that its elongation is attenuated and is twisted, is spun into slightly through fly frame Yarn, and by the reeling roving on bobbin；
(9) gained rove makes its attenuating attenuate, and be wound on bobbin through 10~50 times of drawing-off of past in step (8) Upper formation coil；
(10) coil forms cheese through automatic winder, while removing the impurity on yarn and fault, and by institute Cheese is stated through doubling winder coiling on spool, two-for-one twister is recycled to twist the yarn；
(11) the bobbin weaving yarns obtained in step (10) are at embryo cloth；
(12) embryo cloth is splitted along drawn needle side using scutcher, then by the embryo cloth by flame or in red-hot gold Metal surface burning-off surface fine hair, is finally handled with caustic lye of soda；
(13) dyeing processing is carried out to treated embryo cloth in step (12), fabric is uniformly put into dye vat, ice is added Acetic acid and neutralizing acid, then dyestuff is put into, 60~100 DEG C of dye vat temperature, be 2~15 hours into the cylinder time.
(14) the sample cloth cleaned, be formed and preshrunk obtains finished fabric.
Embryo cloth grammes per square metre described in step (11) is 145~150g/m2。
Embryo cloth described in step (12) is 80m/min~140m/ by the speed of service of flame or red-hot metal surface min。
Carrying out cleaning process to the sample cloth in step (14) is that the sample cloth temperature is cleaned when being down to 50 DEG C.
The beneficial effects of the present invention are:
A kind of double-sided cloth provided by the invention fabric compared with traditional double-sided cloth is well-pressed, wrinkle resistance is more preferable, is not easy pilling Corrugation；Size is more stable, overhangs and feels, feel is finer and smoother；Washed long with the general gloss of silk fabrics it is non-discolouring, meanwhile, protect The sweat-absorbing breathable performance of raw cotton fabric is stayed, the double-sided cloth processing method is with process is succinct, processing cost is low, high production efficiency The characteristics of, the production efficiency of double-sided cloth is effectively increased, production cost has been saved.
Detailed description of the invention
Fig. 1 is a kind of process flow chart of double-sided cloth processing method of the present invention.
Specific embodiment
Specifically illustrate embodiments of the present invention with reference to the accompanying drawing, these embodiments be only given in order to illustrate Purpose can not be interpreted as limitation of the invention, including attached drawing is only for reference and illustrates use, does not constitute to the invention patent The limitation of protection scope, because without departing from the spirit and scope of the present invention, many can be carried out to the present invention and changed Become.
Embodiment 1
A kind of double-sided cloth provided in this embodiment, the cloth composition of the double-sided cloth are 100% cotton cloth.
As shown in Figure 1, a kind of processing method of double-sided cloth provided in this embodiment the following steps are included:
(1) sorting is carried out to raw cotton, and the raw cotton handle except matter, the process is by manually dividing raw cotton Inspection, removes the impurity that general scutcher is difficult to, main to detect: filoplume, nylon wire, cloth is broken, colo(u)r streak, flax silk etc.；
(2) raw cotton for choosing different grades and length in proportion mixed (be 85% according to 1 grade of cotton and 2 grades of cotton ratios: 15% ratio carries out proportion mixing), the characteristics of arranging in pairs or groups and use, can give full play to different material by distributing cotton, reaching rationally makes With steady production improves yarn quality and reduces the purpose of spinning cost；
(3) raw cotton mixed in step (2) is separated, secondary removal of impurities processing using blowing-carding machinery, is removed miscellaneous Matter, fault and short fibre make gained raw cotton fiber formation sliver arranged in parallel；
(4) combing is carried out to gained sliver in step (3) and separates it into single fiber state, and removed remaining in cotton roll Impurity, fault and staple fiber；
(5) gained sliver in step (4) press and to form uniform broadband shape cotton layer, the cotton layer using and roll up Associative mechanism, in the process along with mixing and parallel drafting, more tends to cotton fiber in parallel, structure constantly improves at cloth cotton roll；
(6) gained cloth cotton roll in step (5) is carried out point being combed into sliver using combing machine, the sliver is combed and opens, stretch, And remove undesirable set of staple fiber, impurity and staple fiber knot grain so that yarn evenness it is uniform, it is bright and clean, strongly significantly improve；
(7) gained sliver in step (6) merged using drawing frame, mixed and drawing-off, be spun into ripe bar；
(8) ripe bar described in step (7) passes through 4 times of drawing-offs, so that its elongation is attenuated and is twisted, is spun into rove through fly frame, And by the reeling roving on bobbin；
(9) gained rove makes its attenuating attenuate through 10 times of drawing-off of past in step (8), and is wound on shape on bobbin At coil；
(10) coil forms cheese through automatic winder, while removing the impurity on yarn and fault, and by institute State cheese through doubling winder two or three cotton yarns and together coiling on spool, recycle two-for-one twister to the yarn into Row twisting, so that manufactured yarn has the physical properties such as certain strength, elasticity, gloss；
(11) yarn for twisted in step (10) is made in order, and covers on mercerizing machine set yarn roller, make described Yarn roller stretching is covered, and rotation makes yarn immerse lye under stretching state, the concentration of lye is 230g/L~270g/L, lixiviating After make to cover yarn roller and loosen, and the yarn is removed from roller, is cleaned with cold water, and by the treated yarn weaving at Embryo cloth, fabric width: 52 〞, the embryo cloth grammes per square metre are 145~150g/m2；
(12) embryo cloth is splitted along drawn needle side using scutcher, then by the embryo cloth by flame or in red-hot gold Metal surface burning-off surface fine hair, the embryo cloth are 80m/min by the speed of service of flame or red-hot metal surface, are finally used Caustic lye of soda is handled；
(13) dyeing processing is carried out to treated embryo cloth in step (12), fabric is uniformly put into dye vat, ice is added Acetic acid and neutralizing acid, then dyestuff is put into, 95 DEG C of dye vat temperature, be 10 hours into the cylinder time.
(14) the sample cloth cleaned, be formed and preshrunk obtains finished fabric, the sample cloth temperature is down to 50 degree Shi Jinhang cleaning.
Embodiment 2
A kind of double-sided cloth provided in this embodiment, the cloth composition of the double-sided cloth are 100% cotton cloth.
As shown in Figure 1, a kind of processing method of double-sided cloth provided in this embodiment the following steps are included:
(1) sorting is carried out to raw cotton, and the raw cotton handle except matter, the process is by manually dividing raw cotton Inspection, removes the impurity that general scutcher is difficult to, main to detect: filoplume, nylon wire, cloth is broken, colo(u)r streak, flax silk etc.；
(2) raw cotton for choosing different grades and length in proportion mixed (be 85% according to 1 grade of cotton and 2 grades of cotton ratios: 15% ratio carries out proportion mixing), the characteristics of arranging in pairs or groups and use, can give full play to different material by distributing cotton, reaching rationally makes With steady production improves yarn quality and reduces the purpose of spinning cost；
(3) raw cotton mixed in step (2) is separated, secondary removal of impurities processing using blowing-carding machinery, makes gained Raw cotton fiber formation sliver arranged in parallel；
(4) combing is carried out to gained sliver in step (3) and separates it into single fiber state, and removed remaining in cotton roll Impurity, fault and staple fiber；
(5) gained sliver in step (4) press and to form uniform broadband shape cotton layer, the cotton layer using and roll up Associative mechanism, in the process along with mixing and parallel drafting, more tends to cotton fiber in parallel, structure constantly improves at cloth cotton roll；
(6) gained cloth cotton roll in step (5) is carried out point being combed into sliver using combing machine, the sliver is combed and opens, stretch, And remove undesirable set of staple fiber, impurity and staple fiber knot grain so that yarn evenness it is uniform, it is bright and clean, strongly significantly improve；
(7) gained sliver in step (6) merged using drawing frame, mixed and drawing-off, be spun into ripe bar；
(8) ripe bar described in step (7) passes through 8 times of drawing-offs, so that its elongation is attenuated and is twisted, is spun into rove through fly frame, And by the reeling roving on bobbin；
(9) gained rove makes its attenuating attenuate through 35 times of drawing-off of past in step (8), and is wound on shape on bobbin At coil；
(10) coil forms cheese through automatic winder, while removing the impurity on yarn and fault, and by institute State cheese through doubling winder two or three cotton yarns and together coiling on spool, recycle two-for-one twister to the yarn into Row twisting, so that manufactured yarn has the physical properties such as certain strength, elasticity, gloss；
(11) yarn for twisted in step (10) is made in order, and covers on mercerizing machine set yarn roller, make described Yarn roller stretching is covered, and rotation makes yarn immerse lye under stretching state, the concentration of lye is 230g/L~270g/L, lixiviating After make to cover yarn roller and loosen, and the yarn is removed from roller, is cleaned with cold water, and by the treated yarn weaving at Embryo cloth, fabric width: 52 〞, the embryo cloth grammes per square metre are 145~150g/m2；
(12) embryo cloth is splitted along drawn needle side using scutcher, then by the embryo cloth by flame or in red-hot gold Metal surface burning-off surface fine hair, the embryo cloth are 120m/min by the speed of service of flame or red-hot metal surface, finally It is handled with caustic lye of soda；
(13) dyeing processing is carried out to treated embryo cloth in step (12), fabric is uniformly put into dye vat, ice is added Acetic acid and neutralizing acid, then dyestuff is put into, 95 DEG C of dye vat temperature, be 10 hours into the cylinder time.
(14) the sample cloth cleaned, be formed and preshrunk obtains finished fabric, the sample cloth temperature is down to 50 degree Shi Jinhang cleaning.
Embodiment 3
A kind of double-sided cloth provided in this embodiment, the cloth composition of the double-sided cloth are 100% cotton cloth.
As shown in Figure 1, a kind of processing method of double-sided cloth provided in this embodiment the following steps are included:
(1) sorting is carried out to raw cotton, and the raw cotton handle except matter, the process is by manually dividing raw cotton Inspection, removes the impurity that general scutcher is difficult to, main to detect: filoplume, nylon wire, cloth is broken, colo(u)r streak, flax silk etc.；
(2) raw cotton for choosing different grades and length in proportion mixed (be 85% according to 1 grade of cotton and 2 grades of cotton ratios: 15% ratio carries out proportion mixing), the characteristics of arranging in pairs or groups and use, can give full play to different material by distributing cotton, reaching rationally makes With steady production improves yarn quality and reduces the purpose of spinning cost；
(3) raw cotton mixed in step (2) is separated, secondary removal of impurities processing using blowing-carding machinery, makes gained Raw cotton fiber formation sliver arranged in parallel；
(4) combing is carried out to gained sliver in step (3) and separates it into single fiber state, and removed remaining in cotton roll Impurity, fault and staple fiber；
(5) gained sliver in step (4) press and to form uniform broadband shape cotton layer, the cotton layer using and roll up Associative mechanism, in the process along with mixing and parallel drafting, more tends to cotton fiber in parallel, structure constantly improves at cloth cotton roll；
(6) gained cloth cotton roll in step (5) is carried out point being combed into sliver using combing machine, the sliver is combed and opens, stretch, And remove undesirable set of staple fiber, impurity and staple fiber knot grain so that yarn evenness it is uniform, it is bright and clean, strongly significantly improve；
(7) gained sliver in step (6) merged using drawing frame, mixed and drawing-off, be spun into ripe bar；
(8) ripe bar described in step (7) passes through 12 times of drawing-offs, so that its elongation is attenuated and is twisted, is spun into rove through fly frame, And by the reeling roving on bobbin；
(9) gained rove makes its attenuating attenuate through 50 times of drawing-off of past in step (8), and is wound on shape on bobbin At coil；
(10) coil forms cheese through automatic winder, while removing the impurity on yarn and fault, and by institute State cheese through doubling winder two or three cotton yarns and together coiling on spool, recycle two-for-one twister to the yarn into Row twisting, so that manufactured yarn has the physical properties such as certain strength, elasticity, gloss；
(11) yarn for twisted in step (10) is made in order, and covers on mercerizing machine set yarn roller, make described Yarn roller stretching is covered, and rotation makes yarn immerse lye under stretching state, the concentration of lye is 230g/L~270g/L, lixiviating After make to cover yarn roller and loosen, and the yarn is removed from roller, is cleaned with cold water, and by the treated yarn weaving at Embryo cloth, fabric width: 52 〞, the embryo cloth grammes per square metre are 145~150g/m2；
(12) embryo cloth is splitted along drawn needle side using scutcher, then by the embryo cloth by flame or in red-hot gold Metal surface burning-off surface fine hair, the embryo cloth are 140m/min by the speed of service of flame or red-hot metal surface, finally It is handled with caustic lye of soda；
(13) dyeing processing is carried out to treated embryo cloth in step (12), fabric is uniformly put into dye vat, ice is added Acetic acid and neutralizing acid, then dyestuff is put into, 95 DEG C of dye vat temperature, be 10 hours into the cylinder time.
(14) the sample cloth cleaned, be formed and preshrunk obtains finished fabric, the sample cloth temperature is down to 50 degree Shi Jinhang cleaning.
The cloth made to embodiment 3 carry out analysis be found to have feel is finer and smoother, glossiness more preferably, sweat-absorbing breathable performance More preferable feature, while this method effectively increases the production efficiency of double-sided cloth, has saved production cost.
The foregoing is merely the preferable specific embodiments of the present invention, but scope of protection of the present invention is not limited thereto, In the technical scope disclosed by the present invention, any changes or substitutions that can be easily thought of by anyone skilled in the art, It should be covered by the protection scope of the present invention.

Claims (5)

1. a kind of double-sided cloth, it is characterised in that: the cloth composition of the double-sided cloth is cotton cloth.
2. a kind of processing method of double-sided cloth, which comprises the following steps:
(1) sorting is carried out to raw cotton, and the raw cotton handle except matter；
(2) different grades are chosen in proportion and the raw cotton of length is mixed；
(3) raw cotton mixed in step (2) is separated, secondary removal of impurities processing using blowing-carding machinery, makes gained raw cotton Fibers parallel arranges to form sliver；
(4) combing is carried out to gained sliver in step (3) and separates it into single fiber state, and removed remaining miscellaneous in cotton roll Matter, fault and staple fiber；
(5) gained sliver in step (4) press and to form uniform broadband shape cotton layer, the cotton layer using and roll up joint Cloth cotton roll is made in machine；
(6) gained cloth cotton roll in step (5) is carried out point being combed into sliver using combing machine, the sliver is combed and opens, stretch, and is removed Remove undesirable set of staple fiber, impurity and staple fiber knot grain；
(7) gained sliver in step (6) merged using drawing frame, mixed and drawing-off, be spun into ripe bar；
(8) ripe bar described in step (7) passes through 4~12 times of drawing-offs, so that its elongation is attenuated and is twisted, is spun into rove through fly frame, And by the reeling roving on bobbin；
(9) gained rove makes its attenuating attenuate through 10~50 times of drawing-off of past in step (8), and is wound on shape on bobbin At coil；
(10) coil forms cheese through automatic winder, while removing the impurity on yarn and fault, and by the cylinder Sub- yarn, on spool, recycles two-for-one twister to twist the yarn through doubling winder coiling；
(11) the bobbin weaving yarns obtained in step (10) are at embryo cloth；
(12) embryo cloth is splitted along drawn needle side using scutcher, then by the embryo cloth by flame or in red-hot metal watch Face burning-off surface fine hair, is finally handled with caustic lye of soda；
(13) dyeing processing is carried out to treated embryo cloth in step (12), fabric is uniformly put into dye vat, glacial acetic acid is added And neutralizing acid, then dyestuff is put into, 60~100 DEG C of dye vat temperature, be 2~15 hours into the cylinder time.
(14) the sample cloth cleaned, be formed and preshrunk obtains finished fabric.
3. a kind of double-sided cloth processing method according to claim 2, it is characterised in that: embryo cloth grammes per square metre described in step (11) For 145~150g/m2。
4. a kind of double-sided cloth processing method according to claim 2, it is characterised in that: embryo cloth described in step (12) passes through The speed of service of flame or red-hot metal surface is 80m/min~140m/min.
5. a kind of double-sided cloth processing method according to claim 2, it is characterised in that: to the sample cloth in step (14) Carrying out cleaning process is that the sample cloth temperature is cleaned when being down to 50 DEG C.
CN201710783524.6A 2017-09-01 2017-09-01 A kind of double-sided cloth and its processing method Pending CN109423739A (en)