CN105586699A - Double-faced fabric and processing method thereof - Google Patents
Double-faced fabric and processing method thereof Download PDFInfo
- Publication number
- CN105586699A CN105586699A CN201510989318.1A CN201510989318A CN105586699A CN 105586699 A CN105586699 A CN 105586699A CN 201510989318 A CN201510989318 A CN 201510989318A CN 105586699 A CN105586699 A CN 105586699A
- Authority
- CN
- China
- Prior art keywords
- cloth
- fabric
- double
- gained
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a double-faced fabric and a processing method thereof. The processing method includes the steps that raw cotton is sorted, mixed, separated through blowing-carding equipment, pressed to form a cotton layer, carded through a combing machine, spun into drawn slivers, spun into rough yarn and spun into cheese, gray cloth is manufactured, fuzz on the surface of the gray cloth is burnt off through flames or on the full-hot metal, finally treatment is conducted with caustic lye of soda, fabric is evenly put in a dye vat, glacial acetic acid and neutralization acid are added, dye is added, a sample fabric is obtained through high-temperature vat dyeing, the sample fabric is cleaned, shaped and pre-shrunk, and the finished fabric is obtained. The double-faced fabric is stiff and smooth in fabric, better in anti-wrinkling performance, not prone to pill or wrinkle, more stable in size, good in drooping sense and smoother in hand feeling, has gloss similar to that of silk fabric, and is washable and free of color change; meanwhile, the sweat absorbing performance and breathability of raw cotton fabric are kept, and the processing method effectively improves production efficiency of the double-faced fabric and reduces production cost.
Description
Technical field
The present invention relates to cloth production and processing manufacturing technology field, be specifically related to a kind of double-sided cloth and processing method thereof.
Background technology
Double-sided cloth is the cloth that often will use in people's daily life, in daily life, bring into play huge effect, be applied to a lot of aspects of daily life, such as this fabric can be made stamp, also can make solid color fabric and use, along with economic level improves constantly, people also improve constantly product quality requirement, such as finer and smoother feel, better glossiness, better absorbing sweat gas permeability etc., therefore, we also need product to make the demand that meets people of further improving.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of feel exquisiteness, good double-sided cloth and the processing method thereof of glossiness for above-mentioned the deficiencies in the prior art.
The present invention for addressing the above problem adopted technical scheme is:
The invention provides a kind of double-sided cloth, the cloth composition of described double-sided cloth is cotton cloth.
The processing method that the invention provides a kind of double-sided cloth, comprises the following steps:
(1) raw cotton is carried out to go-on-go, and described raw cotton is removed to matter processing;
(2) raw cotton of choosing in proportion different grades and length mixes;
(3) raw cotton mixing in step (2) is utilized to blowing-carding machinery separates, secondary removal of impurities processing, make the gained raw cotton fiber formation sliver that is arranged in parallel;
(4) gained sliver in step (3) is carried out to combing and make it be separated into ultimate fibre state, and remove impurity residual in lap, fault and short fiber;
(5) gained sliver in step (4) is pressed and forms the cotton layer of uniform broadband shape, described cotton layer passes through and rolls up combination machine and makes cloth lap;
(6) utilize combing machine to divide to gained cloth lap in step (5) and be combed into sliver, described sliver comb is opened, stretched, and remove nonconforming short fiber, impurity and short fiber knot grain;
(7) to gained sliver in step (6) utilize that drawing frame merges, mixing and drawing-off, be spun into ripe;
(8) described in step (7) ripe make its elongation attenuate and twist through 4～12 times of drawing-offs, be spun into rove through fly frame, and by described reeling roving on bobbin;
(9) in step (8), gained rove, through the past drawing-off of 10～50 times, makes it take out long attenuating, and it is formed to cop on bobbin;
(10) described cop forms cheese through automatic winder, removes impurity and fault on yarn simultaneously, and by described cheese through doubling winder around rolling up on spool, recycling two-for-one twister described yarn is twisted;
(11) be woven into embryo cloth with the cheese of gained in step (10);
(12) utilize scutcher that described embryo cloth is cut open along drawn needle limit, more described embryo cloth is passed through to flame or at red-hot burning-off surface, metal surface fine hair, finally process with caustic lye of soda;
(13) to the processing of dyeing of treated embryo cloth in step (12), fabric is evenly dropped into dye vat, add glacial acetic acid and neutralizing acid, then drop into dyestuff, 60～100 DEG C of dye vat temperature, entering the cylinder time is 2～15 hours. .
(14) to described sample cloth clean, sizing and preshrunk obtains finished fabric.
Further, described in step (11), embryo cloth grammes per square metre is 145～150g/m2。
Further, in step (14), described sample cloth being carried out to cleaning process is that described sample Bu Wendu is down to 50 and cleans while spending.
Beneficial effect of the present invention is:
A kind of double-sided cloth provided by the invention fabric compared with traditional double-sided cloth is well-pressed, wrinkle resistance better, it is wrinkling to be difficult for balling-up; Size is more stable, overhangs sense well, and feel is finer and smoother; There is the gloss that silk fabrics is general and wash for a long time nondiscolouring, meanwhile, retained the absorbing sweat permeability of former cotton face fabric, this double-sided cloth processing method has the advantages that operation is succinct, processing cost is low, production efficiency is high, effectively improve the production efficiency of double-sided cloth, saved production cost.
Brief description of the drawings
Fig. 1 is the process chart of a kind of double-sided cloth processing method of the present invention.
Detailed description of the invention
Specifically illustrate embodiments of the present invention below in conjunction with accompanying drawing; the providing of these embodiment is only used to the object of explanation; can not be interpreted as limitation of the invention; comprise that accompanying drawing is only for reference and use is described; do not form the restriction to scope of patent protection of the present invention; because without departing from the spirit and scope of the present invention, can carry out many changes to the present invention.
Embodiment 1
A kind of double-sided cloth that the present embodiment provides, the cloth composition of described double-sided cloth is 100% cotton cloth.
The processing method of a kind of double-sided cloth that as shown in Figure 1, the present embodiment provides comprises the following steps:
(1) raw cotton is carried out to go-on-go, and described raw cotton is removed to matter processing, this operation is by manually carrying out go-on-go to raw cotton, removes general scutcher and is difficult to the impurity of removing, and mainly detects: filoplume, nylon wire, cloth are broken, colo(u)r streak, flax silk etc.;
(2) raw cotton of choosing in proportion different grades and length mixes (ratio that is 85%:15% according to 1 grade of cotton and 2 grades of cotton ratios is carried out proportioning mixing), collocation is used, can give full play to the feature of different material through distributing cotton, reach reasonable use, the object of steady production, raising yarn quality and reduction spinning cost;
(3) raw cotton mixing in step (2) is utilized to blowing-carding machinery separates, secondary removal of impurities processing, removal of contamination, fault and short fiber, make the gained raw cotton fiber formation sliver that is arranged in parallel;
(4) gained sliver in step (3) is carried out to combing and make it be separated into ultimate fibre state, and remove impurity residual in lap, fault and short fiber;
(5) gained sliver in step (4) is pressed and forms the cotton layer of uniform broadband shape, described cotton layer passes through and rolls up combination machine and makes cloth lap, in process, be accompanied by and mix and parallel drafting, make cotton fiber more be tending towards parallel, structure is constantly improved;
(6) utilize combing machine to divide to gained cloth lap in step (5) and be combed into sliver, described sliver comb is opened, stretched, and remove nonconforming short fiber, impurity and short fiber knot grain, so that yarn evenness is even, bright and clean, brute force obviously improves;
(7) to gained sliver in step (6) utilize that drawing frame merges, mixing and drawing-off, be spun into ripe;
(8) described in step (7) ripe make its elongation attenuate and twist through 4 times of drawing-offs, be spun into rove through fly frame, and by described reeling roving on bobbin;
(9) in step (8), gained rove, through the past drawing-off of 10 times, makes it take out long attenuating, and it is formed to cop on bobbin;
(10) described cop forms cheese through automatic winder, remove impurity and fault on yarn simultaneously, and by described cheese through doubling winder two or three cotton yarns and together around rolling up on spool, recycling two-for-one twister is twisted described yarn, so that the yarn of making has the physical properties such as certain brute force, elasticity, gloss;
(11) yarn of twisting in step (10) is made in order, and be enclosed within on mercerising mantle yarn roller, make described cover yarn roller stretching, and rotation makes yarn immerse alkali lye under stretching state, described concentration of lye is 230g/L～270g/L, after lixiviating, making to overlap yarn roller loosens, and described yarn is taken off from roller, clean with cold water, and treated described yarn weaving is become to embryo cloth, fabric width: 52 〞, described embryo cloth grammes per square metre is 145～150g/m2;
(12) utilize scutcher that described embryo cloth is cut open along drawn needle limit, again by described embryo cloth by flame or at burning-off surface, red-hot metal surface fine hair, described embryo cloth is 80m/min by the speed of service of flame or red-hot metal surface, finally processes with caustic lye of soda;
(13) to the processing of dyeing of treated embryo cloth in step (12), fabric is evenly dropped into dye vat, add glacial acetic acid and neutralizing acid, then drop into dyestuff, 95 DEG C of dye vat temperature, entering the cylinder time is 10 hours.
(14) to described sample cloth clean, sizing and preshrunk obtains finished fabric, described sample Bu Wendu is down to 50 and cleans while spending.
Embodiment 2
A kind of double-sided cloth that the present embodiment provides, the cloth composition of described double-sided cloth is 100% cotton cloth.
The processing method of a kind of double-sided cloth that as shown in Figure 1, the present embodiment provides comprises the following steps:
(1) raw cotton is carried out to go-on-go, and described raw cotton is removed to matter processing, this operation is by manually carrying out go-on-go to raw cotton, removes general scutcher and is difficult to the impurity of removing, and mainly detects: filoplume, nylon wire, cloth are broken, colo(u)r streak, flax silk etc.;
(2) raw cotton of choosing in proportion different grades and length mixes (ratio that is 85%:15% according to 1 grade of cotton and 2 grades of cotton ratios is carried out proportioning mixing), collocation is used, can give full play to the feature of different material through distributing cotton, reach reasonable use, the object of steady production, raising yarn quality and reduction spinning cost;
(3) raw cotton mixing in step (2) is utilized to blowing-carding machinery separates, secondary removal of impurities processing, make the gained raw cotton fiber formation sliver that is arranged in parallel;
(4) gained sliver in step (3) is carried out to combing and make it be separated into ultimate fibre state, and remove impurity residual in lap, fault and short fiber;
(5) gained sliver in step (4) is pressed and forms the cotton layer of uniform broadband shape, described cotton layer passes through and rolls up combination machine and makes cloth lap, in process, be accompanied by and mix and parallel drafting, make cotton fiber more be tending towards parallel, structure is constantly improved;
(6) utilize combing machine to divide to gained cloth lap in step (5) and be combed into sliver, described sliver comb is opened, stretched, and remove nonconforming short fiber, impurity and short fiber knot grain, so that yarn evenness is even, bright and clean, brute force obviously improves;
(7) to gained sliver in step (6) utilize that drawing frame merges, mixing and drawing-off, be spun into ripe;
(8) described in step (7) ripe make its elongation attenuate and twist through 8 times of drawing-offs, be spun into rove through fly frame, and by described reeling roving on bobbin;
(9) in step (8), gained rove, through the past drawing-off of 35 times, makes it take out long attenuating, and it is formed to cop on bobbin;
(10) described cop forms cheese through automatic winder, remove impurity and fault on yarn simultaneously, and by described cheese through doubling winder two or three cotton yarns and together around rolling up on spool, recycling two-for-one twister is twisted described yarn, so that the yarn of making has the physical properties such as certain brute force, elasticity, gloss;
(11) yarn of twisting in step (10) is made in order, and be enclosed within on mercerising mantle yarn roller, make described cover yarn roller stretching, and rotation makes yarn immerse alkali lye under stretching state, described concentration of lye is 230g/L～270g/L, after lixiviating, making to overlap yarn roller loosens, and described yarn is taken off from roller, clean with cold water, and treated described yarn weaving is become to embryo cloth, fabric width: 52 〞, described embryo cloth grammes per square metre is 145～150g/m2;
(12) utilize scutcher that described embryo cloth is cut open along drawn needle limit, again by described embryo cloth by flame or at burning-off surface, red-hot metal surface fine hair, described embryo cloth is 120m/min by the speed of service of flame or red-hot metal surface, finally processes with caustic lye of soda;
(13) to the processing of dyeing of treated embryo cloth in step (12), fabric is evenly dropped into dye vat, add glacial acetic acid and neutralizing acid, then drop into dyestuff, 95 DEG C of dye vat temperature, entering the cylinder time is 10 hours.
(14) to described sample cloth clean, sizing and preshrunk obtains finished fabric, described sample Bu Wendu is down to 50 and cleans while spending.
Embodiment 3
A kind of double-sided cloth that the present embodiment provides, the cloth composition of described double-sided cloth is 100% cotton cloth.
The processing method of a kind of double-sided cloth that as shown in Figure 1, the present embodiment provides comprises the following steps:
(1) raw cotton is carried out to go-on-go, and described raw cotton is removed to matter processing, this operation is by manually carrying out go-on-go to raw cotton, removes general scutcher and is difficult to the impurity of removing, and mainly detects: filoplume, nylon wire, cloth are broken, colo(u)r streak, flax silk etc.;
(2) raw cotton of choosing in proportion different grades and length mixes (ratio that is 85%:15% according to 1 grade of cotton and 2 grades of cotton ratios is carried out proportioning mixing), collocation is used, can give full play to the feature of different material through distributing cotton, reach reasonable use, the object of steady production, raising yarn quality and reduction spinning cost;
(3) raw cotton mixing in step (2) is utilized to blowing-carding machinery separates, secondary removal of impurities processing, make the gained raw cotton fiber formation sliver that is arranged in parallel;
(4) gained sliver in step (3) is carried out to combing and make it be separated into ultimate fibre state, and remove impurity residual in lap, fault and short fiber;
(5) gained sliver in step (4) is pressed and forms the cotton layer of uniform broadband shape, described cotton layer passes through and rolls up combination machine and makes cloth lap, in process, be accompanied by and mix and parallel drafting, make cotton fiber more be tending towards parallel, structure is constantly improved;
(6) utilize combing machine to divide to gained cloth lap in step (5) and be combed into sliver, described sliver comb is opened, stretched, and remove nonconforming short fiber, impurity and short fiber knot grain, so that yarn evenness is even, bright and clean, brute force obviously improves;
(7) to gained sliver in step (6) utilize that drawing frame merges, mixing and drawing-off, be spun into ripe;
(8) described in step (7) ripe make its elongation attenuate and twist through 12 times of drawing-offs, be spun into rove through fly frame, and by described reeling roving on bobbin;
(9) in step (8), gained rove, through the past drawing-off of 50 times, makes it take out long attenuating, and it is formed to cop on bobbin;
(10) described cop forms cheese through automatic winder, remove impurity and fault on yarn simultaneously, and by described cheese through doubling winder two or three cotton yarns and together around rolling up on spool, recycling two-for-one twister is twisted described yarn, so that the yarn of making has the physical properties such as certain brute force, elasticity, gloss;
(11) yarn of twisting in step (10) is made in order, and be enclosed within on mercerising mantle yarn roller, make described cover yarn roller stretching, and rotation makes yarn immerse alkali lye under stretching state, described concentration of lye is 230g/L～270g/L, after lixiviating, making to overlap yarn roller loosens, and described yarn is taken off from roller, clean with cold water, and treated described yarn weaving is become to embryo cloth, fabric width: 52 〞, described embryo cloth grammes per square metre is 145～150g/m2;
(12) utilize scutcher that described embryo cloth is cut open along drawn needle limit, again by described embryo cloth by flame or at burning-off surface, red-hot metal surface fine hair, described embryo cloth is 140m/min by the speed of service of flame or red-hot metal surface, finally processes with caustic lye of soda;
(13) to the processing of dyeing of treated embryo cloth in step (12), fabric is evenly dropped into dye vat, add glacial acetic acid and neutralizing acid, then drop into dyestuff, 95 DEG C of dye vat temperature, entering the cylinder time is 10 hours.
(14) to described sample cloth clean, sizing and preshrunk obtains finished fabric, described sample Bu Wendu is down to 50 and cleans while spending.
The made cloth of embodiment 3 is analyzed and found to have that feel is finer and smoother, glossiness is better, the better feature of absorbing sweat permeability, and the method has effectively improved the production efficiency of double-sided cloth simultaneously, has saved production cost.
Above-described embodiment is preferably embodiment of the present invention; but embodiments of the present invention are not restricted to the described embodiments; other any do not deviate from change, the modification done under Spirit Essence of the present invention and principle, substitutes, combination, simplify; all should be equivalent substitute mode, within being included in protection scope of the present invention.
Claims (5)
1. a double-sided cloth, is characterized in that: the cloth composition of described double-sided cloth is cotton cloth.
2. a processing method for double-sided cloth, is characterized in that, comprises the following steps:
(1) raw cotton is carried out to go-on-go, and described raw cotton is removed to matter processing;
(2) raw cotton of choosing in proportion different grades and length mixes;
(3) raw cotton mixing in step (2) is utilized to blowing-carding machinery separates, secondary removal of impurities processing,Make the gained raw cotton fiber formation sliver that is arranged in parallel;
(4) gained sliver in step (3) is carried out to combing and make it be separated into ultimate fibre state, and remove lapIn residual impurity, fault and short fiber;
(5) gained sliver in step (4) is pressed and forms the cotton layer of uniform broadband shape, described cotton layer againPass through and roll up combination machine and make cloth lap;
(6) utilize combing machine to divide to gained cloth lap in step (5) and be combed into sliver, by described sliver combOpen, stretch, and remove nonconforming short fiber, impurity and short fiber knot grain;
(7) to gained sliver in step (6) utilize that drawing frame merges, mixing and drawing-off, be spun into ripe;
(8) described in step (7) ripe through 4～12 times of drawing-offs, make its elongation attenuate and twist, through roveMachine is spun into rove, and by described reeling roving on bobbin;
(9) in step (8), gained rove, through the past drawing-off of 10～50 times, makes it take out long attenuating, and by itOn bobbin, form cop;
(10) described cop forms cheese through automatic winder, removes impurity and fault on yarn simultaneously,And by described cheese through doubling winder around rolling up on spool, recycling two-for-one twister described yarn is twisted;
(11) be woven into embryo cloth with the cheese of gained in step (10);
(12) utilize scutcher that described embryo cloth is cut open along drawn needle limit, then by described embryo cloth by flame or red-hotMetal surface burning-off surface fine hair, finally process with caustic lye of soda;
(13) to the processing of dyeing of treated embryo cloth in step (12), fabric is evenly dropped into dye vat,Add glacial acetic acid and neutralizing acid, then drop into dyestuff, 60～100 DEG C of dye vat temperature, entering the cylinder time is 2～15 hours.
(14) to described sample cloth clean, sizing and preshrunk obtains finished fabric.
3. a kind of double-sided cloth processing method according to claim 2, is characterized in that: step (11)Described in embryo cloth grammes per square metre be 145～150g/m2。
4. a kind of double-sided cloth processing method according to claim 2, is characterized in that: step (12)Described in embryo cloth be 80m/min～140m/min by the speed of service of flame or red-hot metal surface.
5. a kind of double-sided cloth processing method according to claim 2, is characterized in that: step (14)In described sample cloth is carried out to cleaning process is that described sample Bu Wendu cleans while being down to 50 DEG C.