CN109355955A - 包塑抗氧化钢丝绳加工工艺 - Google Patents

包塑抗氧化钢丝绳加工工艺 Download PDF

Info

Publication number
CN109355955A
CN109355955A CN201811226619.9A CN201811226619A CN109355955A CN 109355955 A CN109355955 A CN 109355955A CN 201811226619 A CN201811226619 A CN 201811226619A CN 109355955 A CN109355955 A CN 109355955A
Authority
CN
China
Prior art keywords
plastic
steel cord
processing technology
resistant steel
oxidation resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811226619.9A
Other languages
English (en)
Inventor
王建江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Hieasy Metal Technology Co Ltd
Original Assignee
Jiangsu Hieasy Metal Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Hieasy Metal Technology Co Ltd filed Critical Jiangsu Hieasy Metal Technology Co Ltd
Priority to CN201811226619.9A priority Critical patent/CN109355955A/zh
Publication of CN109355955A publication Critical patent/CN109355955A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种加工工艺，本发明涉及钢丝绳领域，具体涉及一种包塑抗氧化钢丝绳加工工艺，所述包塑抗氧化钢丝绳加工工艺，包括以下步骤：步骤一：预处理；步骤二：拉拔；步骤三：热处理；步骤四：捻股成绳；步骤五：涂装抗氧化层；步骤六：包塑处理；本发明设计合理，提供了一种包塑抗氧化钢丝绳加工工艺，所述包塑抗氧化钢丝绳加工工艺通过在钢丝绳表面涂装抗氧化层隔绝钢丝绳本体长时间暴露在空气中发生氧化，同时通过对钢丝绳进行包塑处理，避免人们直接接触钢丝绳本体发生意外被划伤。

Description

包塑抗氧化钢丝绳加工工艺
技术领域
本发明涉及钢丝绳领域，尤其是涉及包塑抗氧化钢丝绳加工工艺。
背景技术
传统的钢丝绳抗氧化效果一般，钢丝绳长期暴露在空气中容易氧化，导致钢丝绳使用寿命比较短，于此同时，钢丝绳表面比较锋利，人们移动钢丝绳的时候容易发生意外割伤。
发明内容
本发明为解决上述提出到的问题，为此提供了一种包塑包塑抗氧化钢丝绳加工工艺，所述包塑包塑抗氧化钢丝绳加工工艺的步骤包括：
步骤一；预处理：将不锈钢盘条置于放线架上，用机械进行清洁处理，清洁完成后进入涂硼设备进行涂硼处理，最后进入烘干设备烘干，得预处理线材；
步骤二；拉拔：将预处理线材置于拉拔机进行多次拉拔，拉拔完成后收线得到半成品线材；
步骤三；热处理：将拉拔处理后的半成品线材放入热处理炉进行加热处理，加热完成后进行清洗、冷却；
步骤四；拧股成绳：将热处理后的半品线材放于拧股机上进行捻股合绳，得成品钢丝绳；
步骤五；涂装抗氧化层：对钢丝绳表面进行抗氧化层的涂装；
步骤六；包塑处理：将涂装完成后的钢丝绳放在塑料包覆机上进行包塑处理。
作为优选，所述步骤三所述热处理炉的温度在700-800℃范围内。
本发明的有益效果是：本发明设计合理，提供了一种包塑抗氧化钢丝绳加工工艺，所述包塑抗氧化钢丝绳加工工艺通过在钢丝绳表面涂装抗氧化层隔绝钢丝绳本体长时间暴露在空气中发生氧化，同时通过对钢丝绳进行包塑处理，避免人们直接接触钢丝绳本体发生意外被划伤。
具体实施方式
本说明书中公开的所有特征，或公开的所有方法或过程中的步骤，除了互相排斥的特征和/或步骤以外，均可以以任何方式组合。
本说明书的任一特征，除非特别叙述，均可被其他等效或具有类似目的的替代特征加以替换。即，除非特别叙述，每个特征只是一系列等效或类似特征中的一个例子而已。
步骤一；预处理：将不锈钢盘条置于放线架上，用机械进行清洁处理，清洁完成后进入涂硼设备进行涂硼处理，最后进入烘干设备烘干，得预处理线材；
步骤二；拉拔：将预处理线材置于拉拔机进行多次拉拔，拉拔完成后收线得到半成品线材；
步骤三；热处理：将拉拔处理后的半成品线材放入热处理炉进行加热处理，加热完成后进行清洗、冷却；
步骤四；拧股成绳：将热处理后的半品线材放于拧股机上进行捻股合绳，得成品钢丝绳；
步骤五；涂装抗氧化层：对钢丝绳表面进行抗氧化层的涂装；
步骤六；包塑处理：将涂装完成后的钢丝绳放在塑料包覆机上进行包塑处理。
本发明的有益效果是：本发明设计合理，提供了一种包塑抗氧化钢丝绳加工工艺，所述包塑抗氧化钢丝绳加工工艺通过在钢丝绳表面涂装抗氧化层隔绝钢丝绳本体长时间暴露在空气中发生氧化，同时通过对钢丝绳进行包塑处理，避免人们直接接触钢丝绳本体发生意外被划伤。
本发明并不局限于前述的具体实施方式。本发明扩展到任何在本说明书中披露的新特征或任何新的组合，以及披露的任一新的方法或过程的步骤或任何新的组合。

Claims (2)

1.一种包塑抗氧化钢丝绳加工工艺，其特征在于，它包括以下步骤：
步骤一；预处理：将不锈钢盘条置于放线架上，用机械进行清洁处理，清洁完成后进入涂硼设备进行涂硼处理，最后进入烘干设备烘干，得预处理线材；
步骤二；拉拔：将预处理线材置于拉拔机进行多次拉拔，拉拔完成后收线得到半成品线材；
步骤三；热处理：将拉拔处理后的半成品线材放入热处理炉进行加热处理，加热完成后进行清洗、冷却；
步骤四；拧股成绳：将热处理后的半品线材放于拧股机上进行捻股合绳，得成品钢丝绳；
步骤五；涂装抗氧化层：对钢丝绳表面进行抗氧化层的涂装；
步骤六；包塑处理：将涂装完成后的钢丝绳放在塑料包覆机上进行包塑处理。
2.根据权利要求1所述的一种抗氧化钢丝绳加工工艺，其特征在于，所述步骤三所述热处理炉的温度在700-800℃范围内。
CN201811226619.9A 2018-10-22 2018-10-22 包塑抗氧化钢丝绳加工工艺 Withdrawn CN109355955A (zh)