CN1093150C - 一种聚氯乙烯组合物 - Google Patents

一种聚氯乙烯组合物 Download PDF

Info

Publication number
CN1093150C
CN1093150C CN97106545A CN97106545A CN1093150C CN 1093150 C CN1093150 C CN 1093150C CN 97106545 A CN97106545 A CN 97106545A CN 97106545 A CN97106545 A CN 97106545A CN 1093150 C CN1093150 C CN 1093150C
Authority
CN
China
Prior art keywords
pvc
polyvinyl chloride
molecular sieve
chloride resin
resin material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN97106545A
Other languages
English (en)
Other versions
CN1207400A (zh
Inventor
闫里选
张为民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Chlor Alkali Chemical Co Ltd
Original Assignee
Shanghai Chlor Alkali Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Chlor Alkali Chemical Co Ltd filed Critical Shanghai Chlor Alkali Chemical Co Ltd
Priority to CN97106545A priority Critical patent/CN1093150C/zh
Publication of CN1207400A publication Critical patent/CN1207400A/zh
Application granted granted Critical
Publication of CN1093150C publication Critical patent/CN1093150C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种新型聚氯乙烯(PVC)加工助剂粉末状铝硅酸盐分子筛，该PVC助剂较大地提高了PVC树脂的凝胶化能力，有效地降低了PVC树脂物料的粘度，提高了PVC树脂材料的缺口冲击强度和延伸率，改善了PVC材料的物理机械性能，降低了PVC材料的生产成本。该助剂应用在软质PVC专用料和硬质PVC专用料的生产中，现已应用于建筑用管材、板材，电缆绝缘套管和纺织纱管等PVC产品的生产。

Description

一种聚氯乙烯组合物
本发明涉及一种新型聚氯乙烯(PVC)加工助剂，具体地说涉及一种粉末状铝硅酸盐分子筛PVC加工助剂。
在PVC加工领域，特别是硬质PVC加工中，加工助剂是与之配套的重要材料，目前PVC加工助剂中以丙烯酸酯类(ACR)应用最为广泛。如德国的R·盖希特编著的《塑料添加剂手册》(1992年3月中国石化出版社出版)中讲到，聚丙烯酸酯(ACR)作为PVC抗冲击改性剂具有比较理想的性能，它能提高PVC树脂的凝胶化能力，改善PVC树脂的物理机械性能，提高缺口冲击强度，并且能改善耐光、耐侯和耐老化性。目前，国内的ACR年生产能力约3500吨，难以满足工业生产的需要。而且，ACR的价格偏高，用它作助剂的PVC制品成本相对较高。
本发明的目的是提供一种新型的PVC加工助剂，该PVC加工助剂是粉末状铝硅酸盐分子筛，该助剂较大地提高PVC树脂的凝胶化能力，改进了PVC树脂的加工性能和物理机械性能，提高了PVC树脂的抗冲击性能。而且，该加工助剂价格低廉，具有较强的市场竞争能力。
本发明是这样买现的，这种新型的聚氯乙烯(PVC)加工助剂是粉末状铝硅酸盐分子筛无机化合物，其最小单胞可由下述化学分子式表示：
      Mx/n[(AlO2)x·(SiO2)y]·wH2O
式中：M表示碱金属阳离子，如Li、Na、K或碱土金属阳离子如
      Ba、Ca、Mg，
      w为整数，表示每个单胞中的水分子数，
      x为整数；表示每个单胞中AlO2四面体的总数，
    y为整数，表示每个单胞中SiO2四面体的总数，且y/x≥1，
    n表示阳离子M的价数。
本发明的粉末状铝硅酸盐分子式是A型分子筛，其最小单胞的化学分子式为：Na12(AlO2)12(SiO2)12·27H2O
本发明的新型PVC加工助剂粉末状铝硅酸盐分子筛用于软质PVC或硬质PVC专用料的配方组成(重量份)如下：
PVC树脂                                 100
三盐基硫酸铅(3PbO·PbSO4·H2O)        3.2～4.2
二盐基亚磷酸铅(2PbO·PbHPO4·1/2H2O)  0.8～1.4
硬脂酸铅(C17H35COO)2Pb               0.3～0.7
硬脂酸(C17H35COOH)                    0.3～0.7
石蜡                                    0.1～0.2
粉末状铅硅酸盐分子筛                    3～8
分子筛因其结构中有与小分子直径相当的孔结构，广泛用于吸附和分离领域。粉末状铝硅酸盐分子筛为白色超细粉末，其结构为硅氧四面体和铝氧四面体组成的无机高分子化合物。用本发明的粉末状铝硅酸盐分子筛作为PVC加工助剂，在PVC树脂中的分散性较好，增强了分子筛和PVC高分子结构的键合能力。从而使PVC树脂中有机-无机混合体系中的粘度降低，提高PVC树脂的流动性和塑化性能，有效地提高PVC树脂的凝胶化能力，明显地缩短PVC物料的塑化时间。分散在PVC树脂中的粉末状分子筛小颗粒可以形成连接PVC树脂分子链的结点，有利于形成PVC树脂的三维网络结构，使PVC树脂的力学性能有所改善。其中，冲击强度和延伸率有一定程度的提高。
本发明的新型PVC加工助剂粉末状铝硅酸盐A型分子筛(以下简称分子筛)和现有技术中以丙烯酸酯(ACR)为加工助剂对PVC树脂的凝胶化能力的影响经测试，结果如下：试验的基体配方(重量份)：
PVC树脂             100
三盐基硫酸铅        3.2
二盐基亚磷酸铅      0.8
硬脂酸铅            0.3
石蜡                0.1在Brabender转矩流变仪测得的流变性能如下：
    试样 塑化时间(秒) 最大扭矩(牛顿) 平衡扭矩(牛顿)
基体配方     88     41.8     23.5
添加3份分子筛     30     53.4     22.5
添加5份分子筛     26     54.9     22.9
添加3份ACR     56     46.7     25.2
添加5份ACR     60     51.2     26.5
由以上结果可以看出，当PVC树脂加工中使用了分子筛加工助剂后，物料的塑化时间明显缩短，且小于添加相同份数的ACR，因此本发明的分子筛对提高PVC树脂的凝胶化能力是比较显著的。另外，当物料熔融后，分子筛所兼有的润滑功能可有效地降低物料的粘度。
本发明的分子筛和现有技术中的丙烯酸酯(ACR)为加工助剂对PVC树脂的物理机械性能的影响经测试，结果如下：
试验的基体配方同前凝胶化能力测试。
加入不同类型加工助剂后，PVC树脂材料的力学性能如下：
    试样 冲击强度(KJ/M2) 拉伸强度(MPa)   延伸率(％)
基体配方     5.00     54.85     11.5
添加3份分子筛     6.20     55.76     24.0
添加5份分子筛     6.48     51.90     34.8
添加3份ACR     5.55     58.19     22.4
添加5份ACR     5.02     58.95     12.0
由以上结果可以看出，加入本发明分子筛的PVC材料的缺口冲击强度、延伸率均有一定程度的提高，对拉伸强度影响较小。从抗冲性能看，添加分子筛比添加ACR的效果好。
本发明的新型PVC加工助剂分子筛与现有技术中的丙烯酸酯类(ACR)加工助剂相比具有如下优点：一、提高了PVC树脂的凝胶化能力，并能有效地降低PVC树脂物料的粘度。二、提高了PVC树脂材料的缺口冲击强度和延伸率，对拉伸强度影响较小，改进了PVC材料的物理机械性能。三、由于本发明的分子筛价格比ACR低，降低了生产成本，因此具有较强的市场竞争力。
本发明的新型PVC加工助剂粉末状铝硅酸盐分子筛应用在软质PVC专用料和硬质PVC专用料的生产中。现已用于电线绝缘套管、建筑用管材、板材和纺织纱管等产品生产。
下面是本发明新型PVC加工助剂粉末状铝硅酸盐A型分子筛[Na12(AlO2)12(SiO2)12·27H2O]应用于PVC树脂中的几个实施例(各组份为重量份)。
    组成   实施例1   实施例2   实施例3
PVC树脂     100     100     100
三盐基硫酸铅     3.2     3.8     4.2
二盐基亚磷酸铅     0.8     1.2     1.4
硬脂酸铅     0.7     0.5     0.3
硬脂酸     0.3     0.5     0.7
石蜡     0.2     0.1     /
A型分子筛     3     5     8

Claims (1)

1、一种聚氯乙烯组合物，其特征在于该组合物的配方组成(重量份)如下：
聚氯乙烯树脂                       100
粉末状铝硅酸盐分子筛               3～8
三盐基硫酸铅                       3.2～4.2
二盐基亚磷酸铅                     0.8～1.4
硬脂酸铅                           0.3～0.7
硬脂酸                             0.3～0.7
石蜡                               0.1～0.2
CN97106545A 1997-08-01 1997-08-01 一种聚氯乙烯组合物 Expired - Fee Related CN1093150C (zh)