CN109280538A - 一种树干用粘虫胶 - Google Patents
一种树干用粘虫胶 Download PDFInfo
- Publication number
- CN109280538A CN109280538A CN201811104036.9A CN201811104036A CN109280538A CN 109280538 A CN109280538 A CN 109280538A CN 201811104036 A CN201811104036 A CN 201811104036A CN 109280538 A CN109280538 A CN 109280538A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixing
- mass ratio
- insect sticker
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种树干用粘虫胶，属于病虫害防治技术领域。本发明以聚乙二醇、N，N‑二甲基丙烯酰胺等原料，合成氢键增强的抗撕裂形状记忆水凝胶基料，具有良好的拉伸性能并且不需外来添加物的实现驱动，实现很好的抗拉伸效果；加入的自制辅剂具有双亲性，在体系中可自组装形成囊泡，与环保的黏虫、杀虫效果、植物的光合作用及其自身生长相关联，构成环保多关联的粘虫胶体系；对天牛进行预处理培养，刺激其体内胃液及类激素化合物的分泌，配合本胶体的多孔结构，避免自身的霉变，进而长效保持高抗拉伸及环保性能。本发明解决了目前常用粘虫胶的抗拉伸及环保性不佳的问题。
Description
技术领域
本发明涉及一种树干用粘虫胶，属于病虫害防治技术领域。
背景技术
随着社会的发展，人们对环保意识的增强，人们逐渐发现使用化学农药会对环境和生态系统产生破坏性的影响。所谓的无公害防治方法是指防治措施对人、畜、禽、鱼、蜜蜂及有益昆虫(即害虫的天敌)安全无伤害，同时对生态平衡无破坏作用，农产品符合无公害农业要求。所以，现在对于影响农林业生产的害虫的防治也由单纯依靠化学方法转向无公害的防治方法。因此，利用无公害的防治方法在农林业的病虫害防治中显得尤为重要。利用许多害虫具有上下树的习性，在树干涂抹无公害粘虫胶进行害虫的防治，可以收到事半功倍的效果。因此，研究和应用无公害防治措施，减少害虫防治造成的环境污染，已经成为人们共识，也是今后发展方向。利用粘虫胶防治森林病虫害作为无公害防治方法之一，越来越受到人们的重视。但是现在已商业化的粘虫胶板产品，都不同程度的存在不易施工、有刺激性气味、抗拉伸弱易流淌、粘性差、使用期短等缺点，因此，不能满足人们的需求。
发明内容
本发明所要解决的技术问题：针对目前常用粘虫胶的抗拉伸及环保性不佳的问题，提供一种树干用粘虫胶。
为解决上述技术问题，本发明采用如下所述的技术方案是：
一种树干用粘虫胶，按质量份数计，包括如下组分：10~15份酚醛树脂、6~10份环氧树脂、4~8份微晶石蜡、5~10份十二烷基苯磺酸钠、2~5份助剂，还包括：25~40份复合粘虫胶基料、12~20份复合诱虫成分。
所述复合粘虫胶基料的制备方法，包括如下步骤：
（1）于25~35℃，按质量比1：6~10：13取聚乙二醇、二氯乙烷、三乙胺混合，搅拌，移至冰水浴，加入聚乙烯醇质量12~20倍的试剂A混合振荡，移出冰水浴，室温静置，过滤，取滤液按质量比7~12：5加入2~5℃的乙醚混合，静置，抽滤，取滤渣干燥，得干燥物；
（2）按质量比3：1~2：15~25：5取2-乙烯基-4,6-二氨基-1,3,5-三嗪、N,N-二甲基丙烯酰胺、二甲基亚砜、干燥物混合搅拌，加入干燥物质量8~15%的TiO2、干燥物质量3~6倍的自制辅剂、干燥物质量18~30%的2-羟基-4-(2-羟乙氧基)-2-甲基苯丙酮混合，紫外光交联引发处理，水浸，出料，即得复合粘虫胶基料。
所述步骤（1）中的试剂A：按质量比1：3~6：15取丙烯酰氯、二氯甲烷、水混合，即得试剂A。
所述步骤（2）中的自制辅剂：自制辅剂：于35~45℃，按重量份数计，取60~80份（N-脒基）十二烷基丙烯酰胺、30~50份聚乙二醇磷酸酯、4~8份对二氯苯于CO2气氛下混合搅拌，即得自制辅剂。
所述复合诱虫成分的制备方法，包括如下步骤：
S1.按质量份数计，取10~15份预处理天牛料、3~6份巴氏芽孢杆菌粉、6~10份葡萄糖、2~5份NaH2PO4、7~15份牛肉膏蛋白胨、4~8份蜂蜜、8~14份麸皮、150~200份水于密闭混合，于28~32℃，振荡摇床，培养4~7天，过滤，取滤液灭菌，真空蒸发，得浓缩液，于35~45℃，取浓缩液按质量比6：1：0.2~0.5加入植物精油、氯菊酯混合，得混合料；
S2.按质量比为5：1~3：0.3：20~30取混合料、胶料、辛烯基琥珀酸淀粉钠、水混合，剪切分散，得乳液，取乳液加入乳液质量8~12%的硫酸钠溶液混合搅拌，降温至20~28℃，加入乳液质量8~12%的甲醛溶液，用试剂B调节pH，室温静置，抽滤，取滤渣水洗，抽真空干燥，即得复合诱虫成分。
所述步骤S1中的预处理天牛料：取天牛成虫用木屑喂养3~5天，在喂养过程中，每隔4~7h用天牛成虫质量2~4倍的山楂汁对其进行喷淋，培养完成，得预培养天牛成虫，取预培养天牛成虫按质量比6~10：1加入无水乙醇混合，研磨，即得预处理天牛料。
所述步骤S1中的植物精油：茉莉花精油、山茶花精油、腊梅花精油中的任意一种。
所述步骤S2中的胶料：按质量比5：1~3：1取桃胶、紫胶、阿胶混合，即得胶料。
所述步骤S2中的试剂B：按质量比1：10~15取NaOH溶液、碳酸钠溶液混合，即得试剂B。
所述助剂：按质量比1：4~8：3取防老剂RD、松香、凡士林混合，即得助剂。
本发明与其他方法相比，有益技术效果是：
（1）本发明以聚乙二醇、N，N-二甲基丙烯酰胺等原料，合成氢键增强的抗撕裂形状记忆水凝胶基料，具有良好的拉伸性能，在其单体共聚过程中，可形成强弱不同的氢键作用，其中强氢键对凝胶网络具有增强作用、弱氢键可提高凝胶网络能量分散效果，二者协同作用获得了高强度抗撕裂的水凝胶，同时，部分氢键可在CO2的作用下发生氢键的解离和重建，从而凝胶在CO2的作用下会有可逆的体积及模量改变，而通过日间升温作用及加入TiO2的光催化作用，可释放CO2使得本体系具有形状记忆效应，并且不需外来添加物的实现驱动，实现很好的抗拉伸效果；
（2）本发明加入的自制辅剂具有双亲性，在体系中可自组装形成囊泡，其结构中的脒基团也可在与CO2作用中带上电荷，在同种电荷相互排斥作用下，使得体系囊泡腔体增大，对粘附的虫类起到包覆作用，CO2的来源来自于树木及粘附虫类的呼吸作用，而在日间光合作用下，树木吸收CO2，胶体升温过程中释放部分CO2，造成局部浓度高，可对所吸附的虫起到窒息杀灭作用，同时有利于提高植物光合作用吸收CO2的能力，进而本发明可起到对温室气体CO2的贮存、释放处理，并且与环保的黏虫、杀虫效果、植物的光合作用及其自身生长相关联，构成环保多关联的粘虫胶体系；
（3）本发明对天牛进行预处理培养，刺激其体内胃液及类激素化合物的分泌，接着粉碎，与巴氏芽孢杆菌粉等混合发酵，产生多种有机质及暴露培养后天牛体内的类激素信息物，对虫类具有吸引作用，胶料的加入可提高对于树干的亲和性及粘性，巴氏芽孢杆菌发酵过程中也可产生多种抑菌多肽，配合本胶体的多孔结构，避免自身的霉变，进而长效保持高抗拉伸及环保性能。
具体实施方式
试剂A：按质量比1：3~6：15取丙烯酰氯、二氯甲烷、水混合，即得试剂A。
试剂B：按质量比1：10~15取质量分数为20%的NaOH溶液、浓度0.1mol/L的碳酸钠溶液混合，即得试剂B。
自制辅剂：于35~45℃，按重量份数计，取60~80份（N-脒基）十二烷基丙烯酰胺、30~50份聚乙二醇磷酸酯、4~8份对二氯苯于CO2气氛下混合，以400~700r/min磁力搅拌40~60min，即得自制辅剂。
胶料：按质量比5：1~3：1取桃胶、紫胶、阿胶混合，即得胶料。
预处理天牛料：取天牛成虫用木屑喂养3~5天，在喂养过程中，每隔4~7h用天牛成虫质量2~4倍的山楂汁对其进行喷淋，培养完成后，得预培养天牛成虫，取预培养天牛成虫按质量比6~10：1加入无水乙醇混合，于碾磨机以350~600r/min研磨1~3h，即得预处理天牛料。
植物精油：茉莉花精油、山茶花精油、腊梅花精油中的任意一种。
助剂：按质量比1：4~8：3取防老剂RD、松香、凡士林混合，即得助剂。
复合粘虫胶基料的制备方法，包括如下步骤：
（1）于25~35℃，按质量比1：6~10：13取聚乙二醇、二氯乙烷、三乙胺混合，以350~600r/min磁力搅拌30~55min后，移至冰水浴，加入聚乙烯醇质量12~20倍的试剂A混合，以250~300r/min振荡25~50min，移出冰水浴，室温静置20~24h，过滤，取滤液按质量比7~12：5加入2~5℃的乙醚混合，静置15~30min后，抽滤，取滤渣于60~80℃烘箱干燥4~8h，得干燥物；
（2）按质量比3：1~2：15~25：5取2-乙烯基-4,6-二氨基-1,3,5-三嗪、N,N-二甲基丙烯酰胺、二甲基亚砜、干燥物于反应釜混合，以500~800r/min磁力搅拌30~60min，加入干燥物质量8~15%的TiO2、干燥物质量3~6倍的自制辅剂、干燥物质量18~30%的2-羟基-4-(2-羟乙氧基)-2-甲基苯丙酮混合，移至透明塑料模具中用紫外光交联引发30~45min，移至盛有去离子水的容器室温浸泡1~3天，出料，即得复合粘虫胶基料。
复合诱虫成分的制备方法，包括如下步骤：
S1.按质量份数计，取10~15份预处理天牛料、3~6份巴氏芽孢杆菌粉、6~10份葡萄糖、2~5份NaH2PO4、7~15份牛肉膏蛋白胨、4~8份蜂蜜、8~14份麸皮、150~200份无菌水于密闭发酵罐混合，于28~32℃，以180~220r/min振荡摇床，培养4~7天，过滤，取滤液用紫光灯灭菌后，于45~60℃真空蒸发至原体积的30~45%，得浓缩液，于35~45℃，取浓缩液按质量比6：1：0.2~0.5加入植物精油、氯菊酯混合，得混合料；
S2.按质量比为5：1~3：0.3：20~30取混合料、胶料、辛烯基琥珀酸淀粉钠、去离子水混合，以2000~3000r/min剪切分散10~15min，得乳液，取乳液加入乳液质量8~12%的浓度0.1mol/L的硫酸钠溶液混合搅拌，降温至20~28℃，加入乳液质量8~12%的质量分数为37%的甲醛溶液，用试剂B调节pH至9.2~9.6，室温静置20~24h，抽滤，取滤渣用去离子水清洗3~5次后，于30~45℃抽真空干燥，即得复合诱虫成分。
一种树干用粘虫胶，按质量份数计，包括如下组分：10~15份酚醛树脂、6~10份环氧树脂、4~8份微晶石蜡、5~10份十二烷基苯磺酸钠、2~5份助剂、25~40份复合粘虫胶基料、12~20份复合诱虫成分。
一种树干用粘虫胶的制备方法，包括如下步骤：
（1）按质量份数计，取10~15份酚醛树脂、6~10份环氧树脂、4~8份微晶石蜡、5~10份十二烷基苯磺酸钠、2~5份助剂、25~40份复合粘虫胶基料、12~20份复合诱虫成分；
（2）于25~40℃，先取酚醛树脂、环氧树脂、微晶石蜡、十二烷基苯磺酸钠、复合诱虫成分于反应釜混合，以500~800r/min磁力搅拌40~60min，升温至90~110℃，加入助剂、复合粘虫胶基料混合，以2000~3000r/min剪切分散6~10min，即得树干用粘虫胶。
试剂A：按质量比1：3：15取丙烯酰氯、二氯甲烷、水混合，即得试剂A。
试剂B：按质量比1：10取质量分数为20%的NaOH溶液、浓度0.1mol/L的碳酸钠溶液混合，即得试剂B。
自制辅剂：于35℃，按重量份数计，取60份（N-脒基）十二烷基丙烯酰胺、30份聚乙二醇磷酸酯、4份对二氯苯于CO2气氛下混合，以400r/min磁力搅拌40min，即得自制辅剂。
胶料：按质量比5：1：1取桃胶、紫胶、阿胶混合，即得胶料。
预处理天牛料：取天牛成虫用木屑喂养3天，在喂养过程中，每隔4h用天牛成虫质量2倍的山楂汁对其进行喷淋，培养完成后，得预培养天牛成虫，取预培养天牛成虫按质量比6：1加入无水乙醇混合，于碾磨机以350r/min研磨1h，即得预处理天牛料。
植物精油：茉莉花精油。
助剂：按质量比1：4：3取防老剂RD、松香、凡士林混合，即得助剂。
复合粘虫胶基料的制备方法，包括如下步骤：
（1）于25℃，按质量比1：6：13取聚乙二醇、二氯乙烷、三乙胺混合，以350r/min磁力搅拌30min后，移至冰水浴，加入聚乙烯醇质量12倍的试剂A混合，以250r/min振荡25min，移出冰水浴，室温静置20h，过滤，取滤液按质量比7：5加入2℃的乙醚混合，静置15min后，抽滤，取滤渣于60℃烘箱干燥4h，得干燥物；
（2）按质量比3：1：15：5取2-乙烯基-4,6-二氨基-1,3,5-三嗪、N,N-二甲基丙烯酰胺、二甲基亚砜、干燥物于反应釜混合，以500r/min磁力搅拌30min，加入干燥物质量8%的TiO2、干燥物质量3倍的自制辅剂、干燥物质量18%的2-羟基-4-(2-羟乙氧基)-2-甲基苯丙酮混合，移至透明塑料模具中用紫外光交联引发30min，移至盛有去离子水的容器室温浸泡1天，出料，即得复合粘虫胶基料。
复合诱虫成分的制备方法，包括如下步骤：
S1.按质量份数计，取10份预处理天牛料、3份巴氏芽孢杆菌粉、6份葡萄糖、2份NaH2PO4、7份牛肉膏蛋白胨、4份蜂蜜、8份麸皮、150份无菌水于密闭发酵罐混合，于28℃，以180r/min振荡摇床，培养4天，过滤，取滤液用紫光灯灭菌后，于45℃真空蒸发至原体积的30%，得浓缩液，于35℃，取浓缩液按质量比6：1：0.2加入植物精油、氯菊酯混合，得混合料；
S2.按质量比为5：1：0.3：20取混合料、胶料、辛烯基琥珀酸淀粉钠、去离子水混合，以2000r/min剪切分散10min，得乳液，取乳液加入乳液质量8%的浓度0.1mol/L的硫酸钠溶液混合搅拌，降温至20℃，加入乳液质量8%的质量分数为37%的甲醛溶液，用试剂B调节pH至9.2，室温静置20h，抽滤，取滤渣用去离子水清洗3次后，于30℃抽真空干燥，即得复合诱虫成分。
一种树干用粘虫胶，按质量份数计，包括如下组分：10份酚醛树脂、6份环氧树脂、4份微晶石蜡、5份十二烷基苯磺酸钠、2份助剂、25份复合粘虫胶基料、12份复合诱虫成分。
一种树干用粘虫胶的制备方法，包括如下步骤：
（1）按质量份数计，取10份酚醛树脂、6份环氧树脂、4份微晶石蜡、5份十二烷基苯磺酸钠、2份助剂、25份复合粘虫胶基料、12份复合诱虫成分；
（2）于25℃，先取酚醛树脂、环氧树脂、微晶石蜡、十二烷基苯磺酸钠、复合诱虫成分于反应釜混合，以500r/min磁力搅拌40min，升温至90℃，加入助剂、复合粘虫胶基料混合，以2000r/min剪切分散6min，即得树干用粘虫胶。
试剂A：按质量比1：6：15取丙烯酰氯、二氯甲烷、水混合，即得试剂A。
试剂B：按质量比1：15取质量分数为20%的NaOH溶液、浓度0.1mol/L的碳酸钠溶液混合，即得试剂B。
自制辅剂：于45℃，按重量份数计，取80份（N-脒基）十二烷基丙烯酰胺、50份聚乙二醇磷酸酯、8份对二氯苯于CO2气氛下混合，以700r/min磁力搅拌60min，即得自制辅剂。
胶料：按质量比5：3：1取桃胶、紫胶、阿胶混合，即得胶料。
预处理天牛料：取天牛成虫用木屑喂养5天，在喂养过程中，每隔7h用天牛成虫质量4倍的山楂汁对其进行喷淋，培养完成后，得预培养天牛成虫，取预培养天牛成虫按质量比10：1加入无水乙醇混合，于碾磨机以600r/min研磨3h，即得预处理天牛料。
植物精油：山茶花精油。
助剂：按质量比1：8：3取防老剂RD、松香、凡士林混合，即得助剂。
复合粘虫胶基料的制备方法，包括如下步骤：
（1）于35℃，按质量比1：10：13取聚乙二醇、二氯乙烷、三乙胺混合，以600r/min磁力搅拌55min后，移至冰水浴，加入聚乙烯醇质量20倍的试剂A混合，以300r/min振荡50min，移出冰水浴，室温静置24h，过滤，取滤液按质量比12：5加入5℃的乙醚混合，静置30min后，抽滤，取滤渣于80℃烘箱干燥8h，得干燥物；
（2）按质量比3：2：25：5取2-乙烯基-4,6-二氨基-1,3,5-三嗪、N,N-二甲基丙烯酰胺、二甲基亚砜、干燥物于反应釜混合，以800r/min磁力搅拌60min，加入干燥物质量15%的TiO2、干燥物质量6倍的自制辅剂、干燥物质量30%的2-羟基-4-(2-羟乙氧基)-2-甲基苯丙酮混合，移至透明塑料模具中用紫外光交联引发45min，移至盛有去离子水的容器室温浸泡3天，出料，即得复合粘虫胶基料。
复合诱虫成分的制备方法，包括如下步骤：
S1.按质量份数计，取15份预处理天牛料、6份巴氏芽孢杆菌粉、10份葡萄糖、5份NaH2PO4、15份牛肉膏蛋白胨、8份蜂蜜、14份麸皮、200份无菌水于密闭发酵罐混合，于32℃，以220r/min振荡摇床，培养7天，过滤，取滤液用紫光灯灭菌后，于60℃真空蒸发至原体积的45%，得浓缩液，于45℃，取浓缩液按质量比6：1：0.5加入植物精油、氯菊酯混合，得混合料；
S2.按质量比为5：3：0.3：30取混合料、胶料、辛烯基琥珀酸淀粉钠、去离子水混合，以3000r/min剪切分散15min，得乳液，取乳液加入乳液质量12%的浓度0.1mol/L的硫酸钠溶液混合搅拌，降温至28℃，加入乳液质量12%的质量分数为37%的甲醛溶液，用试剂B调节pH至9.6，室温静置24h，抽滤，取滤渣用去离子水清洗5次后，于45℃抽真空干燥，即得复合诱虫成分。
一种树干用粘虫胶，按质量份数计，包括如下组分：15份酚醛树脂、10份环氧树脂、8份微晶石蜡、10份十二烷基苯磺酸钠、5份助剂、40份复合粘虫胶基料、20份复合诱虫成分。
一种树干用粘虫胶的制备方法，包括如下步骤：
（1）按质量份数计，取15份酚醛树脂、10份环氧树脂、8份微晶石蜡、10份十二烷基苯磺酸钠、5份助剂、40份复合粘虫胶基料、20份复合诱虫成分；
（2）于40℃，先取酚醛树脂、环氧树脂、微晶石蜡、十二烷基苯磺酸钠、复合诱虫成分于反应釜混合，以800r/min磁力搅拌60min，升温至110℃，加入助剂、复合粘虫胶基料混合，以3000r/min剪切分散10min，即得树干用粘虫胶。
试剂A：按质量比1：5：15取丙烯酰氯、二氯甲烷、水混合，即得试剂A。
试剂B：按质量比1：13取质量分数为20%的NaOH溶液、浓度0.1mol/L的碳酸钠溶液混合，即得试剂B。
自制辅剂：于40℃，按重量份数计，取70份（N-脒基）十二烷基丙烯酰胺、40份聚乙二醇磷酸酯、6份对二氯苯于CO2气氛下混合，以500r/min磁力搅拌50min，即得自制辅剂。
胶料：按质量比5：2：1取桃胶、紫胶、阿胶混合，即得胶料。
预处理天牛料：取天牛成虫用木屑喂养4天，在喂养过程中，每隔6h用天牛成虫质量3倍的山楂汁对其进行喷淋，培养完成后，得预培养天牛成虫，取预培养天牛成虫按质量比8：1加入无水乙醇混合，于碾磨机以500r/min研磨2h，即得预处理天牛料。
植物精油：腊梅花精油。
助剂：按质量比1：6：3取防老剂RD、松香、凡士林混合，即得助剂。
复合粘虫胶基料的制备方法，包括如下步骤：
（1）于30℃，按质量比1：8：13取聚乙二醇、二氯乙烷、三乙胺混合，以500r/min磁力搅拌45min后，移至冰水浴，加入聚乙烯醇质量17倍的试剂A混合，以282r/min振荡29min，移出冰水浴，室温静置22h，过滤，取滤液按质量比11：5加入3℃的乙醚混合，静置20min后，抽滤，取滤渣于70℃烘箱干燥6h，得干燥物；
（2）按质量比3：1.5：21：5取2-乙烯基-4,6-二氨基-1,3,5-三嗪、N,N-二甲基丙烯酰胺、二甲基亚砜、干燥物于反应釜混合，以600r/min磁力搅拌50min，加入干燥物质量12%的TiO2、干燥物质量5倍的自制辅剂、干燥物质量20%的2-羟基-4-(2-羟乙氧基)-2-甲基苯丙酮混合，移至透明塑料模具中用紫外光交联引发40min，移至盛有去离子水的容器室温浸泡2天，出料，即得复合粘虫胶基料。
复合诱虫成分的制备方法，包括如下步骤：
S1.按质量份数计，取13份预处理天牛料、5份巴氏芽孢杆菌粉、8份葡萄糖、3份NaH2PO4、11份牛肉膏蛋白胨、6份蜂蜜、12份麸皮、170份无菌水于密闭发酵罐混合，于30℃，以200r/min振荡摇床，培养5天，过滤，取滤液用紫光灯灭菌后，于50℃真空蒸发至原体积的40%，得浓缩液，于40℃，取浓缩液按质量比6：1：0.3加入植物精油、氯菊酯混合，得混合料；
S2.按质量比为5：2：0.3：25取混合料、胶料、辛烯基琥珀酸淀粉钠、去离子水混合，以2500r/min剪切分散13min，得乳液，取乳液加入乳液质量10%的浓度0.1mol/L的硫酸钠溶液混合搅拌，降温至23℃，加入乳液质量11%的质量分数为37%的甲醛溶液，用试剂B调节pH至9.4，室温静置22h，抽滤，取滤渣用去离子水清洗4次后，于40℃抽真空干燥，即得复合诱虫成分。
一种树干用粘虫胶，按质量份数计，包括如下组分：12份酚醛树脂、8份环氧树脂、6份微晶石蜡、7份十二烷基苯磺酸钠、3份助剂、30份复合粘虫胶基料、15份复合诱虫成分。
一种树干用粘虫胶的制备方法，包括如下步骤：
（1）按质量份数计，取12份酚醛树脂、8份环氧树脂、6份微晶石蜡、7份十二烷基苯磺酸钠、3份助剂、35份复合粘虫胶基料、15份复合诱虫成分；
（2）于30℃，先取酚醛树脂、环氧树脂、微晶石蜡、十二烷基苯磺酸钠、复合诱虫成分于反应釜混合，以600r/min磁力搅拌50min，升温至100℃，加入助剂、复合粘虫胶基料混合，以2500r/min剪切分散8min，即得树干用粘虫胶。
对比例1：与实施例1的制备方法基本相同，唯有不同的是缺少复合粘虫胶基料。
对比例2：与实施例1的制备方法基本相同，唯有不同的是缺少复合诱虫成分。
对比例3：上海市某公司生产的树干用粘虫胶。
将上述实施例与对比例得到的树干用粘虫胶进行检测，具体检测方法如下：1.初粘性：按照GB/T4852—2002滚球法，采用CZY-G型初粘性测试仪测试；2.持粘性：将粘虫胶在120℃熔化，辊涂在黄色塑料板上，涂层厚度2mm，放入35℃耐黄变试验机中，用200W仿太阳光UV灯照射72h，测试粘性保持时间；3.抗拉伸性能：将粘虫胶在120℃熔化，辊涂在黄色塑料板上，涂层厚度2mm，55℃下竖 直放置24h，并计算垂流距离，垂流距离越长拉伸性能越不好；4.环保性：闻有无刺鼻味道，得到的结果如表1所示。
表1：
| 检测项目 | 实施例1 | 实施例2 | 实施例3 | 对比例1 | 对比例2 | 对比例3 |
| 初粘力/球号 | 22 | 19 | 21 | 14 | 17 | 10 |
| 粘性保持时间/d | 72 | 65 | 68 | 50 | 52 | 45 |
| 垂流距离/mm | 0 | 1.3 | 1.5 | 4.8 | 3.9 | 5.2 |
| 有无刺鼻味道 | 无 | 无 | 无 | 无 | 无 | 有点刺鼻 |
综合上述，从表1可以看出本发明的树干用粘虫胶效果更好，值得推广使用，以上所述仅为本发明的较佳方式，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含再本发明的保护范围之内。
Claims (10)
1.一种树干用粘虫胶，按质量份数计，包括如下组分：10~15份酚醛树脂、6~10份环氧树脂、4~8份微晶石蜡、5~10份十二烷基苯磺酸钠、2~5份助剂，其特征在于，还包括：25~40份复合粘虫胶基料、12~20份复合诱虫成分。
2.根据权利要求1所述一种树干用粘虫胶，其特征在于，所述复合粘虫胶基料的制备方法，包括如下步骤：
（1）于25~35℃，按质量比1：6~10：13取聚乙二醇、二氯乙烷、三乙胺混合，搅拌，移至冰水浴，加入聚乙烯醇质量12~20倍的试剂A混合振荡，移出冰水浴，室温静置，过滤，取滤液按质量比7~12：5加入2~5℃的乙醚混合，静置，抽滤，取滤渣干燥，得干燥物；
（2）按质量比3：1~2：15~25：5取2-乙烯基-4,6-二氨基-1,3,5-三嗪、N,N-二甲基丙烯酰胺、二甲基亚砜、干燥物混合搅拌，加入干燥物质量8~15%的TiO2、干燥物质量3~6倍的自制辅剂、干燥物质量18~30%的2-羟基-4-(2-羟乙氧基)-2-甲基苯丙酮混合，紫外光交联引发处理，水浸，出料，即得复合粘虫胶基料。
3.根据权利要求2所述一种树干用粘虫胶，其特征在于，所述步骤（1）中的试剂A：按质量比1：3~6：15取丙烯酰氯、二氯甲烷、水混合，即得试剂A。
4.根据权利要求2所述一种树干用粘虫胶，其特征在于，所述步骤（2）中的自制辅剂：自制辅剂：于35~45℃，按重量份数计，取60~80份（N-脒基）十二烷基丙烯酰胺、30~50份聚乙二醇磷酸酯、4~8份对二氯苯于CO2气氛下混合搅拌，即得自制辅剂。
5.根据权利要求1所述一种树干用粘虫胶，其特征在于，所述复合诱虫成分的制备方法，包括如下步骤：
S1.按质量份数计，取10~15份预处理天牛料、3~6份巴氏芽孢杆菌粉、6~10份葡萄糖、2~5份NaH2PO4、7~15份牛肉膏蛋白胨、4~8份蜂蜜、8~14份麸皮、150~200份水于密闭混合，于28~32℃，振荡摇床，培养4~7天，过滤，取滤液灭菌，真空蒸发，得浓缩液，于35~45℃，取浓缩液按质量比6：1：0.2~0.5加入植物精油、氯菊酯混合，得混合料；
S2.按质量比为5：1~3：0.3：20~30取混合料、胶料、辛烯基琥珀酸淀粉钠、水混合，剪切分散，得乳液，取乳液加入乳液质量8~12%的硫酸钠溶液混合搅拌，降温至20~28℃，加入乳液质量8~12%的甲醛溶液，用试剂B调节pH，室温静置，抽滤，取滤渣水洗，抽真空干燥，即得复合诱虫成分。
6.根据权利要求5所述一种树干用粘虫胶，其特征在于，所述步骤S1中的预处理天牛料：取天牛成虫用木屑喂养3~5天，在喂养过程中，每隔4~7h用天牛成虫质量2~4倍的山楂汁对其进行喷淋，培养完成，得预培养天牛成虫，取预培养天牛成虫按质量比6~10：1加入无水乙醇混合，研磨，即得预处理天牛料。
7.根据权利要求5所述一种树干用粘虫胶，其特征在于，所述步骤S1中的植物精油：茉莉花精油、山茶花精油、腊梅花精油中的任意一种。
8.根据权利要求5所述一种树干用粘虫胶，其特征在于，所述步骤S2中的胶料：按质量比5：1~3：1取桃胶、紫胶、阿胶混合，即得胶料。
9.根据权利要求5所述一种树干用粘虫胶，其特征在于，所述步骤S2中的试剂B：按质量比1：10~15取NaOH溶液、碳酸钠溶液混合，即得试剂B。
10.根据权利要求1所述一种树干用粘虫胶，其特征在于，所述助剂：按质量比1：4~8：3取防老剂RD、松香、凡士林混合，即得助剂。