CN109183227A - A kind of Novel wool blended knitting yarn and its preparation process - Google Patents
A kind of Novel wool blended knitting yarn and its preparation process Download PDFInfo
- Publication number
- CN109183227A CN109183227A CN201811422524.4A CN201811422524A CN109183227A CN 109183227 A CN109183227 A CN 109183227A CN 201811422524 A CN201811422524 A CN 201811422524A CN 109183227 A CN109183227 A CN 109183227A
- Authority
- CN
- China
- Prior art keywords
- fiber
- bamboo charcoal
- total amount
- weight
- wool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Novel wool blended knitting yarns, including mercerized wool fiber, bamboo charcoal fiber, vilofty fiber and cashmere fibres, the mercerized wool fiber and bamboo charcoal fiber, which are twist twisted together, forms core, and the lateral surface of core forms line skin in the mixed volume cladding of reticular structure by vilofty fiber and cashmere fibres.The present invention can make stocking yarn have a bacteriostasis, and ventilative to lead wet effect good, comfortable and easy to wear, sufficiently meet people's lives demand, be conducive to marketing.
Description
[technical field]
The present invention relates to the technical field of yarn, the skill of especially a kind of Novel wool blended knitting yarn and its preparation process
Art field.
[background technique]
Stocking yarn, for hand-Braided Fabrics or the yarn of production knitwear.It is divided into cotton stocking yarn by raw material, knitting woollen yarn, mixes
Spinning.It is divided into carded knitting yarn and combed hosiery yarn by spinning unit.Conventionally used raw material is preferable, and yarn is bright and clean, and the twist is small, hand
Sense is soft.Textile can be stained with dirt in human body wearing process, these dirts become various thin under hot humid environment
The nutrient source of bacteria microorganism breeding.The harm of various bacteriums is very big in life, can be easy to make one to generate various diseases and influence body
Body health, can also generate some epidemic germs, quality of life is caused to decline.Or Conventional bacteria breeding leads to some stinks
Generation.
[summary of the invention]
The object of the invention is to solve the problems of the prior art, a kind of Novel wool blended knitting yarn and its system are proposed
Standby technique can make stocking yarn have a bacteriostasis, and ventilative to lead wet effect good, comfortable and easy to wear, sufficiently meet people's lives need
It asks, is conducive to marketing.
To achieve the above object, the invention proposes a kind of Novel wool blended knitting yarns, including mercerized wool fiber, bamboo
Carbon fibe, vilofty fiber and cashmere fibres, the mercerized wool fiber and bamboo charcoal fiber are twist twisted together and form line
The lateral surface of core, core forms line skin in the mixed volume cladding of reticular structure by vilofty fiber and cashmere fibres.
Preferably, the mercerized wool fiber and bamboo charcoal fiber are twisted according to 1:2 interleaved.
Preferably, the weight of the mercerized wool fiber accounts for the 15-20% of total amount, the weight of the bamboo charcoal fiber is accounted for always
The 20-25% of amount, the weight of the vilofty fiber account for the 20-30% of total amount, and the weight of the cashmere fibres accounts for total amount
30-40%.
Preferably, the cross section of the bamboo charcoal fiber is in quincunx.
To achieve the above object, the invention proposes a kind of preparation process of Novel wool blended knitting yarn, successively include
Following steps:
Step 1: raw material selection is accounted for the mercerized wool fiber of the 15-20% of total amount by weight, weight accounts for the 20- of total amount
25% bamboo charcoal fiber, weight account for the vilofty fiber of the 20-30% of total amount, and weight accounts for the cashmere of the 30-40% of total amount
Fiber is constituted, and it is 100% that the weight of each section fiber, which always matches,；
Step 2: pretreatment, by step 1 selection mercerized wool fiber and cashmere fibres respectively by dyeing → and
Hair → carding → spun yarn → winder, is prepared into pure wool single thread；Wherein when being handled with hair, by deionized water and crude oil AL-106
Be mixed into mixed solution with antistatic agent FK-302, by the way of high-pressure atomization to mercerized wool fiber and cashmere fibres into
Horizontal high voltage infiltration, after infiltration in the environment of 30-40 DEG C closed standing 18-20h；In carding processing, using doffer speed
20r/min, cylinder speed 350r/min, licker-in speed 500r/min, cylinder and cover board interval 0.35mm, 0.22mm, 0.22mm,
0.35mm, carding machine rear car tripe use gauze bottom drain, and import gauge is set as 15mm, and feed plate raises 5mm；In spun yarn processing,
Spinning frame is arranged, the roundness and roller gauge of middle rear roller before adjusting, reel cage gross pressure table is unified to 0.08Pa, shakes
Shelves pressure 190N before frame, 1.3 times of spun yarn back area draft, roller gauge 22mm × 35mm, nip gauge 3.5mm, twist 400T/
M, ingot speed 9000-10000r/min；
Step 3: yarn preparation, the mercerized wool fiber and bamboo charcoal fiber handled using step 2 are twist twisted together shape
At core, the cashmere fibres that the lateral surface of core is handled using vilofty fiber and step 2 are in the mixed volume cladding of reticular structure
Line skin is formed, steam humidification is formed to obtain Novel wool blended knitting yarn.
Preferably, in the step 2 deionized water and crude oil AL-106 and antistatic agent FK-302 mass fraction
Than being followed successively by 10:5:1.
Preferably, the temperature in workshop is 20-25 DEG C in the step 2, the humidity in workshop is 70-80%.
Beneficial effects of the present invention: the present invention is by by mercerized wool fiber, bamboo charcoal fiber, vilofty fiber and goat
Down Fiber is combined together, and by assay optimization, stocking yarn can be made to have a bacteriostasis, ventilative to lead that wet effect is good, and dress is relaxed
It is suitable, sufficiently meet people's lives demand, is conducive to marketing.
Feature and advantage of the invention will be described in detail by embodiment combination attached drawing.
[Detailed description of the invention]
Fig. 1 is a kind of structural schematic diagram of Novel wool blended knitting yarn of the present invention.
In figure: 1- mercerized wool fiber, 2- bamboo charcoal fiber, 3- vilofty fiber, 4- cashmere fibres.
[specific embodiment]
Refering to fig. 1, a kind of Novel wool blended knitting yarn of the present invention, including mercerized wool fiber 1, bamboo charcoal fiber 2, Wei Lao
Husband spy's fiber 3 and cashmere fibres 4, the mercerized wool fiber 1 and bamboo charcoal fiber 2 are twist twisted together and form core, core
Lateral surface form line skin in the mixed volume cladding of reticular structure by vilofty fiber 3 and cashmere fibres 4, the mercerized wool is fine
Dimension 1 and bamboo charcoal fiber 2 are twisted according to 1:2 interleaved, and the weight of the mercerized wool fiber 1 accounts for the 15-20% of total amount, described
The weight of bamboo charcoal fiber 2 accounts for the 20-25% of total amount, and the weight of the vilofty fiber 3 accounts for the 20-30% of total amount, the mountain
The weight of cashmere fiber 4 accounts for the 30-40% of total amount, and the cross section of the bamboo charcoal fiber 2 is in quincunx.
To achieve the above object, the invention proposes a kind of preparation process of Novel wool blended knitting yarn, successively include
Following steps:
Step 1: raw material selection is accounted for the mercerized wool fiber 1 of the 15-20% of total amount by weight, weight accounts for the 20- of total amount
25% bamboo charcoal fiber 2, weight account for the vilofty fiber 3 of the 20-30% of total amount, and weight accounts for the goat of the 30-40% of total amount
Down Fiber 4 is constituted, and it is 100% that the weight of each section fiber, which always matches,；
Step 2: pretreatment, by step 1 selection mercerized wool fiber 1 and cashmere fibres 4 respectively by dyeing →
With hair → carding → spun yarn → winder, it is prepared into pure wool single thread；Wherein when being handled with hair, by deionized water and crude oil AL-
106 and antistatic agent FK-302 is mixed into mixed solution, fine to mercerized wool fiber 1 and cashmere by the way of high-pressure atomization
Dimension 4 carry out high pressure infiltrations, after infiltration in the environment of 30-40 DEG C closed standing 18-20h；In carding processing, using doffer's speed
Degree 20r/min, cylinder speed 350r/min, licker-in speed 500r/min, cylinder and cover board interval 0.35mm, 0.22mm,
0.22mm, 0.35mm, carding machine rear car tripe use gauze bottom drain, and import gauge is set as 15mm, and feed plate raises 5mm；In spun yarn
When processing, spinning frame is arranged, the roundness and roller gauge of middle rear roller, reel cage gross pressure table uniformly arrive before adjusting
0.08Pa, shelves pressure 190N before reel cage, are twisted by 1.3 times of spun yarn back area draft, roller gauge 22mm × 35mm, nip gauge 3.5mm
Degree is 400T/m, ingot speed 9000-10000r/min；
Step 3: yarn preparation, the mercerized wool fiber 1 and bamboo charcoal fiber 2 handled using step 2 are twist twisted together
Core is formed, the cashmere fibres 4 that the lateral surface of core is handled using vilofty fiber 3 and step 2 are in the mixed volume of reticular structure
Cladding forms line skin, and steam humidification is formed to obtain Novel wool blended knitting yarn,
Deionized water and the mass parts ratio of crude oil AL-106 and antistatic agent FK-302 are followed successively by the step 2
10:5:1, the temperature in workshop is 20-25 DEG C in the step 2, and the humidity in workshop is 70-80%.
Mercerized wool fiber 1, bamboo charcoal fiber 2, vilofty fiber 3 and cashmere fibres 4 by being incorporated in by the present invention
Together, by assay optimization, it can make stocking yarn that there is bacteriostasis, it is ventilative that lead wet effect good, and it is comfortable and easy to wear, sufficiently meet people
Life requirement, be conducive to marketing.
Above-described embodiment is the description of the invention, is not limitation of the invention, after any pair of simple transformation of the present invention
Scheme all belong to the scope of protection of the present invention.
Claims (7)
1. a kind of Novel wool blended knitting yarn, it is characterised in that: including mercerized wool fiber (1), bamboo charcoal fiber (2), Wei Lao
Husband spy's fiber (3) and cashmere fibres (4), the mercerized wool fiber (1) and bamboo charcoal fiber (2) are twist twisted together and form line
The lateral surface of core, core forms line skin in the mixed volume cladding of reticular structure by vilofty fiber (3) and cashmere fibres (4).
2. a kind of Novel wool blended knitting yarn as described in claim 1, it is characterised in that: the mercerized wool fiber (1)
It is twisted according to 1:2 interleaved with bamboo charcoal fiber (2).
3. a kind of Novel wool blended knitting yarn as described in claim 1, it is characterised in that: the mercerized wool fiber (1)
Weight account for the 15-20% of total amount, the weight of the bamboo charcoal fiber (2) accounts for the 20-25% of total amount, the vilofty fiber
(3) weight accounts for the 20-30% of total amount, and the weight of the cashmere fibres (4) accounts for the 30-40% of total amount.
4. a kind of Novel wool blended knitting yarn as described in claim 1, it is characterised in that: the cross of the bamboo charcoal fiber (2)
Section is in quincunx.
5. a kind of preparation process of Novel wool blended knitting yarn, it is characterised in that: successively the following steps are included:
Step 1: raw material selection is accounted for the mercerized wool fiber (1) of the 15-20% of total amount by weight, weight accounts for the 20- of total amount
25% bamboo charcoal fiber (2), weight account for the vilofty fiber (3) of the 20-30% of total amount, and weight accounts for the 30-40%'s of total amount
Cashmere fibres (4) are constituted, and it is 100% that the weight of each section fiber, which always matches,；
Step 2: pretreatment, by step 1 selection mercerized wool fiber (1) and cashmere fibres (4) respectively through dyeing →
With hair → carding → spun yarn → winder, it is prepared into pure wool single thread；Wherein when being handled with hair, by deionized water and crude oil AL-
106 and antistatic agent FK-302 is mixed into mixed solution, to mercerized wool fiber (1) and cashmere by the way of high-pressure atomization
Fiber (4) carry out high pressure infiltration, after infiltration in the environment of 30-40 DEG C closed standing 18-20h；In carding processing, using road
Husband speed 20r/min, cylinder speed 350r/min, licker-in speed 500r/min, cylinder and cover board interval 0.35mm, 0.22mm,
0.22mm, 0.35mm, carding machine rear car tripe use gauze bottom drain, and import gauge is set as 15mm, and feed plate raises 5mm；In spun yarn
When processing, spinning frame is arranged, the roundness and roller gauge of middle rear roller, reel cage gross pressure table uniformly arrive before adjusting
0.08Pa, shelves pressure 190N before reel cage, are twisted by 1.3 times of spun yarn back area draft, roller gauge 22mm × 35mm, nip gauge 3.5mm
Degree is 400T/m, ingot speed 9000-10000r/min；
Step 3: yarn preparation, the mercerized wool fiber (1) and bamboo charcoal fiber (2) handled using step 2 are twist twisted together
Core is formed, the lateral surface of core is in reticular structure using the cashmere fibres (4) that vilofty fiber (3) and step 2 are handled
Mixed volume cladding forms line skin, and steam humidification is formed to obtain Novel wool blended knitting yarn.
6. a kind of preparation process of Novel wool blended knitting yarn as claimed in claim 5, it is characterised in that: the step 2
Middle deionized water and the mass parts ratio of crude oil AL-106 and antistatic agent FK-302 are followed successively by 10:5:1.
7. a kind of preparation process of Novel wool blended knitting yarn as claimed in claim 5, it is characterised in that: the step 2
The temperature in middle workshop is 20-25 DEG C, and the humidity in workshop is 70-80%.