CN109338540A - A kind of antibacterial blended yarn and preparation method thereof - Google Patents
A kind of antibacterial blended yarn and preparation method thereof Download PDFInfo
- Publication number
- CN109338540A CN109338540A CN201811436027.XA CN201811436027A CN109338540A CN 109338540 A CN109338540 A CN 109338540A CN 201811436027 A CN201811436027 A CN 201811436027A CN 109338540 A CN109338540 A CN 109338540A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibacterial
- fiber
- blended yarn
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of antibacterial blended yarns, are formed by each component of following parts by weight is blended: 10~15 parts of bamboo charcoal fiber, 20~25 parts of chitin fiber, 10~20 parts of apocynum fibre, 15~25 parts of long-staple cotton fiber, 30~40 parts of aloe viscose rayon, 20~30 parts of antibacterial viscose fiber.The present invention also provides the preparation methods of above-mentioned antibacterial blended yarn, comprising the following steps: bamboo charcoal fiber and chitin fiber are mixed and made into the first cotton roll by S1., and apocynum fibre is mixed with long-staple cotton fiber and the second cotton roll is made；S2. aloe viscose rayon and the first cotton roll are mixed and made into first carded sliver, antibacterial viscose fiber is mixed with the second cotton roll and second carded sliver is made；S3. ripe bar is made through mixing in doubling step in first carded sliver, second carded sliver, then antibacterial blended yarn successively is made through Roving Frames, spinning process.Scribbled anti-microbial property prepared by the present invention is excellent.
Description
Technical field
The present invention relates to spinning fields, and in particular to a kind of antibacterial blended yarn and preparation method thereof.
Background technique
With the raising of the increasingly developed and living standards of the people of social economy, the consumption idea of people is constantly updated, right
Quality of life and living environment are increasingly paid attention to, also higher and higher to the Functional Requirement of clothes, especially to the antibacterial of clothes
Etc. requirement be also continuously improved, garment surface has dust in the external world, bacterium, also there is sweat, oil from human body
The secretion such as rouge are unfavorable for human health so that a large amount of bacteriums breed rapidly.How anti-microbial property good mixed yarn is prepared
Line is those skilled in the art's urgent problem to be solved.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of good scribbleds of anti-microbial property, and provide the yarn
Preparation method.
The technical scheme to solve the above technical problems is that a kind of antibacterial blended yarn, by following parts by weight
Each component is blended to be formed: 10~15 parts of bamboo charcoal fiber, 20~25 parts of chitin fiber, 10~20 parts of apocynum fibre, long-staple cotton
15~25 parts of fiber, 30~40 parts of aloe viscose rayon and 20~30 parts of antibacterial viscose fiber.
Based on the above technical solution, the present invention can also be improved as follows.
Further, the preparation method of the antibacterial viscose fiber is to mix antibacterial agent with regenerated cellulose viscose, is passed through
Wet process weaves to obtain the antibacterial viscose fiber.
Further, the additive amount of the antibacterial agent is 1~6wt% of regenerated cellulose viscose.
Further, the antibacterial agent is silver zeolite antimicrobial agent.
Further, the partial size of the silver zeolite antimicrobial agent is less than or equal to 2.0 μm.
Yarn of the invention has good gas permeability, anti-microbial property, while yarn is comfortably soft.
The present invention also provides the preparation methods of above-mentioned antibacterial blended yarn, comprising the following steps:
S1. the bamboo charcoal fiber of 10~15 parts by weight is mixed with the chitin fiber of 20~25 parts by weight and the first cotton is made
Volume, is mixed and made into the second cotton roll for the long-staple cotton fiber of the apocynum fibre of 10~20 parts by weight and 15~25 parts by weight；
S2., the aloe viscose rayon of 30~40 parts by weight is mixed to the first cotton roll and is made first carded sliver, by 20~30
The antibacterial viscose fiber of parts by weight and the second cotton roll are mixed and made into second carded sliver；
S3. ripe bar is made through mixing in doubling step in first carded sliver, second carded sliver, then successively by Roving Frames,
Antibacterial blended yarn is made in spinning process.
Based on the above technical solution, the present invention can also be improved as follows.
Further, pre-process apocynum fibre before step S1: control regain is 13~17%, to spreading out
Flaxen fiber sprinkling and crude oil and water, balance 4~8h, are subject to apocynum fibre weight, according to weight percent addition 0.2~
0.6% and crude oil and 0.5~0.8% water.
Further, the first cotton roll is made using the first opening and cleaning step, the second cotton roll is made using the second opening and cleaning step；
In first opening and cleaning step, Beater Speed controls the Beater Speed control in 480~540r/min, the second opening and cleaning step
System is in 560~640r/min.
Further, first carded sliver is made using the first carding step, second carded sliver is made using the second carding step；It is described
In first carding step cylinder revolving speed be 300~350r/min, doffing speed be 30~35r/min, thorn rod revolving speed be 780~
810r/min, the gauge pierced between rod and cylinder are 0.15mm, and the gauge between cylinder and doffer is 0.12mm, the second cotton carding work
The revolving speed of cylinder is 320~370r/min in sequence, and doffing speed is 40~45r/min, and thorn rod revolving speed is 780~900r/min,
The gauge pierced between rod and cylinder is 0.15mm, and the gauge between cylinder and doffer is 0.12mm.
Preparation method of the invention can be by bamboo charcoal fiber, chitin fiber, apocynum fibre, long-staple cotton fiber, aloe
The good antibacterial blended yarn of yarn quality is made in viscose rayon and antibacterial viscose fiber, which has good gas permeability
Energy, anti-microbial property, and it is comfortable soft.
Specific embodiment
Principles and features of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
The present invention provides a kind of antibacterial blended yarns, are formed by each component of following parts by weight is blended: bamboo charcoal fiber 10
~15 parts, 20~25 parts of chitin fiber, 10~20 parts of apocynum fibre, 15~25 parts of long-staple cotton fiber, aloe viscose rayon
30~40 parts and 20~30 parts of antibacterial viscose fiber.
Further, the preparation method of the antibacterial viscose fiber is to mix antibacterial agent with regenerated cellulose viscose, is passed through
Wet process weaves to obtain the antibacterial viscose fiber.
Further, the additive amount of the antibacterial agent is 1~6wt% of regenerated cellulose viscose.
Further, the antibacterial agent is silver zeolite antimicrobial agent.
Further, the partial size of the silver zeolite antimicrobial agent is less than or equal to 2.0 μm.
The present invention also provides the preparation methods of above-mentioned antibacterial blended yarn, comprising the following steps:
S1. the bamboo charcoal fiber of 10~15 parts by weight is mixed with the chitin fiber of 20~25 parts by weight and the first cotton is made
Volume, is mixed and made into the second cotton roll for the long-staple cotton fiber of the apocynum fibre of 10~20 parts by weight and 15~25 parts by weight；
S2., the aloe viscose rayon of 30~40 parts by weight is mixed to the first cotton roll and is made first carded sliver, by 20~30
The antibacterial viscose fiber of parts by weight and the second cotton roll are mixed and made into second carded sliver；
S3. ripe bar is made through mixing in doubling step in first carded sliver, second carded sliver, then successively by Roving Frames,
Antibacterial blended yarn is made in spinning process.
Further, pre-process apocynum fibre before step S1: control regain is 13~17%, to spreading out
Flaxen fiber sprinkling and crude oil and water, balance 4~8h, are subject to apocynum fibre weight, according to weight percent addition 0.2~
0.6% and crude oil and 0.5~0.8% water.
Further, the first cotton roll is made using the first opening and cleaning step, the second cotton roll is made using the second opening and cleaning step；
In first opening and cleaning step, Beater Speed controls the Beater Speed control in 480~540r/min, the second opening and cleaning step
System is in 560~640r/min.
Further, first carded sliver is made using the first carding step, second carded sliver is made using the second carding step；It is described
In first carding step cylinder revolving speed be 300~350r/min, doffing speed be 30~35r/min, thorn rod revolving speed be 780~
810r/min, the gauge pierced between rod and cylinder are 0.15mm, and the gauge between cylinder and doffer is 0.12mm, the second cotton carding work
The revolving speed of cylinder is 320~370r/min in sequence, and doffing speed is 40~45r/min, and thorn rod revolving speed is 780~900r/min,
The gauge pierced between rod and cylinder is 0.15mm, and the gauge between cylinder and doffer is 0.12mm.
Preparation method of the invention can be by bamboo charcoal fiber, chitin fiber, apocynum fibre, long-staple cotton fiber, aloe
The good antibacterial blended yarn of yarn quality is made in viscose rayon and antibacterial viscose fiber, which has good gas permeability
Energy, anti-microbial property, and it is comfortable soft.
Embodiment 1
It prepares antibacterial viscose fiber: silver zeolite antimicrobial agent (1~2 μm of partial size) being taken to be added in regenerated cellulose viscose, silver
The additive amount of zeolite antibacterial agent is the 4wt% of regenerated cellulose viscose, then weaves to obtain antibacterial viscose fiber through wet process.
The antibacterial blended yarn of the present embodiment blended is formed by each component of following parts by weight: 12 parts of bamboo charcoal fiber, crust
22 parts of cellulose fiber, 10 parts of apocynum fibre, 25 parts of long-staple cotton fiber, 40 parts of aloe viscose rayon, 28 parts of antibacterial viscose fiber.
The preparation method is as follows:
(1) apocynum fibre of above-mentioned quality is pre-processed, control regain is 13%, is sprayed to apocynum fibre
With crude oil and water, balance 4~8h, be subject to apocynum fibre weight, according to weight percent be added 0.2% and crude oil and
0.5% water；
(2) bamboo charcoal fiber of above-mentioned parts by weight and chitin fiber are mixed and the first cotton is made through the first opening and cleaning step
Volume, wherein Beater Speed control mixes simultaneously by pretreated apocynum fibre with long-staple cotton fiber in 480r/min by above-mentioned
The second cotton roll is made through the second opening and cleaning step, wherein Beater Speed control is in 560r/min.
(3) aloe viscose rayon is mixed with above-mentioned first cotton roll and passes through the first carding step and first carded sliver is made,
Middle cylinder revolving speed is 300r/min, doffing speed 30r/min, and thorn rod revolving speed is 780r/min, pierces the gauge between rod and cylinder
For 0.15mm, the gauge between cylinder and doffer is 0.12mm, and antibacterial viscose fiber mixes with above-mentioned second cotton roll and passes through second
Second carded sliver is made in carding step, and wherein the revolving speed of cylinder is 350r/min, doffing speed 40r/min, and thorn rod revolving speed is
900r/min, the gauge pierced between rod and cylinder are 0.15mm, and the gauge between cylinder and doffer is 0.12mm；
(4) ripe bar is made through mixing in doubling step in first carded sliver, second carded sliver, then successively passes through Roving Frames, fine sand process
Antibacterial blended yarn is made.
Embodiment 2
It prepares antibacterial viscose fiber: silver zeolite antimicrobial agent (1~2 μm of partial size) being taken to be added in regenerated cellulose viscose, silver
The additive amount of zeolite antibacterial agent is the 6wt% of regenerated cellulose viscose, then weaves to obtain antibacterial viscose fiber through wet process.
The antibacterial blended yarn of the present embodiment blended is formed by each component of following parts by weight: 15 parts of bamboo charcoal fiber, crust
25 parts of cellulose fiber, 20 parts of apocynum fibre, 15 parts of long-staple cotton fiber, 37 parts of aloe viscose rayon, 20 parts of antibacterial viscose fiber.
The preparation method is as follows:
(1) apocynum fibre of above-mentioned quality is pre-processed, control regain is 17%, is sprayed to apocynum fibre
With crude oil and water, balance 4~8h, be subject to apocynum fibre weight, according to weight percent be added 0.6% and crude oil and
0.8% water；
(2) bamboo charcoal fiber of above-mentioned parts by weight and chitin fiber are mixed and the first cotton is made through the first opening and cleaning step
Volume, wherein Beater Speed control mixes simultaneously by pretreated apocynum fibre with long-staple cotton fiber in 540r/min by above-mentioned
The second cotton roll is made through the second opening and cleaning step, wherein Beater Speed control is in 600r/min.
(3) aloe viscose rayon is mixed with above-mentioned first cotton roll and passes through the first carding step and first carded sliver is made,
Middle cylinder revolving speed is 350r/min, doffing speed 32r/min, and thorn rod revolving speed is 800r/min, pierces the gauge between rod and cylinder
For 0.15mm, the gauge between cylinder and doffer is 0.12mm, and antibacterial viscose fiber mixes with above-mentioned second cotton roll and passes through second
Second carded sliver is made in carding step, and wherein the revolving speed of cylinder is 370r/min, doffing speed 45r/min, and thorn rod revolving speed is
780r/min, the gauge pierced between rod and cylinder are 0.15mm, and the gauge between cylinder and doffer is 0.12mm；
(4) ripe bar is made through mixing in doubling step in first carded sliver, second carded sliver, then successively passes through Roving Frames, fine sand process
Antibacterial blended yarn is made.
Embodiment 3
It prepares antibacterial viscose fiber: silver zeolite antimicrobial agent (1~2 μm of partial size) being taken to be added in regenerated cellulose viscose, silver
The additive amount of zeolite antibacterial agent is the 1wt% of regenerated cellulose viscose, then weaves to obtain antibacterial viscose fiber through wet process.
The antibacterial blended yarn of the present embodiment blended is formed by each component of following parts by weight: 10 parts of bamboo charcoal fiber, crust
20 parts of cellulose fiber, 17 parts of apocynum fibre, 18 parts of long-staple cotton fiber, 30 parts of aloe viscose rayon, 30 parts of antibacterial viscose fiber.
The preparation method is as follows:
(1) apocynum fibre of above-mentioned quality is pre-processed, control regain is 15%, is sprayed to apocynum fibre
With crude oil and water, balance 4~8h, be subject to apocynum fibre weight, according to weight percent be added 0.5% and crude oil and
0.7% water；
(2) bamboo charcoal fiber of above-mentioned parts by weight and chitin fiber are mixed and the first cotton is made through the first opening and cleaning step
Volume, wherein Beater Speed control mixes simultaneously by pretreated apocynum fibre with long-staple cotton fiber in 500r/min by above-mentioned
The second cotton roll is made through the second opening and cleaning step, wherein Beater Speed control is in 640r/min.
(3) aloe viscose rayon is mixed with above-mentioned first cotton roll and passes through the first carding step and first carded sliver is made,
Middle cylinder revolving speed is 320r/min, doffing speed 35r/min, and thorn rod revolving speed is 810r/min, pierces the gauge between rod and cylinder
For 0.15mm, the gauge between cylinder and doffer is 0.12mm, and antibacterial viscose fiber mixes with above-mentioned second cotton roll and passes through second
Second carded sliver is made in carding step, and wherein the revolving speed of cylinder is 320r/min, doffing speed 42r/min, and thorn rod revolving speed is
800r/min, the gauge pierced between rod and cylinder are 0.15mm, and the gauge between cylinder and doffer is 0.12mm；
(4) ripe bar is made through mixing in doubling step in first carded sliver, second carded sliver, then successively passes through Roving Frames, fine sand process
Antibacterial blended yarn is made.
Effect example
The micro qualitative side of carrier in the Anti-microbial Performance Tests method of reference textile industry standard FZ/T01021-92 fabric
Method carries out antibiotic rate measurement to the yarn samples of embodiment 1,2,3, and the results are shown in Table 1:
| Embodiment number | Antibiotic rate | Antibiotic rate after washing 20 times |
| Embodiment 1 | 96.8 | 96.2 |
| Embodiment 2 | 97.1 | 96.5 |
| Embodiment 3 | 96.8 | 96.0 |
From table 1 it follows that the antibacterial blended yarn anti-microbial property being prepared with this method is excellent.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all in spirit of the invention and
Within principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of antibacterial blended yarn, which is characterized in that formed by each component of following parts by weight is blended: bamboo charcoal fiber 10~15
Part, 20~25 parts of chitin fiber, 10~20 parts of apocynum fibre, 15~25 parts of long-staple cotton fiber, aloe viscose rayon 30~
40 parts and 20~30 parts of antibacterial viscose fiber.
2. antibacterial blended yarn according to claim 1, which is characterized in that the preparation method of the antibacterial viscose fiber is
Antibacterial agent is mixed with regenerated cellulose viscose, weaves to obtain the antibacterial viscose fiber through wet process.
3. antibacterial blended yarn according to claim 2, which is characterized in that the additive amount of the antibacterial agent is regenerated fiber
1~6wt% of plain viscose.
4. antibacterial blended yarn according to claim 3, which is characterized in that the antibacterial agent is silver zeolite antimicrobial agent.
5. antibacterial blended yarn according to claim 4, which is characterized in that the partial size of the silver zeolite antimicrobial agent be less than etc.
In 2.0 μm.
6. a kind of preparation method of antibacterial blended yarn as described in claim 1, which comprises the following steps:
S1., the bamboo charcoal fiber of 10~15 parts by weight is mixed to the chitin fiber of 20~25 parts by weight and is made the first cotton roll,
10~20 parts by weight apocynum fibres are mixed with the long-staple cotton fiber of 15~25 parts by weight and the second cotton roll is made；
S2. the aloe viscose rayon of 30~40 parts by weight is mixed with first cotton roll and is made first carded sliver, by 20~30
The antibacterial viscose fiber of parts by weight mixes with second cotton roll and second carded sliver is made；
S3. ripe bar is made through mixing in doubling step in first carded sliver, second carded sliver, then successively through Roving Frames, spun yarn work
Antibacterial blended yarn is made in sequence.
7. the preparation method of antibacterial blended yarn according to claim 6, which is characterized in that will be spreaded out before step S1
Flaxen fiber is pre-processed: control regain is 13~17%, to apocynum fibre sprinkling and crude oil and water, balances 4~8h, with
Subject to apocynum fibre weight, according to weight percent be added 0.2~0.6% and crude oil and 0.5~0.8% water.
8. the preparation method of antibacterial blended yarn according to claim 6, which is characterized in that use the first opening and cleaning step
The first cotton roll is made, the second cotton roll is made using the second opening and cleaning step；In first opening and cleaning step, Beater Speed control
In 480~540r/min, the second opening and cleaning step, Beater Speed is controlled in 560~640r/min.
9. the preparation method of antibacterial blended yarn according to claim 6, which is characterized in that use the first carding step system
First carded sliver is obtained, second carded sliver is made using the second carding step；In first carding step cylinder revolving speed be 300~
350r/min, doffing speed are 30~35r/min, and thorn rod revolving speed is 780~810r/min, and the gauge pierced between rod and cylinder is
0.15mm, the gauge between cylinder and doffer are 0.12mm, and the revolving speed of cylinder is 320~370r/ in second carding step
Min, doffing speed are 40~45r/min, and thorn rod revolving speed is 780~900r/min, and the gauge pierced between rod and cylinder is 0.15mm,
Gauge between cylinder and doffer is 0.12mm.