CN109181495A - A kind of environmental protection coating material and preparation method thereof - Google Patents
A kind of environmental protection coating material and preparation method thereof Download PDFInfo
- Publication number
- CN109181495A CN109181495A CN201811152266.2A CN201811152266A CN109181495A CN 109181495 A CN109181495 A CN 109181495A CN 201811152266 A CN201811152266 A CN 201811152266A CN 109181495 A CN109181495 A CN 109181495A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- coating material
- protection coating
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental protection coating materials and preparation method thereof, are related to building material technical field.The present invention is mainly grouped as by the group of following parts by weight: fine sand, and 5 parts -10 parts；Middle sand, 3 parts -8 parts；Wood fibre, 3 parts -15 parts；Filler, 4 parts -7 parts；Water soluble acrylic acid epoxy modified resin, 50 parts -65 parts；Diatomite, 15 parts -20 parts；Pigment iron oxide red, 5 parts -8 parts；Antibacterial agent, 0.7 part -1.5 parts.The present invention passes through using fine sand, middle sand natural material and the wood fibre processed using natural reproducible timber by chemical treatment, Mechanical Method as aggregate; using water soluble acrylic acid epoxy modified resin and diatomite environment-friendly materials as base; the coating of production has many advantages, such as that film contraction is small, hardness is high, wearability is good, electrical insulation properties are excellent, pollution-free, corrosion-resistant, has preferable protecting effect.
Description
Technical field
The invention belongs to building material technical fields, more particularly to a kind of environmental protection coating material and a kind of preparation of environmental protection coating material
Method.
Background technique
Coating is mainly made of high molecular polymer, natural color stone sand and relevant auxiliary agent, hard after dry and hard solidification
Such as stone, decorative effect exactly likes marble or granite.Imitation marble paint belongs to the texture coating in art coatings, through its decoration
Building afterwards has natural true natural colour, gives graceful, serious aesthetic feeling, is suitable for the interior of all kinds of buildings
External decoration and building materials and ornaments and protection.
Currently, existing building materials coating, in order to reach various protective effects, many ingredients of addition have certain harmfulness,
And general more environmentally friendly aqueous latex paint water resistance, in terms of compared with oil paint there is also larger gap,
In use usually occur crack, fall off, is mouldy, validity period is shorter, not acid and alkali-resistance the problems such as.
Summary of the invention
The purpose of the present invention is to provide a kind of environmental protection coating materials and preparation method thereof, by a variety of natural materials rationally to match
Than carry out processing be prepared, solve environment-friendly water-based emulsion paint water resistance, in terms of compared with oil paint
There are larger gaps, in use usually occur crack, fall off, is mouldy, validity period is shorter, not acid and alkali-resistance the problem of.
The present invention is achieved by the following technical solutions:
The present invention is a kind of environmental protection coating material and preparation method thereof, is mainly grouped as by the group of following parts by weight:
Fine sand, 5 parts -10 parts；
Middle sand, 3 parts -8 parts；
Wood fibre, 3 parts -15 parts；
Filler, 4 parts -7 parts；
Water soluble acrylic acid epoxy modified resin, 50 parts -65 parts；
Diatomite, 15 parts -20 parts；
Pigment iron oxide red, 5 parts -8 parts；
Antibacterial agent, 0.7 part -1.5 parts.
Further, a kind of environmental protection coating material, is mainly grouped as by the group of following parts by weight:
Fine sand, 5.2 parts -9.5 parts；
Middle sand, 3.5 parts -7.9 parts；
Wood fibre, 3.1 parts -14 parts；
Filler, 4.2 parts -6.8 parts；
Water soluble acrylic acid epoxy modified resin, 51 parts -64 parts；
Diatomite, 15.5 parts -19 parts；
Pigment iron oxide red, 5.3 parts -7.8 parts；
Antibacterial agent, 0.8 part -1.4 parts.
Further, the method for modifying of the water soluble acrylic acid epoxy modified resin is, is 950-1000's by parts by weight
The CoatOSil2287 water that parts by weight are 20-30 is added under 400-600r/min stirring condition in water-based epoxy acrylic resin
Property emulsion paint auxiliary agent stir 30 minutes as modifying agent, then store 48 hours, obtain the epoxy-modified tree of the water soluble acrylic acid
Rouge has film and shrinks the advantages that small, hardness is high, wearability is good, electrical insulation properties are excellent, pollution-free, corrosion-resistant.
Further, the filler is any one in calcium carbonate, talcum powder and china clay.
Further, the diatomite be the non-burning diatomite of wet concentration, dioxide-containing silica range therein be 85% with
On, the mesh number range of diatomite is in 200-325 mesh.
Further, the antibacterial agent is chitosan class natural antibacterial agent.
Further, the preparation method of a kind of environmental protection coating material, comprises the following steps:
Step 1: being 3 parts -15 parts of wood fibre, 5 parts -8 parts of pigment iron oxide red, 50 parts -65 parts by parts by weight
Water is added in blender and is stirred for water soluble acrylic acid epoxy modified resin, revolving speed 400-600r/min, stirs 10 minutes,
Amount of water is controlled in 20%-30%, obtains mixed liquor；
Step 2: fine sand, 3 parts -8 parts of middle sand, 15 parts -20 parts of diatomite that parts by weight are 5 parts -10 parts are passed through upper
Material machine sequentially adds in the mixed liquor, and revolving speed is adjusted to 1200-1500r/min, stirs 15-20 minutes；
Step 3: adding parts by weight is 4 parts -7 parts of filler and 0.7 part -1.5 parts of antibacterial agent, with 400-600r/
Min revolving speed stirs 10-30 minutes and obtains the environmental protection coating material.
The invention has the following advantages:
1, the present invention is by passing through chemical treatment, machinery with fine sand, middle sand natural material and with natural reproducible timber
The wood fibre that method is processed is aggregate, raw using water soluble acrylic acid epoxy modified resin and diatomite environment-friendly materials as base
The coating of production has many advantages, such as that film contraction is small, hardness is high, wearability is good, electrical insulation properties are excellent, pollution-free, corrosion-resistant,
Has preferable protecting effect.
2, the present invention has good sunshade thermal insulation and anti-flammability by pigment iron oxide red and wood fibre, recycles
Natural antibacterial agent, it is therefore prevented that the problems such as cracking, fall off and is mouldy occurs in coating, is conducive to the service life for improving building materials.
Certainly, it implements any of the products of the present invention and does not necessarily require achieving all the advantages described above at the same time.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's all other embodiment obtained without creative efforts belongs to the model that the present invention protects
It encloses.
Embodiment one
The group of following parts by weight is selected to be grouped as: 10 parts of fine sand；5 parts of middle sand；10 parts of wood fibre；5 parts of porcelain clay filler；Water
60 parts of modified resin of acrylic acid epoxy of property；18 parts of diatomite；7 parts of pigment iron oxide red；0.8 part of antibacterial agent.
Step 1: being 10 parts of wood fibre, 7 parts of pigment iron oxide red, 60 parts of water soluble acrylic acid ring by parts by weight
Water is added in blender and is stirred for oxygen modified resin, revolving speed 400r/min, stirs 10 minutes, and amount of water control exists
25%, obtain mixed liquor；
Step 2: the fine sand, 5 parts of middle sand, 18 parts of diatomite that parts by weight are 10 parts are sequentially added by feeder
In mixed liquor, revolving speed is adjusted to 1200r/min, stirs 15 minutes；
Step 3: adding parts by weight is 5 parts of porcelain clay filler and 0.8 part of antibacterial agent, with the stirring of 400r/min revolving speed
Obtain environmental protection coating material within 10 minutes.
Embodiment two
The group of following parts by weight is selected to be grouped as: 8 parts of fine sand；8 parts of middle sand；5 parts of wood fibre；5 parts of pearl filler；Water
55 parts of modified resin of acrylic acid epoxy of property；15 parts of diatomite；5 parts of pigment iron oxide red；1.2 parts of antibacterial agent.
Step 1: being 5 parts of wood fibre, 5 parts of pigment iron oxide red, 55 parts of water soluble acrylic acid epoxy by parts by weight
Water is added in blender and is stirred for modified resin, revolving speed 500r/min, stirs 10 minutes, amount of water control 20%,
Obtain mixed liquor；
Step 2: fine sand, 8 parts of middle sand, 15 parts of diatomite that parts by weight are 8 parts are sequentially added by feeder mixed
It closes in liquid, revolving speed is adjusted to 1400r/min, stirs 18 minutes；
Step 3: adding parts by weight is 5 parts of pearl filler and 1.2 parts of antibacterial agent, stirred with 500r/min revolving speed
It mixes 20 minutes and obtains environmental protection coating material.
Embodiment three
The group of following parts by weight is selected to be grouped as: 5 parts of fine sand；5 parts of middle sand；15 parts of wood fibre；5 parts of talcum powder；
55 parts of water soluble acrylic acid epoxy modified resin；10 parts of diatomite；6 parts of pigment iron oxide red；1 part of antibacterial agent.
Step 1: being 15 parts of wood fibre, 6 parts of pigment iron oxide red, 55 parts of water soluble acrylic acid ring by parts by weight
Water is added in blender and is stirred for oxygen modified resin, revolving speed 600r/min, stirs 10 minutes, and amount of water control exists
30%, obtain mixed liquor；
Step 2: fine sand, 5 parts of middle sand, 10 parts of diatomite that parts by weight are 5 parts are sequentially added by feeder mixed
It closes in liquid, revolving speed is adjusted to 1500r/min, stirs 20 minutes；
Step 3: adding parts by weight is 5 parts of talcum powder and 1 part of antibacterial agent, with the stirring of 600r/min revolving speed
Obtain environmental protection coating material within 30 minutes.
Present invention disclosed above preferred embodiment is only intended to help to illustrate the present invention.There is no detailed for preferred embodiment
All details are described, are not limited the invention to the specific embodiments described.Obviously, according to the content of this specification,
It can make many modifications and variations.These embodiments are chosen and specifically described to this specification, is in order to better explain the present invention
Principle and practical application, so that skilled artisan be enable to better understand and utilize the present invention.The present invention is only
It is limited by claims and its full scope and equivalent.
Claims (7)
1. a kind of environmental protection coating material, which is characterized in that be mainly grouped as by the group of following parts by weight:
Fine sand, 5 parts -10 parts；
Middle sand, 3 parts -8 parts；
Wood fibre, 3 parts -15 parts；
Filler, 4 parts -7 parts；
Water soluble acrylic acid epoxy modified resin, 50 parts -65 parts；
Diatomite, 15 parts -20 parts；
Pigment iron oxide red, 5 parts -8 parts；
Antibacterial agent, 0.7 part -1.5 parts.
2. a kind of environmental protection coating material according to claim 1, which is characterized in that be mainly grouped as by the group of following parts by weight:
Fine sand, 5.2 parts -9.5 parts；
Middle sand, 3.5 parts -7.9 parts；
Wood fibre, 3.1 parts -14 parts；
Filler, 4.2 parts -6.8 parts；
Water soluble acrylic acid epoxy modified resin, 51 parts -64 parts；
Diatomite, 15.5 parts -19 parts；
Pigment iron oxide red, 5.3 parts -7.8 parts；
Antibacterial agent, 0.8 part -1.4 parts.
3. a kind of environmental protection coating material according to claim 1, which is characterized in that the water soluble acrylic acid epoxy modified resin
Method of modifying is, by water-based epoxy acrylic resin that parts by weight are 950-1000 under 400-600r/min stirring condition, adds
Enter CoatOSil2287 aqueous latex paint auxiliary agent that parts by weight are 20-30 as modifying agent, stirring 30 minutes, then to store 48 small
When, obtain the water soluble acrylic acid epoxy modified resin.
4. a kind of environmental protection coating material according to claim 1, which is characterized in that the filler is calcium carbonate, talcum powder and porcelain
Any one in soil.
5. a kind of environmental protection coating material according to claim 1, which is characterized in that the diatomite is the non-burning diatom of wet concentration
Soil, dioxide-containing silica range therein are 85% or more, and the mesh number range of diatomite is in 200-325 mesh.
6. a kind of environmental protection coating material according to claim 1, which is characterized in that the antibacterial agent is chitosan class natural antibacterial
Agent.
7. a kind of preparation method of environmental protection coating material as described in claim 1-7 any one, which is characterized in that including following several
A step:
Step 1: being 3 parts -15 parts of wood fibre, 5 parts -8 parts of pigment iron oxide red, 50 parts -65 parts aqueous by parts by weight
Water is added in blender and is stirred for acrylic acid epoxy modified resin, revolving speed 400-600r/min, stirs 10 minutes, adds water
Amount control obtains mixed liquor in 20%-30%；
Step 2: the fine sand, 3 parts -8 parts of middle sand, 15 parts -20 parts of diatomite that parts by weight are 5 parts -10 parts are passed through feeder
It sequentially adds in the mixed liquor, revolving speed is adjusted to 1200-1500r/min, stirs 15-20 minutes；
Step 3: adding parts by weight is 4 parts -7 parts of filler and 0.7 part -1.5 parts of antibacterial agent, turned with 400-600r/min
Speed stirring obtains the environmental protection coating material in 10-30 minutes.