CN109097180A - 一种全合成切削液 - Google Patents
一种全合成切削液 Download PDFInfo
- Publication number
- CN109097180A CN109097180A CN201811318718.XA CN201811318718A CN109097180A CN 109097180 A CN109097180 A CN 109097180A CN 201811318718 A CN201811318718 A CN 201811318718A CN 109097180 A CN109097180 A CN 109097180A
- Authority
- CN
- China
- Prior art keywords
- agent
- cutting fluid
- fully synthetic
- synthetic cutting
- fluid according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种全合成切削液，配方包括：2‑5％的单乙醇胺、3‑7％的三乙醇胺、3‑6％的三元酸、11‑18％的润滑剂、1‑2％的耦合剂、2‑5％的渗透剂、0.3％的消泡剂、6‑10％的极压剂及0.5‑1％的乳化剂，余量为自来水；将搅拌机进行清洗后烘干，依次加入单乙醇胺、三乙醇胺和三元酸，在常温下以80‑100rpm的速度搅拌20‑30min，待其充分溶解；继续搅拌，依次加入润滑剂、耦合剂、渗透剂、极压剂及乳化剂，持续搅拌20‑30min；依次加入自来水和消泡剂，在50‑80rpm的速度下搅拌5min即可，该全合成切削液，采用特别的渗透剂材料，这种原料为树脂行业使用，有很强的水溶性能和清洗拨离性能，用少量偶合成份可达到好的极佳的水溶性能，减少泡沫的产生，不仅环保性能好，还具有非常优异润滑性能，适合高润滑工艺加工。
Description
技术领域
本发明涉及切削液技术领域，具体为一种全合成切削液。
背景技术
切削液是一种用在金属切削、磨加工过程中，用来冷却和润滑刀具和加工件的工业用液体，切削液由多种超强功能助剂经科学复合配合而成，水基的切削液可分为乳化液、半合成切削液和全合成切削液，全合成切削液则是仅使用化学合成基础油(即不含矿物油)的水溶性切削液，现有的全合成切削液水溶性能和清洗拨离性能不高，且润滑效果不佳。
发明内容
本发明的目的在于提供一种全合成切削液，以解决上述背景技术中提出的问题。
为了解决上述技术问题，本发明提供如下技术方案：一种全合成切削液，配方包括：2-5％的单乙醇胺、3-7％的三乙醇胺、3-6％的三元酸、11-18％的润滑剂、1-2％的耦合剂、2-5％的渗透剂、0.3％的消泡剂、6-10％的极压剂及0.5-1％的乳化剂，余量为自来水。
根据上述技术方案，所述单乙醇胺水溶液热压灭菌后置于避光的气密容器内，并存放于阴凉、干燥处。
根据上述技术方案，所述三乙醇胺在操作时工作人员需佩戴自吸过滤式防尘口罩，戴化学安全防护眼镜，穿防毒物渗透工作服，戴橡胶手套。
根据上述技术方案，所述三元酸为磷酸或柠檬酸中的一种或两种。
根据上述技术方案，所述润滑剂为硅油、硅酸酯、磷酸酯、氟油、酯类油和合成烃油中的一种或多种。
根据上述技术方案，所述耦合剂为一种矽烷耦合剂。
根据上述技术方案，所述渗透剂为一种环氧树脂渗透剂。
根据上述技术方案，所述消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷中的一种或多种。
根据上述技术方案，所述极压剂为硫化油酸和硫化棉籽油的一种或两种。
根据上述技术方案，所述乳化剂为阿拉伯胶和烷基苯磺酸钠的一种或两种。
与现有技术相比，本发明所达到的有益效果是：该发明，采用特别的渗透剂材料，这种原料为树脂行业使用，有很强的水溶性能和清洗拨离性能，用少量偶合成份可达到好的极佳的水溶性能，减少泡沫的产生，同时增加润滑性能。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种技术方案：一种全合成切削液；
实施例1：
一种全合成切削液，配方包括：35％的单乙醇胺、5％的三乙醇胺、5％的三元酸、15％的润滑剂、2％的耦合剂、2％的渗透剂、0.3％的消泡剂、5％的极压剂、1％的乳化剂和29.7％的自来水。
其制备工艺包括以下步骤：
1)按照各组分的质量百分含量分别是：35％的单乙醇胺、5％的三乙醇胺、5％的三元酸、15％的润滑剂、2％的耦合剂、2％的渗透剂、0.3％的消泡剂、5％的极压剂、1％的乳化剂和29.7％的自来水进行称取；
2)将搅拌机进行清洗后烘干，依次加入单乙醇胺、三乙醇胺和三元酸，在常温下以80-100rpm的速度搅拌20-30min，待其充分溶解；
3)继续搅拌，依次加入润滑剂、耦合剂、渗透剂、极压剂及乳化剂，持续搅拌20-30min；
4)依次加入自来水和消泡剂，在50-80rpm的速度下搅拌5min即可；
其中，单乙醇胺水溶液热压灭菌后置于避光的气密容器内，并存放于阴凉、干燥处；三乙醇胺在操作时工作人员需佩戴自吸过滤式防尘口罩，戴化学安全防护眼镜，穿防毒物渗透工作服，戴橡胶手套；三元酸为磷酸或柠檬酸中的一种或两种；润滑剂为硅油、硅酸酯、磷酸酯、氟油、酯类油和合成烃油中的一种或多种；耦合剂为一种矽烷耦合剂；渗透剂为一种环氧树脂渗透剂；消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷中的一种或多种；极压剂为硫化油酸和硫化棉籽油的一种或两种；乳化剂为阿拉伯胶和烷基苯磺酸钠的一种或两种。
实施例2：
一种全合成切削液，配方包括：35％的单乙醇胺、5％的三乙醇胺、5％的三元酸、15％的润滑剂、2％的耦合剂、3.5％的渗透剂、0.3％的消泡剂、5％的极压剂、1％的乳化剂和28.2％的自来水。
其制备工艺包括以下步骤：
1)按照各组分的质量百分含量分别是：35％的单乙醇胺、5％的三乙醇胺、5％的三元酸、15％的润滑剂、2％的耦合剂、3.5％的渗透剂、0.3％的消泡剂、5％的极压剂、1％的乳化剂和28.2％的自来水进行称取；
2)将搅拌机进行清洗后烘干，依次加入单乙醇胺、三乙醇胺和三元酸，在常温下以80-100rpm的速度搅拌20-30min，待其充分溶解；
3)继续搅拌，依次加入润滑剂、耦合剂、渗透剂、极压剂及乳化剂，持续搅拌20-30min；
4)依次加入自来水和消泡剂，在50-80rpm的速度下搅拌5min即可；
其中，单乙醇胺水溶液热压灭菌后置于避光的气密容器内，并存放于阴凉、干燥处；三乙醇胺在操作时工作人员需佩戴自吸过滤式防尘口罩，戴化学安全防护眼镜，穿防毒物渗透工作服，戴橡胶手套；三元酸为磷酸或柠檬酸中的一种或两种；润滑剂为硅油、硅酸酯、磷酸酯、氟油、酯类油和合成烃油中的一种或多种；耦合剂为一种矽烷耦合剂；渗透剂为一种环氧树脂渗透剂；消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷中的一种或多种；极压剂为硫化油酸和硫化棉籽油的一种或两种；乳化剂为阿拉伯胶和烷基苯磺酸钠的一种或两种。
实施例3：
一种全合成切削液，配方包括：35％的单乙醇胺、5％的三乙醇胺、5％的三元酸、15％的润滑剂、2％的耦合剂、5％的渗透剂、0.3％的消泡剂、5％的极压剂、1％的乳化剂和26.7％的自来水。
其制备工艺包括以下步骤：
1)按照各组分的质量百分含量分别是：35％的单乙醇胺、5％的三乙醇胺、5％的三元酸、15％的润滑剂、2％的耦合剂、5％的渗透剂、0.3％的消泡剂、5％的极压剂、1％的乳化剂和26.7％的自来水进行称取；
2)将搅拌机进行清洗后烘干，依次加入单乙醇胺、三乙醇胺和三元酸，在常温下以80-100rpm的速度搅拌20-30min，待其充分溶解；
3)继续搅拌，依次加入润滑剂、耦合剂、渗透剂、极压剂及乳化剂，持续搅拌20-30min；
4)依次加入自来水和消泡剂，在50-80rpm的速度下搅拌5min即可；
其中，单乙醇胺水溶液热压灭菌后置于避光的气密容器内，并存放于阴凉、干燥处；三乙醇胺在操作时工作人员需佩戴自吸过滤式防尘口罩，戴化学安全防护眼镜，穿防毒物渗透工作服，戴橡胶手套；三元酸为磷酸或柠檬酸中的一种或两种；润滑剂为硅油、硅酸酯、磷酸酯、氟油、酯类油和合成烃油中的一种或多种；耦合剂为一种矽烷耦合剂；渗透剂为一种环氧树脂渗透剂；消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷中的一种或多种；极压剂为硫化油酸和硫化棉籽油的一种或两种；乳化剂为阿拉伯胶和烷基苯磺酸钠的一种或两种。
各实施例全合成切削液性能对比如下表：
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种全合成切削液，其特征在于：配方包括：2-5％的单乙醇胺、3-7％的三乙醇胺、3-6％的三元酸、11-18％的润滑剂、1-2％的耦合剂、2-5％的渗透剂、0.3％的消泡剂、6-10％的极压剂及0.5-1％的乳化剂，余量为自来水。
2.根据权利要求1所述的一种全合成切削液，其特征在于：所述单乙醇胺水溶液热压灭菌后置于避光的气密容器内，并存放于阴凉、干燥处。
3.根据权利要求1所述的一种全合成切削液，其特征在于：所述三乙醇胺在操作时工作人员需佩戴自吸过滤式防尘口罩，戴化学安全防护眼镜，穿防毒物渗透工作服，戴橡胶手套。
4.根据权利要求1所述的一种全合成切削液，其特征在于：所述三元酸为磷酸或柠檬酸中的一种或两种。
5.根据权利要求1所述的一种全合成切削液，其特征在于：所述润滑剂为硅油、硅酸酯、磷酸酯、氟油、酯类油和合成烃油中的一种或多种。
6.根据权利要求1所述的一种全合成切削液，其特征在于：所述耦合剂为一种矽烷耦合剂。
7.根据权利要求1所述的一种全合成切削液，其特征在于：所述渗透剂为一种环氧树脂渗透剂。
8.根据权利要求1所述的一种全合成切削液，其特征在于：所述消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷中的一种或多种。
9.根据权利要求1所述的一种全合成切削液，其特征在于：所述极压剂为硫化油酸和硫化棉籽油的一种或两种。
10.根据权利要求1所述的一种全合成切削液，其特征在于：所述乳化剂为阿拉伯胶和烷基苯磺酸钠的一种或两种。