CN109095910A - 负离子环保自洁陶瓷砖及其制作方法 - Google Patents
负离子环保自洁陶瓷砖及其制作方法 Download PDFInfo
- Publication number
- CN109095910A CN109095910A CN201811015286.5A CN201811015286A CN109095910A CN 109095910 A CN109095910 A CN 109095910A CN 201811015286 A CN201811015286 A CN 201811015286A CN 109095910 A CN109095910 A CN 109095910A
- Authority
- CN
- China
- Prior art keywords
- parts
- anion
- environmental protection
- ceramic tile
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种负离子环保自洁陶瓷砖及其制作方法，该陶瓷砖包括坯体层和负离子釉层；负离子釉层包括按重量份计的以下原料：球土8～12份、滑石7～9份、白云石12～14份、钾长石28～32份、霞石10～12份、氧化铝7～9份、硅酸锆8～10份、碳化硅2‑5份、碳酸钡8～10份、氧化锌4～6份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.05‑0.1份和负离子材料0.5～1份，制作时，先制备陶瓷坯体；并将负离子釉层的原料混合，进行研磨，过筛后对筛下物进行除铁，进行陈腐后得到负离子釉水；将负离子釉水施釉至陶瓷坯体的表面；再施透明釉，最后进行烧制，即可得到负离子环保自洁陶瓷砖。得到的负离子陶瓷砖能够有效净化空气，并且能够长效释放负氧离子。
Description
技术领域
本发明涉及陶瓷技术领域，尤其是一种负离子环保自洁陶瓷砖及其制作方法。
背景技术
负离子又称负氧离子，是指获得1个或1个以上的电子带负电荷的氧气离子。空气主要成分是氮、氧、二氧化碳和水蒸气。氮占78%，氧占21%，二氧化碳占0.03%，氮对电子无亲和力，只有氧和二氧化碳对电子有亲和力，但氧含量是二氧化碳含量的700倍，因此，空气中生成的负离子绝大多数是空气负氧离子,它是空气中的氧分子结合了自由电子而形成的。它不仅能促成人体合成和储存维生素，强化和激活人体的生理活动；还能净化空气，杀菌消毒。
发明内容
为了解决上述技术问题，本发明提供一种负离子环保自洁陶瓷砖制作方法，得到的负离子陶瓷砖能够有效净化空气，并且能够长效释放负氧离子。
本发明所采取的技术方案是，负离子环保自洁陶瓷砖，包括坯体层和负离子釉层；负离子釉层包括按重量份计的以下原料：球土8～12份、滑石7～9份、白云石12～14份、钾长石28～32份、霞石10～12份、氧化铝7～9份、硅酸锆8～10份、碳化硅2-5份、碳酸钡8～10份、氧化锌4～6份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.05-0.1份和负离子材料0.5～1份。
优选地方案中，球土10份、滑石8份、白云石13份、钾长石30份、霞石11份、氧化铝8份、硅酸锆9份、碳化硅4份、碳酸钡9份、氧化锌5份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.08份和负离子材料 1份。
进一步地，所述负离子材料为电气石超细粉和二氧化钛按重量比8-10:1配制而成，粒径在300nm以下。
进一步地，所述坯体层采用按重量份计的原料制成：钾长石37～40份、钠长石15～20份、黏土15～20份、低温砂10～15份、熟焦7～10份、球土6～8份、膨润土3～5份、硅藻土3-5份、滑石2-3份、陶瓷坯体增强剂0.05份、羧甲基纤维素钠3-5份、减水剂0.5份和腐植酸钠0.03份。
进一步地，所述负离子釉层上还依次设有喷墨打印层和透明釉层。
本发明还涉及所述负离子环保自洁陶瓷砖的制作方法，包括以下步骤：
1）制备陶瓷坯体；并将负离子釉层的原料混合，进行研磨，过筛后对筛下物进行除铁，最后进行陈腐后得到负离子釉水；
2）将负离子釉水施釉至陶瓷坯体的表面；
3）在步骤2）得到的施负离子釉的陶瓷坯体上进行喷墨打印图案后施透明釉，最后进行烧制，即可得到负离子环保自洁陶瓷砖。
进一步地，步骤1）中制备陶瓷坯体时，先按配比称取原料，进行湿球磨，然后喷粉干燥至水分含量为6-8wt%，陈腐24h后进行级配，级配好的原料压制成型，烘干至含水率在0.2-0.3wt%，得到陶瓷坯体。
进一步地，级配时，≥20目占0.1～0.3wt%，20～40目占61～63 wt %，40～60目占27～34 wt % 。
进一步地，步骤1）中负离子釉水制备过程中，研磨后，细度控制在0.5-0.8g/325目/100ml。
进一步地，步骤1）中负离子釉水的比重为1.80-1.82g/mL。
进一步地，烧制温度为1190-1215℃，时间55-65min。
本发明有如下有益效果：
1、可以通过将负离子材料设置在陶瓷砖的中间釉层，其位于透明釉层之下，使之不会被磨损或者消耗掉，能够长效释放负离子，并且湿容量高，可以有效净化空气，提供舒适的环境。
2、在负离子釉层采中球土、滑石、白云石、钾长石、霞石、氧化铝、硅酸锆、碳化硅、碳酸钡、氧化锌、三聚磷酸钠、甲基纤维素、乳化硅油和负离子材料电气石超细粉及二氧化钛，能够改善陶瓷的坯釉结合性能，提高陶瓷釉面硬度，尤其是霞石与硅酸锆的存在，能够加固坯釉结合程度；通过增加碳化硅作为发泡材料，使得烧成后形成气孔，来提升负离子瓷砖的吸湿性能和舒适性能，通过甲基纤维素增稠，增加粘度，更好的与坯体结合。
3、采用钾长石、钠长石、黏土、低温砂、熟焦、球土、膨润土、硅藻土、滑石、陶瓷坯体增强剂、羧甲基纤维素钠、减水剂和腐植酸钠作为坯体原料，硅藻土为多孔材料，具有吸湿性能，采用钾长石、钠长石来钾长石比钠长石降低烧成温度，膨润土、黏土确保可塑性能，便于成型，加入羧甲基纤维素钠一方面提高原料的可塑性，还能降低浆料粘度，增加坯体的干燥强度，减少坯体的处理时间，同时，还能增加烧成样品的吸水率和气孔率，增大吸湿性。熟焦和腐植酸钠的使用，能够起到增强和粘接的作用，促进坯釉的结合，还具有一定的吸附作用，有助于增加陶瓷砖的吸湿性能，提供舒适的环境。
具体实施方式
下面结合实施例来进一步说明本发明，但本发明要求保护的范围并不局限于实施例表述的范围。
实施例1：
负离子环保自洁陶瓷砖，包括坯体层和负离子釉层；
其中坯体层采用按重量份计的原料制成：钾长石38份、钠长石18份、黏土18份、低温砂12份、熟焦8份、球土7份、膨润土4份、硅藻土4份、滑石3份、陶瓷坯体增强剂0.05份、羧甲基纤维素钠4份、减水剂0.5份和腐植酸钠0.03份；
负离子釉层采用按重量份计的以下原料：球土10份、滑石8份、白云石13份、钾长石30份、霞石11份、氧化铝8份、硅酸锆9份、碳化硅4份、碳酸钡9份、氧化锌5份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.08份和负离子材料 1份。
负离子材料为电气石超细粉和二氧化钛按重量比10:1配制而成。
实施例2：
负离子环保自洁陶瓷砖，包括坯体层和负离子釉层；
其中坯体层采用按重量份计的原料制成：钾长石37份、钠长石15份、黏土15份、低温砂10份、熟焦7份、球土6份、膨润土3份、硅藻土3份、滑石2份、陶瓷坯体增强剂0.05份、羧甲基纤维素钠3份、减水剂0.5份和腐植酸钠0.03份；
负离子釉层采用按重量份计的以下原料：球土8份、滑石7份、白云石12份、钾长石28份、霞石10份、氧化铝7份、硅酸锆8份、碳化硅2份、碳酸钡8份、氧化锌4份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.05份和负离子材料 1份。
负离子材料为电气石超细粉和二氧化钛按重量比10:1配制而成。
实施例3：
负离子环保自洁陶瓷砖，包括坯体层和负离子釉层；
其中坯体层采用按重量份计的原料制成：钾长石40份、钠长石20份、黏土20份、低温砂15份、熟焦10份、球土8份、膨润土5份、硅藻土5份、滑石3份、陶瓷坯体增强剂0.05份、羧甲基纤维素钠5份、减水剂0.5份和腐植酸钠0.03份；
负离子釉层采用按重量份计的以下原料：球土12份、滑石9份、白云石14份、钾长石32份、霞石12份、氧化铝9份、硅酸锆10份、碳化硅5份、碳酸钡10份、氧化锌6份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.1份和负离子材料 1份。
负离子材料为电气石超细粉和二氧化钛按重量比8:1配制而成。
实施例4：
负离子环保自洁陶瓷砖，包括坯体层和负离子釉层；
其中坯体层采用按重量份计的原料制成：钾长石38份、钠长石18份、黏土18份、低温砂12份、熟焦8份、球土7份、膨润土4份、硅藻土4份、滑石3份、陶瓷坯体增强剂0.05份、羧甲基纤维素钠4份、减水剂0.5份和腐植酸钠0.03份；
负离子釉层采用按重量份计的以下原料：球土10份、滑石8份、白云石13份、钾长石30份、霞石11份、氧化铝8份、硅酸锆9份、碳化硅4份、碳酸钡9份、氧化锌5份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.08份和负离子材料 0.6份。
负离子材料为电气石超细粉和二氧化钛按重量比8:1配制而成。
实施例5：
负离子环保自洁陶瓷砖，包括坯体层和负离子釉层；
其中坯体层采用按重量份计的原料制成：钾长石37份、钠长石16份、黏土16份、低温砂14份、熟焦8份、球土7份、膨润土3份、硅藻土5份、滑石3份、陶瓷坯体增强剂0.05份、羧甲基纤维素钠4份、减水剂0.5份和腐植酸钠0.03份；
负离子釉层采用按重量份计的以下原料：球土11份、滑石8份、白云石13份、钾长石29份、霞石11份、氧化铝8份、硅酸锆9份、碳化硅4份、碳酸钡9份、氧化锌5份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.08份和负离子材料 0.8份。
负离子材料为电气石超细粉和二氧化钛按重量比10:1配制而成。
进一步地，根据需要，在所述负离子釉层上还依次设有喷墨打印层和透明釉层。
上述负离子环保自洁陶瓷砖的制作方法，其特征在于，包括以下步骤：
1）先按配比称取原料，进行湿球磨，然后喷粉干燥至水分含量为6-8wt%，陈腐24h后进行级配，级配好的原料压制成型，烘干至含水率在0.2-0.3wt%，得到陶瓷坯体；并将负离子釉层的原料混合，进行研磨，过筛后对筛下物进行除铁，最后进行陈腐后得到负离子釉水；
2）将负离子釉水施釉至陶瓷坯体的表面；比重: 1.82g/ml , 流速：30-32秒，施釉重：40-53g/300x300铁盘。
3）在步骤2）得到的施负离子釉的陶瓷坯体上进行喷墨打印图案后施透明釉，最后进行烧制，即可得到负离子环保自洁陶瓷砖。
优选地方案中，级配时，≥20目占0.1～0.3wt%，20～40目占61～63 wt %，40～60目占27～34 wt % 。
进一步地，负离子釉水制备过程中，研磨后，细度控制在0.5-0.8g/325目/100ml。
烧成：温度1215 ， 60分钟
烧制温度为1190-1215℃，时间55-65min。
采用实施例1中的陶瓷砖进行检验，负离子释放量≥7000个/cm3*s，将4块0.3*0.3m的陶瓷砖放入1m3的空间内进行试验，甲醛去除率达95.2%，甲苯净化率达97.8%，TVOC去除率达96.5%。
上述的实施例仅为本发明的优选技术方案，而不应视为对于本发明的限制，本发明的保护范围应以权利要求记载的技术方案，包括权利要求记载的技术方案中技术特征的等同替换方案为保护范围。即在此范围内的等同替换改进，也在本发明的保护范围之内。
Claims (10)
1.负离子环保自洁陶瓷砖，其特征在于，包括坯体层和负离子釉层；负离子釉层包括按重量份计的以下原料：球土8～12份、滑石7～9份、白云石12～14份、钾长石28～32份、霞石10～12份、氧化铝7～9份、硅酸锆8～10份、碳化硅2-5份、碳酸钡8～10份、氧化锌4～6份、三聚磷酸钠0.32份、甲基纤维素0.13份、乳化硅油0.05-0.1份和负离子材料0.5～1份。
2.根据权利要求1所述的负离子环保自洁陶瓷砖，其特征在于：所述负离子材料为电气石超细粉和二氧化钛按重量比8-10:1配制而成，粒径在300nm以下。
3.根据权利要求1所述的负离子环保自洁陶瓷砖，其特征在于：所述坯体层采用按重量份计的原料制成：钾长石37～40份、钠长石15～20份、黏土15～20份、低温砂10～15份、熟焦7～10份、球土6～8份、膨润土3～5份、硅藻土3-5份、滑石2-3份、陶瓷坯体增强剂0.05份、羧甲基纤维素钠3-5份、减水剂0.5份和腐植酸钠0.03份。
4.根据权利要求1所述的负离子环保自洁陶瓷砖，其特征在于：所述负离子釉层上还依次设有喷墨打印层和透明釉层。
5.权利要求1-4任意一项所述负离子环保自洁陶瓷砖的制作方法，其特征在于，包括以下步骤：
1）制备陶瓷坯体；并将负离子釉层的原料混合，进行研磨，过筛后对筛下物进行除铁，最后进行陈腐后得到负离子釉水；
2）将负离子釉水施釉至陶瓷坯体的表面；
3）在步骤2）得到的施负离子釉的陶瓷坯体上进行喷墨打印图案后施透明釉，最后进行烧制，即可得到负离子环保自洁陶瓷砖。
6.根据权利要求5所述的方法，其特征在于：步骤1）中制备陶瓷坯体时，先按配比称取原料，进行湿球磨，然后喷粉干燥至水分含量为6-8wt%，陈腐24h后进行级配，级配好的原料压制成型，烘干至含水率在0.2-0.3wt%，得到陶瓷坯体。
7.根据权利要求6所述的方法，其特征在于：级配时，≥20目占0.1～0.3wt%，20～40目占61～63 wt %，40～60目 占27～34 wt % 。
8.根据权利要求5所述的方法，其特征在于：步骤1）中负离子釉水制备过程中，研磨后，细度控制在0.5-0.8g/325目/100ml。
9.根据权利要求5所述的方法，其特征在于：步骤1）中负离子釉水的比重为1.80-1.82g/mL。
10.根据权利要求5所述的方法，其特征在于：烧制温度为1190-1215℃，时间55-65min。