CN109084705A - 钢板皮下水波纹检验方法 - Google Patents
钢板皮下水波纹检验方法 Download PDFInfo
- Publication number
- CN109084705A CN109084705A CN201810597332.0A CN201810597332A CN109084705A CN 109084705 A CN109084705 A CN 109084705A CN 201810597332 A CN201810597332 A CN 201810597332A CN 109084705 A CN109084705 A CN 109084705A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- water ripples
- inspection
- defect
- red rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种钢板皮下水波纹检验方法，通过对钢板表面形态进行分析，对钢板表面形态、色差等进行辨别，可以及时发现钢板的水波纹缺陷，避免钢板生产厂生产出批量不合格产品，进一步可以避免加工厂利用不合格钢板进行加工后，零件报废造成的经济损失，及避免工期的延误。
Description
技术领域
本发明涉及对钢表面光洁度要求比较高的工程机械等用钢领域，具体涉及一种用于检验钢板表面水波纹的方法。
背景技术
工程机械用钢等高表面质量要求钢板一般都是做外观件，需经过喷图、抛光、上漆等工序，如果表面有水波纹，抛光、上漆后就会很明显，无法使用。工程机械用钢等高表面质量要求钢板在轧制工序一般不允许抛丸、修磨，主要是钢板抛丸后在物流环节易划伤、生锈，而水波纹一般在钢板皮下，不抛丸很难发现有水波纹，这就存在产生批量水波纹而无法及时发现的风险。
发明内容
本发明主要对工程机械用钢等高表面质量要求钢板表面形态进行分析，提供一种短时间内快速、有效识别水波纹的方法，达到快速处理难题，满足生产需求的目的。
本发明具体采用如下技术方案：
钢板皮下水波纹检验方法，其特征在于采用如下方式进行水波纹缺陷检测：
A、钢板表面存在氧化铁皮破碎的情况下，若裸露部分平整，则没有水波纹缺陷；若裸露部分出现蜂窝状点、线凹不平，则存在水波纹缺陷；
B、反光检查：若钢板表面某区域氧化铁皮的反光比周围其他区域高，则存在水波纹缺陷；
C、“硬边红锈判断法”：新轧制钢板表面呈现铁青色为正常现象，若存在红锈分布，则可能存在隐藏的水波纹，通过红锈与青色部分交界情况进一步判断。
具体地，
若红锈与青色部分柔缓过渡则没有水波纹缺陷；若红锈与青色部分交界边缘硬性交界，界限明显则存在水波纹缺陷。
D、在不破坏钢板表面粗糙度的前提下，采用磨光机打磨钢板表面的方式，验证判断水波纹。
本发明的钢板皮下水波纹检验方法主要应用于对表面光洁度要求比较高的工程机械等用钢领域。因水波纹在钢板皮下，不易于发现，但在加工成零件抛丸后就会显现出来，会导致零件喷图后表面不光洁而判废品。本发明方法对钢板表面形态进行分析，通过对钢板表面形态、色差等进行辨别，可以及时发现钢板的水波纹缺陷，避免钢板生产厂生产出批量不合格产品，进一步可以避免加工厂利用不合格钢板进行加工后，零件报废造成的经济损失，及避免工期的延误， 预测年经济效益可达50万元。
附图说明
图1为实施例一对比验证图；
图2为实施例二对比验证图。
图3为实施例三对比验证图。
图4为实施例四对比验证图。
具体实施方式
本发明的钢板皮下水波纹检验方法具体如下：
一、目视检测法：
1、钢板表面存在氧化铁皮破碎的情况下，若裸露部分平整，则没有水波纹缺陷；若裸露部分出现蜂窝装点、线凹不平，则存在水波纹缺陷。
2、反光检查：钢板表面存在水波纹缺陷的区域，氧化铁皮的反光比周围其他区域高。
3、“硬边红锈判断法”：新轧制钢板表面呈现铁青色为正常现象，若存在红锈分布，则有可能存在隐藏的水波纹。红锈与青色部分柔缓过渡则没有水波纹缺陷，若红锈与青色交界边缘硬性交界，界限明显则存在水波纹缺陷。
二、磨光机打磨检验法：由于客户对钢板表面光洁度的要求不同，在不破坯钢板表面粗糙度的情况下，采取磨光机打磨钢板表面的方法，验证判断水波纹。
实施例一
如图1所示，右图是钢板轧制的表面，可看出钢板表面有斑纹；左图是采取磨光机打磨斑纹后的情况，通过图示出看出，斑纹处存在水波纹。
实施例二
如图2所示，左图是钢板轧制的表面，可看出存在红锈分布，斑点明显；右图是钢板经过抛丸处理，将钢板表面的氧化铁皮抛掉，可看出红锈斑点区域存在水波纹。
实施例三
如图3所示，左图是钢板轧制的表面，可看出某区域反光比较强烈，右图是抛丸后的表面,可看出反光区域存在水波纹。
实施例四
如图4所示，左图是钢板轧制的正常表面,钢板表面是均匀的红色,右图是抛丸后的表面,可看出钢板表面没有水波纹。
Claims (4)
1.一种钢板皮下水波纹检验方法，其特征在于包括：
A、钢板表面存在氧化铁皮破碎的情况下，若裸露部分平整，则没有水波纹缺陷；若裸露部分出现蜂窝状点、线凹不平，则存在水波纹缺陷；
B、反光检查：若钢板表面某区域氧化铁皮的反光比周围其他区域高，则存在水波纹缺陷；
C、“硬边红锈判断法”：新轧制钢板表面呈现铁青色为正常现象，若存在红锈分布，则可能存在隐藏的水波纹，通过红锈与青色部分交界情况进一步判断。
2.如权利要求1所述的钢板皮下水波纹检验方法，其特征在于还包括：在不破坏钢板表面粗糙度的前提下，采取磨光机打磨钢板表面的方法进行检测。
3.如权利要求1所述的钢板皮下水波纹检验方法，其特征在于红锈与青色部分柔缓过渡则没有水波纹缺陷。
4.如权利要求1所述的钢板皮下水波纹检验方法，其特征在于若红锈与青色部分交界边缘硬性交界，界限明显则存在水波纹缺陷。