CN109056032A - 钛合金发黑阳极氧化工艺 - Google Patents
钛合金发黑阳极氧化工艺 Download PDFInfo
- Publication number
- CN109056032A CN109056032A CN201811147278.6A CN201811147278A CN109056032A CN 109056032 A CN109056032 A CN 109056032A CN 201811147278 A CN201811147278 A CN 201811147278A CN 109056032 A CN109056032 A CN 109056032A
- Authority
- CN
- China
- Prior art keywords
- titanium alloy
- washes
- nigrescence
- oxidation
- oxidation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种钛合金发黑阳极氧化工艺,钛合金氧化膜可改善基体的某些表面性能,提高钛合金基体耐磨性,耐蚀性。传统的钛合金黑色着色实验是在重铬酸盐作为阳极氧化电解液的主盐,但重铬酸盐具有很强的致癌性,对环境污染严重。针对含铬黑着色实验存在的问题开发了钛合金无铬黑色阳极氧化。进一步减轻了电解液的毒性,使电解液更环保更清洁。本发明使用两种其他盐类代替重铬酸盐进行实验。
Description
技术领域
本发明具体为航空航天以及半导体领域,具体是一种钛合金发黑阳极氧化工艺。
背景技术
随着航空航天的大力发展,轻金属的应用越来越广泛,由于钛及钛合金具有特殊的优良特性,如比强度高,低密度。无磁性。抗高温,热膨胀系数小以及耐腐蚀性高等优点。但钛合金也处存在一些缺陷,如耐磨性,易氧化,对涂层附着力差等。常需要对钛合金进行表面强化。而电化学法在表面处理技术方面是极其重要的手段之一。
发明内容
本发明的目的是提供一种钛合金发黑阳极氧化工艺。
本发明采用的技术方案是:
一种钛合金发黑阳极氧化工艺,在酸性电解质溶液中利用正直流稳压对钛合金进行发黑阳极氧化;
具体方法为:
(1)除油,除去表面油类污染物,增加润湿性,防止氧化不均匀;
(2)水洗,充分水洗;
(3)酸洗,除去钛合金表面存在的一层不规则的氧化膜,除不净,着色不均匀,容易出现斑点;
(4)水洗,充分水洗;
(5)将水洗干净的钛合金迅速转移到阳极氧化槽中,使用含有定量硫酸锰和硫酸铵的电解质溶液阳极氧化;
(6)水洗,充分水洗;
(7)封孔,为了保护着色膜,用95度以上热水封孔20min。
本发明的有益效果为:
本发明钛合金氧化膜可改善基体的表面性能,提高钛合金基体耐磨性,耐蚀性。
具体实施方式
一种钛合金发黑阳极氧化工艺,钛合金发黑阳极氧化工艺具体方法:
(1)除油:除去表面油类污染物,增加润湿性,防止氧化不均匀。本专利使用的是碱性除油剂麦德美ISOPREP49L;
(2)水洗:充分水洗;
(3)酸洗:除去钛合金表面存在的一层不规则的氧化膜,除不净,着色不均匀,容易出现斑点。通过把硝酸,氢氟酸,水按照2:1:7比例混合可以有效去除钛合金表面氧化膜;
(4)水洗:充分水洗;
(5)将水洗干净的钛合金迅速转移到阳极氧化槽中,使用含有促黑剂硫酸锰浓度16g/L,氧化剂和导电剂硫酸铵浓度16g/L的电解质溶液,在正直流模式下稳压9V。氧化8-12min。就能得到耐磨性较好的黑色钛合金阳极氧化膜;
(6)水洗:充分水洗;
(7)封孔:为了保护着着色膜,用95度以上热水封孔20min。
Claims (1)
1.一种钛合金发黑阳极氧化工艺,其特征在于:
在酸性电解质溶液中利用正直流稳压对钛合金进行发黑阳极氧化;
具体方法为:
(1)除油,除去表面油类污染物,增加润湿性,防止氧化不均匀;
(2)水洗,充分水洗;
(3)酸洗,除去钛合金表面存在的一层不规则的氧化膜,除不净,着色不均匀,容易出现斑点;
(4)水洗,充分水洗;
(5)将水洗干净的钛合金迅速转移到阳极氧化槽中,使用含有定量硫酸锰和硫酸铵的电解质溶液阳极氧化;
(6)水洗,充分水洗;
(7)封孔,为了保护着色膜,用95度以上热水封孔20min。