CN109054312A - The preparation method of PBT fiber master batch - Google Patents
The preparation method of PBT fiber master batch Download PDFInfo
- Publication number
- CN109054312A CN109054312A CN201810833508.8A CN201810833508A CN109054312A CN 109054312 A CN109054312 A CN 109054312A CN 201810833508 A CN201810833508 A CN 201810833508A CN 109054312 A CN109054312 A CN 109054312A
- Authority
- CN
- China
- Prior art keywords
- pigment
- parts
- master batch
- preparation
- pbt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of PBT fiber master batch, and by weight, the master batch is composed of the following components: 23 parts of PBT, 12 parts of pigment, 1.4 parts of cobalt naphthenates, 2.3 parts of aminotriacetic acids, 3.1 parts of sulfamic acids, 0.8 part of zinc dihydrogen phosphate, 1.5 parts of prodans, 2.6 parts of polyoxyethylene oleates, 0.9 part of sodium secondary alkyl sulfonate, 1.1 parts of sodium peroxydisulfates, 2.3 parts of nonylphenol ethylene oxide carboxylics, 1.9 parts of N-Methyl pyrrolidones.Master batch prepared by the present invention is suitable for PBT fiber, and the anti-ultraviolet property of master batch is good.
Description
Technical field
The present invention relates to the preparation methods of PBT fiber master batch.
Background technique
PBT fiber is one kind smaller in chemical synthetic fiber, but in recent years with propylene glycol and butanediol synthesis at
The cost of this decline, PBT slice declines quickly, so that PBT fiber increases quickly.It is greatly to have that PBT fiber, which has,
The method of the form application of color fibre, most energy-saving and environment-friendly production colour PBT fiber is Masterbatch original liquid coloring method.
Occasion is knitted since PBT fiber is largely used in color, it can be by high temperature washing, high-temperature shaping, very in post-processing
The processes such as dye again to high temperature, so to the more demanding of master batch.
Summary of the invention
The purpose of the present invention is to provide a kind of preparation method of PBT fiber master batch, it is fine that the master batch of preparation is suitable for PBT
Dimension, and the anti-ultraviolet property of master batch is good.
To achieve the above object, the technical scheme is to design a kind of preparation methods of PBT fiber master batch, by weight
Part meter is measured, the master batch is composed of the following components:
23 parts of PBT,
12 parts of pigment,
1.4 parts of cobalt naphthenates,
2.3 parts of aminotriacetic acids,
3.1 parts of sulfamic acids,
0.8 part of zinc dihydrogen phosphate,
1.5 parts of prodans,
2.6 parts of polyoxyethylene oleates,
0.9 part of sodium secondary alkyl sulfonate,
1.1 parts of sodium peroxydisulfates,
2.3 parts of nonylphenol ethylene oxide carboxylics,
1.9 parts of N-Methyl pyrrolidones;
The preparation method includes the following steps:
1) pigment first carries out wet grinding decentralized processing, and pigment and liquid phase medium are isolated after partial size is qualified, is taken off under vacuum clean
Decentralized medium is spare;
2) each component is mixed, is squeezed out in double screw extruder, water cooling bracing pelletizing obtains master batch.
Preferably, control pigment particle size D50 is 0.9 hereinafter, D90 is at 1.2 microns or less.
Preferably, the pigment include paratonere 166, pigment red 21 4, paratonere 254, pigment orange 68, pigment yellow 110,
Pigment yellow 180, pigment yellow 183, pigment yellow 196, pigment Green 7, pigment blue 15: 1, pigment blue 15: 3, pigment blue 60, pigment violet
19, one or more of pigment Violet 23, pigment black 7.
The advantages and beneficial effects of the present invention are: master batch prepared by the present invention is suitable for PBT fiber, and the anti-purple of master batch
Outside line performance is good.
The performance and purposes of master batch are to be determined by its component and proportion, and the different component in master batch can mutual shadow
Sound, component and its proportion can determine the final performance of master batch, and if fruit component and its proportion be not mutually coordinated, single component is brought
Beneficial effect, can even be eliminated by other components abatement, when serious, different component is mutually contradicted, and is not had whole comprehensive
Cooperation is used, and negative interaction and substandard products are generated.The present invention passes through a large amount of creative works, verifies repeatedly, obtains the optimal component of master batch
And proportion, so that multiple components combine, are mutually coordinated and generate positive comprehensive effect.
By test, the anti-ultraviolet property of master batch is good, and ultraviolet ray transmissivity is no more than 2.5%, and master batch is suitable for PBT
Fiber.
The present invention handles pigment using wet grinding dispersing method, and Masterbatch is then made together with other various ingredients,
Masterbatch is provided to chemical fibre factory and is spun into colored fiber, can be very good to solve spinning processing problems and downstream Hou Dao factory plus
The Fastness Problems such as migration, colour fading, viscous color pollution are alleviated or avoided in work problem.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more
Add and clearly demonstrate technical solution of the present invention, and not intended to limit the protection scope of the present invention.
The technical solution that the present invention embodies is:
A kind of preparation method of PBT fiber master batch, by weight, the master batch is composed of the following components:
23 parts of PBT,
12 parts of pigment,
1.4 parts of cobalt naphthenates,
2.3 parts of aminotriacetic acids,
3.1 parts of sulfamic acids,
0.8 part of zinc dihydrogen phosphate,
1.5 parts of prodans,
2.6 parts of polyoxyethylene oleates,
0.9 part of sodium secondary alkyl sulfonate,
1.1 parts of sodium peroxydisulfates,
2.3 parts of nonylphenol ethylene oxide carboxylics,
1.9 parts of N-Methyl pyrrolidones;
The preparation method includes the following steps:
1) pigment first carries out wet grinding decentralized processing, and pigment and liquid phase medium are isolated after partial size is qualified, is taken off under vacuum clean
Decentralized medium is spare;
2) each component is mixed, is squeezed out in double screw extruder, water cooling bracing pelletizing obtains master batch.
Pigment particle size D50 is controlled 0.9 hereinafter, D90 is at 1.2 microns or less.
The pigment includes paratonere 166, pigment red 21 4, paratonere 254, pigment orange 68, pigment yellow 110, pigment yellow
180, pigment yellow 183, pigment yellow 196, pigment Green 7, pigment blue 15: 1, pigment blue 15: 3, pigment blue 60, pigment violet 19, pigment
One or more of purple 23, pigment black 7.
By test, the anti-ultraviolet property of master batch is good, and ultraviolet ray transmissivity is no more than 2.5%, and master batch is suitable for PBT
Fiber.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (3)
- The preparation method of 1.PBT fiber master batch, it is characterised in that:By weight, the master batch is composed of the following components:23 parts of PBT,12 parts of pigment,1.4 part cobalt naphthenate,2.3 parts of aminotriacetic acids,3.1 parts of sulfamic acids,0.8 part of zinc dihydrogen phosphate,1.5 parts of prodans,2.6 parts of polyoxyethylene oleates,0.9 part of sodium secondary alkyl sulfonate,1.1 parts of sodium peroxydisulfates,2.3 parts of nonylphenol ethylene oxide carboxylics,1.9 parts of N-Methyl pyrrolidones;The preparation method includes the following steps:1) pigment first carries out wet grinding decentralized processing, and pigment and liquid phase medium are isolated after partial size is qualified, is taken off under vacuum clean Decentralized medium is spare;2) each component is mixed, is squeezed out in double screw extruder, water cooling bracing pelletizing obtains master batch.
- 2. the preparation method of PBT fiber master batch according to claim 1, which is characterized in that control pigment particle size D50 exists 0.9 hereinafter, D90 at 1.2 microns or less.
- 3. the preparation method of PBT fiber master batch according to claim 2, which is characterized in that the pigment includes pigment Red 166, pigment red 21 4, paratonere 254, pigment orange 68, pigment yellow 110, pigment yellow 180, pigment yellow 183, pigment yellow 196, face Expect green 7, pigment blue 15: 1, pigment blue 15: 3, one or more of pigment blue 60, pigment violet 19, pigment Violet 23, pigment black 7.