CN112409852A - Production process of interior wall coating for decoration - Google Patents
Production process of interior wall coating for decoration Download PDFInfo
- Publication number
- CN112409852A CN112409852A CN202011285485.5A CN202011285485A CN112409852A CN 112409852 A CN112409852 A CN 112409852A CN 202011285485 A CN202011285485 A CN 202011285485A CN 112409852 A CN112409852 A CN 112409852A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- interior wall
- solution
- wall coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of an interior wall coating for decoration, which comprises a chemical formula for forming the interior wall coating, wherein the formula comprises the following components in parts by weight: 10-15 parts of epoxy resin modified styrene-acrylic emulsion, 20-30 parts of water, 1-2 parts of polyvinyl alcohol, 5-15 parts of calcium carbonate, 10-20 parts of talcum powder, 3-12 parts of titanium dioxide, 0.5-1.5 parts of film-forming additive, 0.2-0.6 part of dispersing agent, 0.3-0.5 part of defoaming agent, 0.8-1.5 parts of mildew-proof preservative, 8-12 parts of plasticizer, 2-7 parts of stabilizer and 0.1-0.3 part of thickening agent. According to the production process of the interior wall coating for decoration, the coating has the effects of no toxicity, scrubbing resistance, water resistance and strong stability, and meanwhile, the advantages of mildew resistance and corrosion resistance can be achieved, compared with the use of the styrene-acrylic emulsion at the present stage, the epoxy resin modified styrene-acrylic emulsion has the advantages of more obvious water resistance and wear resistance, and the prepared interior wall coating has stronger stability and greatly prolonged service life by being matched with polyvinyl alcohol.
Description
Technical Field
The invention belongs to the technical field of paint production and processing, and particularly relates to a production process of an interior wall paint for decoration.
Background
The coating is traditionally named as paint in China. The coating is a continuous film which is coated on the surface of a protected or decorated object and can form firm adhesion with the coated object, and is a viscous liquid which is prepared by using resin, oil or emulsion as a main material, adding or not adding pigments and fillers, adding corresponding auxiliary agents and using organic solvents or water, and the interior wall coating is the emulsion paint for general decoration. The latex paint is an emulsion paint and is divided into two categories, namely polyvinyl acetate emulsion and acrylic emulsion according to different base materials. The emulsion paint uses water as a diluent, is a coating with convenient construction, safety, water washing resistance and good air permeability, and can be prepared into different colors according to different color matching schemes. The types are as follows: a water-based inner wall paint, an oil-based inner wall paint and a dry powder type inner wall paint belong to water-based paint and mainly comprise five components of water, emulsion, pigment, filler and additive.
The existing production and preparation of the interior wall coating have poor overall effect, and even some coatings using styrene-acrylic emulsion have certain water resistance and wear resistance, the effect is still not obvious enough during the construction of the coating, and the service life is short.
Disclosure of Invention
The invention aims to provide a production process of an interior wall coating for decoration, which aims to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme:
a production process of an interior wall coating for decoration comprises a chemical formula for forming the interior wall coating, wherein the formula comprises the following components in parts by weight: 10-15 parts of epoxy resin modified styrene-acrylic emulsion, 20-30 parts of water, 1-2 parts of polyvinyl alcohol, 5-15 parts of calcium carbonate, 10-20 parts of talcum powder, 3-12 parts of titanium dioxide, 0.5-1.5 parts of film-forming additive, 0.2-0.6 part of dispersing agent, 0.3-0.5 part of defoaming agent, 0.8-1.5 parts of mildew-proof preservative, 8-12 parts of plasticizer, 2-7 parts of stabilizer and 0.1-0.3 part of thickening agent, and the specific steps of the interior wall coating generation process are as follows:
s1, sequentially adding water, a film-forming aid, titanium dioxide, a mildew-proof preservative, calcium carbonate and talcum powder in the formula into a stirring tank, and slowly stirring to form slurry;
s2, sequentially adding the dispersing agent, the defoaming agent, the plasticizer and the stabilizer into the stirring tank, rapidly stirring the stirring tank in the adding process to obtain a colloidal solution after dispersion and dilution after uniform stirring, and adding the pigment to continue stirring until uniform coloring is achieved;
s3, adding the polyvinyl alcohol and the epoxy resin modified styrene-acrylic emulsion into the colored colloidal solution, slowly stirring, quickly stirring until the mixture is uniform, and stopping stirring;
and S4, diluting the thickening agent, adding the diluted thickening agent into a stirring tank, adjusting the viscosity of the solution in the stirring tank, slowly stirring the solution after the viscosity is adjusted, discharging the solution, filtering the solution, standing the solution, and packaging the solution.
Preferably, when titanium dioxide, talcum powder and calcium carbonate are added in S1, the titanium dioxide, talcum powder and calcium carbonate are crushed by a crusher before being added, and are filtered by a filter screen of 300-800 meshes.
Preferably, in S1, the temperature for stirring after the raw materials are added is normal temperature, and the rotation speed of the stirrer is controlled to be 300-600 r/min.
Preferably, in S2, the rotating speed of rapid stirring after the dispersing agent is added is controlled to be 800-1600 r/min, the time of rapid stirring is controlled to be 15-30 min, and still standing is needed for 10-20 min after the dispersing is completed.
Preferably, the pigment is added in the S2 in a proportion of 0.5-1.0% of the total component, and the pigment can be any one of chrome yellow, iron blue, chrome green, zinc oxide and the like according to requirements.
Preferably, in S3, the rotating speed of the stirrer is reduced to 450-600 r/min after the epoxy resin modified styrene-acrylic emulsion and the polyvinyl alcohol are added, the temperature is controlled to be 10-20 ℃, and the stirring time is controlled to be 30 min.
Preferably, in S4, the diluted thickening agent is added, the rotating speed of the stirrer is reduced to 300-450 r/min, the overall viscosity of the solution is adjusted to 90-130 KU, and then the solution is discharged.
The invention has the technical effects and advantages that: according to the production process of the interior wall coating for decoration, the prepared coating has the advantages of being nontoxic, scrubbing-resistant, water-resistant and high in stability through the matching of the mildew-proof preservative, the stabilizer, the epoxy resin modified styrene-acrylic emulsion, the polyvinyl alcohol and the film forming additive, meanwhile, the mildew-proof preservative can be achieved, compared with the use of the styrene-acrylic emulsion at the present stage, the epoxy resin modified styrene-acrylic emulsion has the advantages of being more obvious in water resistance and wear resistance, the prepared stability is higher due to the matching of the polyvinyl alcohol, the service life of the interior wall coating is greatly prolonged, the construction process is simple, the construction cost is not increased, and the interior wall decoration is more convenient to use.
Detailed Description
The technical solutions in the present invention will be described clearly and completely with reference to the contents of the present invention, and it is obvious that the described contents are only a part of the contents of the present invention, and not all of the contents. All other matters which can be obtained by a person skilled in the art without making creative efforts based on the contents of the present invention belong to the protection scope of the present invention.
Example 1
The invention provides a production process of an interior wall coating for decoration, which comprises a chemical formula for forming the interior wall coating, wherein the formula comprises the following components in parts by weight: 10 parts of epoxy resin modified styrene-acrylic emulsion, 20 parts of water, 1 part of polyvinyl alcohol, 5 parts of calcium carbonate, 10 parts of talcum powder, 3 parts of titanium dioxide, 0.5 part of film-forming additive, 0.2 part of dispersing agent, 0.3 part of defoaming agent, 0.8 part of mildew-proof preservative, 8 parts of plasticizer, 2 parts of stabilizer and 0.1 part of thickening agent, wherein the specific steps of the interior wall coating generation process are as follows:
s1, sequentially adding water, a film-forming aid, titanium dioxide, a mildew-proof preservative, calcium carbonate and talcum powder in the formula into a stirring tank, and slowly stirring to form slurry;
s2, sequentially adding the dispersing agent, the defoaming agent, the plasticizer and the stabilizer into the stirring tank, rapidly stirring the stirring tank in the adding process to obtain a colloidal solution after dispersion and dilution after uniform stirring, and adding the pigment to continue stirring until uniform coloring is achieved;
s3, adding the polyvinyl alcohol and the epoxy resin modified styrene-acrylic emulsion into the colored colloidal solution, slowly stirring, quickly stirring until the mixture is uniform, and stopping stirring;
and S4, diluting the thickening agent, adding the diluted thickening agent into a stirring tank, adjusting the viscosity of the solution in the stirring tank, slowly stirring the solution after the viscosity is adjusted, discharging the solution, filtering the solution, standing the solution, and packaging the solution.
Specifically, in the step S1, when titanium dioxide, talcum powder and calcium carbonate are added, the titanium dioxide, talcum powder and calcium carbonate are crushed by a crusher before being added, and are filtered by a filter screen with 300 meshes.
Specifically, in S1, the temperature at which the raw materials are added and stirred is normal temperature, and the rotation speed of the stirrer is controlled to 300 r/min.
Specifically, in S2, the rotation speed of rapid stirring after the dispersant is added is controlled at 800r/min, the time of rapid stirring is controlled at 15min, and the mixture still needs to be kept for 10min after the dispersion is completed.
Specifically, in S2, the proportion of the added pigment is 0.5% of the total component proportion, and the pigment may be any one of the group of chrome yellow, iron blue, chrome green, zinc oxide and the like as required.
Specifically, in S3, after the epoxy resin modified styrene-acrylic emulsion and the polyvinyl alcohol are added, the rotating speed of the stirrer is reduced to 450r/min, the temperature is controlled at 10 ℃, and the stirring time is controlled at 30 min.
Specifically, in S4, the diluted thickening agent is added, the rotating speed of the stirrer is reduced to 300r/min, the overall viscosity of the solution is adjusted to 90KU, and then the solution is discharged.
Example 2
A production process of an interior wall coating for decoration comprises a chemical formula for forming the interior wall coating, wherein the formula comprises the following components in parts by weight: 12 parts of epoxy resin modified styrene-acrylic emulsion, 25 parts of water, 1.5 parts of polyvinyl alcohol, 10 parts of calcium carbonate, 15 parts of talcum powder, 7 parts of titanium dioxide, 1.0 part of film-forming additive, 0.4 part of dispersing agent, 0.4 part of defoaming agent, 1.2 parts of mildew-proof preservative, 10 parts of plasticizer, 5 parts of stabilizer and 0.2 part of thickening agent, wherein the specific steps of the interior wall coating generation process are as follows:
s1, sequentially adding water, a film-forming aid, titanium dioxide, a mildew-proof preservative, calcium carbonate and talcum powder in the formula into a stirring tank, and slowly stirring to form slurry;
s2, sequentially adding the dispersing agent, the defoaming agent, the plasticizer and the stabilizer into the stirring tank, rapidly stirring the stirring tank in the adding process to obtain a colloidal solution after dispersion and dilution after uniform stirring, and adding the pigment to continue stirring until uniform coloring is achieved;
s3, adding the polyvinyl alcohol and the epoxy resin modified styrene-acrylic emulsion into the colored colloidal solution, slowly stirring, quickly stirring until the mixture is uniform, and stopping stirring;
and S4, diluting the thickening agent, adding the diluted thickening agent into a stirring tank, adjusting the viscosity of the solution in the stirring tank, slowly stirring the solution after the viscosity is adjusted, discharging the solution, filtering the solution, standing the solution, and packaging the solution.
Specifically, when titanium dioxide, talcum powder and calcium carbonate are added in S1, the titanium dioxide, talcum powder and calcium carbonate are crushed by a crusher before being added, and are filtered by a 600-mesh filter screen.
Specifically, in S1, the temperature at which the raw materials are added and stirred is normal temperature, and the rotation speed of the stirrer is controlled at 450 r/min.
Specifically, in S2, the rotation speed of rapid stirring after the dispersant is added is controlled at 1200r/min, the time of rapid stirring is controlled at 25min, and the mixture still needs to be left for 15min after the dispersion is completed.
Specifically, in S2, the proportion of the added pigment is 0.75% of the total component proportion, and the pigment may be any one of the group of chrome yellow, iron blue, chrome green, zinc oxide and the like as required.
Specifically, in S3, after the epoxy resin modified styrene-acrylic emulsion and the polyvinyl alcohol are added, the rotating speed of the stirrer is reduced to 540r/min, the temperature is controlled to be 15 ℃, and the stirring time is controlled to be 30 min.
Specifically, in S4, the diluted thickening agent is added, the rotating speed of the stirrer is reduced to 380r/min, the overall viscosity of the solution is adjusted to 110KU, and then the solution is discharged.
Example 3
A production process of an interior wall coating for decoration comprises a chemical formula for forming the interior wall coating, wherein the formula comprises the following components in parts by weight: 15 parts of epoxy resin modified styrene-acrylic emulsion, 30 parts of water, 2 parts of polyvinyl alcohol, 15 parts of calcium carbonate, 20 parts of talcum powder, 12 parts of titanium dioxide, 1.5 parts of film-forming additive, 0.6 part of dispersing agent, 0.5 part of defoaming agent, 1.5 parts of mildew-proof preservative, 12 parts of plasticizer, 7 parts of stabilizer and 0.3 part of thickening agent, wherein the specific steps of the interior wall coating generation process are as follows:
s1, sequentially adding water, a film-forming aid, titanium dioxide, a mildew-proof preservative, calcium carbonate and talcum powder in the formula into a stirring tank, and slowly stirring to form slurry;
s2, sequentially adding the dispersing agent, the defoaming agent, the plasticizer and the stabilizer into the stirring tank, rapidly stirring the stirring tank in the adding process to obtain a colloidal solution after dispersion and dilution after uniform stirring, and adding the pigment to continue stirring until uniform coloring is achieved;
s3, adding the polyvinyl alcohol and the epoxy resin modified styrene-acrylic emulsion into the colored colloidal solution, slowly stirring, quickly stirring until the mixture is uniform, and stopping stirring;
and S4, diluting the thickening agent, adding the diluted thickening agent into a stirring tank, adjusting the viscosity of the solution in the stirring tank, slowly stirring the solution after the viscosity is adjusted, discharging the solution, filtering the solution, standing the solution, and packaging the solution.
Specifically, when titanium dioxide, talcum powder and calcium carbonate are added in S1, the titanium dioxide, talcum powder and calcium carbonate are crushed by a crusher before being added, and are filtered by a 800-mesh filter screen.
Specifically, in S1, the temperature at which the raw materials are added and stirred is normal temperature, and the rotation speed of the stirrer is controlled at 600 r/min.
Specifically, in S2, the rotation speed of rapid stirring after the dispersant is added is controlled at 1600r/min, the time of rapid stirring is controlled at 30min, and the mixture is allowed to stand for 20min after the dispersion is completed.
Specifically, in S2, the proportion of the pigment added is 1.0% of the total component proportion, and the pigment may be any one of the group of chrome yellow, iron blue, chrome green, zinc oxide, and the like, as required.
Specifically, in S3, after the epoxy resin modified styrene-acrylic emulsion and the polyvinyl alcohol are added, the rotating speed of the stirrer is reduced to 600r/min, the temperature is controlled to be 20 ℃, and the stirring time is controlled to be 30 min.
Specifically, in S4, the diluted thickening agent is added, the rotating speed of the stirrer is reduced to 450r/min, the overall viscosity of the solution is adjusted to 130KU, and then the solution is discharged.
Specifically, according to the production process of the interior wall coating for decoration, when the coating obtained in the embodiment 1-3 is measured, and the proportion of the epoxy resin modified styrene-acrylic emulsion 12 parts, the water 25 parts, the polyvinyl alcohol 1.5 parts, the calcium carbonate 10 parts, the talcum powder 15 parts, the titanium dioxide 7 parts, the film-forming assistant 1.0 part, the dispersing agent 0.4 part, the defoaming agent 0.4 part, the mildew-proof preservative 1.2 parts, the plasticizer 10 parts, the stabilizer 5 parts, the thickening agent 0.2 part and the pigment is 0.75%, the prepared coating has a better effect, is better in water resistance, scrubbing resistance and wear resistance, and greatly prolongs the service life of the interior wall coating.
Finally, it should be noted that: although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that modifications may be made to the embodiments or portions thereof without departing from the spirit and scope of the invention.
Claims (7)
1. A production process of an interior wall coating for decoration is characterized by comprising the following steps: comprises a chemical formula for forming the interior wall coating, and the weight parts of each component in the formula are as follows: 10-15 parts of epoxy resin modified styrene-acrylic emulsion, 20-30 parts of water, 1-2 parts of polyvinyl alcohol, 5-15 parts of calcium carbonate, 10-20 parts of talcum powder, 3-12 parts of titanium dioxide, 0.5-1.5 parts of film-forming additive, 0.2-0.6 part of dispersing agent, 0.3-0.5 part of defoaming agent, 0.8-1.5 parts of mildew-proof preservative, 8-12 parts of plasticizer, 2-7 parts of stabilizer and 0.1-0.3 part of thickening agent, and the specific steps of the interior wall coating generation process are as follows:
s1, sequentially adding water, a film-forming aid, titanium dioxide, a mildew-proof preservative, calcium carbonate and talcum powder in the formula into a stirring tank, and slowly stirring to form slurry;
s2, sequentially adding the dispersing agent, the defoaming agent, the plasticizer and the stabilizer into the stirring tank, rapidly stirring the stirring tank in the adding process to obtain a colloidal solution after dispersion and dilution after uniform stirring, and adding the pigment to continue stirring until uniform coloring is achieved;
s3, adding the polyvinyl alcohol and the epoxy resin modified styrene-acrylic emulsion into the colored colloidal solution, slowly stirring, quickly stirring until the mixture is uniform, and stopping stirring;
and S4, diluting the thickening agent, adding the diluted thickening agent into a stirring tank, adjusting the viscosity of the solution in the stirring tank, slowly stirring the solution after the viscosity is adjusted, discharging the solution, filtering the solution, standing the solution, and packaging the solution.
2. The method for preparing a process for producing an interior wall paint for decoration according to claim 1, wherein: and S1, when adding the titanium dioxide, the talcum powder and the calcium carbonate, crushing the mixture by a crusher before adding the titanium dioxide, the talcum powder and the calcium carbonate, and filtering the mixture by a filter screen of 300-800 meshes.
3. The method for preparing a process for producing an interior wall paint for decoration according to claim 1, wherein: in S1, the temperature for stirring after the raw materials are added is normal temperature, and the rotating speed of the stirrer is controlled to be 300-600 r/min.
4. The method for preparing a process for producing an interior wall paint for decoration according to claim 1, wherein: and S2, after the dispersing agent is added, the rotating speed of rapid stirring is controlled to be 800-1600 r/min, the time of rapid stirring is controlled to be 15-30 min, and still standing is needed for 10-20 min after the dispersing is finished.
5. The method for preparing a process for producing an interior wall paint for decoration according to claim 1, wherein: in S2, the proportion of the added pigment is 0.5-1.0% of the total component proportion, and the pigment can be any one of chrome yellow, iron blue, chrome green, zinc oxide and the like according to the requirement.
6. The method for preparing a process for producing an interior wall paint for decoration according to claim 1, wherein: and S3, after the epoxy resin modified styrene-acrylic emulsion and the polyvinyl alcohol are added, the rotating speed of the stirrer is reduced to 450-600 r/min, the temperature is controlled to be 10-20 ℃, and the stirring time is controlled to be 30 min.
7. The method for preparing a process for producing an interior wall paint for decoration according to claim 1, wherein: and S4, adding the diluted thickening agent, reducing the rotating speed of the stirrer to 300-450 r/min, adjusting the overall viscosity of the solution to 90-130 KU, and discharging.