CN1145385A - Lustre paint and its prepn. tech. - Google Patents
Lustre paint and its prepn. tech. Download PDFInfo
- Publication number
- CN1145385A CN1145385A CN 96111929 CN96111929A CN1145385A CN 1145385 A CN1145385 A CN 1145385A CN 96111929 CN96111929 CN 96111929 CN 96111929 A CN96111929 A CN 96111929A CN 1145385 A CN1145385 A CN 1145385A
- Authority
- CN
- China
- Prior art keywords
- add
- mins
- rev
- deionized water
- stirrings
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A magic paint as decorative material able to generate different refracted colours from different angles and light beams is made up of phenyl propyl emulsion, colour-variable synthetic mica powder, phenmethylol, propanediol, thickening agent, disperser, defoaming agent, antimildew agent, synthetic pigment, essence, ammonia water and deionized water through preparing dispersing liquid, preparing basic material, mixing the basic material with dispersing liquid, filter, addition of thickening agent, colouring, and regulating pH value to 8-8.5, and features no poison, water-proof nature and high adhesion.
Description
The present invention relates to coating, particularly water-soluble decorative paint.
It is of a great variety that existing market is coated, (1) organic coating can be divided three classes, wherein contain various kinds of resin, closing the flock coating of multiple chemical fibre in addition, is exactly this class coating (CN1102193A) as " multi-colour paint for internal wall ", and it is full that this class coating has coating, strong adhesion, advantages such as color-variable, but closed multiple toxic substance, complex manufacturing.(2) inorganic paint, generally all adopting polyvinyl alcohol is main raw material, is equipped with various stone flour modulation and forms, such as " tempering ", " imitative porcelain " coating, this class coating is nontoxic, and cost is low, but has dull coloring, and decorative effect is poor, easy peeling, shedding, be full of cracks, characteristics such as need heat during production.(3) high-grade emulsion paint, as " multicolor finish " (CN1124266A), be main raw material with the benzene emulsion, have film smooth, advantage such as water-fast, its problem is not have the effect of colors changing hue, its decorative effect is perfect not enough.
Effect of the present invention is to overcome the problem that prior art exists, develop a kind of nontoxic, strong adhesion, water-fast washing, rich color change, the perfect coating of decorative effect, and the production technique of normal temperature processing.
Effect of the present invention adopts following prescription to realize:
Composition weight %
Benzene emulsion 50～60
Phenylcarbinol 1.5～2
Propylene glycol 4.5～6.5
Tr thickening material 2～3
SG-8000 dispersion agent 0.3～0.5
SPA-102 defoamer 0.1～0.5
Mould inhibitor sodium pentachlorophenate 0.01
Compound mica 2～4
Basic color 0.1～0.5
Essence 0.01
Ammoniacal liquor is an amount of
The deionized water surplus
Wherein benzene emulsion is the commercially available emulsion that contains 48% polyphenyl propionic acid fat.Phenylcarbinol, propylene glycol are the technical pure product of content 99%, and thickening material is commercially available Tr-thickening material.Dispersion agent is commercially available SG-800 type dispersion agent.Defoamer is commercially available SPA-102 type defoamer.Mould inhibitor is a sodium pentachlorophenate.Compound mica is commercially available color changing type mica powder, and its granularity is 300 orders.Ammoniacal liquor is analytical pure ammoniacal liquor.
The blending process of coating of the present invention is:
(1) preparation dispersion liquid: in deionized water, add dispersion agent, 900 rev/mins of stirrings at a high speed, slowing down behind the froth breaking 300 rev/mins adds the mica powder stirring, stirs well; (2) preparation base-material: with phenylcarbinol, propylene glycol stirs in the small amount of deionized water high speed, and 600 rev/mins of stirrings of middling speed add benzene emulsion, add essence again, and mould inhibitor stirs; (3) hybrid filtering: under 300 rev/mins of stirrings, slowly add base-material in the dispersion liquid, restir 1 hour, add defoamer and make no bubble, filter with 100 eye mesh screens, (4) thickening toning: under 150 rev/mins of stirrings of low speed, drip thickening material, add the required tone of basic color furnishing, go into ammoniacal liquor at last, transfer pH value to 8～8.5 to be into product.
The distinguishing feature that coating of the present invention is is:
1, coating of the present invention belongs to water-borne coatings, is nontoxic, non-harmful green product, and the employing high-grade emulsion paint of filming is coated with in being, so firm especially, water-fast washing can reach 1000 times, at 100 hours no changes of filming of bubbly water.
2, be that main raw material makes coating have safety non-toxic with the benzene emulsion, rapidly dry, color clear, shelf-stable, coating is ventilative, and is water-fast, alkaline-resisting, anti-aging, characteristics such as strong adhesion.
3, decorative effect is splendid: owing to be weighting agent with the color changing type mica powder in batching, make coating in different light rays, the brilliance that the different angles refraction is different, and can adopt different forms of construction work, reach different decorative effects, such as: cloud is mould, the various decorative patterns of silk, cloud, illusion-colour or the like, reaches multicoloured decorative effect.
Further specify the present invention below in conjunction with embodiment.
Embodiment 1
Take by weighing 28.6 kilograms of deionized waters, add 0.3 kilogram of SG-8001 dispersion agent, high-speed stirring (900 rev/mins) makes it evenly to be decelerated to 300 rev/mins to froth breaking after 10 minutes, slowly adds 3 kilograms of mica powders while stirring, and it is stand-by that restir was made into dispersion liquid in 30 minutes; With 1.5 kilograms of phenylcarbinols, 4.5 kilograms of propylene glycol, 3 kilograms of deionized waters, high-speed stirring made it evenly to be decelerated to 600 rev/mins in 10 minutes, added 55 kilograms of benzene emulsions, added 0.01 kilogram in essence, and 0.01 kilogram of mould inhibitor stirs 30 public clocks, is mixed with base-material; In 300 rev/mins under the stirring at low speed, slowly join base-material in the dispersion liquid, restir 60 minutes adds 0.4 kilogram of defoamer, to there not being bubble, filter with 100 eye mesh screens, under 150 rev/mins of stirrings, in filter pulp, drip 2.5 kilograms of thickening materials, add 0.2 kilogram of basic color then, add 0.98 kilogram of ammoniacal liquor at last, transfer pH value to reach 8.3, promptly make 100 kilograms of finished products.All technological process is all carried out at normal temperatures.
Claims (3)
1, a kind of honorable coating, by benzene emulsion, phenylcarbinol, propylene glycol, thickening material, defoamer, mould inhibitor are formed, and its prescription is:
Composition weight %
Benzene emulsion 50～60
Phenylcarbinol 1.5～2
Propylene glycol 4.5～6.5
Tr thickening material 2～3
SG-8000 dispersion agent 0.3～0.5
SPA-102 defoamer 0.1～0.5
Mould inhibitor sodium pentachlorophenate 0.01
Compound mica 2～4
Basic color 0.1～0.5
Essence 0.01
Ammoniacal liquor is an amount of
The deionized water surplus
2, coating according to claim 1 is characterized in that, compound mica is a color changing type, and its granularity is 300 orders.
3, a kind of processing method of producing claim 1 is:
(1) preparation dispersion liquid: in deionized water, add dispersion agent, 900 rev/mins of stirrings at a high speed add mica powder and stir behind the froth breaking, (2) preparation base-material: with phenylcarbinol, propylene glycol stirred 10 minutes in the small amount of deionized water high speed, be decelerated to 600 rev/mins, add benzene emulsion, add essence, mould inhibitor, restir 30 minutes, (3) hybrid filtering: under 300 rev/mins of stirrings, slowly join base-material in the dispersion liquid, restir 60 minutes, add defoamer,, filter with 100 eye mesh screens to there not being bubble, (4) under 150 rev/mins of stirrings, in filter pulp, drip thickening material, add basic color then, add ammoniacal liquor at last, transfer pH value to 8～8.5 to be finished product.