CN103643342A - Textile line made of polyester fiber and preparation method of the same - Google Patents
Textile line made of polyester fiber and preparation method of the same Download PDFInfo
- Publication number
- CN103643342A CN103643342A CN201310571536.4A CN201310571536A CN103643342A CN 103643342 A CN103643342 A CN 103643342A CN 201310571536 A CN201310571536 A CN 201310571536A CN 103643342 A CN103643342 A CN 103643342A
- Authority
- CN
- China
- Prior art keywords
- braided wire
- preparation
- masterbatch
- polyester fiber
- cut sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a textile line made of polyester fiber. The textile line is colored, is red, orange, yellow, green, cyan, blue or purple or a combination of the colors. The textile line has one or more of an ultraviolet resistant function, an antibacterial function, an antioxidant function and an anti-aging function. The invention provides a preparation method for the textile line made of polyester fiber. The method comprises the steps of: drying, i.e. drying white slices and masterbatches; mixing, i.e. mixing the dried white slices and masterbatches; fusion, i.e. subjecting the mixture to fusion; spinning, i.e. spinning the fused mixture to form a textile; and oiling, i.e. adding an oiling agent to the textile. The textile line made of polyester fiber provided by the invention can be in various colors, and has uniform color in line with the requirements. The preparation method of the textile line has the characteristics of simplicity, small pollution, and good coloring efficiency.
Description
Technical field
The present invention relates to a kind of braided wire, the invention particularly relates to a kind of braided wire being formed by polyester fiber.
The present invention relates to a kind of preparation method of braided wire, the invention particularly relates to a kind of preparation method of the braided wire of being made by polyester fiber.
Background technology
In conventional art, polyester fiber is widely used in apparel industry.The braided wire of being made by polyester fiber is netrual colour mostly.Netrual colour refers to white or black.But in actual production, the braided wire that urgent hope is made by polyester fiber can be various colors.
Summary of the invention
In traditional textile industry, generally adopt decoration method to paint to braided wire.But due to the self attributes of polyester fiber, its dyeability is poor, adopt traditional decoration method not reach requirement.
The invention provides a kind of braided wire of being made by polyester fiber, it can be various chromatic colours.The invention provides a kind of preparation method of the braided wire of being made by polyester fiber, it can be produced and be various coloured braided wires.
The invention discloses a kind of braided wire of being made by polyester fiber, the color of this braided wire is chromatic colour.
Preferably, described braided wire is the combination of a kind of or above-mentioned color of red, orange, yellow, green, blue, blue, purple.
Preferably, described braided wire has one or more in anti-ultraviolet function, antibacterial functions, anti-oxidation function or anti-aging function.
The preparation method who the invention provides a kind of braided wire of being made by polyester fiber, it comprises the following steps:
Dry, white cut sheet is dried, Masterbatch is dried;
Mix, by completing dry described white cut sheet and described Masterbatch, mix;
Melting, carries out melting by mixture;
Spinning, carries out spinning by the mixture after melting and forms textiles;
Oil, on textiles, add finish.
Preferably, ultraviolet screening mother granule is dried, by completing dry white cut sheet, Masterbatch and ultraviolet screening mother granule, mixes.
Preferably, antibacterial matrices is dried, by completing dry white cut sheet, Masterbatch and antibacterial matrices, mixes.
Preferably, anti-oxidant master batch is dried, by completing dry white cut sheet, Masterbatch and anti-oxidant master batch, mixes.
Preferably, anti-aging master batch is dried, by completing dry white cut sheet, Masterbatch and anti-aging master batch, mixes.
Preferably, described Masterbatch is the combination of a kind of or above-mentioned color of red, orange, yellow, green, blue, blue, purple.
The present invention adopts above structure and method, has the following advantages:
The braided wire that should be made by polyester fiber can be shades of colour.The color of this braided wire evenly meets the requirements.
The preparation processing method of this braided wire is simple, pollute little, colouring excellent in efficiency.
Accompanying drawing explanation
Fig. 1 has shown the first embodiment of the preparation method of the braided wire of being made by polyester fiber.
Fig. 2 has shown the second embodiment of the preparation method of the braided wire of being made by polyester fiber.
Fig. 3 reality preparation method's the 3rd embodiment of the braided wire made by polyester fiber.
Fig. 4 reality preparation method's the 4th embodiment of the braided wire made by polyester fiber.
Fig. 5 reality preparation method's the 5th embodiment of the braided wire made by polyester fiber.
The specific embodiment
Below in conjunction with accompanying drawing, preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be those skilled in the art will recognize that, protection scope of the present invention is made to more explicit defining.
In the embodiment of the braided wire of being made by polyester fiber in the present invention, the color of this braided wire is chromatic colour.The polyester that polyester fiber (polyester fibre) refers to, formed by organic dibasic acid and dihydroxylic alcohols polycondensation is through the synthetic fiber of spinning gained.Chromatic colour is different from netrual colour, and chromatic colour refers to the combination of a kind of or above-mentioned color that is red, orange, yellow, green, blue, blue, purple.Due to the color-variable of this braided wire of being made by polyester fiber, color is evenly effective, thereby meets the requirements.
Fig. 1 has shown a kind of preparation method of the braided wire of being made by polyester fiber.
As shown in Figure 1, in the preparation method's of the braided wire of being made by polyester fiber in the present invention embodiment, this preparation method comprises the following steps:
(1) dry, white cut sheet is dried, Masterbatch is dried;
(2) mix, by completing dry described white cut sheet and described Masterbatch, mix;
(3) melting, carries out melting by mixture;
(4) spinning, carries out spinning by the mixture after melting and forms textiles;
(5) oil, on textiles, add finish.
In step (1), the moisture in white cut sheet and Masterbatch is removed.White cut sheet refers to the raw material of the polyester fiber being white in color.Masterbatch claims again look female, Masterbatch is comprised of pigment or dyestuff, carrier and three kinds of fundamentals of additive, that the pigment of super quantity or dyestuff are attached among resin and the aggregation obtaining equably, can claim condensed pigment (PigmentConcentration), so his tinting strength, tinting power is higher than pigment itself.Because the quantity of white cut sheet is more, thereby dialogue section adopts cyclonic separation drying unit.To Masterbatch, adopt hot blast to dry.In step (1), can also comprise a step, the quantity of the quantity of Masterbatch and white cut sheet is controlled, to meet the color requirement of last braided wire.
In step (2), mix, by completing dry white cut sheet and Masterbatch, mix, make white cut sheet and Masterbatch form mixture.
In step (3), melting, carries out melting by mixture, makes mixture in molten condition.
In step (4), spinning, carries out spinning by the mixture after melting and forms textiles.Spinning comprises two steps, spray silk and curing.Spray silk refers to that the mixture in molten condition sprays from spinnerets.Solidify and refer to that the mixture solidified spraying becomes braided wire from spinnerets.
In step (5), oil, finish is coated to the surface of braided wire.Finish is polyester oiling agent.Finish can be eliminated the static on braided wire surface, can improve the saturation degree of braided wire.
One preferred embodiment in, be that with the difference of above-described embodiment this braided wire has anti-ultraviolet function.As shown in Figure 2, corresponding method and the difference of above-described embodiment are as ultraviolet screening mother granule is dried with it, in step (2), by completing dry white cut sheet, Masterbatch and ultraviolet screening mother granule, mix.It is compound that ultraviolet screening mother granule adopts two kinds of ultraviolet (UV) resistant agent to carry out, then mix the auxiliary agents such as carrier, dispersant and make.
One preferred embodiment in, be that with the difference of above-described embodiment this braided wire has antibacterial functions.As shown in Figure 3, corresponding method and the difference of above-described embodiment are as antibacterial matrices is dried with it, in step (2), by completing dry white cut sheet, Masterbatch and antibacterial matrices, mix.
One preferred embodiment in, be that with the difference of above-described embodiment this braided wire has anti-oxidation function.As shown in Figure 4, corresponding method and the difference of above-described embodiment are as anti-oxidant master batch is dried with it, in step (2), by completing dry white cut sheet, Masterbatch and anti-oxidant master batch, mix.
One preferred embodiment in, be that with the difference of above-described embodiment this braided wire has anti-aging function.As shown in Figure 5, corresponding method and the difference of above-described embodiment are as anti-aging master batch is dried with it, in step (2), by completing dry white cut sheet, Masterbatch and anti-aging master batch, mix.
Each embodiment in this description all adopts the mode of going forward one by one to describe, and each embodiment stresses is the difference with other embodiment, between each embodiment identical similar part mutually referring to.
Above-described embodiment is only technical conceive and the feature of the invention of this reality of explanation, and its object is to allow person skilled in the art can understand content of the present invention and implement according to this, can not limit the scope of the invention with this.All equivalences that Spirit Essence is done according to the present invention change or modify, within all should being encompassed in protection scope of the present invention.
Claims (9)
1. a braided wire of being made by polyester fiber, is characterized in that: the color of this braided wire is chromatic colour.
2. braided wire according to claim 1, is characterized in that: described braided wire is the combination of a kind of or above-mentioned color of red, orange, yellow, green, blue, blue, purple.
3. braided wire according to claim 1, is characterized in that: described braided wire has one or more in anti-ultraviolet function, antibacterial functions, anti-oxidation function or anti-aging function.
4. a preparation method for the braided wire of being made by polyester fiber as described in one of claims 1 to 3, is characterized in that: it comprises the following steps
Dry, white cut sheet is dried, Masterbatch is dried;
Mix, by completing dry described white cut sheet and described Masterbatch, mix;
Melting, carries out melting by mixture;
Spinning, carries out spinning by the mixture after melting and forms textiles;
Oil, on textiles, add finish.
5. preparation method according to claim 4, is characterized in that: in step (1), ultraviolet screening mother granule is dried, in step (2), by completing dry white cut sheet, Masterbatch and ultraviolet screening mother granule, mixes.
6. preparation method according to claim 4, is characterized in that: in step (1), antibacterial matrices is dried, in step (2), by completing dry white cut sheet, Masterbatch and antibacterial matrices, mixes.
7. preparation method according to claim 4, is characterized in that: in step (1), anti-oxidant master batch is dried, in step (2), by completing dry white cut sheet, Masterbatch and anti-oxidant master batch, mixes.
8. preparation method according to claim 4, is characterized in that: in step (1), anti-aging master batch is dried, in step (2), by completing dry white cut sheet, Masterbatch and anti-aging master batch, mixes.
9. preparation method according to claim 4, is characterized in that: described Masterbatch is the combination of a kind of or above-mentioned color of red, orange, yellow, green, blue, blue, purple.