CN109023618A - 涤锦共混高弹色纱及其生产方法 - Google Patents

涤锦共混高弹色纱及其生产方法 Download PDF

Info

Publication number
CN109023618A
CN109023618A CN201810807258.0A CN201810807258A CN109023618A CN 109023618 A CN109023618 A CN 109023618A CN 201810807258 A CN201810807258 A CN 201810807258A CN 109023618 A CN109023618 A CN 109023618A
Authority
CN
China
Prior art keywords
blended
brocade
dyed yarn
weight
elastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810807258.0A
Other languages
English (en)
Inventor
张国龙
杨建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhangjiagang New Silk Chemical Fiber Co Ltd
Original Assignee
Zhangjiagang New Silk Chemical Fiber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhangjiagang New Silk Chemical Fiber Co Ltd filed Critical Zhangjiagang New Silk Chemical Fiber Co Ltd
Priority to CN201810807258.0A priority Critical patent/CN109023618A/zh
Publication of CN109023618A publication Critical patent/CN109023618A/zh
Pending legal-status Critical Current

Abstract

本申请公开了一种涤锦共混高弹色纱及其生产方法，该涤锦共混高弹色纱，包括：50～70重量份的涤纶纤维；以及30～50重量份的锦纶纤维。本发明的纱线，综合了涤纶的刚性和防腐性，以及锦纶的良好手感、高弹性和耐磨性性能，可制作具有一定弹性且手感柔软、耐磨性好的织物。

Description

涤锦共混高弹色纱及其生产方法
技术领域
本申请属于纺织技术领域，特别是涉及一种涤锦共混高弹色纱及其生产方法。
背景技术
随着社会发展时代进步，人们的审美与消费观念的多元化，对于各种服装面料的需求多样化；设计是一种艺术，把艺术融于服装面料，使服装在展现不同的视觉美感的同时要求面料同时具备一定的弹性和手感良好等功能。
发明内容
本发明的目的在于提供一种涤锦共混高弹色纱及其生产方法，以克服现有技术中的不足。
为实现上述目的，本发明提供如下技术方案：
本申请实施例公开一种涤锦共混高弹色纱，包括：
50～70重量份的涤纶纤维；以及
30～50重量份的锦纶纤维。
优选的，在上述的涤锦共混高弹色纱中，还包括：
10～25重量份的抗菌纤维。
优选的，在上述的涤锦共混高弹色纱中，所述抗菌纤维是指负载有抗菌剂的涤纶纤维或锦纶纤维。
优选的，在上述的涤锦共混高弹色纱中，所述抗菌纤维中，抗菌剂按照重量的负载量为2～3％。
优选的，在上述的涤锦共混高弹色纱中，所述抗菌剂选自银、铜、氧化锌、氧化镁、氧化钙、氧化铜、磷酸二氢铵、碳酸锂中的一种或多种的组合。
优选的，在上述的涤锦共混高弹色纱中，包括：
60重量份的涤纶纤维；以及
40重量份的锦纶纤维。
相应的，本申请还公开了一种涤锦共混高弹色纱的生产方法，将涤纶纤维和锦纶纤维按比例混合后，混纺成纱线。
优选的，在上述的涤锦共混高弹色纱的生产方法中，还包括对纱线的着色。
本申请还公开了一种面料，由任一所述的涤锦共混高弹色纱编织而成。
优选的，在上述的面料的生产方法中，包括：
将涤纶纤维和锦纶纤维按比例混合后，混纺成纱线，并织造成面料；
对面料进行染色。
优选的，在上述的面料的生产方法中，面料染色方法包括：
(1)、将分散染料倒入浸轧机中，将面料放入浸轧机中浸轧，二浸二轧，轧余率为60～70％；
(2)、将浸轧后的针织面料放入烘箱中烘干，烘干温度为60～90℃，烘干时间为10～30分钟；
(3)、将烘干后的面料进行焙烘，焙烘温度为100～120℃，烘焙时间为30～60秒；
(4)、烘焙后的面料在还原清洗液中进行二次浸轧，一浸一轧，轧余率为70～80％，还原清洗液包括烧碱15～20g/L和保险粉25～35g/L；
(5)、二次浸轧后的面料进行蒸气固色，蒸箱温度为90～100℃；
(6)、将蒸气固色的面料进行水洗，并脱水和干燥，获得面料。
与现有技术相比，本发明的优点在于：本发明的纱线，综合了涤纶的刚性和防腐性，以及锦纶的良好手感、高弹性和耐磨性性能，可制作具有一定弹性且手感柔软、耐磨性好的织物。
具体实施方式
涤纶织物具有较高的强度与弹性恢复能力，因此，其坚牢耐用、抗皱免烫。涤纶织物吸湿性较差，夏季穿着有闷热感，同时冬季易带静电、影响舒适性。不过洗后极易干燥，且湿强几乎不下降，不变形，有良好的洗可穿性能。涤纶是合纤织物中耐热性最好的面料，具有热塑性，可制做百褶裙，褶裥持久。涤纶织物的耐光性较好，除比腈纶差外，其耐晒能力胜过天然纤维织物。尤其是在玻璃后面的耐晒能力很好，几乎与腈纶不相上下。涤纶织物耐各种化学品性能良好。酸、碱对其破坏程度都不大，同时不怕霉菌，不怕虫蛀。
锦纶强力、耐磨性好，居所有纤维之首。它的耐磨性是棉纤维的10倍，是干态粘胶纤维的10倍，是湿态纤维的140倍。因此，其耐用性极佳。而且锦纶还具有弹性好、手感好的优点。
本发明的面料，综合了涤纶的刚性和防腐性，以及锦纶的良好手感、高弹性和耐磨性性能，可制作具有一定弹性且手感柔软、耐磨性好的织物。
本发明通过下列实施例作进一步说明：根据下述实施例，可以更好地理解本发明。然而，本领域的技术人员容易理解，实施例所描述的具体的物料比、工艺条件及其结果仅用于说明本发明，而不应当也不会限制权利要求书中所详细描述的本发明。
实施例1
将60重量份涤纶纤维、40重量份锦纶纤维和20重量份的抗菌纤维按比例混合后，混纺成纱线。抗菌纤维是指负载有抗菌剂的涤纶纤维或锦纶纤维，抗菌剂按照重量的负载量为2.5％，抗菌剂为银。
将涤锦共混高弹色纱编织成面料。
将分散染料倒入浸轧机中，将面料放入浸轧机中浸轧，二浸二轧，轧余率为70％；将浸轧后的针织面料放入烘箱中烘干，烘干温度为70℃，烘干时间为20分钟；将烘干后的面料进行焙烘，焙烘温度为110℃，烘焙时间为40秒；烘焙后的面料在还原清洗液中进行二次浸轧，一浸一轧，轧余率为75％，还原清洗液包括烧碱20g/L和保险粉25g/L；二次浸轧后的面料进行蒸气固色，蒸箱温度为100℃；将蒸气固色的面料进行水洗，并脱水和干燥，获得面料。
获得的面料同时具备了涤纶的刚性和防腐性，以及锦纶的良好手感、高弹性和耐磨性性能，同时还具有一定的抗菌性能。
实施例2
将70重量份涤纶纤维、30重量份锦纶纤维和15重量份的抗菌纤维按比例混合后，混纺成纱线。抗菌纤维是指负载有抗菌剂的涤纶纤维或锦纶纤维，抗菌剂按照重量的负载量为3％，抗菌剂为银。
将涤锦共混高弹色纱编织成面料。
将分散染料倒入浸轧机中，将面料放入浸轧机中浸轧，二浸二轧，轧余率为70％；将浸轧后的针织面料放入烘箱中烘干，烘干温度为70℃，烘干时间为20分钟；将烘干后的面料进行焙烘，焙烘温度为120℃，烘焙时间为40秒；烘焙后的面料在还原清洗液中进行二次浸轧，一浸一轧，轧余率为75％，还原清洗液包括烧碱20g/L和保险粉25g/L；二次浸轧后的面料进行蒸气固色，蒸箱温度为100℃；将蒸气固色的面料进行水洗，并脱水和干燥，获得面料。
获得的面料同时具备了涤纶的刚性和防腐性，以及锦纶的良好手感、高弹性和耐磨性性能，同时还具有一定的抗菌性能。
实施例3
将50重量份涤纶纤维、50重量份锦纶纤维和10重量份的抗菌纤维按比例混合后，混纺成纱线。抗菌纤维是指负载有抗菌剂的涤纶纤维或锦纶纤维，抗菌剂按照重量的负载量为2％，抗菌剂为银。
将涤锦共混高弹色纱编织成面料。
将分散染料倒入浸轧机中，将面料放入浸轧机中浸轧，二浸二轧，轧余率为60％；将浸轧后的针织面料放入烘箱中烘干，烘干温度为70℃，烘干时间为20分钟；将烘干后的面料进行焙烘，焙烘温度为110℃，烘焙时间为40秒；烘焙后的面料在还原清洗液中进行二次浸轧，一浸一轧，轧余率为75％，还原清洗液包括烧碱20g/L和保险粉25g/L；二次浸轧后的面料进行蒸气固色，蒸箱温度为100℃；将蒸气固色的面料进行水洗，并脱水和干燥，获得面料。
获得的面料同时具备了涤纶的刚性和防腐性，以及锦纶的良好手感、高弹性和耐磨性性能，同时还具有一定的抗菌性能。
最后，还需要说明的是，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。

Claims (8)

1.一种涤锦共混高弹色纱，其特征在于，包括：
50～70重量份的涤纶纤维；以及
30～50重量份的锦纶纤维。
2.根据权利要求1所述的涤锦共混高弹色纱，其特征在于，还包括：
10～25重量份的抗菌纤维。
3.根据权利要求2所述的涤锦共混高弹色纱，其特征在于，所述抗菌纤维是指负载有抗菌剂的涤纶纤维或锦纶纤维。
4.根据权利要求3所述的涤锦共混高弹色纱，其特征在于，所述抗菌纤维中，抗菌剂按照重量的负载量为2～3％。
5.根据权利要求3所述的涤锦共混高弹色纱，其特征在于，所述抗菌剂选自银、铜、氧化锌、氧化镁、氧化钙、氧化铜、磷酸二氢铵、碳酸锂中的一种或多种的组合。
6.根据权利要求1所述的涤锦共混高弹色纱，其特征在于，包括：
60重量份的涤纶纤维；以及
40重量份的锦纶纤维。
7.权利要求1至6任一所述涤锦共混高弹色纱的生产方法，其特征在于，将涤纶纤维和锦纶纤维按比例混合后，混纺成纱线。
8.根据权利要求7所述涤锦共混高弹色纱的生产方法，其特征在于，还包括对纱线的着色。
CN201810807258.0A 2018-07-21 2018-07-21 涤锦共混高弹色纱及其生产方法 Pending CN109023618A (zh)