CN108976666A - 一种高强度防水保温板及其制备方法 - Google Patents

一种高强度防水保温板及其制备方法 Download PDF

Info

Publication number
CN108976666A
CN108976666A CN201810902174.5A CN201810902174A CN108976666A CN 108976666 A CN108976666 A CN 108976666A CN 201810902174 A CN201810902174 A CN 201810902174A CN 108976666 A CN108976666 A CN 108976666A
Authority
CN
China
Prior art keywords
parts
waterproofness
strength
thermal insulation
aluminium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810902174.5A
Other languages
English (en)
Inventor
郑贝贝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taizhou Zhi Zi Technology Co Ltd
Original Assignee
Taizhou Zhi Zi Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taizhou Zhi Zi Technology Co Ltd filed Critical Taizhou Zhi Zi Technology Co Ltd
Priority to CN201810902174.5A priority Critical patent/CN108976666A/zh
Publication of CN108976666A publication Critical patent/CN108976666A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种高强度防水保温板，包括以下按照重量份的原料：聚氯乙烯树脂60‑80份、聚丙烯酸酯乳液20‑30份、羧甲基纤维素钠15‑25份、多孔陶粒20‑30份、二氧化硅10‑20份、硅酸镁铝20‑30份、二乙烯基苯1‑3份、丙烯酸二甲氨基乙酯5‑10份、壬基酚聚氧乙烯醚2‑4份、麦麸5‑10份、玻璃纤维3‑5份、发泡剂1‑2份、阻燃剂1‑3份、增塑剂2‑4份、去离子水60‑80份。本发明还公开了所述高强度防水保温板的制备方法。本发明制备的保温板在各种原料的共同配合作用下，具有良好的防水性能，可以用于建筑外墙的铺设。

Description

一种高强度防水保温板及其制备方法
技术领域
本发明涉及建筑材料技术领域，具体是一种高强度防水保温板及其制备方法。
背景技术
随着我国城市建设的快速发展，庞大的建筑能耗已经成为我国经济和社会发展的巨大负担，因此，绿色节能已成为当今建筑发展的主旋律。保温材料在建筑节能过程中扮演着非常重要的角色，保温板在建筑领域应用十分广泛。保温板是以树脂为原料加上其他的原辅料与聚含物，挤塑压出成型而制造的硬质泡沫塑料板，可使减少建筑物外围护结构厚度，从而增加室内使用面积。
保温板是隔离室内环境与外部环境一种常用材料，保温板使用时往往在其外部涂覆有砂浆，起到防护作用，但砂浆吸水性能较好，导致雨水容易浸润至保温板处，现有的保温板强度一般、防水效果不够好，雨水浸润后吸水，容易导致寿命降低，影响建筑墙体的安全性能。
发明内容
本发明的目的在于提供一种高强度防水保温板，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种高强度防水保温板，包括以下按照重量份的原料：聚氯乙烯树脂60-80份、聚丙烯酸酯乳液20-30份、羧甲基纤维素钠15-25份、多孔陶粒20-30份、二氧化硅10-20份、硅酸镁铝20-30份、二乙烯基苯1-3份、丙烯酸二甲氨基乙酯5-10份、壬基酚聚氧乙烯醚2-4份、麦麸5-10份、玻璃纤维3-5份、发泡剂1-2份、阻燃剂1-3份、增塑剂2-4份、去离子水60-80份。
作为本发明进一步的方案：包括以下按照重量份的原料：聚氯乙烯树脂65-75份、聚丙烯酸酯乳液22-28份、羧甲基纤维素钠18-22份、多孔陶粒22-28份、二氧化硅12-18份、硅酸镁铝22-28份、二乙烯基苯1.5-2.5份、丙烯酸二甲氨基乙酯6-9份、壬基酚聚氧乙烯醚2.5-3.5份、麦麸6-9份、玻璃纤维3.5-4.5份、发泡剂1.2-1.8份、阻燃剂1.5-2.5份、增塑剂2.5-3.5份、去离子水65-75份。
作为本发明再进一步的方案：包括以下按照重量份的原料：聚氯乙烯树脂70份、聚丙烯酸酯乳液25份、羧甲基纤维素钠20份、多孔陶粒25份、二氧化硅15份、硅酸镁铝25份、二乙烯基苯2份、丙烯酸二甲氨基乙酯8份、壬基酚聚氧乙烯醚3份、麦麸8份、玻璃纤维4份、发泡剂1.5份、阻燃剂2份、增塑剂3份、去离子水70份。
作为本发明再进一步的方案：所述阻燃剂由三氧化二锑、氢氧化镁、氢氧化铝按重量比1:3:1混合而成。
作为本发明再进一步的方案：所述增塑剂由邻苯二甲酸二辛酯、邻苯二甲酸二丁酯按重量比2:1混合而成。
所述高强度防水保温板的制备方法，步骤如下：
1)将聚氯乙烯树脂、多孔陶粒、二氧化硅、硅酸镁铝、麦麸、玻璃纤维分别粉碎后过200-300目筛，获得各自的粉末；
2)将步骤1)获得的聚氯乙烯树脂、多孔陶粒、二氧化硅、玻璃纤维粉末混合后加入去离子水，以300-500r/min转速、80-100℃温度条件下进行搅拌，搅拌过程中缓慢加入聚丙烯酸酯乳液、羧甲基纤维素钠、丙烯酸二甲氨基乙酯，加料后继续搅拌30-50min，静置1-1.5h，获得混合物Ⅰ；
3)向步骤2)获得的混合物Ⅰ中加入步骤1)获得的硅酸镁铝、麦麸粉末，同时加入二乙烯基苯、壬基酚聚氧乙烯醚、发泡剂、阻燃剂、增塑剂，置于超声波环境下，以600-800r/min搅拌20-30min，获得混合物Ⅱ；
4)对步骤3)获得的混合物Ⅱ进行浓缩，将浓缩后的混合物Ⅱ倒入模具中，加压成型，再将加压成型得到的板材送入烘箱中烘干，冷却，即可。
作为本发明再进一步的方案：步骤3)所述的超声波频率为50-60KHz。
上述保温板在制备防水材料领域中的应用。
与现有技术相比，本发明的有益效果是：
本发明制备的保温板在各种原料的共同配合作用下，材料强度高，能够承受较强的外部压力，不易断裂，方便铺设，使用寿命长；能够有效隔绝热量，起到保温的作用，避免夏季室内高温传导至室内或冬季室内热量散失；材料表面光滑，具有良好的防水性能，可以用于建筑外墙的铺设，不会因雨水浸泡导致脱落，安全性能高。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种高强度防水保温板，包括以下按照重量份的原料：聚氯乙烯树脂60份、聚丙烯酸酯乳液20份、羧甲基纤维素钠15份、多孔陶粒20份、二氧化硅10份、硅酸镁铝20份、二乙烯基苯1份、丙烯酸二甲氨基乙酯5份、壬基酚聚氧乙烯醚2份、麦麸5份、玻璃纤维3份、发泡剂1份、阻燃剂1份、增塑剂2份、去离子水60份。
其中，所述阻燃剂由三氧化二锑、氢氧化镁、氢氧化铝按重量比1:3:1混合而成。
其中，所述增塑剂由邻苯二甲酸二辛酯、邻苯二甲酸二丁酯按重量比2:1混合而成。
本实施例中，所述高强度防水保温板的制备方法，步骤如下：
1)将聚氯乙烯树脂、多孔陶粒、二氧化硅、硅酸镁铝、麦麸、玻璃纤维分别粉碎后过200目筛，获得各自的粉末；
2)将步骤1)获得的聚氯乙烯树脂、多孔陶粒、二氧化硅、玻璃纤维粉末混合后加入去离子水，以300r/min转速、80℃温度条件下进行搅拌，搅拌过程中缓慢加入聚丙烯酸酯乳液、羧甲基纤维素钠、丙烯酸二甲氨基乙酯，加料后继续搅拌30min，静置1h，获得混合物Ⅰ；
3)向步骤2)获得的混合物Ⅰ中加入步骤1)获得的硅酸镁铝、麦麸粉末，同时加入二乙烯基苯、壬基酚聚氧乙烯醚、发泡剂、阻燃剂、增塑剂，置于超声波环境下，以600r/min搅拌20min，获得混合物Ⅱ；
4)对步骤3)获得的混合物Ⅱ进行浓缩，将浓缩后的混合物Ⅱ倒入模具中，加压成型，再将加压成型得到的板材送入烘箱中烘干，冷却，即可。
其中，步骤3)所述的超声波频率为50KHz。
实施例2
一种高强度防水保温板，包括以下按照重量份的原料：聚氯乙烯树脂65份、聚丙烯酸酯乳液22份、羧甲基纤维素钠18份、多孔陶粒22份、二氧化硅12份、硅酸镁铝22份、二乙烯基苯1.5份、丙烯酸二甲氨基乙酯9份、壬基酚聚氧乙烯醚3.5份、麦麸9份、玻璃纤维4.5份、发泡剂1.8份、阻燃剂2.5份、增塑3.5份、去离子水75份。
其中，所述阻燃剂由三氧化二锑、氢氧化镁、氢氧化铝按重量比1:3:1混合而成。
其中，所述增塑剂由邻苯二甲酸二辛酯、邻苯二甲酸二丁酯按重量比2:1混合而成。
本实施例中，所述高强度防水保温板的制备方法，步骤如下：
1)将聚氯乙烯树脂、多孔陶粒、二氧化硅、硅酸镁铝、麦麸、玻璃纤维分别粉碎后过260目筛，获得各自的粉末；
2)将步骤1)获得的聚氯乙烯树脂、多孔陶粒、二氧化硅、玻璃纤维粉末混合后加入去离子水，以400r/min转速、90℃温度条件下进行搅拌，搅拌过程中缓慢加入聚丙烯酸酯乳液、羧甲基纤维素钠、丙烯酸二甲氨基乙酯，加料后继续搅拌40min，静置1.2h，获得混合物Ⅰ；
3)向步骤2)获得的混合物Ⅰ中加入步骤1)获得的硅酸镁铝、麦麸粉末，同时加入二乙烯基苯、壬基酚聚氧乙烯醚、发泡剂、阻燃剂、增塑剂，置于超声波环境下，以700r/min搅拌25min，获得混合物Ⅱ；
4)对步骤3)获得的混合物Ⅱ进行浓缩，将浓缩后的混合物Ⅱ倒入模具中，加压成型，再将加压成型得到的板材送入烘箱中烘干，冷却，即可。
其中，步骤3)所述的超声波频率为55KHz。
实施例3
一种高强度防水保温板，包括以下按照重量份的原料：聚氯乙烯树脂70份、聚丙烯酸酯乳液25份、羧甲基纤维素钠20份、多孔陶粒25份、二氧化硅15份、硅酸镁铝25份、二乙烯基苯2份、丙烯酸二甲氨基乙酯8份、壬基酚聚氧乙烯醚3份、麦麸8份、玻璃纤维4份、发泡剂1.5份、阻燃剂2份、增塑剂3份、去离子水70份。
其中，所述阻燃剂由三氧化二锑、氢氧化镁、氢氧化铝按重量比1:3:1混合而成。
其中，所述增塑剂由邻苯二甲酸二辛酯、邻苯二甲酸二丁酯按重量比2:1混合而成。
本实施例中，所述高强度防水保温板的制备方法，步骤如下：
1)将聚氯乙烯树脂、多孔陶粒、二氧化硅、硅酸镁铝、麦麸、玻璃纤维分别粉碎后过260目筛，获得各自的粉末；
2)将步骤1)获得的聚氯乙烯树脂、多孔陶粒、二氧化硅、玻璃纤维粉末混合后加入去离子水，以400r/min转速、90℃温度条件下进行搅拌，搅拌过程中缓慢加入聚丙烯酸酯乳液、羧甲基纤维素钠、丙烯酸二甲氨基乙酯，加料后继续搅拌40min，静置1.2h，获得混合物Ⅰ；
3)向步骤2)获得的混合物Ⅰ中加入步骤1)获得的硅酸镁铝、麦麸粉末，同时加入二乙烯基苯、壬基酚聚氧乙烯醚、发泡剂、阻燃剂、增塑剂，置于超声波环境下，以700r/min搅拌25min，获得混合物Ⅱ；
4)对步骤3)获得的混合物Ⅱ进行浓缩，将浓缩后的混合物Ⅱ倒入模具中，加压成型，再将加压成型得到的板材送入烘箱中烘干，冷却，即可。
其中，步骤3)所述的超声波频率为55KHz。
实施例4
一种高强度防水保温板，包括以下按照重量份的原料：包括以下按照重量份的原料：聚氯乙烯树脂75份、聚丙烯酸酯乳液28份、羧甲基纤维素钠22份、多孔陶粒28份、二氧化硅18份、硅酸镁铝28份、二乙烯基苯2.5份、丙烯酸二甲氨基乙酯6份、壬基酚聚氧乙烯醚2.5份、麦麸6份、玻璃纤维3.5份、发泡剂1.2份、阻燃剂1.5份、增塑剂2.5份、去离子水65份。
其中，所述阻燃剂由三氧化二锑、氢氧化镁、氢氧化铝按重量比1:3:1混合而成。
其中，所述增塑剂由邻苯二甲酸二辛酯、邻苯二甲酸二丁酯按重量比2:1混合而成。
本实施例中，所述高强度防水保温板的制备方法，步骤如下：
1)将聚氯乙烯树脂、多孔陶粒、二氧化硅、硅酸镁铝、麦麸、玻璃纤维分别粉碎后过260目筛，获得各自的粉末；
2)将步骤1)获得的聚氯乙烯树脂、多孔陶粒、二氧化硅、玻璃纤维粉末混合后加入去离子水，以400r/min转速、90℃温度条件下进行搅拌，搅拌过程中缓慢加入聚丙烯酸酯乳液、羧甲基纤维素钠、丙烯酸二甲氨基乙酯，加料后继续搅拌40min，静置1.2h，获得混合物Ⅰ；
3)向步骤2)获得的混合物Ⅰ中加入步骤1)获得的硅酸镁铝、麦麸粉末，同时加入二乙烯基苯、壬基酚聚氧乙烯醚、发泡剂、阻燃剂、增塑剂，置于超声波环境下，以700r/min搅拌25min，获得混合物Ⅱ；
4)对步骤3)获得的混合物Ⅱ进行浓缩，将浓缩后的混合物Ⅱ倒入模具中，加压成型，再将加压成型得到的板材送入烘箱中烘干，冷却，即可。
其中，步骤3)所述的超声波频率为55KHz。
实施例5
一种高强度防水保温板，包括以下按照重量份的原料：聚氯乙烯树脂80份、聚丙烯酸酯乳液30份、羧甲基纤维素钠25份、多孔陶粒30份、二氧化硅20份、硅酸镁铝30份、二乙烯基苯3份、丙烯酸二甲氨基乙酯10份、壬基酚聚氧乙烯醚4份、麦麸10份、玻璃纤维5份、发泡剂2份、阻燃剂3份、增塑剂4份、去离子水80份。
其中，所述阻燃剂由三氧化二锑、氢氧化镁、氢氧化铝按重量比1:3:1混合而成。
其中，所述增塑剂由邻苯二甲酸二辛酯、邻苯二甲酸二丁酯按重量比2:1混合而成。
本实施例中，所述高强度防水保温板的制备方法，步骤如下：
1)将聚氯乙烯树脂、多孔陶粒、二氧化硅、硅酸镁铝、麦麸、玻璃纤维分别粉碎后过300目筛，获得各自的粉末；
2)将步骤1)获得的聚氯乙烯树脂、多孔陶粒、二氧化硅、玻璃纤维粉末混合后加入去离子水，以500r/min转速、100℃温度条件下进行搅拌，搅拌过程中缓慢加入聚丙烯酸酯乳液、羧甲基纤维素钠、丙烯酸二甲氨基乙酯，加料后继续搅拌50min，静置1.5h，获得混合物Ⅰ；
3)向步骤2)获得的混合物Ⅰ中加入步骤1)获得的硅酸镁铝、麦麸粉末，同时加入二乙烯基苯、壬基酚聚氧乙烯醚、发泡剂、阻燃剂、增塑剂，置于超声波环境下，以800r/min搅拌30min，获得混合物Ⅱ；
4)对步骤3)获得的混合物Ⅱ进行浓缩，将浓缩后的混合物Ⅱ倒入模具中，加压成型，再将加压成型得到的板材送入烘箱中烘干，冷却，即可。
其中，步骤3)所述的超声波频率为60KHz。
对比例1
与实施例3相比，不含二乙烯基苯、壬基酚聚氧乙烯醚，其他与实施例3相同。
对比例2
与实施例3相比，不含麦麸，其他与实施例3相同。
对比例3
与实施例3相比，不含二乙烯基苯壬基酚、聚氧乙烯醚和麦麸，其他与实施例3相同。
对实施例1-5及对比例1-3所制备的保温板进行性能测试，测试结果如表1所示。
表1
从以上结果中可以看出，本发明制备的保温板在各种原料的共同配合作用下，材料强度高，能够承受较强的外部压力，不易断裂，方便铺设，使用寿命长；能够有效隔绝热量，起到保温的作用，避免夏季室内高温传导至室内或冬季室内热量散失；材料表面光滑，具有良好的防水性能，可以用于建筑外墙的铺设，不会因雨水浸泡导致脱落，安全性能高。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。

Claims (8)

1.一种高强度防水保温板，其特征在于，包括以下按照重量份的原料：聚氯乙烯树脂60-80份、聚丙烯酸酯乳液20-30份、羧甲基纤维素钠15-25份、多孔陶粒20-30份、二氧化硅10-20份、硅酸镁铝20-30份、二乙烯基苯1-3份、丙烯酸二甲氨基乙酯5-10份、壬基酚聚氧乙烯醚2-4份、麦麸5-10份、玻璃纤维3-5份、发泡剂1-2份、阻燃剂1-3份、增塑剂2-4份、去离子水60-80份。
2.根据权利要求1所述的高强度防水保温板，其特征在于，包括以下按照重量份的原料：聚氯乙烯树脂65-75份、聚丙烯酸酯乳液22-28份、羧甲基纤维素钠18-22份、多孔陶粒22-28份、二氧化硅12-18份、硅酸镁铝22-28份、二乙烯基苯1.5-2.5份、丙烯酸二甲氨基乙酯6-9份、壬基酚聚氧乙烯醚2.5-3.5份、麦麸6-9份、玻璃纤维3.5-4.5份、发泡剂1.2-1.8份、阻燃剂1.5-2.5份、增塑剂2.5-3.5份、去离子水65-75份。
3.根据权利要求2所述的高强度防水保温板，其特征在于，包括以下按照重量份的原料：聚氯乙烯树脂70份、聚丙烯酸酯乳液25份、羧甲基纤维素钠20份、多孔陶粒25份、二氧化硅15份、硅酸镁铝25份、二乙烯基苯2份、丙烯酸二甲氨基乙酯8份、壬基酚聚氧乙烯醚3份、麦麸8份、玻璃纤维4份、发泡剂1.5份、阻燃剂2份、增塑剂3份、去离子水70份。
4.根据权利要求1所述的高强度防水保温板，其特征在于，所述阻燃剂由三氧化二锑、氢氧化镁、氢氧化铝按重量比1:3:1混合而成。
5.根据权利要求4所述的高强度防水保温板，其特征在于，所述增塑剂由邻苯二甲酸二辛酯、邻苯二甲酸二丁酯按重量比2:1混合而成。
6.一种如权利要求1-5任一所述的高强度防水保温板的制备方法，其特征在于，包括以下步骤：
1)将聚氯乙烯树脂、多孔陶粒、二氧化硅、硅酸镁铝、麦麸、玻璃纤维分别粉碎后过200-300目筛，获得各自的粉末；
2)将步骤1)获得的聚氯乙烯树脂、多孔陶粒、二氧化硅、玻璃纤维粉末混合后加入去离子水，以300-500r/min转速、80-100℃温度条件下进行搅拌，搅拌过程中缓慢加入聚丙烯酸酯乳液、羧甲基纤维素钠、丙烯酸二甲氨基乙酯，加料后继续搅拌30-50min，静置1-1.5h，获得混合物Ⅰ；
3)向步骤2)获得的混合物Ⅰ中加入步骤1)获得的硅酸镁铝、麦麸粉末，同时加入二乙烯基苯、壬基酚聚氧乙烯醚、发泡剂、阻燃剂、增塑剂，置于超声波环境下，以600-800r/min搅拌20-30min，获得混合物Ⅱ；
4)对步骤3)获得的混合物Ⅱ进行浓缩，将浓缩后的混合物Ⅱ倒入模具中，加压成型，再将加压成型得到的板材送入烘箱中烘干，冷却，即可。
7.根据权利要求6所述的高强度防水保温板的制备方法，其特征在于，步骤3)所述的超声波频率为50-60KHz。
8.一种如权利要求1-5任一所述的保温板在制备防水材料中的应用。
CN201810902174.5A 2018-08-09 2018-08-09 一种高强度防水保温板及其制备方法 Withdrawn CN108976666A (zh)