CN108949083A - 一种高强度保温胶粘剂及其制备方法 - Google Patents

一种高强度保温胶粘剂及其制备方法 Download PDF

Info

Publication number
CN108949083A
CN108949083A CN201810642602.5A CN201810642602A CN108949083A CN 108949083 A CN108949083 A CN 108949083A CN 201810642602 A CN201810642602 A CN 201810642602A CN 108949083 A CN108949083 A CN 108949083A
Authority
CN
China
Prior art keywords
parts
mixture
strength
adhesive
insulation adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810642602.5A
Other languages
English (en)
Inventor
吴伟荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Hui Tian Technology Co Ltd
Original Assignee
Suzhou Hui Tian Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Hui Tian Technology Co Ltd filed Critical Suzhou Hui Tian Technology Co Ltd
Priority to CN201810642602.5A priority Critical patent/CN108949083A/zh
Publication of CN108949083A publication Critical patent/CN108949083A/zh
Pending legal-status Critical Current

Abstract

本发明涉及了一种高强度保温胶粘剂及其制备方法，所述保温胶粘剂包括如下重量份的组分：聚醚多元醇160‑200份、聚酯多元醇180‑230份、合成树脂60‑100份、催化剂4‑10份、有机溶剂120‑180份、表面活性剂20‑50份、润滑剂10‑30份、保温材料100‑150份。本发明所提供的高强度保温胶粘剂，在粘合强度、初粘力方面均具有较好的效果，达到了市场上的使用要求。

Description

一种高强度保温胶粘剂及其制备方法
技术领域
本发明涉及一种高强度保温胶粘剂及其制备方法，属于高分子技术领域。
背景技术
胶粘剂是一种具有很好粘合性能的物质，其通过粘附力和内聚力由表面粘合而起连接物体的作用，保温胶粘剂主要应用于节能建筑、冷藏及其它隔热保温的领域，随着市场使用要求的发展，现在普遍使用的保温胶粘剂在粘合强度、初粘力方面达不到市场的要求。
发明内容
本发明的目的在于提供一种高强度保温胶粘剂，在粘合强度、初粘力方面均具有较好的效果，达到了市场上的使用要求。
为达到上述目的，本发明提供如下技术方案：
一方面，本发明提供一种高强度保温胶粘剂，包括如下重量份的组分：聚醚多元醇160-200份、聚酯多元醇180-230份、合成树脂60-100份、催化剂4-10 份、有机溶剂120-180份、表面活性剂20-50份、润滑剂10-30份、保温材料100-150 份。
进一步地，所述高强度保温胶粘剂包括如下重量份的组分：聚醚多元醇 180-195份、聚酯多元醇190-210份、合成树脂65-75份、催化剂5-7份、有机溶剂160-170份、表面活性剂30-40份、润滑剂20-25份、保温材料105-125份。此条件下，所得保温胶粘剂在粘合强度、初粘力方面效果更佳。
进一步地，所述高强度保温胶粘剂包括如下重量份的组分：聚醚多元醇190 份、聚酯多元醇200份、合成树脂70份、催化剂6份、有机溶剂165份、表面活性剂35份、润滑剂22份、保温材料115份。此条件下，所得保温胶粘剂在粘合强度、初粘力方面效果最佳。
进一步地，所述保温材料包括40-70份的SiO2气凝胶颗粒、60-80份的中空纤维。使保温胶粘剂保温性能较好。
进一步地，所述气凝胶颗粒的粒径大小为80-150nm。
进一步地，所述中空纤维为涤纶中空纤维、聚丙烯中空纤维和硅酸铝中空纤维中的一种或多种。
进一步地，所述中空纤维的直径为20-40μm、长度为0.5-2mm。
进一步地，所述表面活性剂为硬脂酸、铝酸脂和钛酸酯的一种或多种。
进一步地，所述润滑剂为石蜡、丙三醇、硅酸酯和甘油中的一种或多种。
进一步地，所述聚醚多元醇为分子量为1000-2000的聚四氢呋喃二醇或/和四氢呋喃-氧化丙烯共聚二醇。
进一步地，所述聚酯多元醇为分子量在1000-4000的二官能度聚酯多元醇、聚己内酯多元醇和聚碳酸酯多元醇中的一种或多种。
进一步地，所述合成树脂为聚酰胺树脂或/和对叔丁基酚甲醛树脂。
进一步地，所述催化剂为碱性催化剂或者酸性催化剂。
进一步地，所述碱性催化剂为氨水，所述酸性催化剂为对甲苯磺酸。
进一步地，所述有机溶剂为丙酮、环己烷、二甲基亚砜和乙酸乙酯中的一种或多种。
另一方面，本发明还提供一种所述的高强度保温胶粘剂的制备方法，包括如下步骤：
(1)将保温材料与表面活性剂混合，搅拌均匀，得到混合物A；
(2)将有机溶剂、聚醚多元醇和聚酯多元醇加入到反应罐中，将温度升至 100-150℃，搅拌0.5-1小时，然后降温至40-60℃，再加入合成树脂和催化剂，升温至80-110℃，反应2-5小时，然后降温至20-30℃，搅拌均匀，得到混合物 B；
(3)将步骤(1)得到的混合物A和步骤(2)得到的混合物B混合，搅拌均匀，得到混合物C；
(4)将步骤(3)得到的混合物C中加入润滑剂，搅拌均匀得到高强度保温胶粘剂。
本发明的有益效果在于：聚酯多元醇和聚醚多元醇均具有柔韧性好和粘合强度大的优点，合成树脂具有优良的弹性，且具有提高粘合力和柔韧性的作用，催化剂促进各组分之间的反应，使胶粘剂的内聚力增强，本发明保温胶粘剂在特定配比的各组分作用下，使本发明所提供的高强度保温胶粘剂，在粘合强度、初粘力、保温性方面均具有较好的效果，达到了市场上的使用要求。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，并可依照说明书的内容予以实施，以下以本发明的较佳实施例详细说明如后。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步详细描述。以下实施例用于说明本发明，但不用来限制本发明的范围。
实施例一
将100份保温材料与20份表面活性剂硬脂酸混合，搅拌均匀，得到混合物 A。
将120份的丙酮、160份的分子量为1000的聚四氢呋喃二醇和180份的分子量为1000的二官能度聚酯多元醇加入到反应罐中，将温度升至100℃，搅拌 0.5小时，然后降温至40℃，再加入60份聚酰胺树脂，4份对甲苯磺酸，升温至80℃，反应2小时，然后降温至20℃，搅拌均匀，得到混合物B。
将制得的混合物A和得到的混合物B混合，搅拌均匀，得到混合物C，再向混合物C中加入10份润滑剂石蜡，搅拌均匀得到高强度保温胶粘剂。
保温材料包括40份的SiO2气凝胶颗粒、60份的中空纤维，气凝胶颗粒的粒径大小为80nm，中空纤维为涤纶中空纤维，涤纶中空纤维的直径为20μm，长度为0.5mm。
实施例二
将150份保温材料与50份表面活性剂钛酸酯混合，搅拌均匀，得到混合物 A。
将100份的环己烷、80份的二甲基亚砜、100份的分子量为2000的聚四氢呋喃二醇、100份的分子量为2000的四氢呋喃-氧化丙烯共聚二醇、150份的分子量为4000的聚己内酯多元醇和80份的分子量为4000的聚碳酸酯多元醇加入到反应罐中，将温度升至150℃，搅拌1小时，然后降温至60℃，再加入100 份对叔丁基酚甲醛树脂，10份对甲苯磺酸，升温至110℃，反应5小时，然后降温至30℃，搅拌均匀，得到混合物B。
将制得的混合物A和得到的混合物B混合，搅拌均匀，得到混合物C，再向混合物C中加入30份润滑剂甘油，搅拌均匀得到高强度保温胶粘剂。
保温材料包括70份的SiO2气凝胶颗粒和80份的中空纤维，气凝胶颗粒的粒径大小为150nm，中空纤维为硅酸铝中空纤维，中空纤维的直径为40μm，长度为2mm。
实施例三
将140份保温材料与45份表面活性剂铝酸脂混合，搅拌均匀，得到混合物 A。
将90份的二甲基亚砜、60份的乙酸乙酯、180份的分子量为1500的四氢呋喃-氧化丙烯共聚二醇、200份的分子量为2000的聚碳酸酯多元醇加入到反应罐中，将温度升至120℃，搅拌0.8小时，然后降温至50℃，再加入40份对叔丁基酚甲醛树脂和40份聚酰胺树脂，7份对甲苯磺酸，升温至100℃，反应3.5 小时，然后降温至25℃，搅拌均匀，得到混合物B。
将制得的混合物A和得到的混合物B混合，搅拌均匀，得到混合物C，再向混合物C中加入15份润滑剂丙三醇，搅拌均匀得到高强度保温胶粘剂。
保温材料包括70份的SiO2气凝胶颗粒、70份的中空纤维，气凝胶颗粒的粒径大小为140nm，中空纤维为聚丙烯中空纤维，中空纤维的直径为35μm，长度为1.5mm。
实施例四
将115份保温材料与35份表面活性剂铝酸脂混合，搅拌均匀，得到混合物 A。
将70份的丙酮、95份的乙酸乙酯、190份的分子量为1500的聚四氢呋喃二醇、70份的分子量为3000的聚碳酸酯多元醇和130份分子量为1500的二官能度聚酯多元醇加入到反应罐中，将温度升至130℃，搅拌0.7小时，然后降温至55℃，再加入20份对叔丁基酚甲醛树脂和50份聚酰胺树脂，6份对甲苯磺酸，升温至90℃，反应4小时，然后降温至25℃，搅拌均匀，得到混合物B。
将制得的混合物A和得到的混合物B混合，搅拌均匀，得到混合物C，再向混合物C中加入22份润滑剂硅酸酯，搅拌均匀得到高强度保温胶粘剂。
保温材料包括55份的SiO2气凝胶颗粒、60份的中空纤维，气凝胶颗粒的粒径大小为100nm，中空纤维为聚丙烯中空纤维，中空纤维的直径为30μm、长度为1mm。
对比例一
将100份保温材料与20份表面活性剂硬脂酸混合，搅拌均匀，得到混合物 A。
将110份的丙酮、250份的分子量为1000的聚四氢呋喃二醇和180份的分子量为1000的二官能度聚酯多元醇加入到反应罐中，将温度升至100℃，搅拌 0.5小时，然后降温至40℃，再加入60份聚酰胺树脂，4份对甲苯磺酸，升温至80℃，反应2小时，然后降温至20℃，搅拌均匀，得到混合物B。
将制得的混合物A和得到的混合物B混合，搅拌均匀，得到混合物C，再向混合物C中加入10份润滑剂石蜡，搅拌均匀得到高强度保温胶粘剂。
保温材料包括40份的SiO2气凝胶颗粒、60份的中空纤维，气凝胶颗粒的粒径大小为80nm，中空纤维为涤纶中空纤维，涤纶中空纤维的直径为20μm，长度为0.5mm。
对比例二
将150份保温材料与50份表面活性剂钛酸酯混合，搅拌均匀，得到混合物 A。
将100份的环己烷、80份的二甲基亚砜、130份的分子量为2000的聚四氢呋喃二醇、110份的分子量为2000的四氢呋喃-氧化丙烯共聚二醇、150份的分子量为4000的聚己内酯多元醇和100份的分子量为4000的聚碳酸酯多元醇加入到反应罐中，将温度升至150℃，搅拌1小时，然后降温至60℃，再加入100 份对叔丁基酚甲醛树脂，10份对甲苯磺酸，升温至110℃，反应5小时，然后降温至30℃，搅拌均匀，得到混合物B。
将制得的混合物A和得到的混合物B混合，搅拌均匀，得到混合物C，再向混合物C中加入30份润滑剂甘油，搅拌均匀得到高强度保温胶粘剂。
保温材料包括70份的SiO2气凝胶颗粒和80份的中空纤维，气凝胶颗粒的粒径大小为150nm，中空纤维为硅酸铝中空纤维，中空纤维的直径为40μm，长度为2mm。
实施例五
测试实施例一至实施例四制备得到的保温胶粘剂，以及对比例一至对比例二的保温胶粘剂的基材面剥离力。测试标准：检测基材面剥离力的方法根据中华人民共和国国家标准GB/T 2792-1998。结果如下述表1所示：
表1
从上述表1可以看出，相比对比例一至对比例二的保温胶粘剂，实施例一至实施例四所制备的保温胶粘剂均具有较好的粘合强度，且初粘力均较佳，其中实施例三和实施例四在粘合时间较短时即具有好的基材面剥离力，且随着凝固时间的延长，其基材面剥离力达到了极优值，表现出了好的粘合强度，尤其是实施例四的表现最佳。
以上所述实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。

Claims (9)

1.一种高强度保温胶粘剂，其特征在于，包括如下重量份的组分：聚醚多元醇160‐200份、聚酯多元醇180‐230份、合成树脂60‐100份、催化剂4‐10份、有机溶剂120‐180份、表面活性剂20‐50份、润滑剂10‐30份、保温材料100‐150份。
2.如权利要求1所述的一种高强度保温胶粘剂，其特征在于，包括如下重量份的组分：聚醚多元醇180‐195份、聚酯多元醇190‐210份、合成树脂65‐75份、催化剂5‐7份、有机溶剂160‐170份、表面活性剂30‐40份、润滑剂20‐25份、保温材料105‐125份。
3.如权利要求1所述的一种高强度保温胶粘剂，其特征在于，所述保温材料包括40‐70份的SiO2气凝胶颗粒、60‐80份的中空纤维。
4.如权利要求3所述的一种高强度保温胶粘剂，其特征在于，所述气凝胶颗粒的粒径大小为80‐150nm。
5.如权利要求3所述的一种高强度保温胶粘剂，其特征在于，所述中空纤维为涤纶中空纤维、聚丙烯中空纤维和硅酸铝中空纤维中的一种或多种。
6.如权利要求5所述的一种高强度保温胶粘剂，其特征在于，所述中空纤维的直径为20‐40μm、长度为0.5‐2mm。
7.如权利要求1所述的一种高强度保温胶粘剂，其特征在于，所述表面活性剂为硬脂酸、铝酸脂和钛酸酯的一种或多种。
8.如权利要求1所述的一种高强度保温胶粘剂，其特征在于，所述润滑剂为石蜡、丙三醇、硅酸酯和甘油中的一种或多种。
9.一种如权利要求1‐8中任一项所述的高强度保温胶粘剂的制备方法，其特征在于，包括如下步骤：
(1)将保温材料与表面活性剂混合，搅拌均匀，得到混合物A；
(2)将有机溶剂、聚醚多元醇和聚酯多元醇加入到反应罐中，将温度升至100‐150℃，搅拌0.5‐1小时，然后降温至40‐60℃，再加入合成树脂和催化剂，升温至80‐110℃，反应2‐5小时，然后降温至20‐30℃，搅拌均匀，得到混合物B；
(3)将步骤(1)得到的混合物A和步骤(2)得到的混合物B混合，搅拌均匀，得到混合物C；
(4)将步骤(3)得到的混合物C中加入润滑剂，搅拌均匀得到高强度保温胶粘剂。
CN201810642602.5A 2018-06-21 2018-06-21 一种高强度保温胶粘剂及其制备方法 Pending CN108949083A (zh)