CN108947354A - A kind of biomass flowerpot and preparation method thereof - Google Patents
A kind of biomass flowerpot and preparation method thereof Download PDFInfo
- Publication number
- CN108947354A CN108947354A CN201810982001.9A CN201810982001A CN108947354A CN 108947354 A CN108947354 A CN 108947354A CN 201810982001 A CN201810982001 A CN 201810982001A CN 108947354 A CN108947354 A CN 108947354A
- Authority
- CN
- China
- Prior art keywords
- biomass
- flowerpot
- parts
- added
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of biomass flowerpot, which is characterized in that specifically includes the following steps: the processing of (1) biomass material；(2) prepared by blend glue stuff, weighs 20-30 parts of epoxy resin, 2-10 parts of reactive diluent, 1-3 parts of inorganic pigment are added in stirred tank, stir evenly, obtain blend glue stuff；(3) prepared by mixed powder, takes 5-30 part of cement, 25-35 parts of quartz sand, and 1-3 parts of coupling agent, 5-20 parts of biomass material are added in kneader uniformly mixed, obtains mixed powder.(4) obtained mixed powder is added in blend glue stuff obtained in step (3), stirs evenly by flowerpot molding, and curing agent is added, continues to stir, and obtains flowerpot grout material, and reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.The flowerpot of preparation can make full use of biomass resource, be conducive to environmental protection.
Description
Technical field
The invention belongs to flower container Material Field, it is related to a kind of biomass flowerpot and preparation method thereof.
Background technique
Flowerpot is kind an a kind of vessel for flower, for the small inverted round stage in the big bottom end of mouth or terrace edge shape, according to making material
Difference can be divided into many types.It common are ceramic bowl, glass reinforced plastic flower pot, plastic tub, boccaro basin etc..Wherein, such as the work of ceramic bowl
Skill is probably needed by pugging, throwing, texturing, glazing, firing, complex process, and is consumed energy.And glass flowerpot, system
Standby technique is also complex, and airtight moisture permeability.And for plastic flowerpot, preparation process is relatively easy, but plastics
Flowerpot is airtight, is mainly used for soilless cultivation, and cost wants low relative to glass and jardiniere.
More biological material can be generated in agricultural production process, such as the stalk that crops carry over, this kind of life
Material the past it is common be exactly burning disposal, burning disposal can bring biggish pollution to atmosphere, and for further
Stalk processing is processed, such as carbonization is used as fuel, and is fabricated to biogas, and there are higher costs for these processing methods, puts into larger
The problem of, therefore, to the processing of stalk, there are bigger difficulty now.
Chinese invention patent CN107409818A discloses a kind of production side of biology base mycelia material ecological, environmental protective flowerpot
Method, by the way that agricultural crop straw is put into different process moulding mould, inoculation edible fungus species culture growth, shaping and demoulding is formed.
The ecological, environmental protective flowerpot of this method production in use, can be straight as plant is not necessarily to remove flowerpot when being grown in transplanting
Tape splicing basin is transplanted, which 100% can be decomposed into organic matter and utilized by plant as time goes by, is had apparent
Cost advantage and environment-friendly advantage.The flowerpot is made of biological material, is all the cultivation applied to mycelia, use scope
It is relatively narrow, and the flowerpot being prepared is qualitative only by pressure progress, and the easy solution of flowerpot collapses in use, mechanical property
It is poor.
The present invention is directed to be recycled to the biological material in agricultural production process, reduces and utilize cost, and mention
The economic benefit of high biomass, then on the basis of this, it is prepared for a kind of biomass flowerpot, which has preferable mechanical performance,
Can satisfy the use of daily flowerpot, and there is good air permeable humidity retaining performance, and use for a long time can natural degradation,
Necessary organic fertilizer is provided for flowers.
Summary of the invention
In order to solve the problems in the existing technology, a kind of biomass flowerpot and preparation method thereof, the present invention are prepared
Using following methods.
Flowerpot raw material packet is by epoxide-resin glue, cement, soil, quartz sand or miberal powder, reactive diluent, curing agent, biology
Material, wherein biological material is stalk or sawdust.
Specific flowerpot raw material forms as follows by weight: 20-30 parts of epoxy resin, 2-10 parts of reactive diluent, inorganic
Pigment 1-3,5-30 parts of cement, 25-35 parts of quartz sand, 2-10 parts of curing agent, 1-3 parts of coupling agent, 5-20 parts of biomass material.
The smashed partial size of biomass material is less than 500 μm.
Biomass material be stalk or sawdust, stalk include production estimation harvest after remainder, including wheat-straw,
Rice bar, cornstalk, cotton stem, rape straw, sugarcane bar etc., biomass raw material must be smashed, and guarantee that partial size is small
In 500 μm, flowerpot surface smoothness and aesthetics can guarantee in this way, if the partial size of biomass raw material is excessive after crushing, by
Small relative to cement sandstone density in the density of biological particles, in the mixed processes of powder, biological material is not allowed
It is easily blended uniformly, be easy to cause slurry mixing uneven, and be easy to cause hole on flowerpot more after forming, greatly influence
The performance of keeping humidity and mechanical property of flowerpot.
Biological material can be degenerated in a natural environment by bacterium, and then obtain organic fertilizer, to a certain degree
On necessary organic fertilizer can be provided for flowers, be conducive to the growth of flowers.
The present invention uses epoxy resin as glue connection agent, the solidification crosslinked action of cement can be assisted, due to biological material
The density of material is small compared to the density of cement, sandstone, and during powder mixing, difficulty or ease are uniformly mixed, the invention
Use liquid sizing material epoxy resin, can preferably infiltrate biological material, enable and be uniformly mixed in flowerpot slurry, made
It obtains biological material to be evenly distributed in the slurry, and then improves the yield rate and mechanical property of flowerpot.The use of epoxy resin
It can be improved the waterproof water retention property of flowerpot simultaneously, and improve its flexibility.
The present invention provides a kind of biomass flowerpots and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass material；
The temperature of drying is 95-105 DEG C, drying time 3-8h.
Biological material is needed by drying, and the biological material of recycling includes more moisture, if without drying,
It is easy in the preparation process of mixed powder so that cement is cured, so that mixed powder difficulty or ease are uniformly mixed, and then influence
To the uniform performance of slurry, larger difficulty is caused for subsequent molding, reduces the yield rate and performance of flowerpot.
(2) prepared by blend glue stuff
20-30 parts of epoxy resin, 2-10 parts of reactive diluent are weighed, inorganic pigment 1-3 is added in stirred tank, and stirring is equal
It is even, obtain blend glue stuff.
(3) prepared by mixed powder
5-30 parts of cement, 25-35 parts of quartz sand are taken, 1-3 parts of coupling agent, 5-20 parts of biomass material are added in kneader
It is uniformly mixed, obtains mixed powder.
(4) flowerpot molding
Obtained mixed powder is added in step (3) blend glue stuff obtained in, is stirred evenly, curing agent is added,
Continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.
The reactive diluent is as in acrylic glycidol ether, butyl glycidyl ether and phenyl glycidyl ether
It is a kind of.
Described curing agent 2-10 parts.
Curing agent is one of ethylenediamine, hexamethylene diamine, diethylenetriamine, triethylene tetramine, diethylaminopropylamine or more
Kind.
Solidification temperature is 25-40 DEG C, curing time 2-4h.
Using above technical scheme, a kind of preparation-obtained preparation process of biomass flowerpot is simple, at room temperature
It can be cured molding, and used a large amount of biomass material, provide one kind for the use of waste biomass materials
Outlet is conducive to environmental protection.
Specific embodiment
Below in conjunction with specific embodiment, technical scheme of the present invention will be further described.
Embodiment 1
A kind of biomass flowerpot and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass powder；
The partial size of biomass powder is less than 500 μm, and the temperature of drying is 95 DEG C, drying time 8h.
(2) prepared by blend glue stuff
20 parts of epoxy resin, 5 parts of reactive diluent are weighed, inorganic pigment 3 is added in stirred tank, is stirred evenly, and is mixed
Close sizing material.
(3) prepared by mixed powder
Taking 10 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent, 10 parts of biomass powder are added in kneader and are uniformly mixed,
Obtain mixed powder.
(4) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (3), is stirred evenly, curing agent second is added
5 parts of diamines, continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.Solidification
Temperature is 40 DEG C, curing time 4h.
The obtained smooth exquisiteness in flowerpot surface is filled with water and does not leak without obvious hole, and flexibility is good, good mechanical performance.
Embodiment 2
A kind of biomass flowerpot and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass powder；
The partial size of biomass powder is less than 500 μm, and the temperature of drying is 95 DEG C, drying time 8h.
(2) prepared by blend glue stuff
30 parts of epoxy resin, 5 parts of reactive diluent are weighed, inorganic pigment 3 is added in stirred tank, is stirred evenly, and is mixed
Close sizing material.
(3) prepared by mixed powder
Taking 20 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent, 10 parts of biomass material are added in kneader and are uniformly mixed,
Obtain mixed powder.
(4) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (3), is stirred evenly, curing agent second is added
5 parts of diamines, continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.Solidification
Temperature is 40 DEG C, curing time 4h.
The obtained smooth exquisiteness in flowerpot surface is filled with water and does not leak without obvious hole, and flexibility is good, good mechanical performance.
Embodiment 3
A kind of biomass flowerpot and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass powder；
The partial size of biomass powder is less than 500 μm, and the temperature of drying is 95 DEG C, drying time 8h.
(2) prepared by blend glue stuff
20 parts of epoxy resin, 5 parts of reactive diluent are weighed, inorganic pigment 3 is added in stirred tank, is stirred evenly, and is mixed
Close sizing material.
(3) prepared by mixed powder
Taking 10 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent, 5 parts of biomass material are added in kneader and are uniformly mixed,
Obtain mixed powder.
(4) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (3), is stirred evenly, curing agent second is added
5 parts of diamines, continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.Solidification
Temperature is 40 DEG C, curing time 4h.
The obtained smooth exquisiteness in flowerpot surface is filled with water and does not leak without obvious hole, and flexibility is good, good mechanical performance.
Embodiment 4
A kind of biomass flowerpot and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass powder；
The partial size of biomass powder is less than 500 μm, and the temperature of drying is 105 DEG C, drying time 8h.
(2) prepared by blend glue stuff
20 parts of epoxy resin, 5 parts of reactive diluent are weighed, inorganic pigment 3 is added in stirred tank, is stirred evenly, and is mixed
Close sizing material.
(3) prepared by mixed powder
Taking 10 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent, 10 parts of biomass material are added in kneader and are uniformly mixed,
Obtain mixed powder.
(4) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (3), is stirred evenly, curing agent two is added
5 parts of ethylene triamine, continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.
Solidification temperature is 40 DEG C, curing time 4h.
The obtained smooth exquisiteness in flowerpot surface is filled with water and does not leak without obvious hole, and flexibility is good, good mechanical performance.
Embodiment 5
A kind of biomass flowerpot and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass powder；
The partial size of biomass powder is less than 500 μm, and the temperature of drying is 95 DEG C, drying time 8h.
(2) prepared by blend glue stuff
20 parts of epoxy resin, 5 parts of reactive diluent are weighed, inorganic pigment 3 is added in stirred tank, is stirred evenly, and is mixed
Close sizing material.
(3) prepared by mixed powder
Taking 10 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent, 10 parts of biomass material are added in kneader and are uniformly mixed,
Obtain mixed powder.
(4) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (3), is stirred evenly, curing agent second is added
5 parts of diamines, continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.Solidification
Temperature is 35 DEG C, curing time 5h.
The obtained smooth exquisiteness in flowerpot surface is filled with water and does not leak without obvious hole, and flexibility is good, good mechanical performance.
Comparative example 1
A kind of tool biomass flowerpot and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, biomass powder is obtained；
The partial size of biomass powder is less than 500 μm.
(2) prepared by blend glue stuff
20 parts of epoxy resin, 5 parts of reactive diluent are weighed, inorganic pigment 3 is added in stirred tank, is stirred evenly, and is mixed
Close sizing material.
(3) prepared by mixed powder
Taking 10 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent, 10 parts of biomass powder are added in kneader and are uniformly mixed,
Obtain mixed powder.
(4) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (3), is stirred evenly, curing agent second is added
5 parts of diamines, continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.Solidification
Temperature is 40 DEG C, curing time 4h.
Obtained flowerpot rough surface, there is subtle hole, and being filled with water has infiltration phenomenon, soft, prepares in mixed powder
When there are agglomerations.
Comparative example 2
A kind of tool biomass flowerpot and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass powder；
The partial size of biomass powder is greater than 2mm, and the temperature of drying is 95 DEG C, drying time 8h.
(2) prepared by blend glue stuff
20 parts of epoxy resin, 5 parts of reactive diluent are weighed, inorganic pigment 3 is added in stirred tank, is stirred evenly, and is mixed
Close sizing material.
(3) prepared by mixed powder
Taking 10 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent, 10 parts of biomass powder are added in kneader and are uniformly mixed,
Obtain mixed powder.
(4) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (3), is stirred evenly, curing agent second is added
5 parts of diamines, continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.Solidification
Temperature is 40 DEG C, curing time 4h.
Obtained flowerpot surface is more coarse, can see fibrous particle, and being filled with water has leakage phenomenon, and flexibility is good, mechanics
Function admirable.
Comparative example 3
A kind of tool biomass flowerpot and preparation method thereof, specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass powder；
The partial size of biomass powder is less than 200 μm, and the temperature of drying is 95 DEG C, drying time 8h.
(2) prepared by mixed powder
Taking 10 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent, 10 parts of biomass powder are added in kneader and are uniformly mixed,
Obtain mixed powder.
(3) flowerpot molding
Obtained mixed powder is added to the water, is stirred evenly, flowerpot grout material is obtained, reverse mould solidifies, and forms, and takes off
Mould obtains a kind of biomass flowerpot.Solidification temperature is 40 DEG C, curing time 4h.
The molding of flowerpot difficulty, yield rate are low.
Comparative example 4
A kind of flowerpot and preparation method thereof, specifically includes the following steps:
(1) prepared by blend glue stuff
20 parts of epoxy resin, 5 parts of reactive diluent are weighed, inorganic pigment 3 is added in stirred tank, is stirred evenly, and is mixed
Close sizing material.
(2) prepared by mixed powder
Take 10 parts of cement, 25 parts of quartz sand, 2 parts of coupling agent are added in kneader and are uniformly mixed, and obtain mixed powder.
(3) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (1), is stirred evenly, curing agent two is added
5 parts of ethylene triamine, continue to stir, obtain flowerpot grout material, reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.
Solidification temperature is 40 DEG C, curing time 4h.
The obtained smooth exquisiteness in flowerpot surface is filled with water and does not leak without obvious hole, and flexibility is not good enough, good mechanical performance.
Claims (6)
1. a kind of preparation method of biomass flowerpot, which is characterized in that specifically includes the following steps:
(1) processing of biomass material
The biomass material of recycling is crushed, drying obtains biomass material；
(2) prepared by blend glue stuff
20-30 parts of epoxy resin, 2-10 parts of reactive diluent are weighed, 1-3 parts of inorganic pigment are added in stirred tank, it stirs evenly,
Obtain blend glue stuff；
(3) prepared by mixed powder
Take 5-30 parts of cement, 25-35 parts of quartz sand, 1-3 parts of coupling agent, 5-20 parts of biomass material are added in kneader and mix
Uniformly, mixed powder is obtained.
(4) flowerpot molding
Obtained mixed powder is added in blend glue stuff obtained in step (3), is stirred evenly, curing agent is added, is continued
Stirring obtains flowerpot grout material, and reverse mould solidifies, and forms, and demoulding obtains a kind of biomass flowerpot.
2. a kind of preparation method of biomass flowerpot as described in claim 1, which is characterized in that biomass is former in step (1)
Material is stalk or sawdust, and the smashed partial size of biomass material is less than 500 μm.
3. a kind of preparation method of biomass flowerpot as described in claim 1, which is characterized in that the reactive diluent is third
One of alkenyl glycidol ether, butyl glycidyl ether and phenyl glycidyl ether.
4. a kind of preparation method of biomass flowerpot as described in claim 1, which is characterized in that described curing agent 2-10 parts,
Curing agent is one of ethylenediamine, hexamethylene diamine, diethylenetriamine, triethylene tetramine, diethylaminopropylamine or a variety of.
5. a kind of preparation method of biomass flowerpot as described in claim 1, which is characterized in that solidification temperature is 25-40 DEG C,
Curing time 2-4h.
6. a kind of flowerpot for the biomass that preparation method as described in any one in claim 1-5 obtains.