CN108930073A - A kind of preparation method of fresh water area resistant purse seine - Google Patents
A kind of preparation method of fresh water area resistant purse seine Download PDFInfo
- Publication number
- CN108930073A CN108930073A CN201810876353.6A CN201810876353A CN108930073A CN 108930073 A CN108930073 A CN 108930073A CN 201810876353 A CN201810876353 A CN 201810876353A CN 108930073 A CN108930073 A CN 108930073A
- Authority
- CN
- China
- Prior art keywords
- purse seine
- parts
- added
- fresh water
- water area
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of fresh water area resistant purse seine, including following operating procedure: (1) manganous chloride being added into water, after being mixed evenly, then 12-20 parts of sodium naphthenates are continuously added thereto, after being mixed evenly, after the temperature of mixture is risen to 80-85 DEG C, after isothermal holding 3-4 hours, manganese naphthenate is made；(2) after mixing by manganese naphthenate, organobentonite, melamine cyanurate, it is added into baking oven, after drying and processing, additive is made；(3) it after mixing additive and polyvinyl resin according to the ratio that mass ratio is 1:100-120, is added into high-speed mixer, after mixing, puts into double screw extruder, melt spinning, after knitting forming, purse seine is made.A kind of preparation method of fresh water area resistant purse seine provided by the invention, effectively reduces the cost of manufacture of purse seine, but can guarantee the properties of purse seine, meets requirement of the purse seine in fresh water area.
Description
Technical field
The invention belongs to fishing net preparation technical fields, and in particular to a kind of preparation method of fresh water area resistant purse seine.
Background technique
Purse seine is that fisherman often uses one of netting gear, purse seine fishing be according to the characteristic of fished species cluster, using long band shape or
The netting gears of one capsule both wings surrounds the shoal of fish, using surrounding and seize or in conjunction with enclosing, enclosing the modes such as drag, the shoal of fish is forced to concentrate on bunt or net
Capsule, to reach fishing purpose.Purse seine fishing object is mainly in sociability, epipelagic fish (such as mackerel, sardine).It is existing
There is the purse seine excellent quality in technology, be suitble to use in the seawater, but preparation cost is higher, some to use in fresh water area
Purse seine does not need the various requirement for reaching seawater using purse seine, therefore reduces its preparation cost, can reduce the price of fishing net, drops
The cost of low fishing.
Summary of the invention
The object of the present invention is to provide a kind of fresh water area preparation methods of resistant purse seine.
The present invention is achieved by the following technical solutions.
A kind of preparation method of fresh water area resistant purse seine, including following operating procedure:
(1) by weight, 10-16 parts of manganous chloride are added into 40-50 parts of water, after being mixed evenly, then to it
In continuously add 12-20 parts of sodium naphthenates, after being mixed evenly, after the temperature of mixture is risen to 80-85 DEG C, isothermal holding
After 3-4 hours, manganese naphthenate is made；
(2) by weight, 15-20 parts of manganese naphthenates, 23-25 parts of organobentonites, 5-9 parts of melamine cyanurates are mixed
It after closing uniformly, is added into baking oven, after drying and processing, additive is made；
(3) it after mixing additive and polyvinyl resin according to the ratio that mass ratio is 1:100-120, is added to high-speed mixer
In, it after mixing, puts into double screw extruder, melt spinning, after knitting forming, purse seine is made.
Specifically, in above-mentioned steps (2), the purity of melamine cyanurate is 99%, and Average Particle Diameters are 50 μm.
Specifically, in above-mentioned steps (2), temperature when drying and processing is 75-80 DEG C, and the time of drying and processing is that 3-4 is small
When.
From the above technical scheme, it can be seen that the beneficial effects of the present invention are:
A kind of preparation method of fresh water area resistant purse seine provided by the invention, effectively reduces the cost of manufacture of purse seine,
But can guarantee the properties of purse seine, meet requirement of the purse seine in fresh water area.Aphthenic acids obtained in step (1)
Manganese, the anti-pollution and fishing net that can effectively promote fishing net have excellent mechanical property, and then ensure that fishing net
Quality.
Specific embodiment
Below by specific embodiment, the present invention is described in detail, but the purposes of these illustrative embodiments and
Purpose is only used to enumerate the present invention, not constitutes any type of any restriction to real protection scope of the invention, more non-to incite somebody to action
Protection scope of the present invention is confined to this.
Embodiment 1
A kind of preparation method of fresh water area resistant purse seine, including following operating procedure:
(1) by weight, 10 parts of manganous chloride are added into 40 parts of water, after being mixed evenly, are then continued thereto
12 parts of sodium naphthenates are added, after being mixed evenly, after the temperature of mixture is risen to 80 DEG C, after isothermal holding 3 hours, are made
Manganese naphthenate；
(2) by weight, 15 parts of manganese naphthenates, 23 parts of organobentonites, 5 parts of melamine cyanurates are uniformly mixed
Afterwards, it is added into baking oven, after drying and processing, additive is made；
(3) it after mixing additive and polyvinyl resin according to the ratio that mass ratio is 1:100, is added into high-speed mixer,
After mixing, it puts into double screw extruder, melt spinning, after knitting forming, purse seine is made.
Specifically, in above-mentioned steps (2), the purity of melamine cyanurate is 99%, and Average Particle Diameters are 50 μm.
Specifically, in above-mentioned steps (2), temperature when drying and processing is 75 DEG C, and the time of drying and processing is 3 hours.
Embodiment 2
A kind of preparation method of fresh water area resistant purse seine, including following operating procedure:
(1) by weight, 14 parts of manganous chloride are added into 45 parts of water, after being mixed evenly, are then continued thereto
15 parts of sodium naphthenates are added, after being mixed evenly, after the temperature of mixture is risen to 83 DEG C, after isothermal holding 3.5 hours, system
Obtain manganese naphthenate；
(2) by weight, 18 parts of manganese naphthenates, 24 parts of organobentonites, 7 parts of melamine cyanurates are uniformly mixed
Afterwards, it is added into baking oven, after drying and processing, additive is made；
(3) it after mixing additive and polyvinyl resin according to the ratio that mass ratio is 1:110, is added into high-speed mixer,
After mixing, it puts into double screw extruder, melt spinning, after knitting forming, purse seine is made.
Specifically, in above-mentioned steps (2), the purity of melamine cyanurate is 99%, and Average Particle Diameters are 50 μm.
Specifically, in above-mentioned steps (2), temperature when drying and processing is 75-80 DEG C, and the time of drying and processing is 3.5 small
When.
Embodiment 3
A kind of preparation method of fresh water area resistant purse seine, including following operating procedure:
(1) by weight, 16 parts of manganous chloride are added into 50 parts of water, after being mixed evenly, are then continued thereto
20 parts of sodium naphthenates are added, after being mixed evenly, after the temperature of mixture is risen to 85 DEG C, after isothermal holding 4 hours, are made
Manganese naphthenate；
(2) by weight, 20 parts of manganese naphthenates, 25 parts of organobentonites, 9 parts of melamine cyanurates are uniformly mixed
Afterwards, it is added into baking oven, after drying and processing, additive is made；
(3) it after mixing additive and polyvinyl resin according to the ratio that mass ratio is 1:120, is added into high-speed mixer,
After mixing, it puts into double screw extruder, melt spinning, after knitting forming, purse seine is made.
Specifically, in above-mentioned steps (2), the purity of melamine cyanurate is 99%, and Average Particle Diameters are 50 μm.
Specifically, in above-mentioned steps (2), temperature when drying and processing is 80 DEG C, and the time of drying and processing is 4 hours.
Finally, it is stated that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to skill of the invention
Art scheme is modified or replaced equivalently, and without departing from the objective and range of technical solution of the present invention, should all be covered at this
In the scope of the claims of invention.
Claims (3)
1. a kind of fresh water area preparation method of resistant purse seine, which is characterized in that including following operating procedure:
(1) by weight, 10-16 parts of manganous chloride are added into 40-50 parts of water, after being mixed evenly, then to it
In continuously add 12-20 parts of sodium naphthenates, after being mixed evenly, after the temperature of mixture is risen to 80-85 DEG C, isothermal holding
After 3-4 hours, manganese naphthenate is made；
(2) by weight, 15-20 parts of manganese naphthenates, 23-25 parts of organobentonites, 5-9 parts of melamine cyanurates are mixed
It after closing uniformly, is added into baking oven, after drying and processing, additive is made；
(3) it after mixing additive and polyvinyl resin according to the ratio that mass ratio is 1:100-120, is added to high-speed mixer
In, it after mixing, puts into double screw extruder, melt spinning, after knitting forming, purse seine is made.
2. a kind of preparation method of fresh water area resistant purse seine according to claim 1, which is characterized in that above-mentioned steps
(2) in, the purity of melamine cyanurate is 99%, and Average Particle Diameters are 50 μm.
3. a kind of preparation method of fresh water area resistant purse seine according to claim 1, which is characterized in that above-mentioned steps
(2) in, temperature when drying and processing is 75-80 DEG C, and the time of drying and processing is 3-4 hours.