CN108859294A - 一种耐老化的灯箱布材料及其制备方法 - Google Patents

一种耐老化的灯箱布材料及其制备方法 Download PDF

Info

Publication number
CN108859294A
CN108859294A CN201810513335.1A CN201810513335A CN108859294A CN 108859294 A CN108859294 A CN 108859294A CN 201810513335 A CN201810513335 A CN 201810513335A CN 108859294 A CN108859294 A CN 108859294A
Authority
CN
China
Prior art keywords
parts
weight
heat
lamp box
ageing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810513335.1A
Other languages
English (en)
Inventor
向晓霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Barley Light Box Equipment Co Ltd
Original Assignee
Hefei Barley Light Box Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Barley Light Box Equipment Co Ltd filed Critical Hefei Barley Light Box Equipment Co Ltd
Priority to CN201810513335.1A priority Critical patent/CN108859294A/zh
Publication of CN108859294A publication Critical patent/CN108859294A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供了一种耐老化的灯箱布材料及其制备方法，本发明提供的一种耐老化的灯箱布材料，本发明的灯箱布材料为了提高灯箱布的耐老化性能，在普通的灯箱布的结构上进行了改进，在通常的PVC膜和PET膜之间设置了耐温层，该耐温层的成分由聚对苯二甲酸乙二醇酯、聚苯乙烯树脂、氮丙啶交联剂、十二烷基硫酸钠盐、粘胶纤维、聚乙烯吡咯烷酮、相容剂，由上述成分制备得到的耐温层具有优异的耐温性能，将其设置在PVC膜和PET膜之间，并经过加工后，使得整体的灯箱布材料具有较好的耐老化作用，延长使用寿命。

Description

一种耐老化的灯箱布材料及其制备方法
技术领域
本发明属于灯箱布技术领域，具体地，涉及一种耐老化的灯箱布材料及其制备方法。
背景技术
灯箱布是户外喷绘的广告材料，主要应用于广告灯箱、横幅、大型海报、建筑工地外围墙布景、大型T字状广告牌。灯箱布喷绘使用油性墨，日晒雨淋不易掉色，持久耐用，这也是它区别于室内写真广告材料的最大特性。
目前市场上的灯箱布基本有三部分组成，第一部分是面层 PVC膜，吸附喷绘墨水；第二部分是涤纶经编基布，增强灯箱布的抗撕裂强度；第二部分是底层 PVC膜，通过与面层PVC膜的贴合，使灯箱布的三部分紧密结合在一起。在用灯箱布做内打灯箱时，现有的基布会被老化，影响视觉效果。因此，普通灯箱布使用寿命不理想。
为了解决上述问题，本发明提供一种耐老化的灯箱布材料及其制备方法。
发明内容
针对现有技术中的缺陷，本发明的目的是提供一种耐老化的灯箱布材料及制备方法。
根据本发明提供的一种耐老化的灯箱布材料，所述灯箱布材料包括PVC膜和PET膜，所述PVC膜和PET膜之间还设置耐温层，所述耐温层与PVC膜之间通过粘结剂粘结，所述耐温层与PET膜之间通过粘结剂粘结；
所述耐温层包括如下重量份数的原料：聚对苯二甲酸乙二醇酯13-35份、聚苯乙烯树脂6-13份、氮丙啶交联剂6-11份、十二烷基硫酸钠盐3-9份、粘胶纤维5-21份、聚乙烯吡咯烷酮7-11份、相容剂4.1-7.3份。
优选地，所述耐温层包括如下重量份数的原料：聚对苯二甲酸乙二醇酯13-25份、聚苯乙烯树脂7-13份、氮丙啶交联剂8-11份、十二烷基硫酸钠盐5-9份、粘胶纤维7-21份、聚乙烯吡咯烷酮8-11份、相容剂5.1-7.3份。
优选地，所述耐温层包括如下重量份数的原料：聚对苯二甲酸乙二醇酯17份、聚苯乙烯树脂9份、氮丙啶交联剂9份、十二烷基硫酸钠盐6份、粘胶纤维13份、聚乙烯吡咯烷酮9份、相容剂6.3份。
优选地，所述PVC膜的原料配方为：PVC树脂粉100重量份、聚甲基丙烯酸甲酯10-30重量份、增塑剂3.1-5.9重量份、钛白粉25-39重量份、二甘醇二苯甲酸酯3-7重量份、阻燃剂1.2-1.5重量份、大豆油2-5重量份。
优选地，所述PVC膜的生产工艺为：
（1）按照重量份数称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油；
（2）各原料经配料计量后高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得。
优选地，所述挤出时温度控制在215-218℃。
优选地，所述相容剂由甲基丙烯酸甲酯-丁二烯-苯乙烯的嵌段共聚物、马来酸酐单体、高抗冲聚苯乙烯、接枝反应引发剂发生接枝反应得到。
一种耐老化的灯箱布材料的制备方法，所述制备方法包括如下步骤：
步骤一、按照重量配比称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得PVC膜；
步骤二、按照重量份数称量聚对苯二甲酸乙二醇酯、聚苯乙烯树脂、氮丙啶交联剂、十二烷基硫酸钠盐、粘胶纤维、聚乙烯吡咯烷酮、相容剂，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得耐温层；
步骤三、在PET膜上涂布粘结剂，烘干后采用贴合法与耐温层的一面复合，然后再将粘结剂涂布于耐温层的另外一面，烘干，即可。
与现有技术相比，本发明具有如下的有益效果：
本发明提供的一种耐老化的灯箱布材料，本发明的灯箱布材料为了提高灯箱布的耐老化性能，在普通的灯箱布的结构上进行了改进，在通常的PVC膜和PET膜之间设置了耐温层，该耐温层的成分由聚对苯二甲酸乙二醇酯、聚苯乙烯树脂、氮丙啶交联剂、十二烷基硫酸钠盐、粘胶纤维、聚乙烯吡咯烷酮、相容剂，由上述成分制备得到的耐温层具有优异的耐温性能，将其设置在PVC膜和PET膜之间，并经过加工后，使得整体的灯箱布材料具有较好的耐老化作用，延长使用寿命。
附图说明
通过阅读参照以下附图对非限制性实施例所作的详细描述，本发明的其它特征、目的和优点将会变得更明显：
图1为本发明提供的一种耐老化的灯箱布材料结构示意图。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
结合图1，本实施例提供的一种耐老化的灯箱布材料，所述灯箱布材料包括PVC膜1和PET膜2，所述PVC膜1和PET膜2之间还设置耐温层3，所述耐温层3与PVC膜1之间通过粘结剂粘结，所述耐温层3与PET膜2之间通过粘结剂粘结；
所述耐温层3包括如下重量份数的原料：聚对苯二甲酸乙二醇酯35份、聚苯乙烯树脂6份、氮丙啶交联剂11份、十二烷基硫酸钠盐3份、粘胶纤维21份、聚乙烯吡咯烷酮7份、相容剂7.3份。
作为优选方案，所述PVC膜1的原料配方为：PVC树脂粉100重量份、聚甲基丙烯酸甲酯30重量份、增塑剂3.1重量份、钛白粉39重量份、二甘醇二苯甲酸酯3重量份、阻燃剂1.5重量份、大豆油2重量份。
作为优选方案，所述PVC膜1的生产工艺为：
（1）按照重量份数称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油；
（2）各原料经配料计量后高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得。
作为优选方案，所述挤出时温度控制在218℃。
作为优选方案，所述相容剂由甲基丙烯酸甲酯-丁二烯-苯乙烯的嵌段共聚物、马来酸酐单体、高抗冲聚苯乙烯、接枝反应引发剂发生接枝反应得到。
一种耐老化的灯箱布材料的制备方法，所述制备方法包括如下步骤：
步骤一、按照重量配比称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得PVC膜1；
步骤二、按照重量份数称量聚对苯二甲酸乙二醇酯、聚苯乙烯树脂、氮丙啶交联剂、十二烷基硫酸钠盐、粘胶纤维、聚乙烯吡咯烷酮、相容剂，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得耐温层3；
步骤三、在PET膜2上涂布粘结剂，烘干后采用贴合法与耐温层3的一面复合，然后再将粘结剂涂布于耐温层3的另外一面，烘干，即可。
实施例2
结合图1，本实施例提供的一种耐老化的灯箱布材料，所述灯箱布材料包括PVC膜1和PET膜2，所述PVC膜1和PET膜2之间还设置耐温层3，所述耐温层3与PVC膜1之间通过粘结剂粘结，所述耐温层3与PET膜2之间通过粘结剂粘结；
所述耐温层3包括如下重量份数的原料：聚对苯二甲酸乙二醇酯13份、聚苯乙烯树脂13份、氮丙啶交联剂8份、十二烷基硫酸钠盐9份、粘胶纤维7份、聚乙烯吡咯烷酮11份、相容剂5.1份。
作为优选方案，所述PVC膜1的原料配方为：PVC树脂粉100重量份、聚甲基丙烯酸甲酯10重量份、增塑剂5.9重量份、钛白粉25重量份、二甘醇二苯甲酸酯7重量份、阻燃剂1.2重量份、大豆油5重量份。
作为优选方案，所述PVC膜1的生产工艺为：
（1）按照重量份数称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油；
（2）各原料经配料计量后高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得。
作为优选方案，所述挤出时温度控制在215℃。
作为优选方案，所述相容剂由甲基丙烯酸甲酯-丁二烯-苯乙烯的嵌段共聚物、马来酸酐单体、高抗冲聚苯乙烯、接枝反应引发剂发生接枝反应得到。
一种耐老化的灯箱布材料的制备方法，所述制备方法包括如下步骤：
步骤一、按照重量配比称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得PVC膜1；
步骤二、按照重量份数称量聚对苯二甲酸乙二醇酯、聚苯乙烯树脂、氮丙啶交联剂、十二烷基硫酸钠盐、粘胶纤维、聚乙烯吡咯烷酮、相容剂，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得耐温层3；
步骤三、在PET膜2上涂布粘结剂，烘干后采用贴合法与耐温层3的一面复合，然后再将粘结剂涂布于耐温层3的另外一面，烘干，即可。
实施例3
结合图1，本实施例提供的一种耐老化的灯箱布材料，所述灯箱布材料包括PVC膜1和PET膜2，所述PVC膜1和PET膜2之间还设置耐温层3，所述耐温层3与PVC膜1之间通过粘结剂粘结，所述耐温层3与PET膜2之间通过粘结剂粘结；
所述耐温层3包括如下重量份数的原料：聚对苯二甲酸乙二醇酯17份、聚苯乙烯树脂9份、氮丙啶交联剂9份、十二烷基硫酸钠盐6份、粘胶纤维13份、聚乙烯吡咯烷酮9份、相容剂6.3份。
作为优选方案，所述PVC膜1的原料配方为：PVC树脂粉100重量份、聚甲基丙烯酸甲酯20重量份、增塑剂4.9重量份、钛白粉28重量份、二甘醇二苯甲酸酯5重量份、阻燃剂1.3重量份、大豆油3重量份。
作为优选方案，所述PVC膜1的生产工艺为：
（1）按照重量份数称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油；
（2）各原料经配料计量后高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得。
作为优选方案，所述挤出时温度控制在216℃。
作为优选方案，所述相容剂由甲基丙烯酸甲酯-丁二烯-苯乙烯的嵌段共聚物、马来酸酐单体、高抗冲聚苯乙烯、接枝反应引发剂发生接枝反应得到。
一种耐老化的灯箱布材料的制备方法，所述制备方法包括如下步骤：
步骤一、按照重量配比称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得PVC膜1；
步骤二、按照重量份数称量聚对苯二甲酸乙二醇酯、聚苯乙烯树脂、氮丙啶交联剂、十二烷基硫酸钠盐、粘胶纤维、聚乙烯吡咯烷酮、相容剂，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得耐温层3；
步骤三、在PET膜2上涂布粘结剂，烘干后采用贴合法与耐温层3的一面复合，然后再将粘结剂涂布于耐温层3的另外一面，烘干，即可。
实施例4
结合图1，本实施例提供的一种耐老化的灯箱布材料，所述灯箱布材料包括PVC膜1和PET膜2，所述PVC膜1和PET膜2之间还设置耐温层3，所述耐温层3与PVC膜1之间通过粘结剂粘结，所述耐温层3与PET膜2之间通过粘结剂粘结；
所述耐温层3包括如下重量份数的原料：聚对苯二甲酸乙二醇酯25份、聚苯乙烯树脂7份、氮丙啶交联剂8份、十二烷基硫酸钠盐5份、粘胶纤维13份、聚乙烯吡咯烷酮8份、相容剂5.3份。
作为优选方案，所述PVC膜1的原料配方为：PVC树脂粉100重量份、聚甲基丙烯酸甲酯30重量份、增塑剂5.9重量份、钛白粉39重量份、二甘醇二苯甲酸酯7重量份、阻燃剂1.2重量份、大豆油2重量份。
作为优选方案，所述PVC膜1的生产工艺为：
（1）按照重量份数称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油；
（2）各原料经配料计量后高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得。
作为优选方案，所述挤出时温度控制在215-218℃。
作为优选方案，所述相容剂由甲基丙烯酸甲酯-丁二烯-苯乙烯的嵌段共聚物、马来酸酐单体、高抗冲聚苯乙烯、接枝反应引发剂发生接枝反应得到。
一种耐老化的灯箱布材料的制备方法，所述制备方法包括如下步骤：
步骤一、按照重量配比称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得PVC膜1；
步骤二、按照重量份数称量聚对苯二甲酸乙二醇酯、聚苯乙烯树脂、氮丙啶交联剂、十二烷基硫酸钠盐、粘胶纤维、聚乙烯吡咯烷酮、相容剂，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得耐温层3；
步骤三、在PET膜2上涂布粘结剂，烘干后采用贴合法与耐温层的一面复合，然后再将粘结剂涂布于耐温层的另外一面，烘干，即可。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。

Claims (8)

1.一种耐老化的灯箱布材料，所述灯箱布材料包括PVC膜和PET膜，其特征在于：所述PVC膜和PET膜之间还设置耐温层，所述耐温层与PVC膜之间通过粘结剂粘结，所述耐温层与PET膜之间通过粘结剂粘结；
所述耐温层包括如下重量份数的原料：聚对苯二甲酸乙二醇酯13-35份、聚苯乙烯树脂6-13份、氮丙啶交联剂6-11份、十二烷基硫酸钠盐3-9份、粘胶纤维5-21份、聚乙烯吡咯烷酮7-11份、相容剂4.1-7.3份。
2.根据权利要求1所述的一种耐老化的灯箱布材料，其特征在于：所述耐温层包括如下重量份数的原料：聚对苯二甲酸乙二醇酯13-25份、聚苯乙烯树脂7-13份、氮丙啶交联剂8-11份、十二烷基硫酸钠盐5-9份、粘胶纤维7-21份、聚乙烯吡咯烷酮8-11份、相容剂5.1-7.3份。
3.根据权利要求1所述的一种耐老化的灯箱布材料，其特征在于：所述耐温层包括如下重量份数的原料：聚对苯二甲酸乙二醇酯17份、聚苯乙烯树脂9份、氮丙啶交联剂9份、十二烷基硫酸钠盐6份、粘胶纤维13份、聚乙烯吡咯烷酮9份、相容剂6.3份。
4.根据权利要求1所述的一种耐老化的灯箱布材料，其特征在于：所述PVC膜的原料配方为：PVC树脂粉100重量份、聚甲基丙烯酸甲酯10-30重量份、增塑剂3.1-5.9重量份、钛白粉25-39重量份、二甘醇二苯甲酸酯3-7重量份、阻燃剂1.2-1.5重量份、大豆油2-5重量份。
5.根据权利要求4所述的一种耐老化的灯箱布材料，其特征在于：所述PVC膜的生产工艺为：
（1）按照重量份数称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油；
（2）各原料经配料计量后高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得。
6.根据权利要求5所述的一种耐老化的灯箱布材料，其特征在于：所述挤出时温度控制在215-218℃。
7.根据权利要求1所述的一种耐老化的灯箱布材料，其特征在于：所述相容剂由甲基丙烯酸甲酯-丁二烯-苯乙烯的嵌段共聚物、马来酸酐单体、高抗冲聚苯乙烯、接枝反应引发剂发生接枝反应得到。
8.根据权利要求1所述的一种耐老化的灯箱布材料的制备方法，其特征在于：所述制备方法包括如下步骤：
步骤一、按照重量配比称量PVC树脂粉、聚甲基丙烯酸甲酯、增塑剂、钛白粉、二甘醇二苯甲酸酯、阻燃剂、大豆油，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得PVC膜；
步骤二、按照重量份数称量聚对苯二甲酸乙二醇酯、聚苯乙烯树脂、氮丙啶交联剂、十二烷基硫酸钠盐、粘胶纤维、聚乙烯吡咯烷酮、相容剂，将上述各原料进行高速混合，冷却后经挤出后进行四辊压延，再经冷却定型、切边、卷取后制得耐温层；
步骤三、在PET膜上涂布粘结剂，烘干后采用贴合法与耐温层的一面复合， 然后再将粘结剂涂布于耐温层的另外一面，烘干，即可。
CN201810513335.1A 2018-05-25 2018-05-25 一种耐老化的灯箱布材料及其制备方法 Withdrawn CN108859294A (zh)