CN108818840A - A kind of method that wicker green peel prepares wicker products handle - Google Patents
A kind of method that wicker green peel prepares wicker products handle Download PDFInfo
- Publication number
- CN108818840A CN108818840A CN201810384338.XA CN201810384338A CN108818840A CN 108818840 A CN108818840 A CN 108818840A CN 201810384338 A CN201810384338 A CN 201810384338A CN 108818840 A CN108818840 A CN 108818840A
- Authority
- CN
- China
- Prior art keywords
- wicker
- parts
- handle
- prepares
- green peel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of method that wicker green peel prepares wicker products handle, including following operating procedure：（1）Wicker is put into steamer, cooking liquor is then added thereto, after not crossing the wicker in pot, after cooking liquor is boiled using high fire, small fire isothermal holding；（2）After wicker peeling, after wicker skin is smoothed out with the fingers directly, one end alignment, the other end is cut neatly again, after cutting neatly, the wicker skin cross winding of equal length is woven into wicker skin band, then it places it in polymer fluid, wicker skin band is fixed on the wicker products of suitable size by drying and processing after immersion treatment, and wicker products handle is made.The problem of method that a kind of wicker green peel provided by the invention prepares wicker products handle, effective solution a large amount of wicker green peels pollution environment, waste utilization, resource, while wicker products handle obtained, excellent in mechanical performance are saved, with fresh and elegant style, colour fixation is significant.
Description
Technical field
The invention belongs to wicker products preparation technical fields, and in particular to a kind of wicker green peel prepares wicker products handle
Method.
Background technique
Wicker products are the artifacts of the civil widespread in China, and wicker products raw material are extensive, make full use of toughness
The characteristics of plant, focuses on color, skin texture, pursues naturally, embodies honest, pure and honest, the sincere moral character of the labour common people.Wicker plaiting article system
Product need to handle wicker during braiding, including the techniques such as boiling, peeling, bleaching, after wicker peeling, can produce
Raw a large amount of wicker green peel, not only pollutes the environment, but also cause the waste of resource after directly abandoning.Wicker products handle is
A common component, makes wicker products be easy to carry about with one on some wicker products, and can promote the ornamental of wicker products
Property.
Summary of the invention
The object of the present invention is to provide a kind of waste wicker green peels using in wicker products preparation process to prepare wicker plaiting article
The method of product handle.
The present invention is achieved by the following technical solutions.
A kind of method that wicker green peel prepares wicker products handle, including following operating procedure：
（1）Wicker is put into steamer, cooking liquor is then added thereto, after not crossing the wicker in pot, using high fire by boiling
After liquid boils, small fire isothermal holding 20-30min, wherein cooking liquor is made of the component of following parts by weight：Pfansteihl sodium 11-15
Part, 7-10 parts of sodium phytate, 1-3 parts of ammonium pentaborate, 260-300 parts of water；
（2）Step will be passed through（1）After the wicker peeling of processing, by wicker skin smooth out with the fingers it is straight after, one end alignment, then the other end cut whole
Together, after cutting neatly, the length of every wicker skin is not less than 20cm, and the wicker skin cross winding of equal length is woven into diameter
It for the wicker skin band of 1.5-2.5cm, then places it in polymer fluid, after immersion treatment 8-10min, takes out, dry surface
It after moisture, places it in baking oven, after drying and processing 3-4 hours, wicker skin band is fixed on to the wicker products of suitable size
On, wicker products handle is made, wherein polymer fluid is made of the component of following parts by weight：39-45 parts of konjak starch, hydrogen peroxide
11-15 parts, mass fraction be 3-6 parts of 13% hydrochloric acid, 13-16 parts of ethyl acrylate, 8-12 parts of methyl methacrylate, initiator
0.1-0.3 parts, 0.1-0.2 parts of emulsifier, 210-240 parts of deionized water；
Wherein polymer fluid is made of following methods：2/3rds deionized waters are taken, after its temperature is risen to 55-60 DEG C, Xiang Qi
Middle addition konjak starch, stirs evenly, then slow addition hydrogen peroxide thereto, after mixing evenly, insulation reaction 40-
After 50min, it is 13% hydrochloric acid that mass fraction is added thereto, is mixed evenly, and after continuing insulation reaction 2-3 hours, is made viscous
Liquid is tied, it is spare；
Emulsifier is added into remaining deionized water, after mixing evenly, is heated to 80-85 DEG C, is then successively added thereto
Enter ethyl acrylate, methyl methacrylate, initiator, is uniformly mixed, after insulation reaction 4-5 hours, is added thereto above-mentioned
After persistently stirring 60-70min using the revolving speed of 400r/min, polymer fluid is made in binding liquid obtained.
Specifically, above-mentioned steps（2）In, the mass fraction of hydrogen peroxide is 30%.
Specifically, above-mentioned steps（2）In, initiator is peroxidized t-butyl perbenzoate, peroxidating trimethylacetic acid tertiary butyl ester
In any one.
Specifically, mentioned emulsifier is nonylphenol polyoxyethylene ether, any one in octyl phenol polyoxyethylene ether.
Specifically, above-mentioned steps（2）In, temperature when drying and processing is 60-65 DEG C.
From the above technical scheme, it can be seen that the beneficial effects of the invention are as follows：
The method that a kind of wicker green peel provided by the invention prepares wicker products handle, environmentally protective, at low cost, effective solution
The problem of a large amount of wicker green peels pollution environment, waste utilization saved resource, while wicker products handle obtained, mechanics
It has excellent performance, there is fresh and elegant style, colour fixation is significant, effectively improves the ornamental value of wicker products.Wherein, it walks
Suddenly（1）After the cooking liquor of middle offer, Pfansteihl sodium and sodium phytate synergistic effect, it can effectively expand intercellular, wicker green peel
Gap, so to a certain extent improve the pliability of wicker green peel so that green peel is easily peeled off；Ammonium pentaborate can promote green peel
Colour fixation, effectively extend the service life of wicker products handle；After the present invention is by aoxidizing konjak starch, it is made
Binding liquid with adhesive property, after then binding liquid and homemade organic polymer are mixed again, polymer fluid obtained, bonding
It has excellent performance, can effectively prevent wicker products handle during use there is a phenomenon where loose, meanwhile, according to the present invention
The parts by weight of offer, polymer obtained almost have no irritating odor, asepsis environment-protecting.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, following embodiment carries out the present invention
It is further described.It should be appreciated that specific embodiment party example described herein is only used to explain the present invention, it is not used to limit
The fixed present invention.
Embodiment 1
A kind of method that wicker green peel prepares wicker products handle, including following operating procedure：
（1）Wicker is put into steamer, cooking liquor is then added thereto, after not crossing the wicker in pot, using high fire by boiling
After liquid boils, small fire isothermal holding 20min, wherein cooking liquor is made of the component of following parts by weight：11 parts of Pfansteihl sodium, phytic acid
7 parts of sodium, 1 part of ammonium pentaborate, 260 parts of water；
（2）Step will be passed through（1）After the wicker peeling of processing, by wicker skin smooth out with the fingers it is straight after, one end alignment, then the other end cut whole
Together, after cutting neatly, the length of every wicker skin is 23cm, and the wicker skin cross winding of equal length, which is woven into diameter, is
The wicker skin band of 1.5cm, then places it in polymer fluid, after immersion treatment 8min, takes out, will after drying surface moisture
It is placed in an oven, after drying and processing 3 hours, wicker skin band is fixed on the wicker products of suitable size, and wicker plaiting article is made
Product handle, wherein polymer fluid is made of the component of following parts by weight：39 parts of konjak starch, 11 parts of hydrogen peroxide, mass fraction are
13% 3 parts of hydrochloric acid, 13 parts of ethyl acrylate, 8 parts of methyl methacrylate, 0.1 part of initiator, 0.1 part of emulsifier, deionized water
210 parts；
Wherein polymer fluid is made of following methods：Take 2/3rds deionized waters, after its temperature is risen to 55 DEG C, thereto plus
Enter konjak starch, stir evenly, then slow addition hydrogen peroxide thereto, after mixing evenly, after insulation reaction 40min,
It is 13% hydrochloric acid that mass fraction is added thereto, is mixed evenly, and after continuing insulation reaction 2 hours, binding liquid is made, spare；
Emulsifier is added into remaining deionized water, after mixing evenly, 80 DEG C is heated to, third is then successively added thereto
Olefin(e) acid ethyl ester, methyl methacrylate, initiator are uniformly mixed, after insulation reaction 4 hours, are added thereto obtained above
After persistently stirring 60min using the revolving speed of 400r/min, polymer fluid is made in binding liquid.
Specifically, above-mentioned steps（2）In, the mass fraction of hydrogen peroxide is 30%.
Specifically, above-mentioned steps（2）In, initiator is peroxidized t-butyl perbenzoate.
Specifically, mentioned emulsifier is nonylphenol polyoxyethylene ether.
Specifically, above-mentioned steps（2）In, temperature when drying and processing is 60 DEG C.
Embodiment 2
A kind of method that wicker green peel prepares wicker products handle, including following operating procedure：
（1）Wicker is put into steamer, cooking liquor is then added thereto, after not crossing the wicker in pot, using high fire by boiling
After liquid boils, small fire isothermal holding 25min, wherein cooking liquor is made of the component of following parts by weight：13 parts of Pfansteihl sodium, phytic acid
8 parts of sodium, 2 parts of ammonium pentaborate, 280 parts of water；
（2）Step will be passed through（1）After the wicker peeling of processing, by wicker skin smooth out with the fingers it is straight after, one end alignment, then the other end cut whole
Together, after cutting neatly, the length of every wicker skin is 25cm, and the wicker skin cross winding of equal length, which is woven into diameter, is
The wicker skin band of 2.0cm, then places it in polymer fluid, after immersion treatment 9min, takes out, will after drying surface moisture
It is placed in an oven, after drying and processing 3.5 hours, wicker skin band is fixed on the wicker products of suitable size, and willow is made
Establishment product handle, wherein polymer fluid is made of the component of following parts by weight：42 parts of konjak starch, 13 parts of hydrogen peroxide, mass fraction
For 5 parts of 13% hydrochloric acid, 14 parts of ethyl acrylate, 10 parts of methyl methacrylate, 0.2 part of initiator, 0.1 part of emulsifier, deionization
230 parts of water；
Wherein polymer fluid is made of following methods：Take 2/3rds deionized waters, after its temperature is risen to 58 DEG C, thereto plus
Enter konjak starch, stir evenly, then slow addition hydrogen peroxide thereto, after mixing evenly, after insulation reaction 45min,
It is 13% hydrochloric acid that mass fraction is added thereto, is mixed evenly, and after continuing insulation reaction 2.5 hours, binding liquid is made, standby
With；
Emulsifier is added into remaining deionized water, after mixing evenly, 83 DEG C is heated to, third is then successively added thereto
Olefin(e) acid ethyl ester, methyl methacrylate, initiator are uniformly mixed, and after insulation reaction 4.5 hours, above-mentioned be made is added thereto
Binding liquid, after persistently stirring 65min using the revolving speed of 400r/min, be made polymer fluid.
Specifically, above-mentioned steps（2）In, the mass fraction of hydrogen peroxide is 30%.
Specifically, above-mentioned steps（2）In, initiator is peroxidating trimethylacetic acid tertiary butyl ester.
Specifically, mentioned emulsifier is nonylphenol polyoxyethylene ether.
Specifically, above-mentioned steps（2）In, temperature when drying and processing is 63 DEG C.
Embodiment 3
A kind of method that wicker green peel prepares wicker products handle, including following operating procedure：
（1）Wicker is put into steamer, cooking liquor is then added thereto, after not crossing the wicker in pot, using high fire by boiling
After liquid boils, small fire isothermal holding 30min, wherein cooking liquor is made of the component of following parts by weight：15 parts of Pfansteihl sodium, phytic acid
10 parts of sodium, 3 parts of ammonium pentaborate, 300 parts of water；
（2）Step will be passed through（1）After the wicker peeling of processing, by wicker skin smooth out with the fingers it is straight after, one end alignment, then the other end cut whole
Together, after cutting neatly, the length of every wicker skin is 27cm, and the wicker skin cross winding of equal length, which is woven into diameter, is
The wicker skin band of 2.5cm, then places it in polymer fluid, after immersion treatment 10min, takes out, will after drying surface moisture
It is placed in an oven, after drying and processing 4 hours, wicker skin band is fixed on the wicker products of suitable size, and wicker plaiting article is made
Product handle, wherein polymer fluid is made of the component of following parts by weight：45 parts of konjak starch, 15 parts of hydrogen peroxide, mass fraction are
13% 6 parts of hydrochloric acid, 16 parts of ethyl acrylate, 12 parts of methyl methacrylate, 0.3 part of initiator, 0.2 part of emulsifier, deionized water
240 parts；
Wherein polymer fluid is made of following methods：Take 2/3rds deionized waters, after its temperature is risen to 60 DEG C, thereto plus
Enter konjak starch, stir evenly, then slow addition hydrogen peroxide thereto, after mixing evenly, after insulation reaction 50min,
It is 13% hydrochloric acid that mass fraction is added thereto, is mixed evenly, and after continuing insulation reaction 3 hours, binding liquid is made, spare；
Emulsifier is added into remaining deionized water, after mixing evenly, 85 DEG C is heated to, third is then successively added thereto
Olefin(e) acid ethyl ester, methyl methacrylate, initiator are uniformly mixed, after insulation reaction 5 hours, are added thereto obtained above
After persistently stirring 70min using the revolving speed of 400r/min, polymer fluid is made in binding liquid.
Specifically, above-mentioned steps（2）In, the mass fraction of hydrogen peroxide is 30%.
Specifically, above-mentioned steps（2）In, initiator is peroxidating trimethylacetic acid tertiary butyl ester.
Specifically, mentioned emulsifier is octyl phenol polyoxyethylene ether.
Specifically, above-mentioned steps（2）In, temperature when drying and processing is 65 DEG C.
Comparative example 1
Step（1）Ammonium pentaborate ingredient is not contained in cooking liquor, remaining operating procedure is identical with embodiment 1.
Wicker products handle is made with the method for each embodiment and comparative example respectively, then puts it into boiling water, decocts
After 20min, whether each group wicker products handle is checked there is a phenomenon where decolourizing, test result is as shown in table 1：
The phenomenon that 1 wicker products handle of table decolourizes
After the above-mentioned boiling water for decocting wicker products handle is cooled to room temperature again, it is put into red bubble goldfish thereto, it is normal to raise
It supports, checks the survival condition of goldfish during raising, test result is as shown in table 2：
The survival condition of 2 goldfish of table
As shown in Table 2, wicker products handle asepsis environment-protecting produced by the present invention.
Certainly, the above description is not a limitation of the present invention, and the present invention is also not limited to the example above, the art
Those of ordinary skill, within the essential scope of the present invention, variation, change, addition or the replacement made all should belong to the present invention
Protection scope.
Claims (5)
1. a kind of method that wicker green peel prepares wicker products handle, which is characterized in that including following operating procedure：
（1）Wicker is put into steamer, cooking liquor is then added thereto, after not crossing the wicker in pot, using high fire by boiling
After liquid boils, small fire isothermal holding 20-30min, wherein cooking liquor is made of the component of following parts by weight：Pfansteihl sodium 11-15
Part, 7-10 parts of sodium phytate, 1-3 parts of ammonium pentaborate, 260-300 parts of water；
（2）Step will be passed through（1）After the wicker peeling of processing, by wicker skin smooth out with the fingers it is straight after, one end alignment, then the other end cut whole
Together, after cutting neatly, the length of every wicker skin is not less than 20cm, and the wicker skin cross winding of equal length is woven into diameter
It for the wicker skin band of 1.5-2.5cm, then places it in polymer fluid, after immersion treatment 8-10min, takes out, dry surface
It after moisture, places it in baking oven, after drying and processing 3-4 hours, wicker skin band is fixed on to the wicker products of suitable size
On, wicker products handle is made, wherein polymer fluid is made of the component of following parts by weight：39-45 parts of konjak starch, hydrogen peroxide
11-15 parts, mass fraction be 3-6 parts of 13% hydrochloric acid, 13-16 parts of ethyl acrylate, 8-12 parts of methyl methacrylate, initiator
0.1-0.3 parts, 0.1-0.2 parts of emulsifier, 210-240 parts of deionized water；
Wherein polymer fluid is made of following methods：2/3rds deionized waters are taken, after its temperature is risen to 55-60 DEG C, Xiang Qi
Middle addition konjak starch, stirs evenly, then slow addition hydrogen peroxide thereto, after mixing evenly, insulation reaction 40-
After 50min, it is 13% hydrochloric acid that mass fraction is added thereto, is mixed evenly, and after continuing insulation reaction 2-3 hours, is made viscous
Liquid is tied, it is spare；
Emulsifier is added into remaining deionized water, after mixing evenly, is heated to 80-85 DEG C, is then successively added thereto
Enter ethyl acrylate, methyl methacrylate, initiator, is uniformly mixed, after insulation reaction 4-5 hours, is added thereto above-mentioned
After persistently stirring 60-70min using the revolving speed of 400r/min, polymer fluid is made in binding liquid obtained.
2. the method that a kind of wicker green peel according to claim 1 prepares wicker products handle, which is characterized in that above-mentioned step
Suddenly（2）In, the mass fraction of hydrogen peroxide is 30%.
3. the method that a kind of wicker green peel according to claim 1 prepares wicker products handle, which is characterized in that above-mentioned step
Suddenly（2）In, initiator is peroxidized t-butyl perbenzoate, any one in peroxidating trimethylacetic acid tertiary butyl ester.
4. the method that a kind of wicker green peel according to claim 1 prepares wicker products handle, which is characterized in that above-mentioned cream
Agent is nonylphenol polyoxyethylene ether, any one in octyl phenol polyoxyethylene ether.
5. the method that a kind of wicker green peel according to claim 1 prepares wicker products handle, which is characterized in that above-mentioned step
Suddenly（2）In, temperature when drying and processing is 60-65 DEG C.