CN108755199A - The long vehicle dyeing production of cotton and protein fibre blended yarn weaved fabric - Google Patents
The long vehicle dyeing production of cotton and protein fibre blended yarn weaved fabric Download PDFInfo
- Publication number
- CN108755199A CN108755199A CN201810633497.9A CN201810633497A CN108755199A CN 108755199 A CN108755199 A CN 108755199A CN 201810633497 A CN201810633497 A CN 201810633497A CN 108755199 A CN108755199 A CN 108755199A
- Authority
- CN
- China
- Prior art keywords
- long vehicle
- washing
- short steaming
- speed
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The long vehicle dyeing production of cotton and protein fibre blended yarn weaved fabric, be related to textile production process technical field, by the blended yarn weaved fabric of cotton and protein successively by singing, enzyme heap, primary short steaming high temperature washing, cold dome, secondary short steaming high temperature washing, one-step building, acid dyeing, vital staining, secondary sizing, liquefied ammonia, washing, shape three times and give contracting process.The broadwise washing shrinkage of production fabric is can be controlled within -4%.Its application performance has a wide range of applications market, the superior quality index and safe performance indexes of garment production is fully achieved, especially suitable for high-grade fabric.
Description
Technical field
The present invention relates to the long vehicles of textile production process technical field, especially fabric to dye production technology.
Background technology
Protein fibre is a classification of staple fibre, is referred to by being carried from the natural objects such as milk, soybean, peanut, corn
The protein got is raw material, is dissolved in fiber obtained in appropriate solvent.The fiber starts to realize in the 1930s
Industrialized production stops production in succession with the appearance of numerous synthetic fibers.It is comfortable and easy to wear due to fabric hand softness；Into
Since entering the nineties, and there is the producer to start to extract milk casein from milk to produce " protein fibre of new generation " --- junket
Cellulose fiber (casein fiber), wears for making underwear, it is said that also having certain " maintenance " effect to skin；Product form master
It to be staple fiber.
Although protein fibre has feel similar with skin, surface is glossy, and cost is higher, and feel is excessively soft, shape
Type is difficult to out on shape, fixed effect is poor.Cotton fiber is the mankind earliest as the material of fabric, has fabulous hygroscopicity, hand
Feel harder.
Invention content
Based on the above, the purpose of the present invention is to provide a kind of ingredient stability, by cotton and protein fibre blended yarn weaved fabric
Long vehicle dyeing production.
Fabric of the present invention is the blended yarn weaved fabric of cotton and protein；Production method step successively include singe, enzyme heap, one
Secondary short steaming high temperature washing, cold dome, secondary short steaming high temperature washing, one-step building, acid dyeing, vital staining, secondary sizing, liquid
Ammonia, washing shape and give contracting three times.
The present invention utilizes the hygroscopicity of cotton and plentiful, the soft feel of snugness of fit and protein fibre, surface
Glossiness is good, and excellent resilience tissue processing, the broadwise washing shrinkage for producing fabric is can be controlled within -4%.It is applied
Performance has a wide range of applications market, and the superior quality index and safe performance indexes of garment production is fully achieved, particularly suitable
In high-grade fabric.
The cotton protein matter fiber blended fabric that the method is suitable for heterogeneity ratio produces.
Further, enzyme heap of the present invention, primary short steaming high temperature washing, cold dome, secondary short steaming high temperature washing, acid dye
Color and vital staining carry out under conditions of no caustic soda respectively, avoid protein fibre from meeting caustic soda and melt.
Working solution is formed by enzyme, dispersant and water when enzyme heap, wherein high temperature enzyme 5g/l, dispersant 5g/l.
When primary short steaming high temperature washing, speed 55m/min, the short steaming time is 1min, and steamer temperature is 80~85 DEG C, water
Box temperature degree is 85 DEG C.Cloth cover surface impurity can be fully washed away, following process is conducive to.
When cold dome, speed 60m/min, padding machine pressure be 0.15kg, by refining agent, dispersant, stabilizer, hydrogen peroxide,
Efficient compound boiling, bleaching-bathing method auxiliary agent and water form working solution, wherein refining agent 20g/l, dispersant 2g/l, stabilizer 12g/
L, hydrogen peroxide 20g/l, efficient compound boiling, bleaching-bathing method auxiliary agent：20g/l, make the test bleaching after banking up 24 hours.It is answered using efficient
Mould assembly boiling, bleaching-bathing method auxiliary agent is effectively reacted with the slurry on fabric.
When secondary short steaming high temperature washing, speed 40m/min, the short steaming time is 1min, and steamer temperature is 80~85 DEG C, water
Box temperature degree is 85 DEG C, effectively removes the slurry of fabric surface, and it is white to improve bottom.
When one-step building, speed 65m/min, roll compacting 0.3MPa, drying room temperature are 100 DEG C, it is ensured that cloth cover is wrinkle-free.
When secondary sizing, speed 65m/min, roll compacting 0.3MPa, drying room temperature are 100 DEG C, working solution color fixing agent 10g/
L effectively reduces liquefied ammonia color change situation.
When liquefied ammonia, processing room temperature is 60~90 DEG C, and Processing Room pressure difference is -10~-100Pa, and blanket tension is 0.05
~0.1MPa.
When shaping three times, speed 75m/min, roll compacting is 0.3 MPa, and drying room temperature is 110 DEG C, in working solution plus appropriate
Softening agent improves feel, reaches customer requirement.
Specific implementation mode
One, cotton silk blend dyeing fabric produces：
1, production technology：
Fabric specification：Yarn count 70（Composition：85% cotton, 15% silk）×70（Composition：85% cotton, 15% silk）, density 159 × 121,
Jacquard weave.
2, long vehicle dyes the technological process of production：
It singes, enzyme heap, once short steaming high temperature washing, cold dome, secondary short steaming high temperature washing, one-step building, acid dyeing, activity dye
Color, liquefied ammonia, washing, shapes, gives contracting at secondary sizing three times.
Specific process parameter is as follows：
It singes：
Speed：120m/min, burner 2, flame intensity 7, for mode of singing to burning, cropping must assure that cloth cover singes effect up to 4
Grade, cloth cover are bright and clean.
Enzyme heap：
Speed 60m/min, padding machine pressure：0.15KG forms working solution, wherein enzyme 5g/l by high temperature enzyme, dispersant and water, dispersion
Agent 5g/l, 65 DEG C of working solution temperature, make the test washing after banking up 6 hours.This process main purpose is to make fabric using chemical assistant
The removal of slurry is convenient in fully reaction.
Primary short steaming high temperature washing：
Speed 55m/min, is not banked up, short steaming time 1min, 80~85 DEG C of steamer temperature, 85 DEG C of water tank temperature.
Purpose is to be effectively removed surface size.
Cold dome：
Speed 60m/min, padding machine pressure：0.15KG boils drift by refining agent, dispersant, stabilizer, hydrogen peroxide, efficient compound
Single bath process auxiliary agent and water form working solution, wherein refining agent 20g/l, dispersant 2g/l, stabilizer 12g/l, hydrogen peroxide 20g/l,
Efficient compound boiling, bleaching-bathing method auxiliary agent：20g/l, make the test bleaching after banking up 24 hours.
This process main purpose is to play desizing, blanching effect using efficient compound boiling, bleaching-bathing method auxiliary agent, reduces life
Cost is produced, production technology is shortened.
Secondary short steaming high temperature washing：
Speed 40m/min, short steaming time 1min, 80~85 DEG C of steamer temperature, 85 DEG C of water tank temperature make it float bottom uniform, dyeing
Good level-dyeing property.
One-step building：
Speed：65m/min, roll compacting：0.3MPa, 100 DEG C of drying room temperature.
Door width pulls open as possible, it is ensured that cloth cover is smooth without soft wrinkle.
Acid dyeing：
Acid dyes is selected to be dyed using the characteristic of silk.
Vital staining：
Speed 40m/min, 102 DEG C of steamer temperature, 95 DEG C of washing temperature select Imported Dyestuffs to keep fabric color fastness preferable, can
It meets customer need.
Secondary sizing：
Speed：65m/min, roll compacting：0.3MPa, 100 DEG C of drying room temperature.
Color change is big after this step mainly considers liquefied ammonia, and alkaline-resisting color fixing agent need to be added in hopper, reduces liquefied ammonia production
When fade situation.
Liquefied ammonia：
Process 60~90 DEG C of room temperature, Processing Room -10~-100Pa of pressure difference, blanket 0.05~0.1MPa of tension, speed 45m/
min。
Washing：
Mainly wash away the residual ammonia of fabric surface.
It shapes three times：
Speed：75m/min, roll compacting：0.3 MPa, 110 DEG C of drying room temperature require to add softening agent appropriate according to client's feel.
Preshrunk：
Contracting cloth rate is determined according to shrink testing result, its shrink and feel is made to reach customer requirement.
2, product quality：
Trimmed size：Yarn count 70（85% cotton, 15% silk）×70（85% cotton, 15% silk）, density 180 × 126；Door 57/58.
With《AATCC135-2015(1)IIIA(ii)3X》Standard carry out washing shrinkage experiment, the result is that broadwise washing shrinkage be-
3.5%。
As it can be seen that present invention process is easy to operate, excellent product performance, be fully achieved garment production superior quality index and
Safe performance indexes, especially suitable for high-grade fabric.
Two, the wool blended dyed shell fabrics production of cotton：
1, production technology：
Fabric specification：Yarn count 50（Composition：80% cotton, 20% wool）×50（Composition：80% cotton, 20% wool）, density 127 × 108,
2/2 is right oblique.
2, long vehicle dyes the technological process of production：
It singes, enzyme heap, once short steaming high temperature washing, cold dome, secondary short steaming high temperature washing, one-step building, acid dyeing, activity dye
Color, liquefied ammonia, washing, shapes, gives contracting at secondary sizing three times.
Specific process parameter is as follows：
It singes：
Speed：120m/min, burner 2, flame intensity 7, for mode of singing to burning, cropping must assure that cloth cover singes effect up to 4
Grade, cloth cover are bright and clean.
Enzyme heap：
Speed 60m/min, padding machine pressure：0.15KG forms working solution, wherein high temperature enzyme 5g/l by enzyme, dispersant and water, dispersion
Agent 5g/l, 65 DEG C of working solution temperature, make the test washing after banking up 6 hours.This process main purpose is to make fabric using chemical assistant
The removal of slurry is convenient in fully reaction.
Primary short steaming high temperature washing：
Speed 55m/min, is not banked up, short steaming time 1min, 80~85 DEG C of steamer temperature, and 85 DEG C of water tank temperature can effectively be gone
Except surface size.
Cold dome：
Speed 60m/min, padding machine pressure：0.15KG boils drift by refining agent, dispersant, stabilizer, hydrogen peroxide, efficient compound
Single bath process auxiliary agent and water form working solution, wherein refining agent 20g/l, dispersant 2g/l, stabilizer 12g/l, hydrogen peroxide 20g/l,
Efficient compound boiling, bleaching-bathing method auxiliary agent：20g/l.Make the test bleaching after banking up 24 hours.
This process main purpose is to play desizing, blanching effect using efficient compound boiling, bleaching-bathing method auxiliary agent, reduces life
Cost is produced, production technology is shortened.
Secondary short steaming high temperature washing：
Speed 40m/min, short steaming time 1min, 80~85 DEG C of steamer temperature, 85 DEG C of water tank temperature make it float bottom uniform, dyeing
Good level-dyeing property.
One-step building：
Speed：65m/min, roll compacting：0.3MPa, 100 DEG C of drying room temperature.
Door width pulls open as possible, it is ensured that cloth cover is smooth without soft wrinkle.
Acid dyeing：
Using the characteristic selection acid dyes of wool dye while not influencing the vital staining of cotton again.
Vital staining：
Speed 40m/min, 102 DEG C of steamer temperature, 95 DEG C of washing temperature select Imported Dyestuffs to keep fabric color fastness preferable, can
It meets customer need.
Secondary sizing：
Speed：65m/min, roll compacting：0.3MPa, 100 DEG C of drying room temperature.
Color change is big after this step mainly considers liquefied ammonia, and alkaline-resisting color fixing agent need to be added in hopper, reduces liquefied ammonia production
When fade situation.
Liquefied ammonia：
Process 60~90 DEG C of room temperature, Processing Room -10~-100Pa of pressure difference, blanket 0.05~0.1MPa of tension, speed 45m/
min。
Washing：
Mainly wash away the residual ammonia of fabric surface.
It shapes three times：
Speed：75m/min, roll compacting：0.3 MPa, 110 DEG C of drying room temperature require to add softening agent appropriate according to client's feel.
Preshrunk：
Contracting cloth rate is determined according to shrink testing result, its shrink and feel is made to reach customer requirement.
3, product quality：
Trimmed size：Yarn count 50（80% cotton, 20% wool）×50（80% cotton, 20% wool）, density 150 × 110；Door 57/58.
With《AATCC135-2015(1)IIIA(ii)3X》Standard carry out washing shrinkage experiment, the result is that broadwise washing shrinkage be-
4.0%
As it can be seen that present invention process is easy to operate, the superior quality index and safety of garment production is fully achieved in excellent product performance
Performance indicator, especially suitable for high-grade fabric.
Claims (10)
1. the long vehicle dyeing production of cotton and protein fibre blended yarn weaved fabric, it is characterised in that：The fabric is cotton and albumen
The blended yarn weaved fabric of matter；Production method step include successively singe, enzyme heap, primary short steaming high temperature washing, cold dome, secondary short steaming high temperature
Washing, acid dyeing, vital staining, secondary sizing, liquefied ammonia, washing, shapes and gives contracting at one-step building three times.
2. long vehicle dyeing production according to claim 1, it is characterised in that：The enzyme heap, primary short steaming high-temperature water
It washes, cold dome, secondary short steaming high temperature are washed, acid dyeing and vital staining carry out under conditions of no caustic soda respectively.
3. long vehicle dyeing production according to claim 1, it is characterised in that：When the enzyme heap by enzyme, dispersant and
Water forms working solution, wherein high temperature enzyme 5g/l, dispersant 5g/l.
4. long vehicle dyeing production according to claim 1, it is characterised in that：When the primary short steaming high temperature washing,
Speed is 55m/min, and the short steaming time is 1min, and steamer temperature is 80~85 DEG C, and water tank temperature is 85 DEG C.
5. long vehicle dyeing production according to claim 1, it is characterised in that：When the cold dome, speed 60m/
Min, padding machine pressure be 0.15kg, by refining agent, dispersant, stabilizer, hydrogen peroxide, efficient compound boiling, bleaching-bathing method auxiliary agent and
Water forms working solution, wherein refining agent 20g/l, dispersant 2g/l, stabilizer 12g/l, hydrogen peroxide 20g/l, efficient compound boil
Bleaching-bathing method auxiliary agent：20g/l, make the test bleaching after banking up 24 hours.
6. long vehicle dyeing production according to claim 1, it is characterised in that：When the secondary short steaming high temperature washing,
Speed is 40m/min, and the short steaming time is 1min, and steamer temperature is 80~85 DEG C, and water tank temperature is 85 DEG C.
7. long vehicle dyeing production according to claim 1, it is characterised in that：When the one-step building, speed is
65m/min, roll compacting 0.3MPa, drying room temperature are 100 DEG C.
8. long vehicle dyeing production according to claim 1, it is characterised in that：When the secondary sizing, speed is
65m/min, roll compacting 0.3MPa, drying room temperature are 100 DEG C.
9. long vehicle dyeing production according to claim 1, it is characterised in that：When the liquefied ammonia, processing room temperature is
60~90 DEG C, Processing Room pressure difference is -10~-100Pa, and blanket tension is 0.05~0.1MPa.
10. long vehicle dyeing production according to claim 1, it is characterised in that：Described when shaping three times, speed is
75m/min, roll compacting are 0.3 MPa, and drying room temperature is 110 DEG C.