CN108728986A - Cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric and its long vehicle dyeing production - Google Patents
Cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric and its long vehicle dyeing production Download PDFInfo
- Publication number
- CN108728986A CN108728986A CN201810633498.3A CN201810633498A CN108728986A CN 108728986 A CN108728986 A CN 108728986A CN 201810633498 A CN201810633498 A CN 201810633498A CN 108728986 A CN108728986 A CN 108728986A
- Authority
- CN
- China
- Prior art keywords
- cotton
- polyester
- fabric
- interwoven
- broadwise
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric and its long vehicle dyeing production, are related to the post-processing technology field of fabric, and production procedure has:Singe, cold dome, bleaching, mercerising, preshrunk, dispersion bottoming, high-temperature shaping color development, reduction cleaning, set cotton, sizing, secondary preshrunk;It is -4.0%~0% through broadwise washing size changing rate, difference is less than 2% between warp-wise and broadwise shrink;Determine power elongation >=12% through broadwise, through broadwise tensile elasticity response rate >=55%, flatness is up to 4.0 grades after scalding.Flatness is high after the cotton-polyester blend or cotton polyester interwoven four-side elasticity fabric of the present invention scalds, low through broadwise washing shrinkage, and tensile elasticity response rate is high, is suitable for high-grade clothing.
Description
Technical field
The present invention relates to the post-processing technology fields of fabric.
Background technology
" spandex fabric " is for fabric count by elastic filament to making fabric warp-wise broadwise obtain excellent stretching rebound
Performance.Especially in women's dress market, application gradually be extensive to four-side elasticity fabric, it adapts to the activity of human body, brisk easypro with stretching with contracting
It is suitable, and the good appearance of clothes can be kept.
Common four-side elasticity fabric mostly is made, through weft yarn, also to have using SPH fibers with spandex core-spun yarn in the market(SPH is a kind of
New elastic fiber long filament.SPH fibers are a kind of new elastic fibers occurred in the market in recent years, are by two kinds of PTT, PET
The petchem of different thermodynamic properties through made of composite spinning arranged side by side, then processed by heat treatment without tension to be formed it is similar
The crimped fibre of the thin and close three-dimensional structure of wool)Make through weft yarn.
The general elastic force elongation of four-side elasticity fabric that spandex core-spun yarn is made into is 10%-15%, and spandex content is 3% in fabric
Left and right.
With spandex fabric of the spandex core-spun yarn work through weft yarn, its elastic persistence is less than SPH at present, and made of SPH fibers
Elastic fabric soft fluffy elasticity is good, but stretching is yielding, and extension recovery performance is less than spandex.Therefore, existing spandex fabric face
Material is not the ideal fabric of elastic ready-made clothes.
Invention content
For the above drawbacks described above of the existing technology, the present invention proposes that one kind both has and stretches rebound and three-dimensional sense,
The comfortableness and security for increasing clothes also have many advantages, such as the cotton-polyester blend that quality is high, cloth cover is well-pressed, cotton polyester interwoven spandex fabric
Fabric.
The present invention forms four-side elasticity fabric with cotton-polyester blend or cotton polyester interwoven, and fabric washes size changing rate through broadwise
It is -4.0%~0%, difference is less than 2% between warp-wise and broadwise shrink, determines power elongation >=12% through broadwise, and bullet is stretched through broadwise
Property response rate >=55%, scald after flatness >=4.0 grade.
The above four-side elasticity fabric of the present invention both have extremely strong stretching rebound and three-dimensional sense, can increase clothes comfort and
Safety also has the advantages that quality is high, cloth cover is well-pressed, is suitable for high-grade clothing.
The present invention is another object is that propose the long vehicle dyeing producer of the above cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric
Method.
Production method of the present invention includes that fabric is singed successively, cold dome, bleaching, mercerising, a preshrunk, disperses to beat
Bottom, high-temperature shaping color development, reduction cleaning, set cotton, sizing and secondary preshrunk.
Present invention process facilitates production operation, excellent product performance, be fully achieved garment production superior quality index and
Safe performance indexes, especially suitable for high-grade dress shell fabric.
Further, tension≤0.2MPa of cloth cover when the present invention bleaches.Warp-wise tension cannot be too small in production process,
Ensure that cloth cover is smooth, but tension again cannot be excessive, anti-influence warp-wise elasticity, final tracking production determines that tension is controlled by 0.2MPA
System not only can guarantee cloth cover without wrinkle strip but also can ensure that elasticity is injury-free.
In order to ensure fabric quality and elasticity are injury-free, tension≤0.2MPa of cloth cover when mercerising.
The speed of preshrunk is 40~60m/min, and shrinkage control is 15%~17%, rubber blanket temperature≤120 DEG C.
Speed is determined according to cropping contracting cloth situation, it is ensured that is shunk up to standard;To ensure feel and fabric appearance quality control rubber blanket temperature
It cannot be high.
In order to ensure fabric quality and elasticity are injury-free, tension≤0.2MPa of cloth cover when reduction cleaning.
In order to ensure fabric quality and elasticity are injury-free, tension≤0.2MPa of cloth cover when covering cotton.
The speed of secondary preshrunk is 40~60m/min, and shrinkage control is 15%~17%, rubber blanket temperature≤120 DEG C.
Speed is 30m/min when high-temperature shaping color development, and temperature is 185~190 DEG C, and overfeeding 15% is subject to cropping filling density.
Board overfeeding is determined according to cropping filling density, requires tracking to determine drying chamber further according to the color development temperature and elastic index of disperse dyes
Temperature.
The institutional framework that present invention process is suitable for fabric is one kind in plain weave, Fang Ping, satin weave or jacquard weave.
Specific implementation mode
One, cotton-polyester blend spandex fabric dyed shell fabrics:
Fabric specification:Yarn count 45/40D(60%C, 40%T)×45/40D(60%C, 40%T), density 83 × 70, institutional framework:It is flat
Line.
1, the technological process of production:Singe, cold dome, bleaching(Cold dome), mercerising, give contracting, dispersion bottoming, high-temperature shaping, reduction
Cleaning, shapes, gives contracting at set cotton.
It singes:Speed 120m/min;Burner 2, flame intensity 12, mode of singing is to burning;Cropping must assure that cloth cover is burnt
For capillary effect fruit up to 4 grades, cloth cover is bright and clean
Cold dome:Speed 60m/min;Padding machine pressure 0.15KG;Working solution:Refining agent 6g/l, dispersant 2g/l, stabilizer 8g/l,
Hydrogen peroxide 18g/l, alkali dense 25g/l, remaining is water.Make the test bleaching after banking up 24 hours.This process main purpose is to utilize chemistry
Auxiliary agent makes fabric fully react, and is convenient for the removal of slurry.
Bleaching:Working solution:Refining agent 3g/l, stabilizer 10g/l, dispersant 2g/l, hydrogen peroxide 5g/l, alkali dense 3g/l,
Yu Weishui.Tension≤0.2MPa;95 DEG C of washing temperature banks up 98 DEG C, stacking time 30min of temperature, makes the abundant oxygen of hydrogen peroxide
Change reaction, more effectively remove fabric surface impurity, improves semi-products whiteness.
Mercerising:Fabric stability is improved, broadwise is stablized rich in silky gloss using fabric is made after the alkali dense mercerising of 200g/l
It shrinks.Tension≤0.2MPa of cloth cover when mercerising.
Preshrunk:Speed 40m/min;Contracting cloth rate 15%;Rubber blanket temperature≤120 DEG C.Cropping latitudinal density is 80
Root.Purpose improves warp-wise washing shrinkage.
Disperse bottoming:Using overflow dyeing machine front truck terylene dispersion dyeing, warp-wise tension is controlled, reduces the shadow to shrink to warp-wise
It rings;85 DEG C of drying room temperature, speed 40m/min.
High-temperature shaping color development:Speed 30m/min;190 DEG C of drying room temperature;Overfeeding 15%;Filling density 80.It is beaten using forming machine
Overfeeding high temperature, which bakes, makes its abundant color development.
Reduction cleaning:Speed 50m/min;Working solution:Caustic soda 50g/l, sodium hydrosulfite 50g/l, remaining is water.Steamer temperature
120 DEG C, 95 DEG C of washing temperature, tension≤0.2MPa of cloth cover.Ensure that washing is abundant, fastness is uniform.
Cover cotton:Speed 40m/min;102 DEG C of steamer temperature;95 DEG C of washing temperature;Face tension≤0.2MPa.Select into
Mouth dyestuff keeps its fastness preferable, disclosure satisfy that customer demand.
Sizing:Speed 75m/min;Roll compacting 0.3MPa;110 DEG C of drying room temperature;Overfeeding 18%;It can also be wanted according to client's feel
It asks, softening agent appropriate is added in working solution.
Secondary preshrunk:Contracting cloth rate is determined according to shrink testing result, its shrink and feel is made to reach customer requirement.Speed
For 60m/min, shrinkage control is 17%, rubber blanket temperature≤120 DEG C.
2, product quality:
Trimmed size:45/40D(60%C, 40%T)×45/40D(60%, C40%T), density 120 × 80;Effective gate 47 ".
Make appearance quality inside and outside fabric that can meet customer requirement by process above flow.
According to《ASTM D3107-2007(2011)The standard test method of stretch yarn woven fabric tensile property》Progress in
In quality test, power elongation >=12% is determined through broadwise, through broadwise tensile elasticity response rate >=55%, scald rear flatness up to 4.0
Grade.
According to《AATCC135-2015(3)IIIA(iii)3X》Water-wash test is carried out, it is -4.0% that warp-wise, which washes size changing rate,
It is -3.0% that broadwise, which washes size changing rate, and difference is less than 2% between warp-wise and broadwise shrink, flatness >=4.0 grade after scalding.
Two, cotton polyester interwoven spandex fabric dyed shell fabrics:
Fabric specification:Warp-wise yarn count 40, ingredient cotton, broadwise yarn count 45/40D, ingredient wash packet spandex thread entirely, density 83*70,
Institutional framework:Fang Ping.
1, the technological process of production:Singe, cold dome, bleaching(Cold dome), mercerising, give contracting, dispersion bottoming, high-temperature shaping, reduction
Cleaning, shapes, gives contracting at set cotton.
It singes:Speed 120m/min;Burner 2;Flame intensity 12;Mode of singing is to burning.Cropping must assure that cloth cover is burnt
For capillary effect fruit up to 4 grades, cloth cover is bright and clean.
Cold dome:Speed 60m/min;Padding machine pressure:0.15kg;Working solution:Refining agent 6g/l, dispersant 2g/l, stabilizer
8g/l, hydrogen peroxide 18g/l, alkali dense 25g/l, remaining is water.Make the test bleaching after banking up 24 hours.This process main purpose is to utilize
Chemical assistant makes fabric fully react, and is convenient for the removal of slurry.
Bleaching:Working solution:Refining agent 3g/l, stabilizer 10g/l, dispersant 2g/l, hydrogen peroxide 5g/l, alkali dense 3g/l,
Yu Weishui.Tension≤0.2MPa;Stacking time 30min;Bank up 98 DEG C of temperature, 95 DEG C of washing temperature.Main purpose removal is knitted
Object surface impurity improves semi-products whiteness.
Mercerising:Fabric stability is improved, broadwise is stablized rich in silky gloss using fabric is made after the alkali dense mercerising of 200g/l
It shrinks.Tension≤0.2MPa of cloth cover when mercerising.
Preshrunk:Speed 60m/min;Contracting cloth rate 17%;Rubber blanket temperature≤120 DEG C;Cropping latitudinal density 80,
Warp-wise is improved to shrink.
Disperse bottoming:85 DEG C of drying room temperature;Speed 40m/min.Using overflow dyeing machine front truck terylene dispersion dyeing, warp-wise is controlled
Tension reduces the influence shunk to warp-wise.
High-temperature shaping color development:Speed 30m/min;185 DEG C of drying room temperature;Overfeeding 25%;Filling density 80.It is beaten using forming machine
Overfeeding high temperature, which bakes, makes its abundant color development.
Reduction cleaning:Speed 50m/min;Working solution:Caustic soda 50g/l, sodium hydrosulfite 50g/l, remaining is water.Steamer temperature
120℃;95 DEG C of washing temperature;Tension≤0.2MPa of cloth cover.Ensure that washing is abundant, fastness is uniform.
Cover cotton:Speed 40m/min;102 DEG C of steamer temperature;95 DEG C of washing temperature;Face tension≤0.2MPa.Select into
Mouth dyestuff keeps its fastness preferable, disclosure satisfy that customer demand.
Sizing:Speed 75m/min;Roll compacting:0.3MPa;110 DEG C of drying room temperature;Overfeeding 18%.It can also be wanted according to client's feel
It asks and softening agent appropriate is added in working solution.
Secondary preshrunk:Contracting cloth rate is determined according to shrink testing result, its shrink and feel is made to reach customer requirement.Speed is
40m/min, shrinkage control is 15%, rubber blanket temperature≤120 DEG C.
2, product quality:
Trimmed size:40*45/40D, thread count 120 × 80;Effective gate 47 ".
Make appearance quality inside and outside fabric that can meet customer requirement by process above flow.
According to《ASTM D3107-2007(2011)The standard test method of stretch yarn woven fabric tensile property》, progress in
It is testing, is determining power elongation >=12% through broadwise, through broadwise tensile elasticity response rate >=55%, flatness is up to 4.0 grades after scalding.
According to《AATCC135-2015(3)IIIA(iii)3X》Carry out water-wash test, warp-wise wash size changing rate be-
3.5%, it is -2.0% that broadwise, which washes size changing rate, and difference is less than 2% between warp-wise and broadwise shrink, flatness >=4.0 after scalding
Grade.
Claims (10)
1. cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric, it is characterised in that:It is -4.0%~0% through broadwise washing size changing rate,
Difference is less than 2% between warp-wise and broadwise are shunk;Determine power elongation >=12% through broadwise, through broadwise tensile elasticity response rate >=
55%, flatness >=4.0 grade after scalding.
2. the long vehicle dyeing production of cotton-polyester blend as described in claim 1, cotton polyester interwoven four-side elasticity fabric, feature exist
In:Including fabric is singed successively, cold dome, bleaching, mercerising, a preshrunk, dispersion bottoming, high-temperature shaping color development, restore
Cleaning, set cotton, sizing and secondary preshrunk.
3. the long vehicle dyeing production of cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric, feature exist according to claim 2
In:Tension≤0.2MPa of cloth cover when bleaching.
4. the long vehicle dyeing production of cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric, feature exist according to claim 2
In:Tension≤0.2MPa of cloth cover when mercerising.
5. the long vehicle dyeing production of cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric, feature exist according to claim 2
In:The speed of preshrunk is 40~60m/min, and shrinkage control is 15%~17%, rubber blanket temperature≤120 DEG C.
6. the long vehicle dyeing production of cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric, feature exist according to claim 2
In:Tension≤0.2MPa of cloth cover when reduction cleaning.
7. the long vehicle dyeing production of cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric, feature exist according to claim 2
In:Tension≤0.2MPa of cloth cover when covering cotton.
8. the long vehicle dyeing production of cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric, feature exist according to claim 2
In:The speed of secondary preshrunk is 40~60m/min, and shrinkage control is 15%~17%, rubber blanket temperature≤120 DEG C.
9. the long vehicle dyeing production of cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric, feature exist according to claim 2
In:Speed is 30m/min when high-temperature shaping color development, and temperature is 185-190 DEG C, and overfeeding 15% is subject to cropping filling density.
10. the long vehicle dyeing production of cotton-polyester blend, cotton polyester interwoven four-side elasticity fabric according to claim 2, feature
It is:The institutional framework of the fabric is one kind in plain weave, Fang Ping, satin weave or jacquard weave.