CN108746980A - Hot isostatic press welding titanium target and aluminium jacket partition method - Google Patents
Hot isostatic press welding titanium target and aluminium jacket partition method Download PDFInfo
- Publication number
- CN108746980A CN108746980A CN201810673526.4A CN201810673526A CN108746980A CN 108746980 A CN108746980 A CN 108746980A CN 201810673526 A CN201810673526 A CN 201810673526A CN 108746980 A CN108746980 A CN 108746980A
- Authority
- CN
- China
- Prior art keywords
- aluminium jacket
- welding
- titanium
- hot isostatic
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of hot isostatic press welding titanium targets and aluminium jacket partition method, are related to the technical field of aluminium jacket welding, and one layer of separation layer do not reacted with target or that reaction is insufficient is equipped with before being included in the welding of aluminium jacket, between titanium target material and aluminium jacket;After Diffusion Welding, directly separation layer and aluminium jacket are torn from titanium target material surface.The purpose of the present invention is to provide a kind of hot isostatic press welding titanium targets and aluminium jacket partition method, to avoid during Hot Isostatic Pressing Diffusion aluminium jacket together with product titanium diffusion into the surface, before the welding of aluminium jacket, on product titanium surface and separation layer that pad last layer is not reacted with target on aluminium jacket contact surface or that reaction is not enough, directly separation layer+aluminium jacket can be torn from titanium surface after product diffusion welding, and separation layer does not influence titanium target material.
Description
Technical field
The present invention relates to aluminium jacket welding technology field, more particularly, to a kind of hot isostatic press welding titanium target and aluminium jacket every
From method.
Background technology
Target needs to carry out jacket welding before Hot Isostatic Pressing Diffusion with backboard, that is, target and backboard are assembled
It is put into jacket well, then will carry out welded seal with argon arc welding.It is vacuumized after being welded, the target in jacket is made to be in
Airtight vacuum state.General common jacket material is aluminium jacket, and the welding temperature for commonly using target is 200 DEG C to 1000 DEG C.
For target with aluminium jacket with backboard under the hot isostatic pressing of certain temperature, target and backboard welding surface are diffused in one
It rises, but jacket can be also diffused with target or backboard simultaneously, leads to aluminium jacket and target (titanium after hot isostatic press welding
Material) it is difficult to remove.Turning is needed to remove jacket after valuable titanium target and jacket diffusion, since hot isostatic pressing is inevitable
Ground can make product generate certain deformation, this is resulted in during turning removes jacket, and also meeting is to titanium face, to cause original
The waste of material cost.
The information for being disclosed in the background technology part is merely intended to deepen understanding of the general background technology to the present invention, and
It is not construed as recognizing or implying in any form that the information constitutes the prior art known to those skilled in the art.
Invention content
The purpose of the present invention is to provide a kind of hot isostatic press welding titanium targets and aluminium jacket partition method, to avoid in heat etc.
Aluminium jacket is together with product titanium diffusion into the surface in static pressure diffusion welding process, before the welding of aluminium jacket, product titanium surface with
The separation layer that last layer is not reacted with target or reaction is not enough is padded on aluminium jacket contact surface, it can after product diffusion welding
Directly separation layer+aluminium jacket is torn from titanium surface, and separation layer does not influence titanium target material.
To achieve the above object, the present invention provides following technical scheme:
A kind of hot isostatic press welding titanium target of present invention offer and aluminium jacket partition method, including:
Aluminium jacket welding before, between titanium target material and the aluminium jacket be equipped with one layer it is react with target or react do not fill
The separation layer divided;
After Diffusion Welding, directly the separation layer and the aluminium jacket are torn from the titanium target material surface.
Further, the separation layer includes stainless steel substrates.
Further, the stainless steel substrates material is 304 stainless steels.
Further, the thickness of the stainless steel substrates is 0.1mm-0.2mm.
Further, the stainless steel substrates are covered in the titanium target material and deviate from backboard side, and the ruler of the stainless steel substrates
It is very little identical as the size of the backboard.
Hot isostatic press welding titanium target provided by the invention has the advantages that with aluminium jacket partition method:
A kind of hot isostatic press welding titanium target of present invention offer and aluminium jacket partition method, before being included in the welding of aluminium jacket, titanium
One layer of separation layer do not reacted with target or that reaction is insufficient is equipped between target and aluminium jacket;After Diffusion Welding, directly will
Separation layer and aluminium jacket are torn from titanium target material surface.
Using hot isostatic press welding titanium target provided by the invention and aluminium jacket partition method, to avoid spreading in hot isostatic pressing
Aluminium jacket before the welding of aluminium jacket, connects together with product titanium diffusion into the surface on product titanium surface and aluminium jacket in welding process
Pad last layer react with the target or separation layer that is not enough of reaction in contacting surface, product diffusion weld after can directly by every
Absciss layer+aluminium jacket is torn from titanium surface, and separation layer does not influence titanium target material, due to avoiding the turning jacket after Diffusion Welding
Turning causes the waste of target source material cost and turning aluminium jacket that processing cost is caused to waste to titanium target material surface.
Other features and advantages of the present invention will illustrate in the following description, also, partly become from specification
It obtains it is clear that understand through the implementation of the invention.The purpose of the present invention and other advantages are in specification, claims
And specifically noted structure is realized and is obtained in attached drawing.
Description of the drawings
It, below will be to specific in order to illustrate more clearly of the specific embodiment of the invention or technical solution in the prior art
Embodiment or attached drawing needed to be used in the description of the prior art are briefly described, it should be apparent that, in being described below
Attached drawing is some embodiments of the present invention, for those of ordinary skill in the art, before not making the creative labor
It puts, other drawings may also be obtained based on these drawings.
Fig. 1 is hot isostatic press welding titanium target provided in an embodiment of the present invention and titanium target, separation layer in aluminium jacket partition method
With the structural schematic diagram of aluminium jacket.
Icon:1- aluminium jackets;2- backboards;3- titanium target materials;4- separation layers.
Specific implementation mode
Technical scheme of the present invention is clearly and completely described below in conjunction with attached drawing, it is clear that described implementation
Example is a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill
The every other embodiment that personnel are obtained without making creative work, shall fall within the protection scope of the present invention.
In the description of the present invention, it should be noted that term "center", "upper", "lower", "left", "right", "vertical",
The orientation or positional relationship of the instructions such as "horizontal", "inner", "outside" be based on the orientation or positional relationship shown in the drawings, merely to
Convenient for the description present invention and simplify description, do not indicate or imply the indicated device or element must have a particular orientation,
With specific azimuth configuration and operation, therefore it is not considered as limiting the invention.In addition, term " first ", " second ",
" third " is used for description purposes only, and is not understood to indicate or imply relative importance.
In the description of the present invention, it should be noted that unless otherwise clearly defined and limited, term " installation ", " phase
Even ", " connection " shall be understood in a broad sense, for example, it may be being fixedly connected, may be a detachable connection, or be integrally connected;It can
Can also be electrical connection to be mechanical connection;It can be directly connected, can also indirectly connected through an intermediary, Ke Yishi
Connection inside two elements.For the ordinary skill in the art, above-mentioned term can be understood at this with concrete condition
Concrete meaning in invention.
The specific implementation mode of the present invention is described in detail below in conjunction with attached drawing.It should be understood that this place is retouched
The specific implementation mode stated is merely to illustrate and explain the present invention, and is not intended to restrict the invention.
Term is explained:
Diffusion Welding (Diffusion Bonding, abbreviation DB):Weldment is fitted closely, under certain temperature and pressure
It is kept for a period of time, the atom between contact surface is made mutually to diffuse to form the welding method of connection.
Hot isostatic press (Hot Isostatic Press, abbreviation HIP):Hot isostatic press is to utilize hot isostatic pressing technique
In high temperature and pressure sealing container, using high-pressure inert gas as medium, the sintering blank or different to powder therein or compacting
Kind metal applies each to equal isostatic pressure, the instrument and equipment of the method for formation high-compactness blank (or part).Hot isostatic press
It has become high temperature powder metallurgy, eliminate casting defect, dissimilar metal diffusion connection, Novel engineering ceramics, composite material, fire proofed wood
The advanced forming techniques such as material, high-strength graphite carbon and advanced material develop the key equipment in field.
Aluminium jacket:A kind of closed container needs jacket being evacuated to certain vacuum degree ability after welding for placing product
Hot isostatic pressing is carried out, common material is aluminium.
Fig. 1 is please referred to, below in conjunction with attached drawing to hot isostatic press welding titanium target provided in an embodiment of the present invention and aluminium jacket
Partition method elaborates.
The embodiment provides a kind of hot isostatic press welding titanium targets and aluminium jacket partition method, including:
Aluminium jacket 1 welding before, between titanium target material 3 and aluminium jacket 1 be equipped with one layer it is react with target or react do not fill
The separation layer 4 divided;
After Diffusion Welding, directly separation layer 4 and aluminium jacket 1 are torn from 3 surface of titanium target material.
Existing 1 welding technique of target aluminium jacket removal jacket is difficult, and turning is made to target material surface due to turning aluminium jacket 1
It is wasted at the noble metal target material cost of raw material.The present invention is exactly to solve aluminium jacket 1 and target titanium table in diffusion welding process
The problem of face is spread together.Turning causes target source material to target titanium surface due to avoid the turning jacket after Diffusion Welding
Cost wastes and turning aluminium jacket 1 causes processing cost to waste, and consideration pads last layer on aluminium jacket 1 and target contact surface
Isolated material.
The hot isostatic press welding titanium target that embodiment using the present invention provides and aluminium jacket partition method, to avoid in heat etc.
Aluminium jacket 1 is together with product titanium diffusion into the surface in static pressure diffusion welding process, before the welding of aluminium jacket 1, in product titanium target material 3
Surface and separation layer 4 that pad last layer is not reacted with target on 1 contact surface of aluminium jacket or that reaction is not enough, product diffusion
Directly separation layer 4+ aluminium jacket 1 can be torn from titanium surface after welding, and separation layer 4 does not influence titanium target material 3, avoid because
Turning jacket after Diffusion Welding and turning cause that target source material cost wastes and turning aluminium jacket 1 is made to 3 surface of titanium target material
It is wasted at processing cost.
In the optional scheme of the present embodiment, further, separation layer 4 includes stainless steel substrates.
In the optional scheme of the present embodiment, further, stainless steel substrates material is 304 stainless steels.
In the optional scheme of the present embodiment, further, the thickness of stainless steel substrates is 0.1mm-0.2mm.
In at least one embodiment, the thickness of stainless steel substrates be 0.1mm-0.2mm, such as can with but be not limited only to for
0.1mm、0.11mm、0.12mm、0.13mm、0.14mm、0.15mm、0.16mm、0.17mm、0.18mm、0.19mm、0.2mm。
In the optional scheme of the present embodiment, further, stainless steel substrates are covered in titanium target material 3 and deviate from 2 side of backboard, and
The size of stainless steel substrates is identical as the size of titanium target material 3.
In at least one embodiment, stainless steel substrates be covered in titanium target material 3 deviate from 2 side of backboard, and positioned at titanium target material 3 with
Between aluminium jacket 1, the diameter of stainless steel substrates is identical as 3 race diameter of titanium target material.
The hot isostatic press welding titanium target that the embodiment of the present invention provides is with aluminium jacket partition method, and 3 surface of titanium target material is not
Turning.To avoid the aluminium jacket 1 during Hot Isostatic Pressing Diffusion from being welded in aluminium jacket 1 together with product titanium diffusion into the surface
Before connecing, product titanium surface on 1 contact surface of aluminium jacket pad last layer react with target or react be not enough it is stainless
Steel disc.It is not enough in product with last layer is not reacted with target or reaction is padded on jacket contact surface before aluminium jacket 1 welds
Stainless steel substrates, directly stainless steel substrates+aluminium jacket 1 can be torn from titanium surface after product diffusion welding, and stainless steel is to target
Do not influence.
The hot isostatic press welding titanium target of the present invention is illustrated with aluminium jacket partition method above, still, the present invention
Be not limited to above-mentioned specific embodiment, without departing from the scope of the claims, can carry out various deformations or
Change.The invention includes various changes and modifications within the scope of the claims.
Finally it should be noted that:The above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations;To the greatest extent
Pipe is described in detail invention with reference to foregoing embodiments, it will be understood by those of ordinary skill in the art that:It is still
Either which part or all technical features can be carried out so that technical scheme described in the above embodiments is modified
Equivalent replacement;And these modifications or replacements, it does not separate the essence of the corresponding technical solution various embodiments of the present invention technical side
The range of case.
Claims (5)
1. a kind of hot isostatic press welding titanium target and aluminium jacket partition method, which is characterized in that including:
Aluminium jacket welding before, between titanium target material and the aluminium jacket be equipped with one layer it is react with target or react it is insufficient
Separation layer;
After Diffusion Welding, directly the separation layer and the aluminium jacket are torn from the titanium target material surface.
2. hot isostatic press welding titanium target according to claim 1 and aluminium jacket partition method, which is characterized in that the isolation
Layer includes stainless steel substrates.
3. hot isostatic press welding titanium target according to claim 2 and aluminium jacket partition method, which is characterized in that described stainless
Steel disc material is 304 stainless steels.
4. hot isostatic press welding titanium target according to claim 2 and aluminium jacket partition method, which is characterized in that described stainless
The thickness of steel disc is 0.1mm-0.2mm.
5. hot isostatic press welding titanium target according to claim 2 and aluminium jacket partition method, which is characterized in that described stainless
Steel disc is covered in the titanium target material and deviates from backboard side, and the size of the stainless steel substrates is identical as the size of the backboard.