CN108690545A - Fr阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料 - Google Patents
Fr阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料 Download PDFInfo
- Publication number
- CN108690545A CN108690545A CN201710259529.9A CN201710259529A CN108690545A CN 108690545 A CN108690545 A CN 108690545A CN 201710259529 A CN201710259529 A CN 201710259529A CN 108690545 A CN108690545 A CN 108690545A
- Authority
- CN
- China
- Prior art keywords
- retardant
- fire
- aromatic polyamide
- polyester film
- polyamide paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
FR阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料是由一层聚酯薄膜两面涂以改性阻燃胶和上下表面两层耐高温聚芳酰胺纤维纸经两次阻燃改性,选用进口R级聚胺酯胶粘剂复合而成。其阻燃性通过UL94V0测试。FR阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料是根据市场需求而产生的新一代环保无卤阻燃材料改性的一种绝缘材料。具有价格低、阻燃性能好、介电性能、机械性能高等特点,有着极高的市场应用前景。FR阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料的耐热等级为H级(180℃),具有良好的机械性能,及良好的电气强度,并有良好的耐酸碱腐蚀能力。被广泛应用于电机、变压器、电抗器、新能源产业、生活电器等领域。
Description
技术领域
本发明是新一代环保无卤阻燃材料改性的一种绝缘材料。具有价格低、阻燃性能好、介电性能、机械性能高等特点,有着极高的市场应用前景。被广泛应用于电机、变压器、电抗器、新能源产业、汽车启动电机、生活电器等领域。
背景技术
FR阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料是由一层聚酯薄膜两面涂以改性阻燃胶和上下表面两层耐高温聚芳酰胺纤维纸经两次阻燃改性,选用进口R级聚胺酯胶粘剂复合而成。其阻燃性有着几乎同杜邦T410产品一致的效果,通过UL94V0测试,但其介电性能和机械性能优于杜邦T410产品,其材料价格仅为杜邦T410价格的60-70%。FR阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料于2014年进入市场,是在美国杜邦410产品垄断中国市场60余年的情况下,根据市场需求而产生的新一代环保无卤阻燃材料改性的一种绝缘材料。具有价格低、阻燃性能好、介电性能、机械性能高等特点,有着极高的市场应用前景。被广泛应用于电机、变压器、电抗器、新能源产业、汽车启动电机、生活电器等领域。
FR阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料的耐热等级为H级(180℃),具有良好的机械性能,如抗拉强度和边缘防撕裂性能以及良好的电气强度,其表面平滑,并且对绝缘漆有良好的吸附性。
FR阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料可以与几乎所有的树脂,清漆兼容,比如聚酰亚胺、环氧物类、聚酯类、酚类物质、合成橡胶等,并有良好的耐酸碱腐蚀能力。FR阻燃聚芳酰胺纤维纸聚酯薄膜柔软复合材料完全符合UL94V0的阻燃标准,主要用于有阻燃要求的电机、电器等领域,同时可用于特种变压器、特种电机、汽车电机或其它电器作槽间绝缘、层间绝缘、匝间绝缘、衬垫绝缘等。是一种较为理想的T410的替代产品。
发明内容
(1)、基于成本的考虑,排除阻燃聚酯薄膜和聚酰亚胺薄膜,选用非阻燃普通聚酯薄膜作为改进目标;
(2)、芳纶纤维纸选用国产芳纶纤维纸;
(3)、粘结剂选用进口、耐高温R级HERBERTS-EPS7146-Hardener Z双组份聚氨酯胶粘剂;
(4)、阻燃材料选用进口Doher-9000和Doher-601阻燃剂:
Doher-9000阻燃剂是一种白色结晶粉末材料,容易添加,阻燃效率高、添加量小,与聚合物及树脂的相容性好,热稳定性能优异,其热分解温度≥270℃,耐水性好,无析出、迁移回潮及水滑现象,同时具有优异的介电性能和机械性能。
Doher-601阻燃剂是一种油状液体材料也具有容易添加,阻燃效率高、添加量小等特点,同时具有耐水性好,尤其在280℃高温下在物体中能长期保留95%以上的含量。
上述两种阻燃剂均为添加型无卤阻燃材料。
具体实施方式
将配方量的材料按顺加入搅拌罐,开启搅拌电机,搅拌30min以上,待树脂混合均匀后,将树脂打人高位槽,放入复合机胶槽,待胶液达到规定的液面高度后方可开机生产。
(2)、生产工艺:
a)、Doher-601取树脂量的1.4%用15kg醋酸乙酯调匀,通过复合机均匀的涂敷在聚酯薄膜的两面,进行第一次改性;
b)、将按上述配方量配好的胶粘剂再次通过复合机均匀的涂敷在聚酯薄膜的上下表面,经过80℃、85℃、80℃的烘道将上下两层芳纶纤维纸经过复合辊复合而成。
Claims (2)
1.胶粘剂配方:(按重量百分比)
EPS7146: 38.99%
Hardener Z: 3.89%
Doher-9000: 5.57%
Doher-601: 2.80%
醋酸乙酯: 48.75%。
2.生产工艺:
a)、Doher-601取树脂量的1.4%用15kg醋酸乙酯调匀,通过复合机均匀的涂敷在聚酯薄膜的两面,进行第一次改性。
b)、将按上述配方量配好的胶粘剂再次通过复合机均匀的涂敷在聚酯薄膜的上下表面,经过80℃、85℃、80℃的烘道将上下两层芳纶纤维纸经过复合辊复合而成。