CN106244080A - 一种高效阻燃的双组份聚氨酯胶黏剂 - Google Patents
一种高效阻燃的双组份聚氨酯胶黏剂 Download PDFInfo
- Publication number
- CN106244080A CN106244080A CN201510730284.4A CN201510730284A CN106244080A CN 106244080 A CN106244080 A CN 106244080A CN 201510730284 A CN201510730284 A CN 201510730284A CN 106244080 A CN106244080 A CN 106244080A
- Authority
- CN
- China
- Prior art keywords
- retardant
- polyurethane adhesive
- component polyurethane
- weight portion
- highly effective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高效阻燃的双组份聚氨酯胶黏剂包含的组分和对应组分的重量份如下：聚酯多元醇40重量份；碳酸钙28重量份；阻燃剂20重量份；分子筛2重量份。该双组份聚氨酯胶黏剂即使加入了阻燃剂，也不会对原双组份聚氨酯胶黏剂的性能有明显的影响，大致保持原有的内聚力，粘结强度，颜色外观，黏度，适用时间，发泡率，主固配比。
Description
技术领域
本发明涉及胶黏剂行业技术领域，尤其涉及一种高效阻燃的双组份聚氨酯胶黏剂。
背景技术
在胶黏剂行业中，对胶黏剂性能的要求各种各样，阻燃是其中的一种。目前使用的阻燃剂有卤系，氮系，磷系，无机系几大类。
现有技术中对于聚氨酯胶黏剂适用的阻燃剂主要存在的问题是：1，阻燃剂型号繁多，各有特性，效果也各有不同，难以选择到合适的型号；2，双组份聚氨酯胶黏剂一般用到碳酸钙作为填料，这种填料对氮磷系的阻燃剂的阻燃效果有一定的影响；3，液体阻燃剂有一定的增塑作用，添加后的双组份聚氨酯胶黏剂胶体变软，内聚力受到影响；4，卤系的阻燃剂阻燃效果较好，但是在燃烧与加热过程中会释放有害物质，威胁到人类身体的健康、环境和下一代子孙，这类阻燃剂环保问题一直有争议，不推荐使用；5，无机阻燃剂绿色环保，燃烧无烟雾，但是阻燃效能低下，添加量大，且与有机物热塑性树脂相容性差，不易分散，分散后亲和力也不好，影响材料的抗冲击性能，丧失柔韧性；6，含水份的阻燃剂，其中的水分子与异氰酸酯反应生成二氧化碳气体，对双组份聚氨酯的发泡率影响很大。
发明内容
为了解决现有技术中的问题，本发明的目的是提供一种阻燃效果好、无滴落物的高效阻燃的双组份聚氨酯胶黏剂。该双组份聚氨酯胶黏剂即使加入了阻燃剂，也不会对原双组份聚氨酯胶黏剂的性能有明显的影响，大致保持原有的内聚力，粘结强度，颜色外观，黏度，适用时间，发泡率，主固配比。
为实现上述目的，本发明采用以下技术方案：一种高效阻燃的双组份聚氨酯胶黏剂包含的组分和对应组分的重量份如下：
聚酯多元醇 40重量份；
碳酸钙
28重量份；
阻燃剂
20重量份；
分子筛
2重量份。
优选地方案，所述阻燃剂为氮磷系阻燃剂。
本发明为有阻燃性能的双组份聚氨酯胶黏剂，主要特点有：1， 使用的阻燃剂不对原双组份聚氨酯胶黏剂的性能有明显的影响，大致保持原有的内聚力，粘结强度，颜色外观，黏度，适用时间，发泡率，主固配比；2，阻燃效果可以达到最佳的V0级，离明火自熄且无滴落物；3，在阻燃剂的选择上也注重环保方面的要求，卤素，重金属，有机挥发物的含量均在国家相关标准规定的下限之下；4，工艺简单易操作，阻燃剂采用氮磷系固体粉末状产品，避免了其他系列的阻燃剂的缺陷，固体粉末粒径小，防止胶液沉降，颗粒不均匀的情况。
另外，其还具有以下优点：
1.优异的阻燃性能，可达V0级，离火自熄无滴落物，燃烧烟雾小，可以满足各种外墙保温一体板，防火门，室内造型装饰板等产品的防火要求；
2.环保无毒，本配方采用的配料均能要求达到国内环保要求；
3．双组份聚氨酯胶黏剂的理化性能不受影响；
4. 本配方涉及的原材料来源广泛，聚酯多元醇，碳酸钙，分子筛，氮磷系阻燃剂，均可以用其他同类原料代替。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明了，下面结合具体实例，对本发明进一步详细说明。应该理解，这些描述只是示例性的，而并非要限制本发明的范围。此外，在以下说明中，省略了对公知结构和技术的描述，以避免不必要地混淆本发明的概念。
实施例1，一种高效阻燃的双组份聚氨酯胶黏剂包含以下组分：
聚酯多元醇 40千克；
碳酸钙
28千克；
阻燃剂
20千克；
分子筛
2千克。
上述材料均市售可得，其中，所述聚酯多元醇从山西凯希瑞科技股份有限公司购买所得。所述碳酸钙由新乡市源丰钙业有限公司购买。所述阻燃剂为氮磷系阻燃剂，从广州冠佑化工科技有限公司处购买。所述分子筛从南京永成分子筛有限公司处购得。当然，本配方涉及的原材料来源广泛，聚酯多元醇，碳酸钙，分子筛，氮磷系阻燃剂，均可以用其他同类原料代替。
调配工艺为：将上述配料依次常温常压加入搅拌罐，搅拌均匀成细腻无颗粒乳液出料。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明的保护范围，凡在本发明的精神和原则之内，所作的任何修改、等同替换、均包含在本发明的保护范围之内。
Claims (2)
1.一种高效阻燃的双组份聚氨酯胶黏剂,其特征在于：所述高效阻燃的双组份聚氨酯胶黏剂包含的组分和对应组分的重量份如下：
聚酯多元醇
40重量份；
碳酸钙
28重量份；
阻燃剂
20重量份；
分子筛
2重量份。
2. 如权利要求1所述的一种高效阻燃的双组份聚氨酯胶黏剂,其特征在于：所述阻燃剂为氮磷系阻燃剂。